CN104844121A - 一种无收缩套筒灌浆料及其制备方法 - Google Patents

一种无收缩套筒灌浆料及其制备方法 Download PDF

Info

Publication number
CN104844121A
CN104844121A CN201510289875.2A CN201510289875A CN104844121A CN 104844121 A CN104844121 A CN 104844121A CN 201510289875 A CN201510289875 A CN 201510289875A CN 104844121 A CN104844121 A CN 104844121A
Authority
CN
China
Prior art keywords
grouting material
parts
sleeve grouting
ungauged regions
material according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510289875.2A
Other languages
English (en)
Inventor
邓小旭
周强
程凯斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hubei Chidge Technology Co Ltd
Original Assignee
Hubei Chidge Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hubei Chidge Technology Co Ltd filed Critical Hubei Chidge Technology Co Ltd
Priority to CN201510289875.2A priority Critical patent/CN104844121A/zh
Publication of CN104844121A publication Critical patent/CN104844121A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种灌浆料及制备方法，属于工程材料领域，具体涉及一种无收缩套筒灌浆料及制备方法。该无收缩套筒灌浆料包括如下重量份数的组分：水泥320～500份；粉煤灰10～50份；细骨料400～550份；膨胀组分10～50份；减水剂1～20份；稳定剂0.5～2份；增稠剂0.02～1份；聚丙烯酰胺0.05～5份；膨润土60～150份。该高强无收缩套筒灌浆料具有较好的流动性、可操作时间长、稳定性、填充性、早强、高强、微膨胀性。

Description

一种无收缩套筒灌浆料及其制备方法
技术领域
本发明涉及一种灌浆料及制备方法，属于工程材料领域，具体涉及一种无收缩套筒灌浆料及制备方法。
背景技术
近些年来，随着我国装配式混凝土结构的发展，对节点连接技术提出了新的要求，灌浆套筒连接技术就是在这样的背景下应运而生的。较传统的钢筋焊接和机械连接，套筒连接具有结构和施工两方面的优势。钢筋套筒连接器应用于预制构件中钢筋的连接，是通过无收缩高强灌浆料作为传递荷载和材料间粘结力的媒介。钢筋套筒连接器的使用大大减少了预制构件的安装时间，降低钢筋重叠长度。在钢筋混凝土结构中，钢筋与混凝土两种性质完全不同的材料之所以能够共同工作，主要是依靠钢筋与混凝土之间的粘结应力。
但是，现市场上的灌浆料质量参差不齐，特别是高强微膨胀型的灌浆料还不是很多，因此对于研究一种具有高强、高流动性、微膨胀型的用于无收缩套筒的灌浆料具有重要的意义。
发明内容
本发明主要是解决现有技术所存在的上述的技术问题，提供了一种无收缩套筒灌浆料及制备方法。该高强无收缩套筒灌浆料具有较好的流动性、可操作时间长、稳定性、填充性、早强、高强、微膨胀性。
为了解决上述问题，根据本发明的一个方面，提供了一种无收缩套筒灌浆料，包括如下重量份数的组分：
优化的，上述的一种无收缩套筒灌浆料，所述水泥包括如下重量份数的组分：
硫铝酸盐水泥  200～300份；
硅酸盐水泥    120～200份。
优化的，上述的一种无收缩套筒灌浆料，所述细骨料为多粒级组配的机制石英砂，组配比例按重量份数为：
0.2～0.4mm砂  20～30份；
0.4～0.8mm砂  40～60份；
0.8～2mm砂    10～20份。
优化的，上述的一种无收缩套筒灌浆料，所述膨胀组分为UEA膨胀剂或/和CSA膨胀剂。
优化的，上述的一种无收缩套筒灌浆料，所述的减水剂为聚羧酸盐类高效减水剂、萘系高效减水剂、三聚氰胺高效减水剂、脂肪族高效减水剂、氨基磺酸系高效减水剂中的一种以上。
优化的，上述的一种无收缩套筒灌浆料，所述稳定剂包括如下重量份数的组分：
优化的，上述的一种无收缩套筒灌浆料，所述增稠剂选自羟甲基纤维素、羟乙基纤维素、羟丙基甲基纤维素和膨润土的一种或多种。
优化的，上述的一种无收缩套筒灌浆料，将各组分混合均匀后，以0.13～0.16的水料比加水，使用制浆机快速搅拌制得无收缩套筒灌浆料。
为了解决上述问题，根据本发明的另一个方面，提供了一种制备上述的无收缩套筒灌浆料的方法，包括：将各组分混合均匀后，以0.12～0.14的水料比加水，使用制浆机快速搅拌制得无收缩套筒灌浆料。
因此，本发明具有如下优点：该高强无收缩套筒灌浆料具有较好的流动性、可操作时间长、稳定性、填充性、早强、高强、微膨胀性。
具体实施方式
以下通过实施例形式对本发明的上述内容再作进一步的详细说明，但不应将此理解为本发明上述主题的范围仅限于以下的实施例，凡基于本发明上述内容所实现的技术均属于本发明的范围。
实施例：
一种无收缩套筒灌浆料，包括如下重量份数的组分：
其中，细骨料为多粒级组配的机制石英砂，组配比例按重量份数为：
0.2～0.4mm砂  20～30份；
0.4～0.8mm砂  40～60份；
0.8～2mm砂    10～20份。
稳定剂包括如下重量份数的组分：
本实施例中的膨胀组份可选择UEA膨胀剂或/和CSA膨胀剂。减水剂为聚羧酸盐类高效减水剂、萘系高效减水剂、三聚氰胺高效减水剂、脂肪族高效减水剂、氨基磺酸系高效减水剂中的一种以上；增稠剂可选自羟甲基纤维素、羟乙基纤维素、羟丙基甲基纤维素和膨润土的一种或几种。
使用时，将该材料加水直接搅拌，水与材料的重量比为0.13～0.16。该高强无收缩套筒灌浆料具有较好的流动性、可操作时间长、稳定性、填充性、早强、高强、微膨胀性。
该材料适用于设备基础的二次灌浆、混凝土结构的加固改造、钢筋和地脚螺栓的锚固、套筒和带肋钢筋间隙灌浆等，加水搅拌后具有较大的流动度和微膨胀性，通过灌注，与螺纹钢筋连接，填充于套筒和带肋钢筋间隙内，形成钢筋灌浆连接接头。
本文中所描述的具体实施例仅仅是对本发明精神作举例说明。本发明所属技术领域的技术人员可以对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代，但并不会偏离本发明的精神或者超越所附权利要求书所定义的范围。

