CN104846131A - Specific durable combustion improver for leather - Google Patents
Specific durable combustion improver for leather Download PDFInfo
- Publication number
- CN104846131A CN104846131A CN201510286370.0A CN201510286370A CN104846131A CN 104846131 A CN104846131 A CN 104846131A CN 201510286370 A CN201510286370 A CN 201510286370A CN 104846131 A CN104846131 A CN 104846131A
- Authority
- CN
- China
- Prior art keywords
- parts
- leather
- combustion improver
- specific durable
- durable combustion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a specific durable combustion improver for leather. The specific durable combustion improver is prepared from the following raw materials in parts by weight: 7-9 parts of zinc cyanurate, 3-5 parts of triethanolamine, 4-6 parts of methyl isobutyl ketone, 3-5.5 parts of a plasticizer, 12-16 parts of polyvinyl chloride, 0.5-1.3 parts of ferrocene, 4-5 parts of sodium carbonate, 7-12 parts of sodium hydroxide, 5-9 parts of acrylamide, 4-7 parts of chlorinated paraffin, 12-22 parts of butyl acetate, 6-9 parts of dioctyl terephthalate, 3-6 parts of hexamethylenetetramine, 4-7 parts of maleic anhydride and 12-17 parts of flame-retardant polyether. The specific durable combustion improver has the beneficial effects of favorable durability, efficient flame retardance, simple preparation process and no human and environment damage.
Description
Technical field
The present invention relates to a kind of special ignition dope of leather of weather resistance.
Background technology
Fire retardant improves material fire resistance, and namely stop material ignited and suppress the auxiliary agent of propagation of flame, it is mainly used in synthesis and natural macromolecular material fire-retardant.Along with the fast development of national economy and the progressively raising of living standards of the people, the application of leatherware is more and more extensive, the same with plastics, rubber, papermaking, the fire-retardant problem of leather, also more and more come into one's own, as sofa artificial leather, upholstery leather, fire-fighting leather and automobile leather etc., all need certain flame retardant properties, especially automobile leather.Leather fire retardant liquid was more and more taken seriously in recent years, but existing leather fire retardant lacks security and the feature of environmental protection, and urgent need is a kind of now has efficient, good endurance, multifunction fire retardant material, meets the vacancy on market.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of leather of weather resistance special ignition dope, has good weather resistance, can highly effective flame-retardant, and preparation technology is simple, does not all injure human body and environment.
For solving prior art problem, technical scheme provided by the invention is, a kind of special ignition dope of leather of weather resistance, and it is made up of the raw material of following parts by weight:
Cyanuric acid zinc 7-9 part, trolamine 3-5 part, methyl iso-butyl ketone (MIBK) 4-6 part, softening agent 3-5.5 part, polyvinyl chloride 12-16 part, ferrocene 0.5-1.3 part, sodium carbonate 4-5 part, sodium hydroxide 7-12 part, acrylamide 5-9 part, clorafin 4-7 part, N-BUTYL ACETATE 12-22 part, dioctyl terephthalate 6-9 part, vulkacit H 3-6 part, MALEIC ANHYDRIDE 4-7 part, flame retarding polyether 12-17 part.
The invention has the beneficial effects as follows: the special ignition dope of leather of weather resistance of the present invention, has good weather resistance, can highly effective flame-retardant, preparation technology is simple, does not all injure human body and environment.
Embodiment
embodiment 1
The special ignition dope of leather of weather resistance, it is made up of the raw material of following parts by weight:
7 parts, cyanuric acid zinc, trolamine 3 parts, methyl iso-butyl ketone (MIBK) 4 parts, 3 parts, softening agent, polyvinyl chloride 12 parts, ferrocene 0.5 part, 4 parts, sodium carbonate, 7 parts, sodium hydroxide, acrylamide 5 parts, clorafin 4 parts, N-BUTYL ACETATE 12 parts, dioctyl terephthalate 6 parts, vulkacit H 3 parts, MALEIC ANHYDRIDE 4 parts, flame retarding polyether 12 parts.
embodiment 2
The special ignition dope of leather of weather resistance, it is made up of the raw material of following parts by weight:
9 parts, cyanuric acid zinc, trolamine 5 parts, methyl iso-butyl ketone (MIBK) 6 parts, 5.5 parts, softening agent, polyvinyl chloride 16 parts, ferrocene 1.3 parts, 5 parts, sodium carbonate, 12 parts, sodium hydroxide, acrylamide 9 parts, clorafin 7 parts, N-BUTYL ACETATE 22 parts, dioctyl terephthalate 9 parts, vulkacit H 6 parts, MALEIC ANHYDRIDE 7 parts, flame retarding polyether 17 parts.
Claims (1)
1. the special ignition dope of the leather of weather resistance, is characterized in that: it is made up of the raw material of following parts by weight:
Cyanuric acid zinc 7-9 part, trolamine 3-5 part, methyl iso-butyl ketone (MIBK) 4-6 part, softening agent 3-5.5 part, polyvinyl chloride 12-16 part, ferrocene 0.5-1.3 part, sodium carbonate 4-5 part, sodium hydroxide 7-12 part, acrylamide 5-9 part, clorafin 4-7 part, N-BUTYL ACETATE 12-22 part, dioctyl terephthalate 6-9 part, vulkacit H 3-6 part, MALEIC ANHYDRIDE 4-7 part, flame retarding polyether 12-17 part.