CN111154560B - 玻璃清洗剂、玻璃清洗剂的制备方法及应用 - Google Patents
玻璃清洗剂、玻璃清洗剂的制备方法及应用 Download PDFInfo
- Publication number
- CN111154560B CN111154560B CN202010016806.5A CN202010016806A CN111154560B CN 111154560 B CN111154560 B CN 111154560B CN 202010016806 A CN202010016806 A CN 202010016806A CN 111154560 B CN111154560 B CN 111154560B
- Authority
- CN
- China
- Prior art keywords
- glass
- cleaning agent
- percent
- glass cleaning
- anionic surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种玻璃清洗剂、玻璃清洗剂的制备方法及应用，其中，玻璃清洗剂包括如下重量百分含量的各组分：有机酸5％‑50％、非离子表面活性剂1％‑6％、阴离子表面活性剂1％‑5％、增稠剂1％‑5％以及水34％‑92％。上述玻璃清洗剂中的各组分配比合理，玻璃清洗剂为酸性清洗体系。其中，有机酸在对玻璃表面去污的同时，对玻璃的腐蚀性弱；而非离子表面活性剂的润湿性强，能有效去除玻璃表面油渍以及不易溶解的颗粒污垢；阴离子表面活性剂具有良好的脱脂性，净洗能力强。经试验验证，采用上述玻璃清洗剂清洗的玻璃合格率均达到90％以上，满足生产需求。
Description
技术领域
本发明涉及玻璃清洗技术领域，特别是涉及一种玻璃清洗剂以及玻璃清洗剂的制备方法及应用。
背景技术
在玻璃的生产过程中，加工的耗材及空气中的灰尘均会导致玻璃釉不同程度的脏污。传统的玻璃清洗多选用碱性清洗剂，但碱性清洗剂中的氢氧根离子对玻璃的腐蚀性强，会断裂玻璃硅氧键，导致产品耐冲击性能有所降低，甚至有部分耐碱性能较差的玻璃在清洗后出现发蓝、朦划伤等外观不良问题。
发明内容
基于此，有必要针对传统的碱性清洗剂对玻璃腐蚀性强的问题，提供一种能够避免对玻璃形成损伤的新型玻璃清洗剂的制备方法及应用。
一种玻璃清洗剂，其包括如下重量百分含量的各组分：
上述玻璃清洗剂中的各组分配比合理，玻璃清洗剂为酸性清洗体系。其中，有机酸在对玻璃表面去污的同时，对玻璃的腐蚀性弱；而非离子表面活性剂的润湿性强，能有效去除玻璃表面油渍以及不易溶解的颗粒污垢；阴离子表面活性剂具有良好的脱脂性，净洗能力强。经试验验证，采用上述玻璃清洗剂清洗的玻璃合格率均达到90％以上，能够满足生产需求。
在其中一个实施例中，包括如下重量百分含量的各组分：
在其中一个实施例中，所述有机酸选自柠檬酸和草酸中的一种或两种。
在其中一个实施例中，所述非离子表面活性剂选自EO/PO嵌段聚醚、异辛醇磷酸酯衍生物和乙氧基化脂肪酸甲酯类衍生物中的一种或几种。
在其中一个实施例中，所述非离子表面活性剂选自脂肪酸甲酯乙氧基化物和月桂醇聚氧乙烯聚氧丙烯醚中的一种或两种。
在其中一个实施例中，所述阴离子表面活性剂选自脂肪酸甲酯乙氧基化物磺酸盐。
在其中一个实施例中，所述阴离子表面活性剂选自脂肪酸甲酯乙氧基化物磺酸钠。
在其中一个实施例中，所述增稠剂为无机盐增稠剂。
本发明还提供一种玻璃清洗剂的制备方法，其包括以下步骤：
将本发明任一项所述的玻璃清洗剂中的有机酸、阴离子表面活性剂、非离子表面活性剂、增稠剂以及水混合。
本发明还提供一种采用本发明任一项所述的玻璃清洗剂清洗玻璃的方法。
具体实施方式
为使本发明的上述目的、特征和优点能够更加明显易懂，下面对本发明的具体实施方式做详细的说明。在下面的描述中阐述了很多具体细节以便于充分理解本发明。但是本发明能够以很多不同于在此描述的其它方式来实施，本领域技术人员可以在不违背本发明内涵的情况下做类似改进，因此本发明不受下面公开的具体实施例的限制。
