CN104817731A - Noiseless comfortable rubber heel lift and preparation method thereof - Google Patents
Noiseless comfortable rubber heel lift and preparation method thereof Download PDFInfo
- Publication number
- CN104817731A CN104817731A CN201510201338.8A CN201510201338A CN104817731A CN 104817731 A CN104817731 A CN 104817731A CN 201510201338 A CN201510201338 A CN 201510201338A CN 104817731 A CN104817731 A CN 104817731A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- styrene
- sulphur
- sky skin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of organic macromolecular compounds and provides a noiseless comfortable rubber heel lift and a preparation method thereof. The noiseless comfortable rubber heel lift comprises natural rubber, butadiene styrene rubber, butadiene-acrylonitrile rubber, high-styrene rubber, rubber powder, white carbon black, mineral oil, anti-aging agent, polyethylene glycol, silane coupling agent, zinc oxide, sulphur and vulcanization accelerating agent. The noiseless comfortable rubber heel lift has the advantages that the heel lift is elastic and noiseless, pressure and discomfort borne by the foot can be reduced, wearing comfort is improved, the trouble of noise is got rid of, and high wear-resisting and anti-slip performance and long service life are achieved.
Description
Technical field
The invention belongs to organic high molecular compound technical field, particularly a kind of quiet comfortable rubber sky skin and preparation method thereof.
Background technology
The aesthetic standards of modern are slender for beautiful with health. after wearing high heel shoes, health forms the attitude of drawing the abdomen of chinning up and chesting out, and seems tall and straight, graceful, the impression of people U.S. is strengthened.High heel shoes are very welcome, strengthen aesthetic feeling, improve confidence, but the slight illness such as low back muscle strain, gonitis, ankle from sprains are also comed one after another, and like that the women of high heel shoes needs to stand for a long time the worry of these slight illness, can not get effectively solving always.The anti-horizontal stand of high heel shoes, height heels, the heel gradient, the large end, sky skin etc. design all extremely important, wherein the design of material of sky skin is particularly important, the sky skin length and width of usual high heel shoes are between 9mm-15mm, and the heel of the Ms that likes to be beautiful is more and more less, footwear and contact area of ground little, need the gravity bearing human body simultaneously, the pressure that it skin bears is very large, this just requires that the hardness of day skin is high, it skin each several part stress equalization, once overbalance will cause wearer's ankle from sprains even to be fractured.All the time, sky skin is all doted in the high polyurethane material of hardness, more than the shore hardness 95A of product, and even up to 70D, but product is nonelastic, can make the strain of wearer's low back muscle, feet from injuring etc.; When walking, sound is very loud, brings embarrassment at quiet office; Urethane is physical crosslinking type, and wear resisting property is general, easily produces burr, affect attractive in appearance after wearing and tearing.
Summary of the invention
Object of the present invention be exactly for prior art exist deficiency and a kind of quiet comfortable rubber sky skin and preparation method thereof is provided, flexible and the quiet feature of described quiet comfortable rubber sky leatherware, decrease pressure and sense of discomfort that wearer's foot bears, improve wearing comfort, break away from noise worried, and there is good wear-resisting and non-skid property, cost performance is high, long service life.
For achieving the above object, the solution that the present invention takes is: a kind of quiet comfortable rubber sky skin, is made up of obtained: natural rubber, styrene-butadiene rubber(SBR), paracril, high styrene rubber, rubber powder, white carbon black, mineral oil, zinc oxide, anti-aging agent, polyoxyethylene glycol, silane coupling agent, sulphur, vulcanization accelerator following raw material.
Further, the weight part of each raw material is as follows:
Natural rubber 20 parts
15-20 parts, styrene-butadiene rubber(SBR)
Paracril 15-20 parts
High styrene rubber 6-10 parts
Rubber powder 15-20 parts
White carbon black 25-30 parts
5-10 parts, mineral oil
2-3 parts, zinc oxide
1-1.5 part, anti-aging agent
Polyoxyethylene glycol 2-3 parts
Silane coupling agent 2-3 parts
5-8 parts, sulphur
Vulcanization accelerator 4-6 parts.
