CN104842079A - Cable bus opening heating ring and application thereof in cable bus copper pipe welding - Google Patents
Cable bus opening heating ring and application thereof in cable bus copper pipe welding Download PDFInfo
- Publication number
- CN104842079A CN104842079A CN201410056359.0A CN201410056359A CN104842079A CN 104842079 A CN104842079 A CN 104842079A CN 201410056359 A CN201410056359 A CN 201410056359A CN 104842079 A CN104842079 A CN 104842079A
- Authority
- CN
- China
- Prior art keywords
- welding
- copper pipe
- copper
- mouth
- pipe
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a cable bus opening heating ring and application thereof in cable bus copper pipe welding. The cable bus opening heating ring comprises a left heating ring and a right heating ring, wherein the left heating ring and the right heating ring both comprise red copper pipes, and cooling circulating ice water pipes connected with the red copper pipes; the red copper pipes are semicircular; connecting blocks are arranged in ports of the red copper pipes; and connecting holes are formed in the connecting blocks. The cable bus opening heating ring uses T3 copper pipes of phi 120* phi 80 mm as conductors, so that the heating speed is fast, the heating welding can be performed for straight ways, three-ways and elbows, the heating of the copper pipes in high altitude is realized, the welding temperature is reached, and the welding operation of the copper pipes in high altitude is finished.
Description
Technical field
The present invention relates to the solder technology of large workpiece copper and copper, being specially a kind of cable bus opening heating collar for powering and the application in the welding of cable bus copper pipe thereof.
Background technology
In brazing connects in the past, copper has the characteristics such as excellent electric conductivity, thermal conductivity, corrosion resistance, ductility and certain intensity.Be used widely in electric, electronics, chemical industry, food, power, traffic and aerospace industry.In fine copper (red copper), add more than 10 plant alloying element, form all kinds of copper alloys of solid solution, if zincification is brass; Adding nickel is copper-nickel alloy; Adding silicon is silicon bronze; Adding aluminium is aluminium bronze etc.
Copper and its alloy can realize connecting by the process such as soldering, electric resistance welding, at today, the melting welding dominate of industry prosperity.The welding of Copper and its alloy is easily realized by processes such as SMAW, TIG weldering, MIG welderings.
1, the method for welding red copper has the methods such as gas welding, manual carbon arc welding, manual electric arc welding and manual argon arc welding, and large scale structure also can adopt automatic welding:
(1) what the gas weld joint red copper of red copper was the most frequently used is banjo fixing butt jointing, and lap joint and T-joint are as far as possible few to be adopted.Gas welding can adopt two kinds of welding wires, and a kind of is welding wire containing deoxidant element, as silk 201,202; Another kind is general copper wire and the slitting of mother metal, adopts gas agent 301 to make flux.Neutral flame should be adopted during gas welding red copper.
(2) the manual electric arc welding edge of red copper, when weldment thickness is greater than 4 millimeters, necessary preheating before weldering, preheat temperature is generally at about 400 ~ 500 DEG C.With the welding of copper 107 welding rod, power supply should adopt DC reverse connection.Should use short arc during welding, welding rod should not do teeter.Reciprocal rectilinear motion made by welding rod, can improve the shaping of weld seam.Long weld seam should adopt backstep welding.Speed of welding should be tried one's best hurry up.During multilayer welding, necessary slag thoroughly between scavenger layer.
Welding should be carried out in draughty place, to prevent copper poisoning phenomenon.Postwelding application butt hammer knocks weld seam, eliminates stress and improves weldquality.
