CN104877487A - Medical waterproof corrosion-resistant anti-rusting coating and preparation method thereof - Google Patents
Medical waterproof corrosion-resistant anti-rusting coating and preparation method thereof Download PDFInfo
- Publication number
- CN104877487A CN104877487A CN201510256493.XA CN201510256493A CN104877487A CN 104877487 A CN104877487 A CN 104877487A CN 201510256493 A CN201510256493 A CN 201510256493A CN 104877487 A CN104877487 A CN 104877487A
- Authority
- CN
- China
- Prior art keywords
- parts
- zinc
- acrylic emulsion
- dioxide
- citric acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a medical waterproof corrosion-resistant anti-rusting coating and a preparation method thereof. The medical waterproof corrosion-resistant anti-rusting coating comprises the following raw materials: acrylic emulsion, silicon oxide, titanium dioxide, talcum powder, citric acid hydrazine, shellac, zinc chrome, zinc phosphate, iron oxide red and zinc oxide. The medical waterproof corrosion-resistant anti-rusting coating is used for preventing rusting or corrosion of medical instruments and has a deoxidation function, the coating film is smooth and bright in appearance, the viscosity of the coating is 55-75 seconds, the first-class adhesion property is achieved, the coating is resistant to salt mist and is free of abnormity within 15-35 days and is resistant to salt and is free of abnormity within 35-55 days, the surface drying time is 1-3 hours, the hard drying time is 18-20 hours, the preparation method is simple, the raw materials are simple and easy to obtain, and the coating can be widely produced to gradually replace conventional materials.
Description
Technical field
The present invention relates to medical material tech field, particularly relate to a kind of medical water-tight corrosion-proof rust proof paint and preparation method thereof.
Background technology
The chemistry of metallic surface from air, extra large ACRYLIC EMULSION etc. or the coating of galvanic corrosion can be protected.Coat the direct invasion that rust proof paint effectively can avoid various corrosives in air in metallic surface, make maximized prolongation metal time limit of service.Physical property and the large class of chemically antirust paint two can be divided into.The former leans on the suitable cooperation of pigment and paint vehicle, forms fine and close paint film to stop the intrusion of corrosives, as iron oxide red, aluminium powder, graphite rust-inhibiting paint etc.; The latter presses down rust effect, as red lead, zinc yellow anticorrosive paint etc. by the chemistry of rust-stabilising pigment.Antirust for metals such as bridge, boats and ships, pipelines.Be applicable to kitchen, toilet, balcony, vault, ACRYLIC EMULSION pond, balcony swimming pool, the moistureproof and ground of warehouse, tunnel, timber floor warm up anti-ACRYLIC EMULSION with the porcelain brick of various suction ACRYLIC EMULSION amount and the stickup floor wall of ACRYLIC EMULSION mud basic unit and the anti-ACRYLIC EMULSION process of floor specialty.
The rust-inhibiting paint used is roughly oily antirust varniss and ACRYLIC EMULSION rust-inhibiting paint two kinds.Oily antirust varniss makes the greasy removal difficulty of material surface, seldom uses.Oily antirust varniss is easy to use, cheap, but because of containing the toxic substance such as nitrite, chromic salt, comparatively large to operator's harm, country limits use, and these type of product performance are single, can not meet the antirust requirement of magnetic alloy material.Be applicable to the antirust of ferrous and nonferrous metals.
Select metal powerful sequestrant inositol six shellac ester to be main component, form with other several ACRYLIC EMULSION additive compounds.Inositol six shellac ester is the Nantural non-toxic Organic chemical products extracted from food crop; when it uses as magneticsubstance rust-preventive agent; at surface and the rapid chelating of metal, the unit molecule complex compound protective membrane of one deck densification can be formed, effectively can suppress corrosion of metal.Material surface after this product treatment keeps primary colors, ACRYLIC EMULSION need not wash and can enter the next procedures such as application.Be applicable to outdoor and have metal antirust under covering and indoor conditions.
