CN104817940A - Antirust paint for metal packing material surfaces and preparation method of antirust paint - Google Patents
Antirust paint for metal packing material surfaces and preparation method of antirust paint Download PDFInfo
- Publication number
- CN104817940A CN104817940A CN201510203356.XA CN201510203356A CN104817940A CN 104817940 A CN104817940 A CN 104817940A CN 201510203356 A CN201510203356 A CN 201510203356A CN 104817940 A CN104817940 A CN 104817940A
- Authority
- CN
- China
- Prior art keywords
- parts
- packing material
- metal packing
- material surface
- proof paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to antirust paint for metal packing material surfaces and a preparation method of the antirust paint. The antirust paint comprises, by mass, 30-50 parts of waterborne organosilicon modified alkyd resin, 3-12 parts of zinc chromate, 1-5 parts of chromium oxide green, 0.5-2 parts of attapulgite, 8-18 parts of sericite, 2-9 parts of sesame oil, 2-10 parts of zinc stearate, 0.3-3.5 parts of melaniline, 3-10 parts of polyethylene glycol, 0.8-5 parts of simethicone, 1-5 parts of sodium benzoate, 0.3-1.2 parts of dimethyl diacetoxyl tin, 0.9-3 parts of trimethylolpropane acrylate, 4-15 parts of alkyl sodium sulfonate, 0.1-0.5 part of lead naphthenate, 0.03-0.1 part of yellow dextrin and 15-25 parts of pure water. The antirust paint has excellent antirust function.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of metal packing material surface rust proof paint and preparation method thereof.
Background technology
Wrapping material refer to and meet for the manufacture of packaging vessel, packing and decorating, packages printing, packed and transported etc. the material that packing of product requirement uses, it comprises metal, plastics, glass, pottery, paper, bamboo basis, the main wrapping material such as wild mushroom class, natural fiber, man-made fiber, matrix material, comprises again the subsidiary material such as coating, tackiness agent, strapping tape, decoration, printing material.Metal packing material comprises tinplate aluminium foil, hoop for barrel, steel band, fastener for bundling articles, bubble-cap aluminium, PTP aluminium foil, aluminium sheet, steel are buckled.Metal packing material has excellent mechanical property and barrier property, and integrated protection performance is good; Appearance looks elegant; Good processability; Aboundresources, the advantages such as offal treatment is good, but shortcoming is exactly easily by corrosion.Guard method well at its surface coating paint.
As wrapping material, generally compare Lay Importance on Practical and outward appearance, and need, to metal, there is good provide protection.Current existing metal packing material surface coating can not have the functions such as shock resistance, obdurability, water-fast, weather-proof, antirust, scratch resistance simultaneously.Such as Chinese invention patent (patent No. 201110281752.6, the applying date 2011/09/21) discloses a kind of formaldehyde-free metal packaging coating, is made up of by weight percentage: saturated polyester resin 40 ~ 60% following component; Masked isocyanate 8 ~ 20%; Pigment 0 ~ 35%; Surplus is solvent and auxiliary agent; Described auxiliary agent comprises siccative and defoamer; Described siccative is organic amine siccative, and described defoamer is butadiene polymer.Coating disclosed in this patent of invention can increase film snappiness, enhancing erosion resistance and scrath resistance.But its rust resistance and corrosion resistance performance is obviously not high.
Summary of the invention
the technical problem solved:for existing metal packing material surface coating performance single, the shortcoming of rust protection ability, the invention provides a kind of metal packing material surface rust proof paint and preparation method thereof, and this coating has excellent rust protection function.
technical scheme:a kind of metal packing material surface rust proof paint, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 30 ~ 50 parts, zinc chromate 3 ~ 12 parts, chromoxide green 1 ~ 5 part, attapulgite 0.5 ~ 2 part, sericite 8 ~ 18 parts, hemp oil 2 ~ 9 parts, Zinic stearas 2 ~ 10 parts, vulkacit D 0.3 ~ 3.5 part, polyoxyethylene glycol 3 ~ 10 parts, dimethyl silicone oil 0.8 ~ 5 part, Sodium Benzoate 1 ~ 5 part, 0.3 ~ 1.2 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 0.9 ~ 3 part, alkyl sodium sulfonate 4 ~ 15 parts, lead naphthenate 0.1 ~ 0.5 part, yellow starch gum 0.03 ~ 0.1 part, pure water 15 ~ 25 parts.
