CN104845511A - Novel gel coat resin for die and preparation method for novel gel coat resin - Google Patents
Novel gel coat resin for die and preparation method for novel gel coat resin Download PDFInfo
- Publication number
- CN104845511A CN104845511A CN201510253771.6A CN201510253771A CN104845511A CN 104845511 A CN104845511 A CN 104845511A CN 201510253771 A CN201510253771 A CN 201510253771A CN 104845511 A CN104845511 A CN 104845511A
- Authority
- CN
- China
- Prior art keywords
- gel coating
- coating resin
- silicon carbide
- novel die
- unsaturated polyester
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides novel gel coat resin for a die. The novel gel coat resin comprises the following components in parts by weight: 80 to 93 parts of unsaturated polyester resin, 0.2 to 2 parts of fumed silica, 0.1 to 0.5 part of a dispersant, 0.1 to 0.5 part of an antifoaming agent, 0.1 to 0.3 part of a polymerization inhibitor, 0.1 to 0.3 part of an initiator, 5 to 15 parts of nanometer silicon carbide and 0.5 to 2 parts of a coupling agent. The invention further discloses a preparation method for the gel coat resin for the die. The gel coat resin for the die has higher mechanical performance and flexibility.
Description
Technical field:
The present invention relates to a kind of gel coating resin, particularly relate to a kind of novel die gel coating resin and preparation method thereof.
Background technology:
Gel coating resin is a kind of special resin in unsaturated polyester resin, provides protective layer for being coated in substrate material surface to it, improves the properties of goods, to goods with beautiful outward appearance, increases the service life.Gel coating resin is mainly matrix with unsaturated polyester resin, is that thixotropic agent forms through blending dispersion with aerosil.Gel coating resin Application Areas is relatively wider, comprises mould gel coating resin, gel coating resin for ship, food grade gel coating resin etc.Wherein, mould gel coating resin is mainly used in making mould, and therefore must have good mechanical property, snappiness, common gel coating resin can not meet above-mentioned requirements completely.
Summary of the invention:
The technical problem to be solved in the present invention is to provide a kind of mould gel coating resin, has good mechanical property and snappiness.
For solving the problems of the technologies described above, technical scheme of the present invention is:
A kind of novel die gel coating resin, it comprises the component of following weight part: unsaturated polyester resin 80 ~ 93 parts, aerosil 0.2 ~ 2 part, dispersion agent 0.1 ~ 0.5 part, defoamer 0.1 ~ 0.5 part, stopper 0.1 ~ 0.3 part, initiator 0.1 ~ 0.3 part, nanometer silicon carbide 5 ~ 15 parts, coupling agent 0.5 ~ 2 part.
Preferably, unsaturated polyester resin of the present invention is 196 type unsaturated polyester resins.
Preferably, dispersion agent of the present invention is BYK-110 or BYK-104S.
Preferably, defoamer of the present invention is methyl-silicone oil.
Preferably, stopper of the present invention is quinhydrones, toluhydroquinone or copper naphthenate.
Preferably, initiator of the present invention is methylethyl ketone peroxide.
Preferably, coupling agent of the present invention is silane coupling agent.
Another technical problem that the present invention will solve is to provide the preparation method of above-mentioned mould gel coating resin.
For solving the problems of the technologies described above, technical scheme is:
A preparation method for novel die gel coating resin, comprises the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.
Compared with prior art, the present invention has following beneficial effect:
Nanometer silicon carbide is after the surface modification of coupling agent, can be scattered in resin matrix equably, interface cohesion between silicon-carbide particle with resin matrix is tightr, define the region of intensity higher than resin matrix, when being subject to external force load, these regions by dynamic changes process to the silicon-carbide particle of rigidity, can add that silicon-carbide particle can hinder crack propagation, therefore obvious enhancement be can play, mechanical property and the flexibility of material significantly improved.
Embodiment:
Describe the present invention in detail below in conjunction with specific embodiment, be used for explaining the present invention in this illustrative examples of the present invention and explanation, but not as a limitation of the invention.
Embodiment 1
A kind of novel die gel coating resin, it comprises the component of following weight part: unsaturated polyester resin 80g, aerosil 2g, dispersion agent 0.5g, defoamer 0.5g, stopper 0.3g, initiator 0.3g, nanometer silicon carbide 14.4g, coupling agent 2g.