The important component part of rust-inhibiting paint. physics rust-stabilising pigment is the pigment that the chemical property of a class own is comparatively stable, they are the physicalies by itself, stable chemical performance, quality is hard, particle is trickle, excellent fillibility, improve the density of paint film, reduce the permeable of paint film thus play antirust effect. red iron oxide just belongs to this kind of material. and the rust-preventing characteristic of metallic aluminium powder is because aluminium powder has flaky texture, formation paint film is tight, also have the ability of stronger reflect UV linear light, paint film aging-resistant ability can be improved.ACRYLIC EMULSION dissolubility, non-combustible, environmentally safe, use safety.Excellent antirust function, can replace slushing oil, fat completely.
The main film forming substance of the clear lacquer is urethane resin, after it is applied to coated article surface, can react and film-forming with the ACRYLIC EMULSION part in air, also can baking-curing film forming. this film has protection against the tide, Defend salt fog, anti-mildew NBC protective performance.Rust-inhibiting paint kind also has a lot, as barium metaborate rust-inhibiting paint, and zinc gray rust-inhibiting paint, epoxy anti-rust paint, iron mica rust-inhibiting paint, chlorinated polyvinyl chloride rust-inhibiting paint etc.Be easy to dispose from metallic surface with alkaline purging method.The surface of more than 1:20 diluent process directly can be carried out coating and spray paint.
Summary of the invention
The invention provides the medical water-tight corrosion-proof rust proof paint and preparation method thereof of a kind of fast drying, good salt tolerance, solve the dry slow and not technical problem such as salt spray resistance of existing medical material.
The present invention is by the following technical solutions: a kind of medical water-tight corrosion-proof rust proof paint, it is as follows that mass fraction proportioning pressed by its raw material: ACRYLIC EMULSION 100 parts, silicon-dioxide 40-60 part, titanium dioxide 20-40 part, talcum powder 15-35 part, citric acid hydrazine 0.3-0.7 part, lac 2-8 part, zinc-chrome yellow 5-25 part, zinc phosphate 1-5 part, red iron oxide 1-3 part, zinc oxide 4-8 part.
As a preferred technical solution of the present invention: it is as follows that mass fraction proportioning pressed by the raw material of described medical water-tight corrosion-proof rust proof paint: ACRYLIC EMULSION 100 parts, silicon-dioxide 45 parts, titanium dioxide 25 parts, talcum powder 20 parts, citric acid hydrazine 0.4 part, lac 3 parts, zinc-chrome yellow 10 parts, zinc phosphate 2 parts, red iron oxide 1.5 parts, 5 parts, zinc oxide.
As a preferred technical solution of the present invention: it is as follows that mass fraction proportioning pressed by the raw material of described medical water-tight corrosion-proof rust proof paint: ACRYLIC EMULSION 100 parts, silicon-dioxide 55 parts, titanium dioxide 35 parts, talcum powder 30 parts, citric acid hydrazine 0.6 part, lac 7 parts, zinc-chrome yellow 20 parts, zinc phosphate 4 parts, red iron oxide 2.5 parts, 7 parts, zinc oxide.
As a preferred technical solution of the present invention: it is as follows that mass fraction proportioning pressed by the raw material of described medical water-tight corrosion-proof rust proof paint: ACRYLIC EMULSION 100 parts, silicon-dioxide 50 parts, titanium dioxide 30 parts, talcum powder 25 parts, citric acid hydrazine 0.5 part, purple 5 parts, zinc-chrome yellow 15 parts, zinc phosphate 3 parts, red iron oxide 2 parts, 6 parts, zinc oxide.
Prepare a method for described medical water-tight corrosion-proof rust proof paint, step is:
The first step: take ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder, citric acid hydrazine, lac, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide according to mass fraction proportioning;
Second step: ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder and lac are dropped in reactor, be heated to 55-75 DEG C, stirs 60-80min with 200-400r/min speed;
3rd step: the liquid after stirring is left standstill 35-75min, adds citric acid hydrazine, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide, drops into shredder grinding 4-6h, packaging after filtering at 80-100 DEG C after mixing.
beneficial effect
One of the present invention medical water-tight corrosion-proof rust proof paint and preparation method thereof adopts above technical scheme compared with prior art, there is following technique effect: 1, antirust for medical apparatus, anticorrosion, there is desoxydatoin, appearance of film smooth, viscosity 55-75s; 2, sticking power one-level, salt spray resistance 15-35d is without exception; 3, salt tolerance 35-55d is without exception, and surface drying 1-3h, does solid work 18-20h, and preparation method is simple, and raw material is simple and easy to get, the widespread production not division of history into periods can replace current material.