(3) manual argon arc welding of red copper is when red copper manual argon arc welding, and the welding wire of employing has silk 201 (special red copper welding wire) and silk 202, also adopts copper wire, as T2.Oxide-film, the wet goods foul of tackling workpiece welding edge and welding wire surface before weldering all must be cleaned out, and avoid producing the defect such as pore, slag inclusion.The method of cleaning has mechanical method of cleaning and soak cleaning method.When banjo fixing butt jointing thickness of slab is less than 3 millimeters, square groove; When thickness of slab is 3 ~ 10 millimeters, open double V-groove, bevel angle is 60 ~ 70 & ordm; ; When thickness of slab is greater than 10 millimeters, open X-type groove, bevel angle is 60 ~ 70 & ordm; ; Lack of penetration for avoiding, generally do not stay root face.According to thickness of slab and groove size, the fit-up gap of banjo fixing butt jointing is chosen within the scope of 0.5 ~ 1.5 millimeter.Red copper manual argon arc welding, normally adopts straight polarity direct current, and namely tungsten electrode connects negative pole.In order to eliminate pore, ensureing that the root of weld fuses and through welding reliably, must speed of welding be improved, reducing argon gas consumption, and preheating weldment.When thickness of slab is less than 3 millimeters, preheat temperature is 150 ~ 300 DEG C; When thickness of slab is greater than 3 millimeters, preheat temperature is 350 ~ 500 DEG C.Preheat temperature is unsuitable too high, otherwise the mechanical performance of welding point is reduced.Also have the carbon arc welding of red copper, the electrode that carbon arc welding uses has carbon electrode and graphite electrode.Red copper carbon arc welding welding wire used is the same with during gas welding, and also can cut bar with mother metal, the flux of available gas welding red copper, as gas agent 301 etc.
(4) ratio-frequency welding is high-frequency induction heating again, and ratio-frequency welding utilizes 10 ~ 500KHz high frequency electric to flow through metal joint face produce resistance heat and apply a kind of welding method that (or not applying) pressure reaches corrupt split.Be characterized in: speed of welding is large, and welding heat affected zone is little, welds and can not clear up workpiece, can weld light-wall pipe, solderable metal pipe, very relatively good to magnetic conductive metal welding, copper is magnetic conduction not.
(5) soldering high temperature furnace welding: can only small workpiece be welded, can not welding be moved.
Comprehensive said method: above-mentioned welding method, owing to all cannot heat copper pipe in high-altitude, reaches institute's welding temperature, so cannot weld φ 120x φ 80mmT3 copper pipe.
Summary of the invention
Technical problem solved by the invention is to provide a kind of cable bus opening heating collar and the application in the welding of cable bus copper pipe thereof, to solve the problem proposed in above-mentioned background technology.
The invention provides following technical scheme:
Cable bus opening heating collar, comprises left heating collar and right heating collar, and wherein left heating collar and right heating collar include copper tube, the down cycles frozen water pipe be connected with copper tube; Described copper tube is set to semicircle, and the port of copper tube is provided with contiguous block; Described contiguous block is provided with connecting hole.
The application of cable bus opening heating collar in the welding of cable bus copper pipe, is included in the welding of straight mouth, vertical tube elbow welding, three-way welding and parallel welding copper bus.
Described straight mouth welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert stainless steel tube, guarantee that the internal diameter of stainless steel tube inserted aligns with copper pipe internal diameter, between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 3 ~ 4 hours;
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, be incubated 20 seconds, turn off equipment, recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of copper pipe.
Preferably, described vertical tube elbow welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert stainless steel tube, guarantee that the internal diameter of stainless steel tube inserted aligns with copper pipe internal diameter, between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 6 ~ 7 hours
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when copper pipe welding position is heated to 730 DEG C, be incubated 20 seconds, turn off equipment, recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of copper pipe.
Preferably, described three-way welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert stainless steel tube, guarantee that the internal diameter of stainless steel tube inserted aligns with copper pipe internal diameter, between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 3 ~ 4 hours;
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, be incubated 20 seconds, turn off equipment, recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of copper pipe.
Preferably, described parallel welding copper bus, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) copper pipe washing trough, makes the counterpart of copper pipe ensure in same plane;
3) copper bar is put into copper pipe groove, in groove, coats silver paste, guarantee steel row and between copper pipe notch and mouth gap one to;
4) install by two broken rings, the heating collar of a copper bar circle composition, and clamp by fixture balance;
5) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
6) starting equipment, Voltage Cortrol is 450V, and electric current is 150A; ;
7) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, weld bond both sides 60% silver solder welds, and is incubated 10 minutes, turns off equipment, and recirculated water continues to keep duty;
8) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of copper pipe.
