CN107779057A - A kind of spray paint for surface of metal product - Google Patents
A kind of spray paint for surface of metal product Download PDFInfo
- Publication number
- CN107779057A CN107779057A CN201711213443.9A CN201711213443A CN107779057A CN 107779057 A CN107779057 A CN 107779057A CN 201711213443 A CN201711213443 A CN 201711213443A CN 107779057 A CN107779057 A CN 107779057A
- Authority
- CN
- China
- Prior art keywords
- parts
- metal product
- spray paint
- agent
- product according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of spray paint for surface of metal product, its component is according to the mass fraction：50 ~ 100 parts of polyester, 50 ~ 80 parts of styrene-acrylic emulsion, 1 ~ 5 part of ethanol, 1 ~ 5 part of D-sorbite, 0.1 ~ 0.5 part of methylhydroxypropylcellulose, 1 ~ 5 part of sodium carboxymethylcellulose, 1 ~ 5 part of hydroquinones, 1 ~ 5 part of oxalic acid, 0.5 ~ 1 part of methyl benzotriazazole, 4 ~ 8 parts of curing agent, 1 part of levelling agent, 20 ~ 40 parts of titanium dioxide, 5 ~ 10 parts of pigment, 10 ~ 15 parts of luminous agent, 1 ~ 5 part of modified adhesive, appropriate deionized water.The spray paint of the present invention is used for surface of metal product, the effect of antirust is kept during long-term use, while inexpensive and can is largely supplied.
Description
Technical field
The present invention relates to surface of metal product technical field of coatings, more particularly to a kind of spray for surface of metal product
Coating.
Background technology
Existing metallic article after shaping can be in its surface spraying last layer coating, for anticorrosion antirust.It is but existing
Some be used for the coating of anticorrosion antirust after much time using effect just become and be broken, when cheap methanol is used for coating
When middle, because its evaporation causes environmental pollution, while methanol is also particularly detrimental to people, thus design a not only nontoxic but also cost compared with
Low coating is extremely urgent.
The content of the invention
In view of the deficienciess of the prior art, the purpose of the present invention be that provide it is a kind of for surface of metal product
Spray paint, the effect of antirust is kept during long-term use, while inexpensive and can is largely supplied.
To achieve these goals, the technical solution adopted by the present invention is such：It is a kind of for surface of metal product
Spray paint, its component are according to the mass fraction：50~100 parts of polyester, 50~80 parts of styrene-acrylic emulsion, 1~5 part of ethanol, sorbose
1~5 part of alcohol, 0.1~0.5 part of methylhydroxypropylcellulose, 1~5 part of sodium carboxymethylcellulose, 1~5 part of hydroquinones, oxalic acid 1
~5 parts, 0.5~1 part of methyl benzotriazazole, 4~8 parts of curing agent, 1 part of levelling agent, 20~40 parts of titanium dioxide, pigment 5~10
Part, 10~15 parts of luminous agent, 1~5 part of modified adhesive, appropriate deionized water.
As a kind of preferred scheme, the curing agent is aliphatic amine.
As a kind of preferred scheme, the levelling agent is polyether-modified organopolysiloxane.
As a kind of preferred scheme, the pigment is acrylic paints.
As a kind of preferred scheme, the luminous agent is calcirm-fluoride.
As a kind of preferred scheme, the modified adhesive is by sodium metasilicate, 3- propyl trimethoxy silicanes, methyl hydroxy propyl
In base sodium cellulosate, cumyl peroxide, ethylene glycol, diethanol amine, acetic acid, 1,2- bis ethanes be prepared.
Compared with prior art, beneficial effects of the present invention：The spray paint of the present invention is used for surface of metal product, long-term
The effect of antirust is kept during use, while inexpensive and can is largely supplied.
Embodiment
With reference to specific embodiment, the invention will be further described.Following examples are only used for clearly illustrating
Technical scheme, and can not be limited the scope of the invention with this.
