CN104844089A - 一种粘合砂浆及其制备方法 - Google Patents
一种粘合砂浆及其制备方法 Download PDFInfo
- Publication number
- CN104844089A CN104844089A CN201510213403.9A CN201510213403A CN104844089A CN 104844089 A CN104844089 A CN 104844089A CN 201510213403 A CN201510213403 A CN 201510213403A CN 104844089 A CN104844089 A CN 104844089A
- Authority
- CN
- China
- Prior art keywords
- parts
- mortar
- water
- mixing
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种粘合砂浆,由下列重量份的原料制成:甲基纤维素2-4、氯化铵1-2、凹凸棒石粘土10-15、膨润土8-10、作物秸秆8-10、羟乙基纤维素2-3、酚醛树脂10-15、水适量、乙二醇8-10、助剂20-25、水泥190-210、海藻酸钙3-4、沙子260-280、气相白炭黑10-15、丝光沸石30-40;本发明砂浆粘结力强,不空鼓,韧性好,不开裂,而且具有环保、防火、抗冻、防水和施工方便的优点;通过使用本发明助剂,提高了砂浆的抗压、抗折强度,改善了和易性、抗流挂性、触变性和防沉降性。
Description
技术领域
本发明属于建筑材料领域,特别涉及一种粘合砂浆及其制备方法。
背景技术
砂浆为建筑用普通材料,属于建筑施工中的必备材料。根据性能划分,砂浆分为很多种,有结合砂浆、嵌缝砂浆、保温砂浆等;按用途分为砌筑砂浆、抹面砂浆(包括装饰砂浆、防水砂浆)、粘结砂浆等。
目前砂浆的性能品质不一,影响着使用。具体来讲影响砂浆性能的因素包括新拌砂浆的和易性、流动性、保水性,还有就是硬化砂浆的强度。需要研究新的砂浆,使其具有优异的施工性和加工性、抗流挂性、触变性、防沉降性、贮存稳定性、改善泵送性和剪切稀化性,还需要寻找新的材料,以提高其使用性能和强度,以及降低综合成本。
发明内容
本发明的目的在于提供一种粘合砂浆及其制备方法,该砂浆粘结力强,不空鼓,韧性好,不开裂,而且具有环保、防火、抗冻、防水和施工方便的优点。
本发明的技术方案如下:
一种粘合砂浆,其特征在于由下列重量份的原料制成:甲基纤维素2-4、氯化铵1-2、凹凸棒石粘土10-15、膨润土8-10、作物秸秆8-10、羟乙基纤维素2-3、酚醛树脂10-15、水适量、乙二醇8-10、助剂20-25、水泥190-210、海藻酸钙3-4、沙子260-280、气相白炭黑10-15、丝光沸石30-40;
所述助剂由下列重量份的原料制成:聚异丁烯0.8-1.2、不锈钢纤维6-7、乙炔炭黑2-3、异辛酸铅0.4-0.5、双季戊四醇六丙烯酸酯4-5、甲基丙烯酸甲酯2-3、氨基树脂0.8-1.2、有机膨润土1-1.4、酒石酸0.6-0.9、硼酸镁晶须1-2、气相三氧化二铝1-2、环氧丙烯酸酯3-4、聚四氟乙烯微粉2-3、薄荷油0.4-0.5、十二烷基苯磺酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水15-18;制备方法为:将水、十二烷基苯磺酸钠、双季戊四醇六丙烯酸酯、甲基丙烯酸甲酯、氨基树脂、气相三氧化二铝、环氧丙烯酸酯、薄荷油混合,加热至70-80℃,加入过硫酸钾搅拌反应15-20分钟,再加入其他剩余成分,加热至80-90℃,搅拌反应30-40分钟,即得。
所述的粘合砂浆的制备方法,其特征在于包括以下步骤:
(1)将凹凸棒石粘土、膨润土混合,粉碎成140-180目颗粒;