In sum, beneficial effect of the present invention:
The present invention utilizes φ 120x φ 80mmT3 copper pipe to do conductor, and firing rate is fast, can to straight-through, threeway, elbow, add thermal weld, realize high-altitude and copper pipe heated, reach institute's welding temperature, thus complete copper pipe at the aerial weld job of height.
Accompanying drawing explanation
Fig. 1 is structural representation of the present invention.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, be clearly and completely described the technical scheme in the embodiment of the present invention, obviously, described embodiment is only the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Cable bus opening heating collar provided by the invention, as shown in Figure 1, comprises left heating collar and right heating collar, wherein left heating collar and the right heating collar down cycles frozen water pipe 2 that includes copper tube 1, be connected with copper tube 1; Copper tube 1 is set to semicircle, and the port of copper tube 1 is provided with contiguous block 3; Contiguous block 3 is provided with connecting hole.
The application of cable bus opening heating collar in the welding of cable bus copper pipe, is included in the welding of straight mouth, vertical tube elbow welding, three-way welding and parallel welding copper bus.
Straight mouth welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding, because every bar copper pipe has 400Kg, heavier, when lifting, take care;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert the stainless steel tube that specification is φ 80x100x3mm, guarantee that the internal diameter of stainless steel tube inserted is that φ 120x φ 80mmT3 copper pipe internal diameter aligns with specification, keep between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 3 ~ 4 hours;
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, (heat time is 15 minutes) insulation 20 seconds, turns off equipment, and recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of φ 120x φ 80mmT3 copper pipe.
Vertical tube elbow welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding, because every bar copper pipe has 400Kg, heavier, when lifting, take care;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert the stainless steel tube that specification is φ 80x100x3mm, guarantee that the internal diameter of stainless steel tube inserted is that φ 120x φ 80mmT3 copper pipe internal diameter aligns with specification, keep between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 6 ~ 7 hours
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, (heat time is approximately 15 minutes) insulation 20 seconds, turns off equipment, and recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of φ 120x φ 80mmT3 copper pipe.
Three-way welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding, because every bar copper pipe has 400Kg, heavier, when lifting, take care;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert the stainless steel tube that specification is φ 80x100x3mm, guarantee that the internal diameter of stainless steel tube inserted is that φ 120x φ 80mmT3 copper pipe internal diameter aligns with specification, keep between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 3 ~ 4 hours;
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, (heat time is approximately 15 minutes) insulation 20 seconds, turns off equipment, and recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of φ 120x φ 80mmT3 copper pipe.
Parallel welding copper bus, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding, because every bar copper pipe has 400Kg, heavier, when lifting, take care;
2) copper pipe washing trough, makes the counterpart of copper pipe ensure in same plane;
3) copper bar is put into φ 120x φ 80mmT3 copper pipe groove, in groove, coats silver paste, guarantee steel row and between φ 120x φ 80mmT3 copper pipe notch and mouth gap one to;
4) install by two broken rings, the heating collar of a copper bar circle composition, and clamp by fixture balance;
5) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
6) starting equipment, Voltage Cortrol is 450V, and electric current is 150A; ;
7) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, weld bond both sides 60% silver solder welds, and is incubated 10 minutes, turns off equipment, and recirculated water continues to keep duty;
8) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of φ 120x φ 80mmT3 copper pipe.
The present invention utilizes φ 120x φ 80mmT3 copper pipe to do conductor, and firing rate is fast, can to straight-through, threeway, elbow, add thermal weld, realize high-altitude and copper pipe heated, reach institute's welding temperature, thus complete copper pipe at the aerial weld job of height.