A kind of metal packing material surface rust proof paint described above, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 33 ~ 45 parts, zinc chromate 5 ~ 10 parts, chromoxide green 2 ~ 5 parts, attapulgite 0.8 ~ 1.7 part, sericite 10 ~ 16 parts, hemp oil 3 ~ 8 parts, Zinic stearas 4 ~ 9 parts, vulkacit D 1 ~ 3 part, polyoxyethylene glycol 4 ~ 8 parts, dimethyl silicone oil 1.4 ~ 4 parts, Sodium Benzoate 2 ~ 4 parts, 0.6 ~ 1 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.3 ~ 2.5 parts, alkyl sodium sulfonate 6 ~ 12 parts, lead naphthenate 0.2 ~ 0.4 part, yellow starch gum 0.05 ~ 0.09 part, pure water 17 ~ 23 parts.
A kind of metal packing material surface rust proof paint described above, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 35 ~ 42 parts, zinc chromate 7 ~ 9 parts, chromoxide green 3 ~ 4 parts, attapulgite 1 ~ 1.5 part, sericite 12 ~ 15 parts, hemp oil 4 ~ 7 parts, Zinic stearas 5 ~ 8 parts, vulkacit D 1.5 ~ 2.5 parts, polyoxyethylene glycol 5 ~ 7 parts, dimethyl silicone oil 2 ~ 3.3 parts, Sodium Benzoate 2.5 ~ 3.5 parts, 0.7 ~ 0.9 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.6 ~ 2.2 parts, alkyl sodium sulfonate 8 ~ 11 parts, lead naphthenate 0.25 ~ 0.35 part, yellow starch gum 0.06 ~ 0.08 part, pure water 18 ~ 21 parts.
A kind of metal packing material surface rust proof paint described above, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 38 parts, zinc chromate 8 parts, chromoxide green 3.5 parts, attapulgite 1.2 parts, sericite 13 parts, hemp oil 5.5 parts, Zinic stearas 6.5 parts, vulkacit D 2 parts, polyoxyethylene glycol 6 parts, dimethyl silicone oil 2.7 parts, Sodium Benzoate 3 parts, 0.8 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.9 parts, alkyl sodium sulfonate 10 parts, lead naphthenate 0.3 part, yellow starch gum 0.07 part, pure water 20 parts.
The preparation method of a kind of metal packing material surface rust proof paint described above, the preparation process of the method is as follows:
The first step: add pure water in a kettle., be warming up to 70 ~ 80 DEG C, add waterborne organic silicon modified alkyd resin, zinc chromate, chromoxide green, attapulgite, sericite, hemp oil, Zinic stearas, vulkacit D, polyoxyethylene glycol, dimethyl silicone oil, Sodium Benzoate, dimethyl oxalic acid tin while stirring;
Second step: control stirring velocity is 1000 ~ 1200r/min, and dispersed with stirring is even;
3rd step: be ground to after fineness is 40 ~ 60 μm with shredder again, then mix with trimethylolpropane acrylates, alkyl sodium sulfonate, lead naphthenate, yellow starch gum, get product after filtration.
In the first step described above, pure water is heated to 75 DEG C.
Controlling stirring velocity in second step described above is 1100r/min.
Being ground to fineness with shredder in the 3rd step described above is 50 μm.
beneficial effect:a kind of metal packing material surface provided by the invention rust proof paint and preparation method thereof; this coating has excellent rust protection function; also there is good shock resistance, snappiness hardness, the performance such as water-fast, weather-proof, to metal packing material, there is well decoration and provide protection.
Embodiment
embodiment
1
a kind of metal packing material surface rust proof paint, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 30 parts, zinc chromate 3 parts, chromoxide green 1 part, attapulgite 0.5 part, sericite 8 parts, hemp oil 2 parts, Zinic stearas 2 parts, vulkacit D 0.3 part, polyoxyethylene glycol 3 parts, dimethyl silicone oil 0.8 part, Sodium Benzoate 1 part, 0.3 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 0.9 part, alkyl sodium sulfonate 4 parts, lead naphthenate 0.1 part, yellow starch gum 0.03 part, pure water 15 parts.