除非另有定义，本文所使用的所有的技术和科学术语与属于本发明的技术领域的技术人员通常理解的含义相同。本文中在本发明的说明书中所使用的术语只是为了描述具体的实施例的目的，不是旨在于限制本发明。本文所使用的术语“及/或”包括一个或多个相关的所列项目的任意的和所有的组合。
本发明一实施例中提供了一种玻璃清洗剂，其包括如下重量百分含量的各组分：
上述玻璃清洗剂中的各组分配比合理，玻璃清洗剂为酸性清洗体系。其中，有机酸在对玻璃表面去污的同时，对玻璃的腐蚀性弱，避免对玻璃形成损伤；而非离子表面活性剂的润湿性强，能有效去除玻璃表面油渍以及不易溶解的颗粒污垢；阴离子表面活性剂具有良好的脱脂性，净洗能力强。经试验验证，采用上述玻璃清洗剂清洗的玻璃合格率均达到90％以上，满足生产需求，且上述玻璃清洗剂消泡能力强，泡沫量少。
发明人发现，传统的玻璃清洗剂中为了达到无泡效果，会在玻璃清洗剂中添加一定量的有机硅消泡剂，如果这种消泡剂若在钢化时未清理干净，会导致钢化凹凸点不良。本申请上述玻璃清洗剂无需添加消泡剂，即可达到消泡效果，泡沫量少。
在其中一个实施例中，玻璃清洗剂包括如下重量百分含量的各组分：
在其中一个实施例中，所述有机酸选自柠檬酸和草酸中的一种或两种。选自柠檬酸、草酸的好处是对玻璃的腐蚀性弱，且为环保材料。
在其中一个实施例中，所述非离子表面活性剂选自EO/PO嵌段聚醚、异辛醇磷酸酯衍生物和乙氧基化脂肪酸甲酯类衍生物中的一种或几种。
在其中一个实施例中，所述非离子表面活性剂选自脂肪酸甲酯乙氧基化物和月桂醇聚氧乙烯聚氧丙烯醚中的一种或两种。
在本实施例中，脂肪酸甲酯乙氧基化物是一种典型的非离子表面活性剂，与传统的脂肪醇乙氧基化物相比，具有低泡沫、高浊点，冷水溶速度快等优点。
在本实施例中，月桂醇聚氧乙烯聚氧丙烯醚润湿性强，能有效去除玻璃表面油渍及不溶性颗粒污垢。
在其中一个实施例中，所述阴离子表面活性剂选自脂肪酸甲酯乙氧基化物磺酸盐。
在其中一个实施例中，所述阴离子表面活性剂选自脂肪酸甲酯乙氧基化物磺酸钠。脂肪酸甲酯乙氧基化物磺酸钠具有良好的脱脂性，可以弥补酸性清洗剂对油脂清洗能力的不足。
在其中一个实施例中，所述增稠剂为无机盐增稠剂，无机盐增稠剂可以为氧化镁和环状酸酐的组合物、氯化锂和氧化镁的组合物或氯化钠。
本发明还提供一种玻璃清洗剂的制备方法，其包括以下步骤：
将本发明任一项所述的玻璃清洗剂中的有机酸、阴离子表面活性剂、非离子表面活性剂、增稠剂以及水混合，即得玻璃清洗剂。
在其中一个实施例中，在将所述的玻璃清洗剂中的有机酸、阴离子表面活性剂、非离子表面活性剂、增稠剂以及水混合的步骤中，混合条件进一步选自在35-50℃下混合均匀。
上述玻璃清洗剂的制备方法的制备方法简单，经试验验证，采用上述玻璃清洗剂清洗的玻璃合格率均达到90％以上，满足生产需求。
为了使本发明的目的及优点更加清楚明白，以下结合实施例对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅用以解释本发明，并不用于限定本发明。
实施例1
一种玻璃清洗剂的制备方法，其包括以下步骤：
1)备料：按照如下质量百分数取用各原料：柠檬酸20％、脂肪酸甲酯乙氧基化物2％、脂肪酸甲酯乙氧基化物磺酸钠2％、氯化钠1％，余量为去离子水。
2)混合：将步骤1)中的各原料在40℃下混合均匀，得到玻璃清洗剂。
3)稀释：将本实施例中清洗剂稀释7倍后用于玻璃清洗。
实施例2
一种玻璃清洗剂的制备方法，其包括以下步骤：
1)备料：按照如下质量百分数取用各原料：柠檬酸20％、月桂醇聚氧乙烯聚氧丙烯醚2％、脂肪酸甲酯乙氧基化物磺酸钠2％、氯化钠1％，余量为去离子水。
2)混合：将步骤1)中的各原料在40℃下混合均匀，得到玻璃清洗剂。
3)稀释：将本实施例中清洗剂稀释7倍后用于玻璃清洗。
实施例3
一种玻璃清洗剂的制备方法，其包括以下步骤：
1)备料：按照如下质量百分数取用各原料：柠檬酸20％、月桂醇聚氧乙烯聚氧丙烯醚1％、脂肪酸甲酯乙氧基化物1％、脂肪酸甲酯乙氧基化物磺酸钠2％、氯化钠1％，余量为去离子水。
