CN105315537A - Transparent plastic material - Google Patents
Transparent plastic material Download PDFInfo
- Publication number
- CN105315537A CN105315537A CN201510843275.6A CN201510843275A CN105315537A CN 105315537 A CN105315537 A CN 105315537A CN 201510843275 A CN201510843275 A CN 201510843275A CN 105315537 A CN105315537 A CN 105315537A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic material
- transparent plastic
- fire retardant
- toughner
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a transparent plastic material. The transparent plastic material is prepared from, by weight, 20-30 parts of ABS plastic, 10-20 parts of phenolic resin, 30-35 parts of PE, 5-15 parts of polyether sulfone resin and 5-10 parts of an additive. The transparent plastic material has higher toughness under the condition of high transparency, the problem of the insufficient toughness of an existing transparent plastic product is avoided, the quality of the plastic product is greatly improved, and the service life is also greatly prolonged. In addition, the plastic product further has good chemical resistance and flame retardant performance, and the comprehensive performance of the product is improved obviously.
Description
Technical field
The present invention relates to Material Field, particularly relate to a kind of transparent plastic material.
Background technology
More existing plasthetics need it to have good transparency, but the performance such as other such as toughness of this plasthetics usual can decline obviously when having better transparency at present, easily damaged when causing this type of plasthetics to use, work-ing life is short, thereby also reduces the quality of clear plastics goods.
Summary of the invention
The object of the present invention is to provide a kind of transparent plastic material, aim to provide transparency good, the plastic material of long service life.
A kind of transparent plastic material, wherein: composed of the following components according to parts by weight:
ABS plastic 20-30 part;
Resol 10-20 part;
PE30-35 part;
Polyethersulfone resin 5-15 part;
Auxiliary agent 5-10 part.
Described transparent plastic material, wherein: described auxiliary agent is made up of toughner, light diffusing agent, fire retardant.
Described transparent plastic material, wherein: the interpolation part by weight of described toughner, light diffusing agent, fire retardant is 1:3:1.
Described transparent plastic material, wherein: described toughner is phosphoric acid ester.
Described transparent transparent plastic material, wherein: described fire retardant is brominated aromatic fire retardant.
Described transparent plastic material, wherein: composed of the following components according to parts by weight:
ABS plastic 25 parts;
15 parts, resol;
PE30 part;
Polyethersulfone resin 10 parts;
Toughner 2 parts;
Light diffusing agent 6 parts;
Fire retardant 2 parts.
Beneficial effect: the invention provides a kind of transparent plastic material, this plastic material has higher toughness when possessing high-clarity, avoid the problem of existing clear plastics goods toughness deficiency, greatly improve plastic cement products quality, work-ing life also extends greatly, plasthetics of the present invention also has good resistance toization and flame retardant properties simultaneously, and product over-all properties is obviously promoted.
Embodiment
For making object of the present invention, technical scheme and advantage clearly, clearly, the present invention is described in more detail below.
The invention provides a kind of transparent plastic material, wherein, composed of the following components according to parts by weight:
ABS plastic 20-30 part;
Resol 10-20 part;
PE30-35 part;
Polyethersulfone resin 5-15 part;
Auxiliary agent 5-10 part.
Wherein, described auxiliary agent is made up of toughner, light diffusing agent, fire retardant.Described toughner is phosphoric acid ester.
In preferred embodiment, the interpolation part by weight of described toughner, light diffusing agent, fire retardant is 1:3:1.Each component in auxiliary agent can be made farthest to play each self-applying according to this proportions auxiliary agent, cause too large loss can not to again plastic cement overall performance simultaneously.
It is preferred that described fire retardant is brominated aromatic fire retardant.Brominated aromatic fire retardant can guarantee that material transparent degree does not reduce while imparting plastic material flame retardant properties of the present invention,
Below in conjunction with specific embodiment, the present invention is described further.
Embodiment 1
Described transparent plastic material, composed of the following components according to parts by weight:
ABS plastic 25 parts;
15 parts, resol;
PE30 part;
Polyethersulfone resin 10 parts;
Toughner 2 parts;
Light diffusing agent 6 parts;
Fire retardant 2 parts.
The preparation method of transparent plastic material of the present invention comprises the following steps:
S1: prepare raw material according to said ratio;
S2: ABS plastic, PE are joined in the mixed pot of heat, temperature is risen to 80 DEG C, adds polyethersulfone resin under rotating speed 350r/min and resol stirs 1h; Temperature is risen to 100 DEG C, under rotating speed 450r/min, add toughner, light diffusing agent, fire retardant, stir 30min, obtain Preblend;
S3: Preblend is placed in twin screw extruder and extrudes, obtains plastic material through cooling, pelletizing.
After tested, the present embodiment gained plastic material transmittance is 95%, and elongation at break is 455%; Wherein, transmittance is according to ASTMD1746 standard testing, and elongation at break is tested by ASTMD638 standard, and following examples are same.
Embodiment 2
Described transparent plastic material, composed of the following components according to parts by weight:
ABS plastic 20 parts;
20 parts, resol;
PE35 part;
Polyethersulfone resin 5 parts;
Toughner 1 part;
Light diffusing agent 3 parts;
Fire retardant 1 part.
The preparation method of transparent plastic material of the present invention comprises the following steps:
S1: prepare raw material according to said ratio;
S2: ABS plastic, PE are joined in the mixed pot of heat, temperature is risen to 80 DEG C, adds polyethersulfone resin under rotating speed 350r/min and resol stirs 1h; Temperature is risen to 100 DEG C, under rotating speed 450r/min, add toughner, light diffusing agent, fire retardant, stir 30min, obtain Preblend;
S3: Preblend is placed in twin screw extruder and extrudes, obtains plastic material through cooling, pelletizing.After tested, the present embodiment gained plastic material transmittance is 92%, and elongation at break is 513%.
The invention provides a kind of transparent plastic material, this plastic material has higher toughness when possessing high-clarity, avoid the problem of existing clear plastics goods toughness deficiency, greatly improve plastic cement products quality, work-ing life also extends greatly, plasthetics of the present invention also has good resistance toization and flame retardant properties simultaneously, and product over-all properties is obviously promoted.
Should be understood that, application of the present invention is not limited to above-mentioned citing, for those of ordinary skills, can be improved according to the above description or convert, and all these improve and convert the protection domain that all should belong to claims of the present invention.
Claims (6)
1. a transparent plastic material, is characterized in that: composed of the following components according to parts by weight:
ABS plastic 20-30 part;
Resol 10-20 part;
PE30-35 part;
Polyethersulfone resin 5-15 part;
Auxiliary agent 5-10 part.
2. transparent plastic material according to claim 1, is characterized in that: described auxiliary agent is made up of toughner, light diffusing agent, fire retardant.
3. transparent plastic material according to claim 2, is characterized in that: the interpolation part by weight of described toughner, light diffusing agent, fire retardant is 1:3:1.
4. transparent plastic material according to claim 3, is characterized in that: described toughner is phosphoric acid ester.
5. transparent transparent plastic material according to claim 4, is characterized in that: described fire retardant is brominated aromatic fire retardant.
6. transparent plastic material according to claim 5, is characterized in that: composed of the following components according to parts by weight:
ABS plastic 25 parts;
15 parts, resol;
PE30 part;
Polyethersulfone resin 10 parts;
Toughner 2 parts;
Light diffusing agent 6 parts;
Fire retardant 2 parts.