A preparation method for metal packing material surface rust proof paint, the preparation process of the method is as follows:
The first step: add pure water in a kettle., be warming up to 70 DEG C, add waterborne organic silicon modified alkyd resin, zinc chromate, chromoxide green, attapulgite, sericite, hemp oil, Zinic stearas, vulkacit D, polyoxyethylene glycol, dimethyl silicone oil, Sodium Benzoate, dimethyl oxalic acid tin while stirring;
Second step: control stirring velocity is 1000r/min, and dispersed with stirring is even;
3rd step: be ground to after fineness is 40 μm with shredder again, then mix with trimethylolpropane acrylates, alkyl sodium sulfonate, lead naphthenate, yellow starch gum, get product after filtration.
embodiment
2
a kind of metal packing material surface rust proof paint, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 50 parts, zinc chromate 12 parts, chromoxide green 5 parts, attapulgite 2 parts, sericite 18 parts, hemp oil 9 parts, Zinic stearas 10 parts, vulkacit D 3.5 parts, polyoxyethylene glycol 10 parts, dimethyl silicone oil 5 parts, Sodium Benzoate 5 parts, 1.2 parts, dimethyl oxalic acid tin, trimethylolpropane acrylates 3 parts, alkyl sodium sulfonate 15 parts, lead naphthenate 0.5 part, yellow starch gum 0.1 part, pure water 25 parts.
A preparation method for metal packing material surface rust proof paint, the preparation process of the method is as follows:
The first step: add pure water in a kettle., be warming up to 80 DEG C, add waterborne organic silicon modified alkyd resin, zinc chromate, chromoxide green, attapulgite, sericite, hemp oil, Zinic stearas, vulkacit D, polyoxyethylene glycol, dimethyl silicone oil, Sodium Benzoate, dimethyl oxalic acid tin while stirring;
Second step: control stirring velocity is 1200r/min, and dispersed with stirring is even;
3rd step: be ground to after fineness is 60 μm with shredder again, then mix with trimethylolpropane acrylates, alkyl sodium sulfonate, lead naphthenate, yellow starch gum, get product after filtration.
embodiment
3
a kind of metal packing material surface rust proof paint, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 33 parts, zinc chromate 5 parts, chromoxide green 2 parts, attapulgite 0.8 part, sericite 10 parts, hemp oil 3 parts, Zinic stearas 4 parts, vulkacit D 1 part, polyoxyethylene glycol 4 parts, dimethyl silicone oil 1.4 parts, Sodium Benzoate 2 parts, 0.6 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.3 parts, alkyl sodium sulfonate 6 parts, lead naphthenate 0.2 part, yellow starch gum 0.05 part, pure water 17 parts.
A preparation method for metal packing material surface rust proof paint, the preparation process of the method is as follows:
The first step: add pure water in a kettle., be warming up to 70 DEG C, add waterborne organic silicon modified alkyd resin, zinc chromate, chromoxide green, attapulgite, sericite, hemp oil, Zinic stearas, vulkacit D, polyoxyethylene glycol, dimethyl silicone oil, Sodium Benzoate, dimethyl oxalic acid tin while stirring;
Second step: control stirring velocity is 1000r/min, and dispersed with stirring is even;
3rd step: be ground to after fineness is 40 μm with shredder again, then mix with trimethylolpropane acrylates, alkyl sodium sulfonate, lead naphthenate, yellow starch gum, get product after filtration.
embodiment
4
a kind of metal packing material surface rust proof paint, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 35 parts, zinc chromate 7 parts, chromoxide green 3 parts, attapulgite 1 part, sericite 12 parts, hemp oil 4 parts, Zinic stearas 5 parts, vulkacit D 1.5 parts, polyoxyethylene glycol 5 parts, dimethyl silicone oil 2 parts, Sodium Benzoate 2.5 parts, 0.7 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.6 parts, alkyl sodium sulfonate 8 parts, lead naphthenate 0.25 part, yellow starch gum 0.06 part, pure water 18 parts.