Its preparation method comprises the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.
Embodiment 2
A kind of novel die gel coating resin, it comprises the component of following weight part: unsaturated polyester resin 93g, aerosil 0.1g, dispersion agent 0.1g, defoamer 0.1g, stopper 0.1g, initiator 0.1g, nanometer silicon carbide 5.9g, coupling agent 0.5g.
Its preparation method comprises the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.
Embodiment 3
A kind of novel die gel coating resin, it comprises the component of following weight part: unsaturated polyester resin 92.2g, aerosil 1g, dispersion agent 0.2g, defoamer 0.2g, stopper 0.2g, initiator 0.2g, nanometer silicon carbide 5g, coupling agent 1g.
Its preparation method comprises the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.
Embodiment 4
A kind of novel die gel coating resin, it comprises the component of following weight part: unsaturated polyester resin 82.2g, aerosil 0.5g, dispersion agent 0.3g, defoamer 0.3g, stopper 0.1g, initiator 0.1g, nanometer silicon carbide 15g, coupling agent 1.5g.
Its preparation method comprises the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.
Embodiment 5
A kind of novel die gel coating resin, it comprises the component of following weight part: unsaturated polyester resin 86g, aerosil 1.5g, dispersion agent 0.4g, defoamer 0.4g, stopper 0.3g, initiator 0.3g, nanometer silicon carbide 10g, coupling agent 1.1g.
Its preparation method comprises the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.
Embodiment 6
A kind of novel die gel coating resin, it comprises the component of following weight part: unsaturated polyester resin 90g, aerosil 1.8g, dispersion agent 0.1g, defoamer 0.5g, stopper 0.2g, initiator 0.2g, nanometer silicon carbide 6g, coupling agent 1.2g.
Its preparation method comprises the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.
Above-described embodiment is illustrative principle of the present invention and effect thereof only, but not for limiting the present invention.Any person skilled in the art scholar all without prejudice under spirit of the present invention and category, can modify above-described embodiment or changes.Therefore, such as have in art usually know the knowledgeable do not depart from complete under disclosed spirit and technological thought all equivalence modify or change, must be contained by claim of the present invention.
Claims (8)
1. a novel die gel coating resin, it is characterized in that: it comprises the component of following weight part: unsaturated polyester resin 80 ~ 93 parts, aerosil 0.2 ~ 2 part, dispersion agent 0.1 ~ 0.5 part, defoamer 0.1 ~ 0.5 part, stopper 0.1 ~ 0.3 part, initiator 0.1 ~ 0.3 part, nanometer silicon carbide 5 ~ 15 parts, coupling agent 0.5 ~ 2 part.
2. a kind of novel die gel coating resin according to claim 1, is characterized in that: described unsaturated polyester resin is 196 type unsaturated polyester resins.
3. a kind of novel die gel coating resin according to claim 1, is characterized in that: described dispersion agent is BYK-110 or BYK-104S.
4. a kind of novel die gel coating resin according to claim 1, is characterized in that: described defoamer is methyl-silicone oil.
5. a kind of novel die gel coating resin according to claim 1, is characterized in that: described stopper is quinhydrones, toluhydroquinone or copper naphthenate.
6. a kind of novel die gel coating resin according to claim 1, is characterized in that: described initiator is methylethyl ketone peroxide.
7. a kind of novel die gel coating resin according to claim 1, is characterized in that: described coupling agent is silane coupling agent.
8. the preparation method of a kind of novel die gel coating resin according to claim 1 ~ 7 any one, is characterized in that comprising the following steps:
(1) nanometer silicon carbide, coupling agent are dissolved in toluene, fully disperse rear oil bath to heat with dispersion agent, logical nitrogen protection, stir and shift out material, stratification after 4 hours, by lower sediment thing washing with acetone, at 80 DEG C, vacuum-drying 12 hours, obtains modified Nano silicon carbide;
(2) mixed with unsaturated polyester resin by modified Nano silicon carbide, add aerosil, dispersion agent, defoamer, stopper, initiator, be stirred to without bulk particle, the compound obtaining mixing is mould gel coating resin.