(2)将甲基纤维素、氯化铵、羟乙基纤维素、海藻酸钙、水混合,搅拌均匀得到浆料;
(3)将助剂、酚醛树脂、作物秸秆、气相白炭黑、乙二醇混合,分散研磨20-30分钟,得到混合物料;
(4)将其他剩余成分与第(1)步、第(2)步、第(3)步得到的物料混合均匀,搅拌反应10-15分钟,即得。
本发明的有益效果
本发明砂浆粘结力强,不空鼓,韧性好,不开裂,而且具有环保、防火、抗冻、防水和施工方便的优点;通过使用本发明助剂,提高了砂浆的抗压、抗折强度,改善了和易性、抗流挂性、触变性和防沉降性。
具体实施方式
一种粘合砂浆,由下列重量份(公斤)的原料制成:甲基纤维素3、氯化铵1.5、凹凸棒石粘土13、膨润土9、作物秸秆9、羟乙基纤维素2.5、酚醛树脂13、水适量、乙二醇9、助剂23、水泥200、海藻酸钙3.5、沙子270、气相白炭黑13、丝光沸石35;
所述助剂由下列重量份(公斤)的原料制成:聚异丁烯1.1、不锈钢纤维6.5、乙炔炭黑2.5、异辛酸铅0.5、双季戊四醇六丙烯酸酯4.5、甲基丙烯酸甲酯2.5、氨基树脂1、有机膨润土1.2、酒石酸0.7、硼酸镁晶须1.5、气相三氧化二铝1.5、环氧丙烯酸酯3.5、聚四氟乙烯微粉2.5、薄荷油0.4、十二烷基苯磺酸钠0.2、过硫酸铵0.1、过硫酸钾0.1、水16;制备方法为:将水、十二烷基苯磺酸钠、双季戊四醇六丙烯酸酯、甲基丙烯酸甲酯、氨基树脂、气相三氧化二铝、环氧丙烯酸酯、薄荷油混合,加热至75℃,加入过硫酸钾搅拌反应18分钟,再加入其他剩余成分,加热至85℃,搅拌反应36分钟,即得。
所述的粘合砂浆的制备方法,包括以下步骤:
(1)将凹凸棒石粘土、膨润土混合,粉碎成150目颗粒;
(2)将甲基纤维素、氯化铵、羟乙基纤维素、海藻酸钙、水混合,搅拌均匀得到浆料;
(3)将助剂、酚醛树脂、气相白炭黑、作物秸秆、乙二醇混合,分散研磨25分钟,得到混合物料;
(4)将其他剩余成分与第(1)步、第(2)步、第(3)步得到的物料混合均匀,搅拌反应13分钟,即得。
实验数据:
该实施例的砂浆28d的抗压强度为45MPa,抗折强度 15MPa,吸水率2.3%,导热系数为0.46W/m·k。
Claims (2)
1.一种粘合砂浆,其特征在于由下列重量份的原料制成:甲基纤维素2-4、氯化铵1-2、凹凸棒石粘土10-15、膨润土8-10、作物秸秆8-10、羟乙基纤维素2-3、酚醛树脂10-15、水适量、乙二醇8-10、助剂20-25、水泥190-210、海藻酸钙3-4、沙子260-280、气相白炭黑10-15、丝光沸石30-40;
所述助剂由下列重量份的原料制成:聚异丁烯0.8-1.2、不锈钢纤维6-7、乙炔炭黑2-3、异辛酸铅0.4-0.5、双季戊四醇六丙烯酸酯4-5、甲基丙烯酸甲酯2-3、氨基树脂0.8-1.2、有机膨润土1-1.4、酒石酸0.6-0.9、硼酸镁晶须1-2、气相三氧化二铝1-2、环氧丙烯酸酯3-4、聚四氟乙烯微粉2-3、薄荷油0.4-0.5、十二烷基苯磺酸钠0.2-0.3、过硫酸铵0.1-0.2、过硫酸钾0.1-0.2、水15-18;制备方法为:将水、十二烷基苯磺酸钠、双季戊四醇六丙烯酸酯、甲基丙烯酸甲酯、氨基树脂、气相三氧化二铝、环氧丙烯酸酯、薄荷油混合,加热至70-80℃,加入过硫酸钾搅拌反应15-20分钟,再加入其他剩余成分,加热至80-90℃,搅拌反应30-40分钟,即得。
2.根据权利要求1所述的粘合砂浆的制备方法,其特征在于包括以下步骤:
(1)将凹凸棒石粘土、膨润土混合,粉碎成140-180目颗粒;
(2)将甲基纤维素、氯化铵、羟乙基纤维素、海藻酸钙、水混合,搅拌均匀得到浆料;
(3)将助剂、酚醛树脂、作物秸秆、气相白炭黑、乙二醇混合,分散研磨20-30分钟,得到混合物料;
(4)将其他剩余成分与第(1)步、第(2)步、第(3)步得到的物料混合均匀,搅拌反应10-15分钟,即得。