A preparation method for metal packing material surface rust proof paint, the preparation process of the method is as follows:
The first step: add pure water in a kettle., be warming up to 75 DEG C, add waterborne organic silicon modified alkyd resin, zinc chromate, chromoxide green, attapulgite, sericite, hemp oil, Zinic stearas, vulkacit D, polyoxyethylene glycol, dimethyl silicone oil, Sodium Benzoate, dimethyl oxalic acid tin while stirring;
Second step: control stirring velocity is 1100r/min, and dispersed with stirring is even;
3rd step: be ground to after fineness is 50 μm with shredder again, then mix with trimethylolpropane acrylates, alkyl sodium sulfonate, lead naphthenate, yellow starch gum, get product after filtration.
embodiment
5
a kind of metal packing material surface rust proof paint, in mass parts containing following composition: waterborne organic silicon modified alkyd resin 38 parts, zinc chromate 8 parts, chromoxide green 3.5 parts, attapulgite 1.2 parts, sericite 13 parts, hemp oil 5.5 parts, Zinic stearas 6.5 parts, vulkacit D 2 parts, polyoxyethylene glycol 6 parts, dimethyl silicone oil 2.7 parts, Sodium Benzoate 3 parts, 0.8 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.9 parts, alkyl sodium sulfonate 10 parts, lead naphthenate 0.3 part, yellow starch gum 0.07 part, pure water 20 parts.
A preparation method for metal packing material surface rust proof paint, the preparation process of the method is as follows:
The first step: add pure water in a kettle., be warming up to 75 DEG C, add waterborne organic silicon modified alkyd resin, zinc chromate, chromoxide green, attapulgite, sericite, hemp oil, Zinic stearas, vulkacit D, polyoxyethylene glycol, dimethyl silicone oil, Sodium Benzoate, dimethyl oxalic acid tin while stirring;
Second step: control stirring velocity is 1100r/min, and dispersed with stirring is even;
3rd step: be ground to after fineness is 50 μm with shredder again, then mix with trimethylolpropane acrylates, alkyl sodium sulfonate, lead naphthenate, yellow starch gum, get product after filtration.
comparative example
1
invention patent mandate notification number is that the patent formulation of CN 102382565B is made up of following component: saturated polyester resin 40 ~ 60%; Masked isocyanate 8 ~ 20%; Pigment 0 ~ 35%; Surplus is solvent and auxiliary agent; Described saturated polyester resin is long-chain reduced branching degree polyester, viscosity 4000 ~ 6000mpa.s/25 DEG C, and acid number is less than or equal to 5mg KOH/g; Described solvent is with the total weight of formaldehyde-free metal packaging coating, and it is composed as follows: isophorone 3 ~ 8%; Solvesso 150# 7 ~ 20%; Second di-n-butyl ether 3 ~ 8%; Dibasic ester 2 ~ 8%; Described auxiliary agent comprises siccative and defoamer; Described siccative is organic amine siccative, and described defoamer is butadiene polymer.
The above-mentioned technical performance index stating the coating of the coating of embodiment 1 ~ embodiment 5 and comparative example 1, its detected result is as follows:
Above the embodiment of the present invention is described in detail, for one of ordinary skill in the art, according to the thought of the embodiment of the present invention, all will change in specific embodiments and applications, in sum, this description should not be construed as limitation of the present invention.
Claims (8)
1. a metal packing material surface rust proof paint, to it is characterized in that in mass parts containing following composition: waterborne organic silicon modified alkyd resin 30 ~ 50 parts, zinc chromate 3 ~ 12 parts, chromoxide green 1 ~ 5 part, attapulgite 0.5 ~ 2 part, sericite 8 ~ 18 parts, hemp oil 2 ~ 9 parts, Zinic stearas 2 ~ 10 parts, vulkacit D 0.3 ~ 3.5 part, polyoxyethylene glycol 3 ~ 10 parts, dimethyl silicone oil 0.8 ~ 5 part, Sodium Benzoate 1 ~ 5 part, 0.3 ~ 1.2 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 0.9 ~ 3 part, alkyl sodium sulfonate 4 ~ 15 parts, lead naphthenate 0.1 ~ 0.5 part, yellow starch gum 0.03 ~ 0.1 part, pure water 15 ~ 25 parts.
