CN104356537A - High-temperature-resistant plastic composite material - Google Patents
High-temperature-resistant plastic composite material Download PDFInfo
- Publication number
- CN104356537A CN104356537A CN201410581007.7A CN201410581007A CN104356537A CN 104356537 A CN104356537 A CN 104356537A CN 201410581007 A CN201410581007 A CN 201410581007A CN 104356537 A CN104356537 A CN 104356537A
- Authority
- CN
- China
- Prior art keywords
- parts
- matrix material
- composite material
- antioxidant
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-temperature-resistant plastic composite material. The composite material comprises the following ingredients in parts by weight: 50-70 parts of polyvinyl chloride, 20-40 parts of glass fibers, 0.1-1 part of a flexibilizer, 0.5-1.5 parts of an antioxidant, 0.1-1 part of a coupling agent, 10-15 parts of calcium carbonate, 5-10 parts of carbon black and 1-10 parts of paraffin. The plastic produced by using the formula is high in flame retardancy and high in stability, cannot generate harmful gas under the condition of high temperature combustion, has a good environmental protection effect, and is low in production cost.
Description
Technical field
The present invention relates to polymeric material field, particularly relate to a kind of high-temperature resistance plastice matrix material.
Background technology
At present, the application of plastics is throughout the every field of industrial or agricultural, life, and within 1999, main thermoplast (PP, PVC, PS, LDPE, HDPE) total amount in the whole world has reached 1.1 1 hundred million tons, and average annual growth rate reaches 5.3%.Major part plastics just start to decomposite hazardous and noxious substances when temperature is more than 80 DEG C, so the application of formula of flame-retardant plastic is also more and more extensive, present formula of flame-retardant plastic mostly is fire-retardant superpolymer, it is not easily ignited, unexpected fire can be reduced, or after igniting, essentially no flame, the intensity of a fire can be avoided to become large, and formula of flame-retardant plastic can also reduce flame propagation velocity and combustionvelocity in addition.But, now a lot of formula of flame-retardant plastic produces toxic gas and to cause in fire poison gas and flue gas to suffocate side effect to human body when materials pyrolysis, the physical and mental health of grievous injury people, environmental-protecting performance is very undesirable, so now people will more focus on Novel non-toxic, the exploitation of smokeless, free of contamination environment friendly flame retardant, production and application.
Summary of the invention
The object of this invention is to provide a kind of stability, resistant to elevated temperatures plastics composite.
The present invention is achieved through the following technical solutions:
A kind of high-temperature resistance plastice matrix material, described matrix material comprises the component of following parts by weight: polyvinyl chloride 50 ~ 70 parts, 20 ~ 40 parts, glass fibre, toughner 0.1 ~ 1 part, antioxidant 0.5 ~ 1.5 part, coupling agent 0.1 ~ 1 part, 10 ~ 15 parts, calcium carbonate, carbon black 5 ~ 10 parts, 1 ~ 10 part, paraffin.
Further, described toughner is CPE.
Further, described antioxidant is antioxidant 1010.
Further, described coupling agent is silane coupling agent.
The invention has the beneficial effects as follows: use the plastics produced by this formula to have flame retardant resistance strong, stability is high, can not cause obnoxious flavour when high-temp combustion, have good environment protecting, and production cost is low.
Embodiment
Below in conjunction with embodiment, the present invention is further described.
Embodiment 1
A kind of high-temperature resistance plastice matrix material, comprises the component of following parts by weight: polyvinyl chloride 50 parts, 20 parts, glass fibre, CPE 0.1 part, antioxidant 1010 0.5 part, silane coupling agent 0.1 part, 10 parts, calcium carbonate, carbon black 5 parts, 1 part, paraffin.
Embodiment 2
A kind of high-temperature resistance plastice matrix material, comprises the component of following parts by weight: polyvinyl chloride 60 parts, 30 parts, glass fibre, CPE 0.5 part, antioxidant 1010 1 part, silane coupling agent 0.5 part, 13 parts, calcium carbonate, carbon black 7 parts, paraffin 5.
Embodiment 1
A kind of high-temperature resistance plastice matrix material, comprises the component of following parts by weight: polyvinyl chloride 70 parts, 40 parts, glass fibre, CPE 1 part, antioxidant 1010 1.5 parts, silane coupling agent 1 part, 15 parts, calcium carbonate, carbon black 10 parts, 10 parts, paraffin.
Use the plastics produced by this formula to have flame retardant resistance strong, stability is high, can not cause obnoxious flavour when high-temp combustion, have good environment protecting, and production cost is low.
The above is only embodiments of the invention, is not restriction the present invention being made to any other form, and any amendment done according to technical spirit of the present invention or equivalent variations, still belong to the present invention's scope required for protection.
Claims (4)
1. a high-temperature resistance plastice matrix material, it is characterized in that: described matrix material comprises the component of following parts by weight: polyvinyl chloride 50 ~ 70 parts, 20 ~ 40 parts, glass fibre, toughner 0.1 ~ 1 part, antioxidant 0.5 ~ 1.5 part, coupling agent 0.1 ~ 1 part, 10 ~ 15 parts, calcium carbonate, carbon black 5 ~ 10 parts, 1 ~ 10 part, paraffin.
2. a kind of high-temperature resistance plastice matrix material according to claim 1, is characterized in that: described toughner is CPE.
3. a kind of high-temperature resistance plastice matrix material according to claim 1, is characterized in that: described antioxidant is antioxidant 1010.
4. a kind of high-temperature resistance plastice matrix material according to claim 1, is characterized in that: described coupling agent is silane coupling agent.