CN104817816A - Polyformaldehyde plastic board - Google Patents
Polyformaldehyde plastic board Download PDFInfo
- Publication number
- CN104817816A CN104817816A CN201510183061.0A CN201510183061A CN104817816A CN 104817816 A CN104817816 A CN 104817816A CN 201510183061 A CN201510183061 A CN 201510183061A CN 104817816 A CN104817816 A CN 104817816A
- Authority
- CN
- China
- Prior art keywords
- parts
- gelatin
- amino acid
- carbon black
- zinc oxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polyformaldehyde plastic board, and belongs to the field of plastic products. The polyformaldehyde plastic board comprises, by weight, 100 parts of polyformaldehyde plastics, 10-15 parts of cane sugar, 8-12 parts of amino acid, 5-8 parts of gelatin, 1-5 parts of anti-aging agents ODA, 2-4 parts of high abrasion resistance carbon black, 8-12 parts of zinc oxide, 4-6 parts of glycerol and 20-30 parts of 2-7 millimeter long glass fibers. Based on the polyformaldehyde plastics, the cane sugar, the amino acid, the gelatin, the anti-aging agents ODA, the high abrasion resistance carbon black, the zinc oxide, the glycerol and the glass fibers are added, so that the polyformaldehyde plastic board with long service life is prepared.
Description
Technical field
The invention belongs to plastics art field, particularly relate to a kind of Polyoxymethylene plastic plate.
Background technology
Polyoxymethylene plastic plate is extruded by forcing machine high temperature with acetal plastic particle, the sheet material obtaining different thickness is extruded through corresponding mould mouth, it is the thermoplastic engineering plastic of a kind of high-melting-point, high crystalline, because of the superperformance that polyoxymethylene plate has, being highly suitable for machining on self-acting lathe, being particularly suitable for for manufacturing precision component.
But due to acetal plastic itself exist heat-resisting, ageing-resistant, resistance to weathering is poor, make with the work-ing life of its obtained Polyoxymethylene plastic plate very short, thus reduce its use range.
Summary of the invention
The invention provides a kind of Polyoxymethylene plastic plate, it can solve due to acetal plastic itself exist heat-resisting, ageing-resistant, resistance to weathering is poor, make with the work-ing life of its obtained Polyoxymethylene plastic plate very short, thus reduce the problem of its use range.
In order to solve the problems of the technologies described above, the technical solution adopted in the present invention is:
It is made up of the component of following parts by weight:
Acetal plastic 100 parts, sucrose 10 parts ~ 15 parts, 8 parts ~ 12 parts, amino acid, 5 parts ~ 8 parts, gelatin, anti-aging agent ODA 1 part ~ 5 parts, high abrasion carbon black 2 parts ~ 4 parts, 8 parts ~ 12 parts, zinc oxide, glycerine 4 parts ~ 6 parts and length are 20 parts ~ 30 parts, the glass fibre of 2 millimeters ~ 7 millimeters.
In technique scheme, technical scheme is more specifically: acetal plastic 100 parts, sucrose 10 parts, amino acid/11 2 parts, 7 parts, gelatin, anti-aging agent ODA 1 part, high abrasion carbon black 2 parts, 12 parts, zinc oxide, glycerine 5 parts and length are 20 parts, the glass fibre of 2 millimeters;
Further, acetal plastic 100 parts, sucrose 15 parts, 8 parts, amino acid, 5 parts, gelatin, anti-aging agent ODA 5 parts, high abrasion carbon black 3 parts, 8 parts, zinc oxide, glycerine 6 parts and length are 25 parts, the glass fibre of 5 millimeters;
Further, acetal plastic 100 parts, sucrose 12 parts, amino acid/11 0 part, 8 parts, gelatin, anti-aging agent ODA 3 parts, high abrasion carbon black 4 parts, 10 parts, zinc oxide, glycerine 4 parts and length are 30 parts, the glass fibre of 7 millimeters.
Owing to adopting technique scheme, the present invention has following beneficial effect:
The present invention, by the basis of acetal plastic, adds sucrose, amino acid, gelatin, anti-aging agent ODA, high abrasion carbon black, zinc oxide, glycerine and glass fibre, thus the Polyoxymethylene plastic plate of obtained long service life.
Embodiment
Below in conjunction with specific examples, the invention will be further described:
Embodiment 1
This Polyoxymethylene plastic plate is made up of following component:
Acetal plastic 1000g, sucrose 100g, amino acid/11 20g, gelatin 70g, anti-aging agent ODA 10g, high abrasion carbon black 20g, zinc oxide 120g, glycerine 50g and length are the glass fibre 200g of 2 millimeters.
Its preparation method is: said components mixed, then through mold cured.
Compare existing Polyoxymethylene plastic plate, the work-ing life of the present embodiment Polyoxymethylene plastic plate improves 1 times.
Embodiment 2
This Polyoxymethylene plastic plate is made up of following component:
Acetal plastic 1000g, sucrose 150g, amino acid 80g, gelatin 50g, anti-aging agent ODA 50g, high abrasion carbon black 30g, zinc oxide 80g, glycerine 60g and length are the glass fibre 250g of 5 millimeters.
Its preparation method is: said components mixed, then through mold cured.
Compare existing Polyoxymethylene plastic plate, the work-ing life of the present embodiment Polyoxymethylene plastic plate improves 1 times.
Embodiment 3
This Polyoxymethylene plastic plate is made up of following component:
Acetal plastic 1000g, sucrose 120g, amino acid/11 00g, gelatin 80g, anti-aging agent ODA 30g, high abrasion carbon black 40g, zinc oxide 100g, glycerine 40g and length are the glass fibre 300g of 7 millimeters.
Its preparation method is: said components mixed, then through mold cured.
Compare existing Polyoxymethylene plastic plate, the work-ing life of the present embodiment Polyoxymethylene plastic plate improves 1 times.
Claims (4)
1. a Polyoxymethylene plastic plate, is characterized in that being made up of the component of following parts by weight:
Acetal plastic 100 parts, sucrose 10 parts ~ 15 parts, 8 parts ~ 12 parts, amino acid, 5 parts ~ 8 parts, gelatin, anti-aging agent ODA 1 part ~ 5 parts, high abrasion carbon black 2 parts ~ 4 parts, 8 parts ~ 12 parts, zinc oxide, glycerine 4 parts ~ 6 parts and length are 20 parts ~ 30 parts, the glass fibre of 2 millimeters ~ 7 millimeters.
2. Polyoxymethylene plastic plate according to claim 1, is characterized in that: acetal plastic 100 parts, sucrose 10 parts, amino acid/11 2 parts, 7 parts, gelatin, anti-aging agent ODA 1 part, high abrasion carbon black 2 parts, 12 parts, zinc oxide, glycerine 5 parts and length are 20 parts, the glass fibre of 2 millimeters.
3. Polyoxymethylene plastic plate according to claim 1, is characterized in that: acetal plastic 100 parts, sucrose 15 parts, 8 parts, amino acid, 5 parts, gelatin, anti-aging agent ODA 5 parts, high abrasion carbon black 3 parts, 8 parts, zinc oxide, glycerine 6 parts and length are 25 parts, the glass fibre of 5 millimeters.
4. Polyoxymethylene plastic plate according to claim 1, is characterized in that: acetal plastic 100 parts, sucrose 12 parts, amino acid/11 0 part, 8 parts, gelatin, anti-aging agent ODA 3 parts, high abrasion carbon black 4 parts, 10 parts, zinc oxide, glycerine 4 parts and length are 30 parts, the glass fibre of 7 millimeters.