2. a kind of metal packing material surface according to claim 1 rust proof paint, to it is characterized in that in mass parts containing following composition: waterborne organic silicon modified alkyd resin 33 ~ 45 parts, zinc chromate 5 ~ 10 parts, chromoxide green 2 ~ 5 parts, attapulgite 0.8 ~ 1.7 part, sericite 10 ~ 16 parts, hemp oil 3 ~ 8 parts, Zinic stearas 4 ~ 9 parts, vulkacit D 1 ~ 3 part, polyoxyethylene glycol 4 ~ 8 parts, dimethyl silicone oil 1.4 ~ 4 parts, Sodium Benzoate 2 ~ 4 parts, 0.6 ~ 1 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.3 ~ 2.5 parts, alkyl sodium sulfonate 6 ~ 12 parts, lead naphthenate 0.2 ~ 0.4 part, yellow starch gum 0.05 ~ 0.09 part, pure water 17 ~ 23 parts.
3. a kind of metal packing material surface according to claim 1 rust proof paint, to it is characterized in that in mass parts containing following composition: waterborne organic silicon modified alkyd resin 35 ~ 42 parts, zinc chromate 7 ~ 9 parts, chromoxide green 3 ~ 4 parts, attapulgite 1 ~ 1.5 part, sericite 12 ~ 15 parts, hemp oil 4 ~ 7 parts, Zinic stearas 5 ~ 8 parts, vulkacit D 1.5 ~ 2.5 parts, polyoxyethylene glycol 5 ~ 7 parts, dimethyl silicone oil 2 ~ 3.3 parts, Sodium Benzoate 2.5 ~ 3.5 parts, 0.7 ~ 0.9 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.6 ~ 2.2 parts, alkyl sodium sulfonate 8 ~ 11 parts, lead naphthenate 0.25 ~ 0.35 part, yellow starch gum 0.06 ~ 0.08 part, pure water 18 ~ 21 parts.
4. a kind of metal packing material surface according to claim 1 rust proof paint, to it is characterized in that in mass parts containing following composition: waterborne organic silicon modified alkyd resin 38 parts, zinc chromate 8 parts, chromoxide green 3.5 parts, attapulgite 1.2 parts, sericite 13 parts, hemp oil 5.5 parts, Zinic stearas 6.5 parts, vulkacit D 2 parts, polyoxyethylene glycol 6 parts, dimethyl silicone oil 2.7 parts, Sodium Benzoate 3 parts, 0.8 part, dimethyl oxalic acid tin, trimethylolpropane acrylates 1.9 parts, alkyl sodium sulfonate 10 parts, lead naphthenate 0.3 part, yellow starch gum 0.07 part, pure water 20 parts.
5. the preparation method of a kind of metal packing material surface as claimed in claim 1 rust proof paint, is characterized in that the preparation process of the method is as follows:
The first step: add pure water in a kettle., be warming up to 70 ~ 80 DEG C, add waterborne organic silicon modified alkyd resin, zinc chromate, chromoxide green, attapulgite, sericite, hemp oil, Zinic stearas, vulkacit D, polyoxyethylene glycol, dimethyl silicone oil, Sodium Benzoate, dimethyl oxalic acid tin while stirring;
Second step: control stirring velocity is 1000 ~ 1200r/min, and dispersed with stirring is even;
3rd step: be ground to after fineness is 40 ~ 60 μm with shredder again, then mix with trimethylolpropane acrylates, alkyl sodium sulfonate, lead naphthenate, yellow starch gum, get product after filtration.
6. the preparation method of a kind of metal packing material surface according to claim 5 rust proof paint, is characterized in that: in the described the first step, pure water is heated to 75 DEG C.
7. the preparation method of a kind of metal packing material surface according to claim 5 rust proof paint, is characterized in that: controlling stirring velocity in described second step is 1100r/min.
8. the preparation method of a kind of metal packing material surface according to claim 5 rust proof paint, is characterized in that: being ground to fineness with shredder in described 3rd step is 50 μm.