To those skilled in the art, obviously the invention is not restricted to the details of above-mentioned one exemplary embodiment, and when not deviating from spirit of the present invention or essential characteristic, the present invention can be realized in other specific forms.Therefore, no matter from which point, all should embodiment be regarded as exemplary, and be nonrestrictive, scope of the present invention is limited by claims instead of above-mentioned explanation, and all changes be therefore intended in the implication of the equivalency by dropping on claim and scope are included in the present invention.
In addition, be to be understood that, although this description is described according to embodiment, but not each embodiment only comprises an independently technical scheme, this narrating mode of description is only for clarity sake, those skilled in the art should by description integrally, and the technical scheme in each embodiment also through appropriately combined, can form other embodiments that it will be appreciated by those skilled in the art that.
Claims (6)
1. cable bus opening heating collar, is characterized in that, comprises left heating collar and right heating collar, and wherein left heating collar and right heating collar include copper tube, the down cycles frozen water pipe be connected with copper tube; Described copper tube is set to semicircle, and the port of copper tube is provided with contiguous block; Described contiguous block is provided with connecting hole.
2. the application of cable bus opening heating collar in the welding of cable bus copper pipe, is characterized in that, is included in the welding of straight mouth, vertical tube elbow welding, three-way welding and parallel welding copper bus.
3. the application of cable bus opening heating collar according to claim 2 in the welding of cable bus copper pipe, is characterized in that, described straight mouth welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert stainless steel tube, guarantee that the internal diameter of stainless steel tube inserted aligns with copper pipe internal diameter, between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 3 ~ 4 hours;
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when copper pipe welding position is heated to 730 DEG C, be incubated 20 seconds, turn off equipment, recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of copper pipe.
4. the application of cable bus opening heating collar according to claim 2 in the welding of cable bus copper pipe, it is characterized in that, described vertical tube elbow welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert stainless steel tube, guarantee that the internal diameter of stainless steel tube inserted aligns with copper pipe internal diameter, between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 6 ~ 7 hours
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, be incubated 20 seconds, turn off equipment, recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of copper pipe.
5. the application of cable bus opening heating collar according to claim 2 in the welding of cable bus copper pipe, it is characterized in that, described three-way welding, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) beat groove, make the counterpart of copper pipe ensure in same plane;
3) in steel pipe, insert stainless steel tube, guarantee that the internal diameter of stainless steel tube inserted aligns with copper pipe internal diameter, between mouth and mouth gap one to;
4) stainless steel tube is exited 40mm to good mouth, be coated with silver paste;
5) counterpart again, guarantee that counterpart parallel clearance is 5 ~ 10mm, the time is 3 ~ 4 hours;
6) heating collar is installed, with the clamping of fixture balance;
7) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
8) starting equipment, Voltage Cortrol is 450V, and electric current is 150A;
9) when φ 120x φ 80mmT3 copper pipe welding position is heated to 730 DEG C, be incubated 20 seconds, turn off equipment, recirculated water continues to keep duty;
10) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of φ 120x φ 80mmT3 copper pipe.
6. the application of cable bus opening heating collar according to claim 2 in the welding of cable bus copper pipe, it is characterized in that, described parallel welding copper bus, comprises the following steps:
1) lift, by lifting steel pipes to the position needing welding;
2) copper pipe washing trough, makes the counterpart of copper pipe ensure in same plane;
3) copper bar is put into copper pipe groove, in groove, coats silver paste, guarantee steel row and between copper pipe notch and mouth gap one to;
4) install by two broken rings, the heating collar of a copper bar circle composition, and clamp by fixture balance;
5) install ice water circulation water pipe, ensure that recirculated water water flowing is unimpeded, pressure is 3.5kg/cm
2;
6) starting equipment, Voltage Cortrol is 450V, and electric current is 150A; ;
7) when copper pipe welding position is heated to 730 DEG C, weld bond both sides 60% silver solder welds, and is incubated 10 minutes, turns off equipment, and recirculated water continues to keep duty;
8) when temperature is down to 390-410 DEG C, fixture of dismantling, completes the straight mouth welding of copper pipe.