The content of the invention
The embodiment of the present invention provides a kind of preparation method of green sweater made of cotton yarns, is carried out for solving green bafta in the prior art
When dress designing is developed, green sweater made of cotton yarns has that green sweater made of cotton yarns feel is poor, obtaining color depth, poor, size is steady according to conventional washing process
Qualitative poor technical problem, reach improve green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect.
The application provides following technical scheme by the embodiment of the application:
A kind of preparation method of green sweater made of cotton yarns, during green sweater made of cotton yarns is made by green cotton fiber, including:It is right
The green cotton fiber is arranged;The green cotton fiber put in order is subjected to spinning fabric, green bafta is formed;Will be described green
Bafta carries out dress designing exploitation and composition, forms green sweater made of cotton yarns;The green sweater made of cotton yarns is immersed in the working solution for adding softening agent
In.
Further, it is described that the green cotton fiber progress arrangement is included:Pre-treatment is carried out to the green cotton fiber;To institute
State green cotton fiber and carry out chloride treatment and soft treatment.
Further, it is described that the green cotton fiber put in order is subjected to spinning fabric, green bafta is formed, including:Will
The green cotton fiber put in order carries out colour-spun yarns with white cotton.
Further, it is described that pre-treatment is carried out to the green cotton fiber, including:Being positioned over concentration to the green cotton fiber is
In 0.5~20g/L treatment fluid, treatment time is 10-120min, and treatment temperature is 10-150 DEG C, and processing bath raio is 1:(5-
50)。
Further, it is described that chloride treatment and soft treatment are carried out to the green cotton fiber, including:Concentration is
0.5~20g/L chloride, concentration are 0.5~20g/L hydrophilic organic silicone softener, and by add acetic acid pH value for 4.5~
Within the scope of 7.5, and treatment time is 10-120min, and treatment temperature is 10-150 DEG C, and processing bath raio is 1:(5-50).
Further, it is described that the green cotton fiber put in order and white cotton are subjected to colour-spun yarns, including:The green cotton fiber is entered
The processing of row stoving process;The green cotton fiber is carried out grabbing cotton PROCESS FOR TREATMENT;Mixed cotton PROCESS FOR TREATMENT is carried out to the green cotton fiber,
Form mixed cotton;Opener PROCESS FOR TREATMENT is carried out to the mixed cotton;Cotton feeding process processing is carried out to the mixed cotton;The mixed cotton is carried out
Lap Technology processing;Carding process processing is carried out to the mixed cotton;Bar is carried out to the mixed cotton and PROCESS FOR TREATMENT is rolled up;To described mixed
Cotton carries out combing processing;Drawing process processing is carried out to the mixed cotton;Process of roving processing is carried out to the mixed cotton;To institute
State mixed cotton and carry out spinning process processing;Winding process processing is carried out to the mixed cotton.
Further, it is described that the green cotton fiber put in order and white cotton are subjected to colour-spun yarns, including:By it is described put in order it is green
Cotton fiber and 10~70% white cotton carry out colour-spun yarns.
Further, the preparation method also includes:The green sweater made of cotton yarns is subjected to desizing or arrangement of deoiling, green cotton is formed
Final products.
Further, it is described to be immersed in the green sweater made of cotton yarns in the working solution for adding softening agent, including:It is hydrophilic by 3~8%
Silicone softening agent dilutes in a small amount of water, then adds in 40 DEG C of working solutions, adjusts PH4.5-7.5, green sweater made of cotton yarns is put into,
Processing 10~30 minutes, the ﹕ of bath raio 1 (10~20).
The embodiment of the present invention has the beneficial effect that:
A kind of preparation method for green sweater made of cotton yarns that one embodiment of the invention is provided, it is whole by being carried out to the green cotton fiber
Reason;Then, the green cotton fiber put in order is subjected to spinning fabric, forms green bafta;Subsequently, by the green bafta
Dress designing exploitation and composition is carried out, green sweater made of cotton yarns is formed;Finally, the green sweater made of cotton yarns is immersed in the working solution for adding softening agent
In, reach improve green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect.
Embodiment one
To enable those skilled in the art to understand the present invention in more detail, the present invention is retouched in detail below in conjunction with accompanying drawing
State.
As described in Figure 1, Fig. 1 is a kind of preparation method of green sweater made of cotton yarns in one embodiment of the invention, applied to passing through green cotton
During fiber makes green sweater made of cotton yarns, including:
Step S110:The green cotton fiber is arranged;
Specifically, as shown in Fig. 2 step S110 includes to the green cotton fiber progress arrangement:
Step S111:Pre-treatment is carried out to the green cotton fiber;
Step S112:Chloride treatment and soft treatment are carried out to the green cotton fiber.
Wherein, step S111 carries out pre-treatment to the green cotton fiber includes:
The green cotton fiber is positioned in the treatment fluid that concentration is 0.5~20g/L, treatment time is 10-120min, place
It is 10-150 DEG C to manage temperature, and processing bath raio is 1:(5-50).
It is preferred that, it is to the preferred embodiment that the green cotton fiber carries out pre-treatment:
The green cotton fiber is positioned in the treatment fluid that concentration is 3g/L, treatment time is 30min, and treatment temperature is 80
DEG C, processing bath raio is 1:20.
Specifically, above-mentioned treatment fluid can be color cotton refining agent.Color cotton refining agent includes by weight percentage, 10-
25% secondary alkyl sulfonate, 15-40% isomeric alcohol polyethenoxy ether, 5-20% polyethers, 1-2% carboxylate chelating point
The water of powder and 30-65%.Secondary alkyl sulfonate is SAS salt or secondary alkyl sulfonic acid sylvite.Isomery alcohol polyoxyethylene
Ether is the polymer of isomery alcohol and oxirane, and structural formula is RO- (C2H4O) n H, R are C8, C11Or C13, n is 3,5,7 or 9.
