CN109206837A - A kind of shock resistance acetal plastic - Google Patents
A kind of shock resistance acetal plastic Download PDFInfo
- Publication number
- CN109206837A CN109206837A CN201710536158.4A CN201710536158A CN109206837A CN 109206837 A CN109206837 A CN 109206837A CN 201710536158 A CN201710536158 A CN 201710536158A CN 109206837 A CN109206837 A CN 109206837A
- Authority
- CN
- China
- Prior art keywords
- shock resistance
- parts
- acetal plastic
- plastic according
- acetal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of shock resistance acetal plastics, are composed of the following parts by weight: acetal plastic, and 100 parts;Gelatin, 10-15 parts;Anti-aging agent ODA, 5 parts;Glass fibre, 10-15 parts;Light stabilizer, 5-10 parts;Filler, 3-5 parts;Lubricant, 5-10 parts;Initiator, 1-3 parts;Crosslinking agent, 3-5 parts;Impact resistance modification agent, 5-10 parts.Plastics of the present invention joined ethylene propylene rubber as impact resistance modification agent, improve the shock resistance of plastics.
Description
Technical field
The present invention relates to a kind of plastics, and in particular to a kind of shock resistance acetal plastic.
Background technique
Polyoxymethylene plastic plate is to be squeezed out with acetal plastic particle by extruder high temperature, is squeezed out by corresponding mold mouth
The plate of different-thickness is obtained, is the thermoplastic engineering plastic of a kind of high-melting-point, high crystalline, because good possessed by polyformaldehyde plate
Good characteristic is highly suitable for machining on automatic lathe, is particularly suitable for being used to manufacture precision component.
However since acetal plastic itself is there are heat-resisting, ageing-resistant, resistance to weathering is poor, so that made from it
The service life of Polyoxymethylene plastic plate is very short, to reduce its use scope.
In view of the above shortcomings, the designer, is actively subject to research and innovation, to found a kind of new structural poly- first
Aldehyde plastics make it with more the utility value in industry.
Summary of the invention
In order to solve the above technical problems, the object of the present invention is to provide a kind of shock resistance acetal plastics.
Technical scheme is as follows:
A kind of shock resistance acetal plastic, which is characterized in that be composed of the following parts by weight:
Further, the glass fibre is the glass fibre of 2-5mm.
Further, the light stabilizer is titanium dioxide.
Further, the filler is silica flour.
Further, the lubricant is oxidic polyethylene.
Further, the initiator is benzoyl peroxide.
Further, the crosslinking agent is dual-tert-butyl dicumyl peroxide.
Further, the impact resistance modification agent is ethylene propylene rubber.
According to the above aspect of the present invention, the present invention has at least the following advantages:
Plastics of the present invention joined ethylene propylene rubber as impact resistance modification agent, improve the shock resistance of plastics.
The above description is only an overview of the technical scheme of the present invention, in order to better understand the technical means of the present invention,
And can be implemented in accordance with the contents of the specification, below with presently preferred embodiments of the present invention.
Specific embodiment
With reference to embodiment, the embodiment of the present invention is furthur described in detail.Following embodiment is used for
Illustrate the present invention, but is not intended to limit the scope of the invention.
A kind of preparation method of shock resistance acetal plastic, including following raw material acetal plastic, gelatin, anti-aging agent ODA,
Glass fibre, light stabilizer, filler, lubricant, initiator, crosslinking agent, impact resistance modification agent, after above-mentioned raw materials are mixed,
It is added in extruding machine, is uniformly mixed at 120 DEG C, then squeezed out using screw machine, obtain acetal plastic.
The concrete component of preparation is as follows.
Embodiment 1
Embodiment 2
Embodiment 3
Plastics of the present invention joined ethylene propylene rubber as impact resistance modification agent, improve the shock resistance of plastics.
The above is only a preferred embodiment of the present invention, it is not intended to restrict the invention, it is noted that for this skill
For the those of ordinary skill in art field, without departing from the technical principles of the invention, can also make it is several improvement and
Modification, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (8)
1. a kind of shock resistance acetal plastic, which is characterized in that be composed of the following parts by weight:
2. a kind of shock resistance acetal plastic according to claim 1, it is characterised in that: the glass fibre is 2-5mm
Glass fibre.
3. a kind of shock resistance acetal plastic according to claim 1, it is characterised in that: the light stabilizer is titanium white
Powder.
4. a kind of shock resistance acetal plastic according to claim 1, it is characterised in that: the filler is silica flour.
5. a kind of shock resistance acetal plastic according to claim 1, it is characterised in that: the lubricant is to aoxidize poly- second
Alkene.
6. a kind of shock resistance acetal plastic according to claim 1, it is characterised in that: the initiator is benzoyl peroxide
Formyl.
7. a kind of shock resistance acetal plastic according to claim 1, it is characterised in that: the crosslinking agent is dual-tert-butyl
Dicumyl peroxide.
8. a kind of shock resistance acetal plastic according to claim 1, it is characterised in that: the impact resistance modification agent is second
Alkene acrylic rubber.