Claims (8)

1.一种无收缩套筒灌浆料，其特征在于，包括如下重量份数的组分：
2.根据权利要求1所述的一种无收缩套筒灌浆料，其特征在于，所述水泥包括如下重量份数的组分：
硫铝酸盐水泥    200～300份；
硅酸盐水泥      120～200份。
3.根据权利要求1所述的一种无收缩套筒灌浆料，其特征在于，所述细骨料为多粒级组配的机制石英砂，组配比例按重量份数为：
0.2～0.4mm砂    20～30份；
0.4～0.8mm砂    40～60份；
0.8～2mm砂      10～20份。
4.根据权利要求1所述的一种无收缩套筒灌浆料，其特征在于，所述膨胀组分为UEA膨胀剂或/和CSA膨胀剂。
5.根据权利要求1所述的一种无收缩套筒灌浆料，其特征在于，所述的减水剂为聚羧酸盐类高效减水剂、萘系高效减水剂、三聚氰胺高效减水剂、脂肪族高效减水剂、氨基磺酸系高效减水剂中的一种以上。
6.根据权利要求1所述的一种无收缩套筒灌浆料，其特征在于，所述稳定剂包括如下重量份数的组分：
7.根据权利要求1所述的一种无收缩套筒灌浆料，其特征在于，所述增稠剂选自羟甲基纤维素、羟乙基纤维素、羟丙基甲基纤维素和膨润土的一种或多种。
8.一种制备权利要求1所述的无收缩套筒灌浆料的方法，其特征在于，将各组分混合均匀后，以0.13～0.16的水料比加水，使用制浆机快速搅拌制得无收缩套筒灌浆料。
CN201510289875.2A 2015-05-29 2015-05-29 一种无收缩套筒灌浆料及其制备方法 Pending CN104844121A (zh)