Preferred further, each component presses row parts by weight:
Natural rubber 20 parts
16 parts, styrene-butadiene rubber(SBR)
Paracril 18 parts
High styrene rubber 8 parts
Rubber powder 15 parts
White carbon black 27 parts
6 parts, mineral oil
3 parts, zinc oxide
1.2 parts, anti-aging agent
Polyoxyethylene glycol 2.4 parts
Silane coupling agent 2.5 parts
6.5 parts, sulphur
Vulcanization accelerator 5 parts.
Further: described natural rubber is natural rubber 3L.
Further: the acrylonitrile content of described paracril is greater than 45%.
Further: described high styrene rubber is high styrene rubber HS860.
Further: described rubber powder is obtained by the our factory's rubber soles substandard products and waste material head pulverizing recovery.
A kind of preparation method preparing aforementioned quiet comfortable rubber sky skin, natural rubber is weighed according to formula rate, styrene-butadiene rubber(SBR), paracril, high styrene rubber, rubber powder, white carbon black, mineral oil, zinc oxide, anti-aging agent, polyoxyethylene glycol, silane coupling agent, sulphur, vulcanization accelerator, by constituent materials except sulphur, Banbury mixer banburying put into by sizing material beyond vulcanization accelerator, 104 degree of binder removals, room temperature places 24 hours, then mixing in two roller mill, and add the sulphur of precise, vulcanization accelerator, mixing evenly after, with uniform sheet slice, finally material is cut into definite shape and puts into rubber sky skin particular manufacturing craft sulfidization molding, curing temperature 160-165 degree, curing time 6-8 minute, namely quiet comfortable rubber sky skin is obtained.
By taking preceding solution, the present invention has following beneficial effect:
1; the present invention obtains quiet comfortable rubber sky skin; hardness, within the scope of 75-85A, still has elasticity, plays certain cushioning effect; the each position of available protecting wearer pin and joint; meanwhile, greatly alleviate noise when walking, quiet office is easily walked; this is fashion and practical perfect adaptation just, and women can obtain comfortable foot feeling simultaneously and spirit is comfortable.
2, the present invention uses the butadiene-acrylonitrile rubber of high acrylonitrile content, improves vulcanization of rubber crosslinking degree, improves the non-skid property of rubber sky skin, more to walk safely guarantee to wearer, avoids the embarrassment of falling down and the pain of injury; Meanwhile, maintain good rubber wear-resisting performance, and phozy limit, greatly reduce day shelling and damage the danger brought, also need not worry the trouble changing sky skin.
3, the present invention uses through pulverizing the rubber soles substandard products and waste material head and the rubber powder that obtains that reclaim, makes full use of waste resource, has to economize on resources, protection of the environment, the advantage such as to reduce costs.
4, wear-resisting sky skin in the market, rely on and add high wear-resistant carbon black raising wear resisting property, but can only black be produced, the quiet comfortable rubber sky skin of the present invention, while keeping excellent rubber wear-resisting performance, can add the sky skin that different pigment obtains different color, more freely can to arrange in pairs or groups high heel shoes, to increase aesthetic feeling.
Embodiment
Now the present invention is further described in conjunction with specific embodiments.