Embodiment：
A kind of spray paint for surface of metal product, its component are according to the mass fraction：50~100 parts of polyester, phenylpropyl alcohol
50~80 parts of emulsion, 1~5 part of ethanol, 1~5 part of D-sorbite, 0.1~0.5 part of methylhydroxypropylcellulose, carboxymethyl cellulose
Plain 1~5 part of sodium, 1~5 part of hydroquinones, 1~5 part of oxalic acid, 0.5~1 part of methyl benzotriazazole, 4~8 parts of curing agent, levelling
1 part of agent, 20~40 parts of titanium dioxide, 5~10 parts of pigment, 10~15 parts of luminous agent, 1~5 part of modified adhesive, deionized water are fitted
Amount.
Preferably, the curing agent is aliphatic amine.
Preferably, the levelling agent is polyether-modified organopolysiloxane.
Preferably, the pigment is acrylic paints.
Preferably, the luminous agent is calcirm-fluoride.
Preferably, the modified adhesive is by sodium metasilicate, 3- propyl trimethoxy silicanes, methylhydroxypropylcellulose
In sodium, cumyl peroxide, ethylene glycol, diethanol amine, acetic acid, 1,2- bis ethanes be prepared.
The spray paint of the present invention is subjected to performance test, specific data are shown in Table 1.
Table 1
| Project | Performance indications | Testing standard |
| Appearance of film | Flat smooth | Range estimation |
| Surface drying time (h) | 0.5 | GB/T 1728-79 |
| Do solid work the time (h) | 5 | GB/T 1728-79 |
| The rust transformation time | 15min | Range estimation |
| Rust transformation degree | 100% | Range estimation |
| Adhesive force (level) | 1 | GB/T 1720-79 |
| Hardness (H) | 2 | GB/T 1720-79 |
| Water resistance h) | 140 | GB/T 1733-93 |
| Acid resistance (h) | 75 | GB/T 1728-79 |
| Toxicity and combustibility | It is nontoxic, it is non-ignitable |
Described above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, some improvement and deformation can also be made, these are improved and deformation
Also it should be regarded as protection scope of the present invention.
Claims (6)
1. a kind of spray paint for surface of metal product, it is characterised in that its component is according to the mass fraction：Polyester 50 ~ 100
Part, 50 ~ 80 parts of styrene-acrylic emulsion, 1 ~ 5 part of ethanol, 1 ~ 5 part of D-sorbite, 0.1 ~ 0.5 part of methylhydroxypropylcellulose, carboxymethyl are fine
Tie up plain 1 ~ 5 part of sodium, 1 ~ 5 part of hydroquinones, 1 ~ 5 part of oxalic acid, 0.5 ~ 1 part of methyl benzotriazazole, 4 ~ 8 parts of curing agent, levelling agent 1
Part, 20 ~ 40 parts of titanium dioxide, 5 ~ 10 parts of pigment, 10 ~ 15 parts of luminous agent, 1 ~ 5 part of modified adhesive, appropriate deionized water.
A kind of 2. spray paint for surface of metal product according to claim 1, it is characterised in that：The curing agent is
Aliphatic amine.
A kind of 3. spray paint for surface of metal product according to claim 1, it is characterised in that：The levelling agent is
Polyether-modified organopolysiloxane.
A kind of 4. spray paint for surface of metal product according to claim 1, it is characterised in that：The pigment is third
Alkene pigment.
A kind of 5. spray paint for surface of metal product according to claim 1, it is characterised in that：The luminous agent is
Calcirm-fluoride.
A kind of 6. spray paint for surface of metal product according to claim 1, it is characterised in that：The modified bonding
Agent by sodium metasilicate, 3- propyl trimethoxy silicanes, methylhydroxypropylcellulose sodium, cumyl peroxide, ethylene glycol,
Diethanol amine, acetic acid, 1,2- bis ethanes are prepared.