CN104878503A - 一种电子级玻璃纤维布的生产工艺 - Google Patents

一种电子级玻璃纤维布的生产工艺 Download PDF

Info

Publication number
CN104878503A
CN104878503A CN201510280857.8A CN201510280857A CN104878503A CN 104878503 A CN104878503 A CN 104878503A CN 201510280857 A CN201510280857 A CN 201510280857A CN 104878503 A CN104878503 A CN 104878503A
Authority
CN
China
Prior art keywords
fiber cloth
glass fiber
electronic
glass fabric
grade glass
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510280857.8A
Other languages
English (en)
Inventor
徐大治
汪洪
童学功
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGCHENG GLASS FIBER CO Ltd OF ANHUI DANFENG GROUP
Original Assignee
TONGCHENG GLASS FIBER CO Ltd OF ANHUI DANFENG GROUP
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGCHENG GLASS FIBER CO Ltd OF ANHUI DANFENG GROUP filed Critical TONGCHENG GLASS FIBER CO Ltd OF ANHUI DANFENG GROUP
Priority to CN201510280857.8A priority Critical patent/CN104878503A/zh
Publication of CN104878503A publication Critical patent/CN104878503A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种电子级玻璃纤维布的生产工艺，包括以下工艺步骤：轻度开纤处理、烘干、扩幅展开、压延处理、快速定型、脱脂处理、加压辊定型、浸渍处理、涂覆绝热材料，等。本发明是一种电子级玻璃纤维布的生产工艺，通过对现有工艺进行改进，在轻度开纤处理后再一次进行深度开纤处理，且深度开纤处理相比较以前开纤程度更大，这样可以减少电子玻璃纤维布的经纬纱间隙、改善玻璃纤维布的均匀性及平整性，提高织物透气性能、含浸性能，且玻璃纤维布表面涂覆一层绝热材料，极大的提高了其耐热性和阻燃性，使其应用范围更加广泛。

Description

一种电子级玻璃纤维布的生产工艺
技术领域
本发明涉及玻璃纤维加工领域，具体涉及一种电子级玻璃纤维布的生产工艺。
背景技术
随着电子行业的飞速发展，印制电路板行业向着高频化、微小化、轻薄化的方向前行，业内越来越要求玻璃纤维布，更加扁平、含浸性更好、表面粗糙度更低、同时对玻璃纤维布的轻薄化、低透气度也越来越提出更多的要求。目前市场上玻璃纤维布的总体生产制程水平相对较低，已经不能满足电子行业的新标准、新要求，在扁平化、透气度、含浸性、厚度、技术应用性等多项指标上，还有待提升。本发明介绍了一种电子级玻璃纤维布的生产工艺，通过对现有工艺进行改进，在轻度开纤处理后再一次进行深度开纤处理，且深度开纤处理相比较以前开纤程度更大，这样可以减少电子玻璃纤维布的经纬纱间隙、改善玻璃纤维布的均匀性及平整性，提高织物透气性能、含浸性能，且玻璃纤维布表面涂覆一层绝热材料，极大的提高了其耐热性和阻燃性，使其应用范围更加广泛。
发明内容
针对现有技术的不足，本发明的目的在于提供一种电子级玻璃纤维布的生产工艺。
本发明解决的技术问题可以采用以下技术方案来实现：一种电子级玻璃纤维布的生产工艺，包括以下工艺步骤：
(1)以喷气织机高速织造后获得未脱脂的玻璃纤维布；
(2)将上述未脱脂的电子级玻璃纤维布进行轻度开纤处理，然后将处理后的电子级玻璃纤维布烘干；
(3)将上述烘干后的玻璃纤维布经一组展开轮扩幅展开；
(4)将上述经扩幅后的玻璃纤维布经压力为5KG/cm2-100KG/cm2的连续压辊进行压延处理，并经过温度350℃-500℃的炉体快速定型；
(5)将上述进行过定型处理的玻璃纤维布用退浆轮卷取放入脱脂炉中，经300℃-500℃、20hrs-64hrs脱脂处理；
(6)将上述经脱脂处理的玻璃纤维布经过压力5KG/cm2-50KG/cm2、孔径为0.1-0.3mm、水温为25℃-85℃、振动频率25Hz-50Hz的高压射流处理、再经过10KG/cm2-100KG/cm2加压辊定型，获得玻璃纤维布；
(7)将上述玻璃纤维布经表面处理剂硅烷偶联剂的浸渍处理后涂覆一层绝热材料，获得电子级玻璃纤维布。
优选的，所述轻度开纤处理是通过将电子级玻璃纤维布放入水洗振动槽进行振动水洗，使玻璃纤维布的经纬纱膨化，纤维之间出现松离实现的。
优选的，所述绝热材料为硼酸盐化合物、卤素化合物、硼酸、无机水合物、溴化合物、氢氧化铝、氢氧化镁、水合菱镁矿、三氧化二锑、二溴四氟乙烷、二溴二氟甲烷、四氯化碳中的任意几种的组合。
有益效果是：本发明是一种电子级玻璃纤维布的生产工艺，通过对现有工艺进行改进，在轻度开纤处理后再一次进行深度开纤处理，且深度开纤处理相比较以前开纤程度更大，这样可以减少电子玻璃纤维布的经纬纱间隙、改善玻璃纤维布的均匀性及平整性，提高织物透气性能、含浸性能，且玻璃纤维布表面涂覆一层绝热材料，极大的提高了其耐热性和阻燃性，使其应用范围更加广泛。
具体实施方式
下面详细说明本发明的优选实施方式。
    本发明一种电子级玻璃纤维布的生产工艺的具体实施方式：一种电子级玻璃纤维布的生产工艺，包括以下工艺步骤：(1)以喷气织机高速织造后获得未脱脂的玻璃纤维布；(2)将上述未脱脂的电子级玻璃纤维布进行轻度开纤处理，然后将处理后的电子级玻璃纤维布烘干；(3)将上述烘干后的玻璃纤维布经一组展开轮扩幅展开；(4)将上述经扩幅后的玻璃纤维布经压力为5KG/cm2-100KG/cm2的连续压辊进行压延处理，并经过温度350℃-500℃的炉体快速定型；(5)将上述进行过定型处理的玻璃纤维布用退浆轮卷取放入脱脂炉中，经300℃-500℃、20hrs-64hrs脱脂处理；(6)将上述经脱脂处理的玻璃纤维布经过压力5KG/cm2-50KG/cm2、孔径为0.1-0.3mm、水温为25℃-85℃、振动频率25Hz-50Hz的高压射流处理、再经过10KG/cm2-100KG/cm2加压辊定型，获得玻璃纤维布；(7)将上述玻璃纤维布经表面处理剂硅烷偶联剂的浸渍处理后涂覆一层绝热材料，获得电子级玻璃纤维布。
所述轻度开纤处理是通过将电子级玻璃纤维布放入水洗振动槽进行振动水洗，使玻璃纤维布的经纬纱膨化，纤维之间出现松离实现的。所述绝热材料为硼酸盐化合物、卤素化合物、硼酸、无机水合物、溴化合物、氢氧化铝、氢氧化镁、水合菱镁矿、三氧化二锑、二溴四氟乙烷、二溴二氟甲烷、四氯化碳中的任意几种的组合。
经过上述工艺步骤后，得到的一种电子级玻璃纤维布，其通过对现有工艺进行改进，在轻度开纤处理后再一次进行深度开纤处理，且深度开纤处理相比较以前开纤程度更大，这样可以减少电子玻璃纤维布的经纬纱间隙、改善玻璃纤维布的均匀性及平整性，提高织物透气性能、含浸性能，且玻璃纤维布表面涂覆一层绝热材料，极大的提高了其耐热性和阻燃性，使其应用范围更加广泛。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书所作的等效结构或等效流程变换，或直接或间接运用在其他相关的技术领域，均同理包括在本发明的专利保护范围内。