2)混合：将步骤1)中的各原料在40℃下混合均匀，得到玻璃清洗剂。
3)稀释：将本实施例中清洗剂稀释7倍后用于玻璃清洗。
实施例4
一种玻璃清洗剂的制备方法，其包括以下步骤：
1)备料：按照如下质量百分数取用各原料：柠檬酸20％、月桂醇聚氧乙烯聚氧丙烯醚0.5％、脂肪酸甲酯乙氧基化物1.5％、脂肪酸甲酯乙氧基化物磺酸钠2％、氯化钠1％，余量为去离子水。
2)混合：将步骤1)中的各原料在40℃下混合均匀，得到玻璃清洗剂。
3)稀释：将本实施例中清洗剂稀释7倍后用于玻璃清洗。
实施例5
一种玻璃清洗剂的制备方法，其包括以下步骤：
1)备料：按照如下质量百分数取用各原料：柠檬酸20％、月桂醇聚氧乙烯聚氧丙烯醚1.5％、脂肪酸甲酯乙氧基化物0.5％、脂肪酸甲酯乙氧基化物磺酸钠2％、氯化钠1％，余量为去离子水。
2)混合：将步骤1)中的各原料在40℃下混合均匀，得到玻璃清洗剂。
3)稀释：将本实施例中清洗剂稀释7倍后用于玻璃清洗。
对比例1
一种玻璃清洗剂的制备方法，其包括以下步骤：
1)备料：按照如下质量百分数取用各原料：氢氧化钠10％、碳酸钠5％、磷酸钠5％、十二烷基苯磺酸钠0.05％、脂肪醇聚氧乙烯醚硫酸钠0.03％、十二烷基硫酸钠0.02％、壬基酚聚氧乙烯醚0.05％、氯化钠0.01％，其余为去离子水。
2)混合：将步骤1)中的各原料在40℃下混合均匀，得到玻璃清洗剂。
效果验证
清洗试验
对实施例1-实施例5、对比例1中的清洗剂进行清洗效果测试。
测试方法为：取6组生产上同一批次的经过抛光粉抛光之后的玻璃作为测试对象，每组200片玻璃，6组玻璃分别对应实施例1-实施例5、对比例1中的清洗剂。使用实施例1-实施例5、对比例1中的清洗剂分别对相应组的玻璃进行清洗，清洗后在台灯下检验玻璃表面抛光粉残留及其他脏污情况，若玻璃表面无任何脏污且无抛光粉残留，则为合格，反之则为不合格。具体测试结果见下表1。
表1
由表1可知，实施例组的合格率明显高于对比例组，且含月桂醇聚氧乙烯聚氧丙烯醚与脂肪酸甲酯乙氧基化物构成的复合非离子表面活性剂的玻璃清洗效果更好。
泡沫测试试验
对实施例1-实施例5、对比例1中的清洗剂进行泡沫测试。
测试方法为：对实施例1-实施例5、对比例1中的清洗剂各取样200g，溶于800g纯净水后放置于2L的玻璃烧杯中，于25℃、每分钟搅拌40次的条件下搅拌2min，测量泡沫高度。具体测试结果见下表2。
表2
由表2可知，实施例中的清洗剂中的泡沫含量相比于对比例组明显较少。
以上所述实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (8)
1.一种玻璃清洗剂，其特征在于，包括如下重量百分含量的各组分：
有机酸 5%-50%、
非离子表面活性剂 1%-6%、
阴离子表面活性剂 1%-5%、
增稠剂 1%-5%、
水 34%-92%；
其中，所述非离子表面活性剂是脂肪酸甲酯乙氧基化物和月桂醇聚氧乙烯聚氧丙烯醚的组合，所述有机酸选自柠檬酸和草酸中的一种或两种，所述阴离子表面活性剂选自脂肪酸甲酯乙氧基化物磺酸盐。
2.如权利要求1所述的玻璃清洗剂，其特征在于，包括如下重量百分含量的各组分：
有机酸 20%-50%、
非离子表面活性剂 1%-6%、
阴离子表面活性剂 1%-3%、
增稠剂 1%-3%、
水 60%-70%。
3.如权利要求1或2所述的玻璃清洗剂，其特征在于：所述阴离子表面活性剂选自脂肪酸甲酯乙氧基化物磺酸钠。
4.如权利要求1或2所述的玻璃清洗剂，其特征在于：所述增稠剂为无机盐增稠剂。
5.根据权利要求1所述的玻璃清洗剂，其特征在于：所述增稠剂选自氯化钠。
6.一种玻璃清洗剂的制备方法，其特征在于：包括以下步骤：
将权利要求1-5任一项所述的玻璃清洗剂中的有机酸、阴离子表面活性剂、非离子表面活性剂、增稠剂以及水混合。
7.根据权利要求6所述的玻璃清洗剂的制备方法，其特征在于：混合条件选自在35-50℃下混合均匀。
8.一种采用权利要求1-5任一项所述的玻璃清洗剂清洗玻璃的方法。