Embodiment 1:
In the present embodiment, quiet comfortable rubber sky skin is made up of by weight following component:
Natural rubber 3L 20 parts
1,502 16 parts, styrene-butadiene rubber(SBR)
Paracril 4,975 18 parts
High styrene rubber HS860 8 parts
Rubber powder 15 parts
White carbon black 27 parts
4,006 6 parts, mineral oil
3 parts, zinc oxide
1,010 1.2 parts, anti-aging agent
Polyoxyethylene glycol PEG4000 2.4 parts
Silane coupling agent Si69 2.5 parts
6.5 parts, sulphur
Accelerator D 1.5 parts
Accelerator DM 1.5 parts
Vulcanizating accelerant NOBS 2 parts
The preparation method of aforementioned quiet comfortable rubber sky skin, natural rubber is weighed according to formula rate, styrene-butadiene rubber(SBR), paracril, high styrene rubber, rubber powder, white carbon black, mineral oil, zinc oxide, anti-aging agent, polyoxyethylene glycol, silane coupling agent, sulphur, vulcanization accelerator, by constituent materials except sulphur, Banbury mixer banburying put into by sizing material beyond vulcanization accelerator, 104 degree of binder removals, room temperature places 24 hours, then mixing in two roller mill, and add the sulphur of precise, vulcanization accelerator, mixing evenly after, with uniform sheet slice, finally material is cut into definite shape and puts into rubber sky skin particular manufacturing craft sulfidization molding, curing temperature 165 degree, curing time 7 minutes, namely quiet comfortable rubber sky skin is obtained.
The above-mentioned quiet comfortable rubber sky skin prepared, density 1.14g/cm
3, wear-resisting 98 mm of hardness 81, DIN
3, xenon lamp aging test is without telling white phenomenon, and ozone ageing is tested without crack performance, dynamic on-slip coefficient level and smooth dry type 0.79 wet type 0.46.
Embodiment 2:
In the present embodiment, a kind of preparation method of quiet comfortable rubber sky skin is identical with the preparation method in embodiment 1, and difference is in formula material:
1,502 15 parts, styrene-butadiene rubber(SBR), paracril 4,975 20 parts, white carbon black 30 parts, 4,006 10 parts, mineral oil, silane coupling agent Si69 3 parts.
The above-mentioned quiet comfortable rubber sky skin prepared, density 1.15g/cm
3, wear-resisting 147 mm of hardness 82, DIN
3, xenon lamp aging test is without telling white phenomenon, and ozone ageing is tested without crack performance, dynamic on-slip coefficient level and smooth dry type 0.81 wet type 0.48.
Embodiment 3:
In the present embodiment, a kind of preparation method of quiet comfortable rubber sky skin is identical with the preparation method in embodiment 1, and difference is in formula material:
1,502 20 parts, styrene-butadiene rubber(SBR), paracril DN003 15 parts, high styrene rubber HS860 6 parts.
The above-mentioned quiet comfortable rubber sky skin prepared, density 1.12g/cm
3, wear-resisting 90 mm of hardness 79, DIN
3, xenon lamp aging test is without telling white phenomenon, and ozone ageing is tested without crack performance, dynamic on-slip coefficient level and smooth dry type 0.76 wet type 0.37.
Embodiment 4:
In the present embodiment, a kind of preparation method of quiet comfortable rubber sky skin is identical with the preparation method in embodiment 1, and difference is in formula material:
Paracril 4,975 20 parts, high styrene rubber HS860 10 parts, rubber powder 20 parts, white carbon black 25 parts, 4,006 5 parts, mineral oil, polyoxyethylene glycol PEG4000 3 parts.
The above-mentioned quiet comfortable rubber sky skin prepared, density 1.10g/cm
3, wear-resisting 195 mm of hardness 77, DIN
3, xenon lamp aging test is without telling white phenomenon, and ozone ageing is tested without crack performance, dynamic on-slip coefficient level and smooth dry type 0.76 wet type 0.36.