Wherein, step S112:Chloride treatment and soft treatment are carried out to the green cotton fiber, including:
The hydrophilic organic silicone softener that chloride that concentration is 0.5~20g/L, concentration are 0.5~20g/L, and lead to
Cross plus acetic acid pH value be 4.5~7.5 within the scope of, and treatment time be 10-120min, treatment temperature be 10-150 DEG C, processing
Bath raio is 1:(5-50).
Specifically, above-mentioned chloride can be zinc chloride, and softening agent selects for the routine techniques of those skilled in the art
It can be achieved, the application is not specifically limited.
It is preferred that, it is described to be to the preferred embodiment that the green cotton fiber carries out chloride treatment and soft treatment:
The hydrophilic organic silicone softener that chloride that concentration is 3g/L, concentration are 5g/L, and by adding acetic acid pH value
Within the scope of 6-7, and treatment time is 20min, and treatment temperature is 50 DEG C, and processing bath raio is 1:20.
Step S120:The green cotton fiber put in order is subjected to spinning fabric, green bafta is formed;
Specifically, the green cotton fiber put in order is carried out spinning fabric by step S120, forms green bafta, bag
Include:The green cotton fiber put in order and white cotton are subjected to colour-spun yarns.
Specifically, the green cotton fiber put in order can carry out colour-spun yarns with 10~70% white cotton.Wherein, green cotton fiber is used
It after this preparation method, have passed through after the sufficient color development of comparison, the characteristics of with color stability, and then mixed give the white of different proportion
Cotton, can reach the product of a variety of color and lusters.
Wherein, as shown in figure 3, the preparation method that the green cotton fiber put in order is carried out into colour-spun yarns with white cotton includes:
Step S121:Stoving process processing is carried out to the green cotton fiber;
Step S122:The green cotton fiber is carried out grabbing cotton PROCESS FOR TREATMENT;
Step S123:Mixed cotton PROCESS FOR TREATMENT is carried out to the green cotton fiber, mixed cotton is formed;
Step S124:Opener PROCESS FOR TREATMENT is carried out to the mixed cotton;
Step S125:Cotton feeding process processing is carried out to the mixed cotton;
Step S126:Lap Technology processing is carried out to the mixed cotton;
Step S127:Carding process processing is carried out to the mixed cotton;
Step S128:Bar is carried out to the mixed cotton and PROCESS FOR TREATMENT is rolled up;
Step S129:Combing processing is carried out to the mixed cotton;
Step S1210:Drawing process processing is carried out to the mixed cotton;
Step S1211:Process of roving processing is carried out to the mixed cotton;
Step S1212:Spinning process processing is carried out to the mixed cotton;
Step S1213:Winding process processing is carried out to the mixed cotton.
Wherein, above-mentioned steps S121~step S1213 PROCESS FOR TREATMENT belongs to the routine techniques choosing of those skilled in the art
Select and can be achieved, therefore the application is no longer specifically described.
Step S130:The green bafta is subjected to dress designing exploitation and composition, green sweater made of cotton yarns is formed;
Specifically, the green bafta is carried out dress designing exploitation and composition by step S130, is formed green sweater made of cotton yarns, is belonged to
The routine techniques selection of those skilled in the art be can be achieved, therefore the application is no longer specifically described.
Step 140:The green sweater made of cotton yarns is immersed in the working solution for adding softening agent.
Specifically, the just described green sweater made of cotton yarns of step 140 is immersed in the working solution for adding softening agent, pass through present treatment
Technique, which can reach, improves green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect.
It is preferred that, it is described by the green sweater made of cotton yarns be immersed in plus softening agent working solution in preferred embodiment be:
3~8% (o.w.f) hydrophilic organic silicone softener dilutes in a small amount of water, then adds in 40 DEG C of working solutions, adjusts
PH4.5-7.5 is saved, green sweater made of cotton yarns is put into, is handled 10~30 minutes, the ﹕ of bath raio 1 (10~20).Sweatshirt vision after washing is certainly
So clean, soft comfortable, color and luster is soft.Specifically, above-mentioned working solution can be water.Wherein described (o.w.f) is On
weight the fabric。
Step S150:The green sweater made of cotton yarns is subjected to desizing or arrangement of deoiling, green cotton final products are formed.
Specifically, the green sweater made of cotton yarns is carried out desizing or arrangement of deoiling by step S150, forms green cotton final products, category
It can be achieved in the routine techniques selection of those skilled in the art, therefore the application is no longer specifically described.
In summary, a kind of preparation method for green sweater made of cotton yarns that the embodiment of the present invention is provided has the following technical effect that:
A kind of preparation method for green sweater made of cotton yarns that one embodiment of the invention is provided, it is whole by being carried out to the green cotton fiber
Reason;Then, the green cotton fiber put in order is subjected to spinning fabric, forms green bafta;Subsequently, by the green bafta
Dress designing exploitation and composition is carried out, green sweater made of cotton yarns is formed;Finally, the green sweater made of cotton yarns is immersed in the working solution for adding softening agent
In, reach improve green sweater made of cotton yarns feel, improve color depth and dimensional stability technique effect, and indices reach GB
Requirement.
, but those skilled in the art once know basic creation although preferred embodiments of the present invention have been described
Property concept, then can make other change and modification to these embodiments.So, appended claims are intended to be construed to include excellent
Select embodiment and fall into having altered and changing for the scope of the invention.
Obviously, those skilled in the art can carry out the essence of various changes and modification without departing from the present invention to the present invention
God and scope.So, if these modifications and modification of the present invention belong to the scope of the claims in the present invention and its equivalent technologies
Within, then the present invention is also intended to comprising including these changes and modification.