Embodiment
Below in conjunction with example, the invention will be further described, and embodiment, only for the present invention will be described, does not form the restriction to right, and other alternative means that it may occur to persons skilled in the art that, all within the scope of the claims in the present invention.
Embodiment 1:
The first step: take ACRYLIC EMULSION 100 parts according to mass fraction proportioning, silicon-dioxide 40 parts, titanium dioxide 20 parts, talcum powder 15 parts, citric acid hydrazine 0.3 part, lac 2 parts, zinc-chrome yellow 5 parts, zinc phosphate 1 part, red iron oxide 1 part, 4 parts, zinc oxide.
Second step: ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder and lac are dropped in reactor, be heated to 55 DEG C, stirs 60min with 200r/min speed.
3rd step: the liquid after stirring is left standstill 35min, adds citric acid hydrazine, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide, drops into shredder grinding 4h, packaging after filtering at 80 DEG C after mixing.
Antirust for medical apparatus, anticorrosion, there is desoxydatoin appearance of film smooth, viscosity 55s; Sticking power one-level, salt spray resistance 15d is without exception; Salt tolerance 35d is without exception, and surface drying 3h, does solid work 20h.
Embodiment 2:
The first step: take ACRYLIC EMULSION 100 parts according to mass fraction proportioning, silicon-dioxide 60 parts, titanium dioxide 40 parts, talcum powder 35 parts, citric acid hydrazine 0.7 part, lac 8 parts, zinc-chrome yellow 25 parts, zinc phosphate 5 parts, red iron oxide 3 parts, 8 parts, zinc oxide.
Second step: ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder and lac are dropped in reactor, be heated to 75 DEG C, stirs 80min with 400r/min speed.
3rd step: the liquid after stirring is left standstill 75min, adds citric acid hydrazine, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide, drops into shredder grinding 6h, packaging after filtering at 100 DEG C after mixing.
Antirust for medical apparatus, anticorrosion, there is desoxydatoin appearance of film smooth, viscosity 60s; Sticking power one-level, salt spray resistance 20d is without exception; Salt tolerance 40d is without exception, and surface drying 3h, does solid work 20h.
Embodiment 3:
The first step: take ACRYLIC EMULSION 100 parts according to mass fraction proportioning, silicon-dioxide 45 parts, titanium dioxide 25 parts, talcum powder 20 parts, citric acid hydrazine 0.4 part, lac 3 parts, zinc-chrome yellow 10 parts, zinc phosphate 2 parts, red iron oxide 1.5 parts, 5 parts, zinc oxide.
Second step: ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder and lac are dropped in reactor, be heated to 55 DEG C, stirs 60min with 200r/min speed.
3rd step: the liquid after stirring is left standstill 35min, adds citric acid hydrazine, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide, drops into shredder grinding 4h, packaging after filtering at 80 DEG C after mixing.
Antirust for medical apparatus, anticorrosion, there is desoxydatoin appearance of film smooth, viscosity 65s; Sticking power one-level, salt spray resistance 25d is without exception; Salt tolerance 45d is without exception, and surface drying 2h, does solid work 19h.
Embodiment 4:
The first step: take ACRYLIC EMULSION 100 parts according to mass fraction proportioning, silicon-dioxide 55 parts, titanium dioxide 35 parts, talcum powder 30 parts, citric acid hydrazine 0.6 part, lac 7 parts, zinc-chrome yellow 20 parts, zinc phosphate 4 parts, red iron oxide 2.5 parts, 7 parts, zinc oxide.
Second step: ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder and lac are dropped in reactor, be heated to 75 DEG C, stirs 80min with 400r/min speed.