After the data preparation of above-described embodiment 1 ~ 4, obtain as following table 1(note: hardness adopts the test of GS-706G sclerometer, DIN is wear-resisting to be tested according to GB/T 9867:2001, xenon lamp aging test adopts xenon lamp aging proofing box Q-Sun Xe-1-S to test 10 days, ozone ageing test adopts ozone trier UA-2074 to test 2 hours (ozone concn 200ppm, temperature 60 degree), dynamic on-slip coefficient is tested according to TM144:2011):
| Embodiment | 1 | 2 | 3 | 4 |
| Density (g/cm 3) | 1.14 | 1.15 | 1.12 | 1.10 |
| Hardness | 81 | 82 | 79 | 77 |
| Wear-resisting (the mm of DIN 3) | 98 | 147 | 90 | 195 |
| Xenon lamp aging is tested | Without telling frost | Without telling frost | Without telling frost | Without telling frost |
| Ozone ageing is tested | Without be full of cracks | Without be full of cracks | Without be full of cracks | Without be full of cracks |
| Dynamic on-slip coefficient (dry type) | 0.79 | 0.81 | 0.76 | 0.76 |
| Dynamic on-slip coefficient (wet type) | 0.46 | 0.48 | 0.37 | 0.36 |
Table
, embodiment 1-4 performance perameter synopsis
In sum, according to the preparation method of quiet comfortable rubber sky skin of the present invention, can obtain and there is elasticity and quiet rubber sky skin, this sole decreases the pressure and sense of discomfort that wearer's foot bears, improve wearing comfort, break away from noise worried, and there is good wear-resisting and non-skid property, long service life.
Above, be only the embodiment utilizing this origination techniques content, the modification that any those skilled in the art use this creation to do, change, all belong to the scope of the claims that this creation is advocated, and be not limited to those disclosed embodiments.
Claims (5)
1. a quiet comfortable rubber sky skin, it is characterized in that, be made up of following raw material obtained: natural rubber, styrene-butadiene rubber(SBR), paracril, high styrene rubber, rubber powder, white carbon black, mineral oil, zinc oxide, anti-aging agent, polyoxyethylene glycol, silane coupling agent, sulphur, vulcanization accelerator.
2. quiet comfortable rubber sky skin according to claim 1, is characterized in that: the parts by weight of each raw material are:
Natural rubber 20 parts
15-20 parts, styrene-butadiene rubber(SBR)
Paracril 15-20 parts
High styrene rubber 6-10 parts
Rubber powder 15-20 parts
White carbon black 25-30 parts
5-10 parts, mineral oil
2-3 parts, zinc oxide
1-1.5 part, anti-aging agent
Polyoxyethylene glycol 2-3 parts
Silane coupling agent 2-3 parts
5-8 parts, sulphur
Vulcanization accelerator 4-6 parts.
3. quiet comfortable rubber sky skin according to claim 2, is characterized in that: be prepared from by following raw materials in part by weight by following component:
Natural rubber 20 parts
16 parts, styrene-butadiene rubber(SBR)
Paracril 18 parts
High styrene rubber 8 parts
Rubber powder 15 parts
White carbon black 27 parts
6 parts, mineral oil
3 parts, zinc oxide
1.2 parts, anti-aging agent
Polyoxyethylene glycol 2.4 parts
Silane coupling agent 2.5 parts
6.5 parts, sulphur
Vulcanization accelerator 5 parts.
4. quiet comfortable rubber sky skin according to claim 1 and 2, is characterized in that: the acrylonitrile content of described paracril is greater than 45%; High styrene rubber is high styrene rubber HS860; Described rubber powder is obtained by the rubber soles substandard products and waste material head pulverizing recovery.
5. prepare a preparation method for the arbitrary described quiet comfortable rubber sky skin of claim 1-4, it is characterized in that: weigh natural rubber, styrene-butadiene rubber(SBR), paracril, high styrene rubber, rubber powder, white carbon black, mineral oil, zinc oxide, anti-aging agent, polyoxyethylene glycol, silane coupling agent, sulphur, vulcanization accelerator according to formula rate; First the sizing material of constituent materials except sulphur, vulcanization accelerator is put into Banbury mixer banburying, 104 degree of binder removals, room temperature places 24 hours, then mixing in two roller mill, and adds sulphur, the vulcanization accelerator of precise, mixing evenly after, with uniform sheet slice, finally material is cut into definite shape and puts into rubber sky skin particular manufacturing craft sulfidization molding, curing temperature 160-165 degree, curing time 6-8 minute, namely obtains quiet comfortable rubber sky skin.