CN104844965A - PVC (polyvinyl chloride) formula - Google Patents
PVC (polyvinyl chloride) formula Download PDFInfo
- Publication number
- CN104844965A CN104844965A CN201510242473.7A CN201510242473A CN104844965A CN 104844965 A CN104844965 A CN 104844965A CN 201510242473 A CN201510242473 A CN 201510242473A CN 104844965 A CN104844965 A CN 104844965A
- Authority
- CN
- China
- Prior art keywords
- parts
- pvc
- formula
- auxiliary agent
- calcium stearate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a PVC (polyvinyl chloride) formula, which is prepared from the following raw materials in parts by weight: 90 to 100 parts of PVC resin, 3 to 6 parts of calcium stearate, 18 to 20 parts of alcohol-soluble resin, 1 to 2 parts of flexibilizer, and 3 to 6 parts of auxiliaries. PVC pipes produced by using the formula have the advantages that the impact resistance property and the strength can be enhanced.
Description
Technical field
The present invention relates to plastic cement pipeline technical field, be specifically related to a kind of PVC and fill a prescription.
Background technology
The main component of PVC is polyvinyl chloride, adds other one-tenth in addition and assigns to strengthen its thermotolerance, toughness, ductility etc.PVC is deeply liked in the world today, is rather popular and a kind of synthetic materials of widespread use.PVC is a kind of tubing of maturation, is mainly used in water supply and sewage work.PVC has acidproof, alkaline-resisting, corrosion-resistant, intensity advantages of higher, but erosion-resisting characteristics is poor.
Summary of the invention
The invention provides a kind of PVC to fill a prescription, utilize the produced PVC of this formula can strengthen erosion-resisting characteristics and intensity.
For achieving the above object, the technical scheme that a kind of finishing material of the present invention and preparation method thereof adopts is: a kind of PVC formula, is made up: PVC resin powder 90-100 part of the raw material of following weight part, calcium stearate 3-6 part, spirit-soluble resin 18-20 part, toughner 1-2 part, auxiliary agent 3-6 part.
Further, be made up of following optimal proportion raw material: PVC resin powder 95 parts, calcium stearate 4.8 parts, spirit-soluble resin 20 parts, toughner 1.4 parts, auxiliary agent 4.9 parts.
Further, auxiliary agent is one or more compositions in coating thickener, wetting agent, film coalescence aid and clear water.
The invention has the beneficial effects as follows: utilize the produced PVC of this formula can strengthen erosion-resisting characteristics and intensity.
Embodiment
Below in conjunction with specific embodiment, the invention will be further described.
Embodiment 1:
A kind of PVC formula of the present invention, is made up of the raw material of following weight part: PVC resin powder 90 parts, calcium stearate 3 parts, spirit-soluble resin 18 parts, toughner 1 part, auxiliary agent 3 parts.
Auxiliary agent is one or more compositions in coating thickener, wetting agent, film coalescence aid and clear water.
Embodiment 2:
A kind of PVC formula of the present invention, is made up of the raw material of following weight part: PVC resin powder 100 parts, calcium stearate 6 parts, spirit-soluble resin 20 parts, toughner 2 parts, auxiliary agent 6 parts.
Auxiliary agent is one or more compositions in coating thickener, wetting agent, film coalescence aid and clear water.
Embodiment 3 is optimum embodiment of the present invention:
A kind of PVC formula of the present invention, is made up of the raw material of following weight part: PVC resin powder 95 parts, calcium stearate 4.8 parts, spirit-soluble resin 20 parts, toughner 1.4 parts, auxiliary agent 4.9 parts.
Auxiliary agent is one or more compositions in coating thickener, wetting agent, film coalescence aid and clear water.
In sum, the produced PVC of this formula is utilized can to strengthen erosion-resisting characteristics and intensity.
Claims (3)
1. a PVC formula, is characterized in that being made up of the raw material of following weight part: PVC resin powder 90-100 part, calcium stearate 3-6 part, spirit-soluble resin 18-20 part, toughner 1-2 part, auxiliary agent 3-6 part.
2. PVC formula as claimed in claim 1, is characterized in that being made up of following optimal proportion raw material: PVC resin powder 95 parts, calcium stearate 4.8 parts, spirit-soluble resin 20 parts, toughner 1.4 parts, auxiliary agent 4.9 parts.
3. PVC formula as claimed in claim 1, is characterized in that: auxiliary agent is one or more compositions in coating thickener, wetting agent, film coalescence aid and clear water.