CN104818132B - 一种触控玻璃钢化工艺之后的清洗剂 - Google Patents
一种触控玻璃钢化工艺之后的清洗剂 Download PDFInfo
- Publication number
- CN104818132B CN104818132B CN201510111719.7A CN201510111719A CN104818132B CN 104818132 B CN104818132 B CN 104818132B CN 201510111719 A CN201510111719 A CN 201510111719A CN 104818132 B CN104818132 B CN 104818132B
- Authority
- CN
- China
- Prior art keywords
- touch
- cleaning agent
- steel process
- glass steel
- control glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种触控玻璃钢化工艺之后的清洗剂,包括重量比为:二甲基苯磺酸钠:2~15%;非离子型表面活性剂:2~15%;十二烷基苯磺酸:1~5%;二乙醇胺:1~5%;50%浓度的液体柠檬酸:2~15%;余量去离子水,所述的非离子型表面活性剂可以包含高碳脂肪醇聚氧乙烯醚(AEO)、聚氧乙烯烷基酰醇胺、脂肪酸甲酯乙氧基化物(FMEE)等中的两种或三种。本发明的触控玻璃钢化工艺之后的清洗剂,使强化后玻璃经过单次短时间浸泡就能,去除表面95%以上化学残留药剂,极大的缩减了后续的清洗工序,和高纯水使用量的优点。
Description
技术领域:
本发明属于玻璃钢化领域中的清洗用品,具体涉及的是一种触控玻璃钢化工艺之后的清洗剂。
背景技术:
现有技术下的钢化工艺完成后,玻璃表面会残留许多化学成分,且由于钢化反应是在极高温度下进行,制品钢化完成后,药剂会在玻璃表面迅速凝固。触控钢化玻璃,由于产业的特殊性,对玻璃的表面洁净度要求非常高,玻璃后续清工序往往需要引用超纯水,经过绵长的清洗工序才能清洗出合格干净的产品。
发明内容:
针对现有技术存在的缺陷,本发明的目的是提供一种可以克服上述缺陷的,可减少极大的缩减了后续的清洗工序,和高纯水使用量的触控玻璃钢化工艺之后的清洗剂。
本发明解决其技术问题所采取的技术方案是:一种触控玻璃钢化工艺之后的清洗剂,关键在于所述的清洗剂包括重量比为:40%浓度的二甲基苯磺酸钠: 1~10%;非离子型表面活性剂 2~10%;30%浓度的烷基苯磺酸: 1~10%;羧甲基纤维素钠:0.5%~3%:二乙醇胺1~10%;二缩丙二醇单甲醚:5~10%;50%浓度的液体柠檬酸:2~15%;余量去离子水。
本发明的触控玻璃钢化工艺之后的清洗剂,使强化后玻璃经过单次短时间浸泡就能,去除表面95%以上化学残留药剂,极大的缩减了后续的清洗工序,和高纯水使用量的优点。
具体实施方式:
一种触控玻璃钢化工艺之后的清洗剂,所述的清洗剂包括重量比为:40%浓度的二甲基苯磺酸钠: 1~10%;非离子型表面活性剂 2~10%;30%浓度的烷基苯磺酸: 1~10%;羧甲基纤维素钠:0.5~3%:二乙醇胺1~10%;二缩丙二醇单甲醚:5~10%;50%浓度的液体柠檬酸:2~15%;余量去离子水。
实施例1
一种触控玻璃钢化工艺之后的清洗剂,包括重量比为:40%浓度的二甲基苯磺酸钠: 5%;非离子型表面活性剂5%;30%浓度的烷基苯磺酸: 5%;羧甲基纤维素钠:3%:二乙醇胺7%;二缩丙二醇单甲醚:8%;50%浓度的液体柠檬酸:10%;余量去离子水。
实施例2
一种触控玻璃钢化工艺之后的清洗剂,包括重量比为:40%浓度的二甲基苯磺酸钠: 1%;非离子型表面活性剂2%;30%浓度的烷基苯磺酸:10%;羧甲基纤维素钠: 3%:二乙醇胺1%;二缩丙二醇单甲醚:5%;50%浓度的液体柠檬酸:2%;余量去离子水。
实施例3
一种触控玻璃钢化工艺之后的清洗剂,包括重量比为:40%浓度的二甲基苯磺酸钠: 10%;非离子型表面活性剂10%;30%浓度的烷基苯磺酸: 10%;羧甲基纤维素钠: 3%:二乙醇胺10%;二缩丙二醇单甲醚: 10%;50%浓度的液体柠檬酸: 15%;余量去离子水。
Claims (1)
1.一种触控玻璃钢化工艺之后的清洗剂,其特征在于,该清洗剂包括重量比为:40%浓度的二甲基苯磺酸钠: 1~10%;非离子型表面活性剂 2~10%;30%浓度的烷基苯磺酸: 1~10%;羧甲基纤维素钠:0.5%~3%:二乙醇胺1~10%;二缩丙二醇单甲醚:5~10%;50%浓度的液体柠檬酸:2~15%;余量去离子水,其中所述非离子型表面活性剂为聚氧乙烯烷基酰醇胺和脂肪酸甲酯乙氧基化物。