Claims (3)

1.一种电子级玻璃纤维布的生产工艺，其特征在于，包括以下工艺步骤：
以喷气织机高速织造后获得未脱脂的玻璃纤维布；
将上述未脱脂的电子级玻璃纤维布进行轻度开纤处理，然后将处理后的电子级玻璃纤维布烘干；
(3)将上述烘干后的玻璃纤维布经一组展开轮扩幅展开；
(4)将上述经扩幅后的玻璃纤维布经压力为5KG/cm2-100KG/cm2的连续压辊进行压延处理，并经过温度350℃-500℃的炉体快速定型；
(5)将上述进行过定型处理的玻璃纤维布用退浆轮卷取放入脱脂炉中，经300℃-500℃、20hrs-64hrs脱脂处理；
(6)将上述经脱脂处理的玻璃纤维布经过压力5KG/cm2-50KG/cm2、孔径为0.1-0.3mm、水温为25℃-85℃、振动频率25Hz-50Hz的高压射流处理、再经过10KG/cm2-100KG/cm2加压辊定型，获得玻璃纤维布；
(7)将上述玻璃纤维布经表面处理剂硅烷偶联剂的浸渍处理后涂覆一层绝热材料，获得电子级玻璃纤维布。
2.根据权利要求1所述的一种电子级玻璃纤维布的生产工艺，其特征在于：所述轻度开纤处理是通过将电子级玻璃纤维布放入水洗振动槽进行振动水洗，使玻璃纤维布的经纬纱膨化，纤维之间出现松离实现的。
3.根据权利要求1所述的一种电子级玻璃纤维布的生产工艺，其特征在于：所述绝热材料为硼酸盐化合物、卤素化合物、硼酸、无机水合物、溴化合物、氢氧化铝、氢氧化镁、水合菱镁矿、三氧化二锑、二溴四氟乙烷、二溴二氟甲烷、四氯化碳中的任意几种的组合。
CN201510280857.8A 2015-05-28 2015-05-28 一种电子级玻璃纤维布的生产工艺 Pending CN104878503A (zh)