3rd step: the liquid after stirring is left standstill 75min, adds citric acid hydrazine, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide, drops into shredder grinding 6h, packaging after filtering at 100 DEG C after mixing.
Antirust for medical apparatus, anticorrosion, there is desoxydatoin appearance of film smooth, viscosity 70s; Sticking power one-level, salt spray resistance 30d is without exception; Salt tolerance 50d is without exception, and surface drying 1.5h, does solid work 18.5h.
Embodiment 5:
The first step: take ACRYLIC EMULSION 100 parts according to mass fraction proportioning, silicon-dioxide 50 parts, titanium dioxide 30 parts, talcum powder 25 parts, citric acid hydrazine 0.5 part, purple 5 parts, zinc-chrome yellow 15 parts, zinc phosphate 3 parts, red iron oxide 2 parts, 6 parts, zinc oxide.
Second step: ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder and lac are dropped in reactor, be heated to 65 DEG C, stirs 70min with 300r/min speed.
3rd step: the liquid after stirring is left standstill 55min, adds citric acid hydrazine, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide, drops into shredder grinding 5h, packaging after filtering at 90 DEG C after mixing.
Antirust for medical apparatus, anticorrosion, there is desoxydatoin appearance of film smooth, viscosity 75s; Sticking power one-level, salt spray resistance 35d is without exception; Salt tolerance 55d is without exception, and surface drying 1h, does solid work 18h.
Claims (5)
1. a medical water-tight corrosion-proof rust proof paint, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described medical water-tight corrosion-proof rust proof paint: ACRYLIC EMULSION 100 parts, silicon-dioxide 40-60 part, titanium dioxide 20-40 part, talcum powder 15-35 part, citric acid hydrazine 0.3-0.7 part, lac 2-8 part, zinc-chrome yellow 5-25 part, zinc phosphate 1-5 part, red iron oxide 1-3 part, zinc oxide 4-8 part.
2. the medical water-tight corrosion-proof rust proof paint of one according to claim 1, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described medical water-tight corrosion-proof rust proof paint: ACRYLIC EMULSION 100 parts, silicon-dioxide 45 parts, titanium dioxide 25 parts, talcum powder 20 parts, citric acid hydrazine 0.4 part, lac 3 parts, zinc-chrome yellow 10 parts, zinc phosphate 2 parts, red iron oxide 1.5 parts, 5 parts, zinc oxide.
3. the medical water-tight corrosion-proof rust proof paint of one according to claim 2, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described medical water-tight corrosion-proof rust proof paint: ACRYLIC EMULSION 100 parts, silicon-dioxide 55 parts, titanium dioxide 35 parts, talcum powder 30 parts, citric acid hydrazine 0.6 part, lac 7 parts, zinc-chrome yellow 20 parts, zinc phosphate 4 parts, red iron oxide 2.5 parts, 7 parts, zinc oxide.
4. the medical water-tight corrosion-proof rust proof paint of one according to claim 1, it is characterized in that: the raw material of described medical water-tight corrosion-proof rust proof paint is as follows by mass fraction proportioning: ACRYLIC EMULSION 100 parts, silicon-dioxide 50 parts, titanium dioxide 30 parts, talcum powder 25 parts, citric acid hydrazine 0.5 part, purple 5 parts, zinc-chrome yellow 15 parts, zinc phosphate 3 parts, red iron oxide 2 parts, 6 parts, zinc oxide.
5. prepare a method for medical water-tight corrosion-proof rust proof paint according to claim 1, it is characterized in that, comprise the steps:
The first step: take ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder, citric acid hydrazine, lac, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide according to mass fraction proportioning;
Second step: ACRYLIC EMULSION, silicon-dioxide, titanium dioxide, talcum powder and lac are dropped in reactor, be heated to 55-75 DEG C, stirs 60-80min with 200-400r/min speed;
3rd step: the liquid after stirring is left standstill 35-75min, adds citric acid hydrazine, zinc-chrome yellow, zinc phosphate, red iron oxide and zinc oxide, drops into shredder grinding 4-6h, packaging after filtering at 80-100 DEG C after mixing.