CN104844961A - Manufacturing method of polyvinyl chloride plain film - Google Patents
Manufacturing method of polyvinyl chloride plain film Download PDFInfo
- Publication number
- CN104844961A CN104844961A CN201510099076.9A CN201510099076A CN104844961A CN 104844961 A CN104844961 A CN 104844961A CN 201510099076 A CN201510099076 A CN 201510099076A CN 104844961 A CN104844961 A CN 104844961A
- Authority
- CN
- China
- Prior art keywords
- polyvinyl chloride
- parts
- plain film
- resin
- tackifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for producing a polyvinyl chloride plain film. The method is characterized by comprising the following steps: using 100 parts of PVC resin, 40-60 parts of a tackifier, 20-40 parts of a heat stabilizer, 50-200 parts of a strengthening agent, 10-20 parts of reinforced resin, 0.5-1.5 parts of a lubricant and 4-6 parts of an accelerant as raw materials to form a formula, and performing high-speed hot mixing, low-speed hot mixing, extrusion, open milling, calendering, cooling, molding, cutting and packaging to produce the polyvinyl chloride plain film. According to the method, the technology is simple, and the manufactured polyvinyl chloride plain film has good quality; the method disclosed by the invention uses a special formula; the film material is uniform to plasticize, flawless, good in toughness, resistant to impact, flame-retardant, good in low temperature performance, resistant to ageing and long in service life.
Description
Technical field
The present invention relates to a kind of manufacture method of polyvinyl chloride plain film.
Background technology
Polyvinyl chloride true qualities are that micro-yellow is translucent, glossy.Transparency is better than polyethylene, polyphenyl alkene, is worse than polystyrene, and different with auxiliary dosage, be divided into soft, rigid polyvinyl chloride, soft goods is soft and tough, and feel is glued, and the hardness of boardy product is higher than Low Density Polyethylene, and lower than polypropylene, in flexion, place there will be albinism.Common product: the polyvinyl chloride such as sheet material, tubing, sole, toy, door and window, wire outer skin, stationery are a kind of macromolecular materials using a chlorine atom to replace a hydrogen atom in polyethylene.
Polyvinyl chloride (PVC) plain film is the base material producing various drip water plate, also for other Blister products and secondary processing matrix band.Existing polyvinyl chloride plain film, sheet material plasticizing uneven, have crackle, poor toughness, not shock-resistant, not fire-retardant, poor performance at low temperatures, aging life-span are short.
Summary of the invention
The technical problem to be solved in the present invention is the defect overcoming prior art, provides a kind of manufacture method of polyvinyl chloride plain film.
In order to solve the problems of the technologies described above, the invention provides following technical scheme:
A kind of method of producing polyvinyl chloride plain film of the present invention, is characterized in that, with polyvinyl chloride resin: 100; Tackifier: 40-60; Thermo-stabilizer: 20-40; Strengthening agent: 50-200; Strengthen resin: 10-20; Lubricant: 0.5-1.5; Promotor: 4-6 is raw material compositing formula, mixes through heat mixing at a high speed, low speed heat, extrude, opens refining the pressure court of a feudal ruler, cooling and shaping, cuts packaging and produce polyvinyl chloride plain film.
Further, according to the mass fraction, it comprises the composition of following proportioning:
Polyvinyl chloride resin: 100;
Tackifier: 30;
Thermo-stabilizer: 20;
Strengthening agent: 50;
Strengthen resin: 10;
Lubricant: 0.5;
Promotor: 4.
Further, according to the mass fraction, it comprises the composition of following proportioning:
Polyvinyl chloride resin: 100;
Tackifier: 50;
Thermo-stabilizer: 40;
Strengthening agent: 200;
Strengthen resin: 20;
Lubricant: 1.5;
Promotor: 4-6.
The beneficial effect that the present invention reaches is:
Present invention process is simple, and obtained polyvinyl chloride plain film quality is good, and the present invention uses special formula, and the plasticizing of this sheet material evenly, flawless, good toughness, shock-resistant, fire-retardant, low-temperature performance is good, aging life-span is long.
Embodiment
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein is only for instruction and explanation of the present invention, is not intended to limit the present invention.
A kind of method of producing polyvinyl chloride plain film of the present invention, is characterized in that, with polyvinyl chloride resin: 100; Tackifier: 40-60; Thermo-stabilizer: 20-40; Strengthening agent: 50-200; Strengthen resin: 10-20; Lubricant: 0.5-1.5; Promotor: 4-6 is raw material compositing formula, mixes through heat mixing at a high speed, low speed heat, extrude, opens refining the pressure court of a feudal ruler, cooling and shaping, cuts packaging and produce polyvinyl chloride plain film.
Further, according to the mass fraction, it comprises the composition of following proportioning:
Polyvinyl chloride resin: 100;
Tackifier: 30;
Thermo-stabilizer: 20;
Strengthening agent: 50;
Strengthen resin: 10;
Lubricant: 0.5;
Promotor: 4.
Further, according to the mass fraction, it comprises the composition of following proportioning:
Polyvinyl chloride resin: 100;
Tackifier: 50;
Thermo-stabilizer: 40;
Strengthening agent: 200;
Strengthen resin: 20;
Lubricant: 1.5;
Promotor: 4-6.
The beneficial effect that the present invention reaches is:
The present invention uses special formula, and the plasticizing of this sheet material evenly, flawless, good toughness, shock-resistant, fire-retardant, low-temperature performance is good, aging life-span is long.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. produce a method for polyvinyl chloride plain film, it is characterized in that, with polyvinyl chloride resin: 100; Tackifier: 40-60; Thermo-stabilizer: 20-40; Strengthening agent: 50-200; Strengthen resin: 10-20; Lubricant: 0.5-1.5; Promotor: 4-6 is raw material compositing formula, mixes through heat mixing at a high speed, low speed heat, extrude, opens refining the pressure court of a feudal ruler, cooling and shaping, cuts packaging and produce polyvinyl chloride plain film.
2. the manufacture method of a kind of polyvinyl chloride plain film according to claim 1, is characterized in that, according to the mass fraction, it comprises the composition of following proportioning:
Polyvinyl chloride resin: 100;
Tackifier: 30;
Thermo-stabilizer: 20;
Strengthening agent: 50;
Strengthen resin: 10;
Lubricant: 0.5;
Promotor: 4.
3. the manufacture method of a kind of polyvinyl chloride plain film according to claim 1, is characterized in that, according to the mass fraction, it comprises the composition of following proportioning:
Polyvinyl chloride resin: 100;
Tackifier: 50;
Thermo-stabilizer: 40;
Strengthening agent: 200;
Strengthen resin: 20;
Lubricant: 1.5;
Promotor: 4-6.