CN104845457A - Fireproof coating with superior fireproof performance - Google Patents
Fireproof coating with superior fireproof performance Download PDFInfo
- Publication number
- CN104845457A CN104845457A CN201510197861.8A CN201510197861A CN104845457A CN 104845457 A CN104845457 A CN 104845457A CN 201510197861 A CN201510197861 A CN 201510197861A CN 104845457 A CN104845457 A CN 104845457A
- Authority
- CN
- China
- Prior art keywords
- parts
- superior
- water
- fire
- fireproof
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a fireproof coating with a superior fireproof performance. The fireproof coating with a superior fireproof performance is prepared from, by weight, 400-600 parts of water, 250-350 parts of a flexible emulsion, 100-200 parts of melamine, 50-100 parts of pentaerythritol, 100-200 parts of a fire retardant and a proper amount of an aqueous thickening agent. The fire retardant is prepared from ammonium sulfate and water by uniformly stirring and dissolving ammonium sulfate and water in a container according to a weight ratio of 1:2. The fireproof coating with a superior fireproof performance is prepared by adopting the flexible emulsion as a base material and melamine and pentaerythritol as the fire retardant, so the coating has the characteristics of long fire retardation time, high stretching and bonding strength, and good fireproof performance; and a solvent formed by dissolving ammonium sulfate in water has a fire retardation performance, so the fire retardation performance of products coated with the solvent is obviously improved.
Description
Technical field
The present invention relates to fire-proof product field, the frie retardant coating that specifically a kind of fire resistance is superior.
Background technology
Pyrophoricity accident can bring extreme loss to people's lives and properties, some products being material with the inflammable substance such as paper, timber, and in production, storage, transport, using, Yi Yinhuo causes burning to have an accident.Along with country is to the attention of trouble-free service and the needs that assure the safety for life and property of the people, these products can be made to have generation that flame retardant resistance just effectively can reduce pyrophoricity accident.
At present, frie retardant coating has two large classes in the world: a class is the frie retardant coating of non-expansion type, though there is very strong fire-resistant and water resistance, thermal insulation is bad, and fire resistance is not high.Another kind of is intumescent coating, especially the thermofin of honeycomb microbubble structure can be formed when meeting fire, heat-proof quality is good, this kind of coating normally using organic polymer as film forming material, this kind of coating excellent in heat insulating performance, fire resistance is good, but foam insulation physical strength is low, easily drops, causes fire resistance to reduce or lost efficacy, in addition cost is higher, ornamental also not ideal enough.
Summary of the invention
The frie retardant coating that fire resistance is superior, is made up of the raw material of following weight parts: 400 ~ 600 parts, water, flexible emulsion 250 ~ 350 parts, trimeric cyanamide 100 ~ 200 parts, tetramethylolmethane 50 ~ 100 parts, fire retardant 100 ~ 200 parts and appropriate water-based thickener; Described fire retardant for raw material with amine sulfate and water, is inserted stirring and dissolving in container with the weight ratio of 1:2 successively and is evenly formed.
As further scheme, be made up of the raw material of following weight parts: 500 parts, water, flexible emulsion 300 parts, trimeric cyanamide 150 parts, tetramethylolmethane 75 parts, fire retardant 150 parts and appropriate thickening material.
As further scheme, described flexible emulsion is selected from polychloroprene latex, isobutylene-isoprene latex, acetate copolymer emulsion or VAE emulsion.
As further scheme, described thickening material is selected from IIEUR class, IIASE class and HEC class.
Compared with prior art, the invention has the beneficial effects as follows: the frie retardant coating that fire resistance provided by the invention is superior, with flexible emulsion for base-material, with trimeric cyanamide and tetramethylolmethane for fire retardant is made, have duration of fire resistance long, tensile bond strength is high, the feature that fire resistance is good; Because the solvent of the water-soluble rear formation of amine sulfate has flame retardant resistance, therefore can significantly improve through the article of this solvent brushing and do not lead combustion.
Embodiment
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
The frie retardant coating that fire resistance is superior, is made up of the raw material of following weight parts: 400 ~ 600 parts, water, flexible emulsion 250 ~ 350 parts, trimeric cyanamide 100 ~ 200 parts, tetramethylolmethane 50 ~ 100 parts, fire retardant 100 ~ 200 parts and appropriate water-based thickener; Described fire retardant for raw material with amine sulfate and water, is inserted stirring and dissolving in container with the weight ratio of 1:2 successively and is evenly formed.The frie retardant coating that fire resistance provided by the invention is superior, with flexible emulsion for base-material, with trimeric cyanamide and tetramethylolmethane for fire retardant is made, have duration of fire resistance long, tensile bond strength is high, the feature that fire resistance is good; Because the solvent of the water-soluble rear formation of amine sulfate has flame retardant resistance, therefore can significantly improve through the article of this solvent brushing and do not lead combustion.
As further scheme, be made up of the raw material of following weight parts: 500 parts, water, flexible emulsion 300 parts, trimeric cyanamide 150 parts, tetramethylolmethane 75 parts, fire retardant 150 parts and appropriate thickening material.
As further scheme, described flexible emulsion is selected from polychloroprene latex, isobutylene-isoprene latex, acetate copolymer emulsion or VAE emulsion.
As further scheme, described thickening material is selected from IIEUR class, IIASE class and HEC class.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
In addition, be to be understood that, although this specification sheets is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of specification sheets is only for clarity sake, those skilled in the art should by specification sheets integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.
Claims (4)
1. the frie retardant coating that a fire resistance is superior, it is characterized in that, be made up of the raw material of following weight parts: 400 ~ 600 parts, water, flexible emulsion 250 ~ 350 parts, trimeric cyanamide 100 ~ 200 parts, tetramethylolmethane 50 ~ 100 parts, fire retardant 100 ~ 200 parts and appropriate water-based thickener; Described fire retardant for raw material with amine sulfate and water, is inserted stirring and dissolving in container with the weight ratio of 1:2 successively and is evenly formed.
2. the frie retardant coating that a kind of fire resistance according to claim 1 is superior, it is characterized in that, be made up of the raw material of following weight parts: 500 parts, water, flexible emulsion 300 parts, trimeric cyanamide 150 parts, tetramethylolmethane 75 parts, fire retardant 150 parts and appropriate thickening material.
3. the frie retardant coating that a kind of fire resistance according to claim 1 is superior, is characterized in that, described flexible emulsion is selected from polychloroprene latex, isobutylene-isoprene latex, acetate copolymer emulsion or VAE emulsion.
4. the frie retardant coating that a kind of fire resistance according to claim 1 is superior, is characterized in that, described thickening material is selected from IIEUR class, IIASE class and HEC class.