CN104817926A - Anticorrosion coating for sprayers - Google Patents
Anticorrosion coating for sprayers Download PDFInfo
- Publication number
- CN104817926A CN104817926A CN201510211036.9A CN201510211036A CN104817926A CN 104817926 A CN104817926 A CN 104817926A CN 201510211036 A CN201510211036 A CN 201510211036A CN 104817926 A CN104817926 A CN 104817926A
- Authority
- CN
- China
- Prior art keywords
- parts
- coating
- atomizer
- corrosion resistant
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anticorrosion coating for sprayers. The coating is prepared from, by mass, 25-38 parts of flexible epoxy resin, 5-16 parts of modified acrylic resin, 8-15 parts of ammonium polyphosphate, 5-8 parts of titanium dioxide, 10-20 parts of sodium hexametaphosphate, 3-5 parts of hexamethyl cellulose and 6-12 parts of sebacic dihydrazide. The anticorrosion coating for sprayers is good in corrosion resistance, less prone to aging and high in mechanical performance.
Description
Technical field
The present invention relates to atomizer technical field, especially, relate to a kind of atomizer corrosion resistant coating.
Background technology
The filmogen of anticorrosive coating has chemical stability in corrosive medium, and its standard is relevant with chemical structure with the composition of filmogen, mainly see it under dry film condition whether easily and corrosive medium react or resolve into small molecules in media as well.No matter consider from cathodic protection or from simple buffer action, the shielding effect of anticorrosive coating is all very important.
Existing of a great variety for atomizer surface coating material, due to corrosion objects such as frequent exposed to pesticides, its resistance to acids and bases is poor, and some toxicity is comparatively large, and some elasticity is bad, and the mechanical property also had is poor.
Summary of the invention
The object of the invention is to provide a kind of atomizer corrosion resistant coating, not corrosion-resistant to solve atomizer coating in prior art, easily aging problem.
For achieving the above object, the invention provides a kind of atomizer corrosion resistant coating, wherein, this coating is made up of the component of following massfraction:
Flexible-epoxy 25 ~ 38 parts;
Acrylic resin modified 5 ~ 16 parts;
Polyphosphoric acid amine 8 ~ 15 parts;
Titanium dioxide 5 ~ 8 parts;
Sodium hexametaphosphate 99 10 ~ 20 parts;
Hexamethyl Mierocrystalline cellulose 3 ~ 5 parts; And
Sebacic dihydrazide 6 ~ 12 parts.
Further, the invention provides a kind of atomizer corrosion resistant coating, wherein, this coating is made up of the component of following massfraction: flexible-epoxy 25 parts; Acrylic resin modified 6 parts; Polyphosphoric acid amine 8 parts; Titanium dioxide 5 parts; Sodium hexametaphosphate 99 12 parts; Hexamethyl Mierocrystalline cellulose 3 parts; And sebacic dihydrazide 6 parts.
Further, the invention provides a kind of atomizer corrosion resistant coating, wherein, this coating is made up of the component of following massfraction: flexible-epoxy 38 parts; Acrylic resin modified 16 parts; Polyphosphoric acid amine 15 parts; Titanium dioxide 8 parts; Sodium hexametaphosphate 99 18 parts; Hexamethyl Mierocrystalline cellulose 5 parts; And sebacic dihydrazide 10 parts.
The present invention has following beneficial effect: the invention provides a kind of atomizer corrosion resistant coating, not only corrosion resistance and good, not easily aging, and mechanical property is high.
Embodiment
A kind of atomizer corrosion resistant coating that this preferred embodiment provides, its specific implementation process is as follows:
Wherein, this atomizer corrosion resistant coating is made up of the component of following massfraction:
Flexible-epoxy 25 ~ 38 parts;
Acrylic resin modified 5 ~ 16 parts;
Polyphosphoric acid amine 8 ~ 15 parts;
Titanium dioxide 5 ~ 8 parts;
Sodium hexametaphosphate 99 10 ~ 20 parts;
Hexamethyl Mierocrystalline cellulose 3 ~ 5 parts; And
Sebacic dihydrazide 6 ~ 12 parts.
Embodiment 1:
Wherein, this atomizer corrosion resistant coating is made up of the component of following massfraction: flexible-epoxy 25 parts; Acrylic resin modified 6 parts; Polyphosphoric acid amine 8 parts; Titanium dioxide 5 parts; Sodium hexametaphosphate 99 12 parts; Hexamethyl Mierocrystalline cellulose 3 parts; And sebacic dihydrazide 6 parts.
Embodiment 2:
Wherein, this atomizer corrosion resistant coating is made up of the component of following massfraction: this coating is made up of the component of following massfraction: flexible-epoxy 38 parts; Acrylic resin modified 16 parts; Polyphosphoric acid amine 15 parts; Titanium dioxide 8 parts; Sodium hexametaphosphate 99 18 parts; Hexamethyl Mierocrystalline cellulose 5 parts; And sebacic dihydrazide 10 parts.
As can be seen from the above description, the above embodiments of the present invention achieve following technique effect:
The invention provides a kind of atomizer corrosion resistant coating, not only corrosion resistance and good, not easily aging, and also mechanical property is high.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention; For a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. an atomizer corrosion resistant coating, is characterized in that, this coating is made up of the component of following massfraction:
Flexible-epoxy 25 ~ 38 parts;
Acrylic resin modified 5 ~ 16 parts;
Polyphosphoric acid amine 8 ~ 15 parts;
Titanium dioxide 5 ~ 8 parts;
Sodium hexametaphosphate 99 10 ~ 20 parts;
Hexamethyl Mierocrystalline cellulose 3 ~ 5 parts; And
Sebacic dihydrazide 6 ~ 12 parts.
2. atomizer corrosion resistant coating according to claim 1, is characterized in that, this coating is made up of the component of following massfraction: flexible-epoxy 25 parts; Acrylic resin modified 6 parts; Polyphosphoric acid amine 8 parts; Titanium dioxide 5 parts; Sodium hexametaphosphate 99 12 parts; Hexamethyl Mierocrystalline cellulose 3 parts; And sebacic dihydrazide 6 parts.
3. atomizer corrosion resistant coating according to claim 1, is characterized in that, this coating is made up of the component of following massfraction: flexible-epoxy 38 parts; Acrylic resin modified 16 parts; Polyphosphoric acid amine 15 parts; Titanium dioxide 8 parts; Sodium hexametaphosphate 99 18 parts; Hexamethyl Mierocrystalline cellulose 5 parts; And sebacic dihydrazide 10 parts.