CN104817412A - Bamboo biomass charcoal based calcium magnesium phosphate fertilizer and preparation method thereof - Google Patents
Bamboo biomass charcoal based calcium magnesium phosphate fertilizer and preparation method thereof Download PDFInfo
- Publication number
- CN104817412A CN104817412A CN201510186566.2A CN201510186566A CN104817412A CN 104817412 A CN104817412 A CN 104817412A CN 201510186566 A CN201510186566 A CN 201510186566A CN 104817412 A CN104817412 A CN 104817412A
- Authority
- CN
- China
- Prior art keywords
- calcium magnesium
- biomass charcoal
- phosphate
- bamboo
- fused
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of a calcium magnesium phosphate fertilizer, in particular to a bamboo biomass charcoal based calcium magnesium phosphate fertilizer and a preparation method thereof. The preparation method comprises the following steps of carrying out high temperature pyrolyzing to bamboos to obtain bamboo-based biomass charcoal and combustible gas; melting, pelletizing and collecting particles after a raw material of the calcium magnesium phosphate fertilizer and 20-24% of biomass charcoal based on the total weight of the raw materials of the calcium magnesium phosphate fertilizer are mixed; cooling the collected particles with negative pressure, and screening; enveloping the screened particles, and packaging to ship, so as to obtain the bamboo biomass charcoal based calcium magnesium phosphate fertilizer. The bamboo biomass charcoal based calcium magnesium phosphate fertilizer provided by the invention is abundant in nutrient, the nutrient elements can be released and coordinated for a long time, the use ratio of the fertilizer nutrients is high, the soil can be effectively improved and fertilized, the use ratio of the fertilizer can be improved, the organic content of the soil can be improved, the soil bulk density can be reduced, the capacity of preserving moisture and fertility of the soil can be improved, the growth of the crops can be promoted, the yield of crops can be significantly improved, the crop quality can be improved, and the significant economic benefit can be realized.
Description
Technical field
The present invention relates to fused(calcium magnesium)phosphate technical field, be specifically related to a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate and preparation method thereof.
Background technology
Fertilising has become one of indispensable technical measures of agriculture production, exceedes half to the contribution rate of crop production.China's utilization rate of fertilizer is always lower, and the utilization ratio as nitrogenous fertilizer this season crop on average only has about 30%, lower than developed country nearly 20 percentage points, and this is because unscientific fertilizing method on the one hand, is then the characteristic due to fertilizer itself on the other hand.Improve utilization rate of fertilizer very urgent, Multifunction fertilizer is used in research and development, is to improve one of important approach of fertilizer utilization efficiency.
Biomass charcoal is the solid product of biomass high-temperature cracking, there is much special character, as there is a large amount of multiple functional groups on porous, high stability, height aromatize, surface, simultaneously with positive and negative 2 kinds of electric charges, can binding molecule regulating YIN and YANG ion, polarity and apolar substance.Starting material, cracking temperature, pyrolysis time etc. are the principal elements affecting biomass charcoal Wuli-Shili-Renli system approach, in general, within the specific limits, along with the rising of cracking temperature, the prolongation in reaction times, the specific surface area of biomass charcoal increases, aromatize structure strengthens, ash oontent and pH raise, and available nutrient and content of calcium and magnesium also increase.
Bamboo is very abundant in south China resource, and vegetative period is short, is a kind of well renewable resources.In industrial and agricultural production, a large amount of bamboos does not effectively utilize and goes out of use, and causes significant wastage.As grown the bamboo of more than 5 years at present by a large amount of scaffolding for construction site, discarded bamboo scaffolding is often treated as building waste and disposes, and causes a large amount of waste.Due to discarded bamboo carbon content high (more than 40%), can be used as the raw material preparing biomass charcoal, cost has larger advantage.
Fused(calcium magnesium)phosphate is greyish-green or taupe brown powder, and phosphorus content is 8%-14%, and main component is the α-Ca that can be dissolved in citric acid
3(PO
4)
2, also containing the element such as magnesium and a small amount of silicon.Magnesium is favourable to formation chlorophyll, and silicon can promote the growth of plant fiber tissue, plant is had prevent preferably the ability of lodging and disease and pest.Fine as base fertilizer effect during cultivating large seedling, plant can slowly absorb required nutrient.Fused(calcium magnesium)phosphate is a kind of multi-element fertilizer, and the aqueous solution, in alkalescence, can improve acid soil, and fine as base fertilizer effect during cultivating large seedling, plant can slowly absorb required nutrient.
But, have no at present and utilize the research of bamboo quality of biomass charcoal and fused(calcium magnesium)phosphate to report.Therefore, a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate is researched and developed to seem particularly important.
Summary of the invention
In order to overcome the shortcoming and defect existed in prior art, the object of the present invention is to provide a kind of preparation method of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, waste resource bamboo is obtained bamboo quality of biomass charcoal by this preparation method, the composite obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate with fused(calcium magnesium)phosphate again, greatly reduce production cost, decrease environmental pollution, the value good economic results in society can brought He apply; And this preparation method's technique is simple, convenient operation and control, steady quality, production efficiency is high, can large-scale industrial production.
Another object of the present invention is to provide a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, this bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate utilizes the physicals of bamboo quality of biomass charcoal, achieve the effective slowly-releasing to fused(calcium magnesium)phosphate, extend the action time of fused(calcium magnesium)phosphate, improve the utilization ratio of fused(calcium magnesium)phosphate, for crop long-time sufficient nutrient supply in vegetative period, and for crop alimentary strengthening provide good technical support.This bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate is used in the plurality of cereals crops such as corn, soybean, paddy rice and vegetables, fruit tree, can realize the single-dose application later stage need not topdress, the level of effective raising soil effective constituent, content and the output of crop kernel nutritive ingredient obviously promote, fertilizer efficiency is lasting, increasing both production and income.
Object of the present invention is achieved through the following technical solutions: a kind of preparation method of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, comprises the steps:
(1) by bamboo Pintsch process, bamboo quality of biomass charcoal and inflammable gas is obtained;
(2) by the raw material of fused(calcium magnesium)phosphate and the rear melting of bamboo quality of biomass charcoal mixing, the granulation that account for fused(calcium magnesium)phosphate total raw material weight 20-24%, pellet is collected; Wherein, the heat needed for melting is burnt by described inflammable gas to be provided;
Described fused(calcium magnesium)phosphate comprises the raw material of following weight part: base manure 20-60 part, mixing Adlerika 0.11-0.15 part, composite fungus agent 0.5-1.5 part and soil improvement agent 0.5-1.5 part; Wherein, described base manure contains the P that weight percent content is 12-20%
2o
5, the weight percent content MgO that is 8-15%, the weight percent content CaO that is 25-32%, weight percent content be the SiO of 20-30%
2, weight percent content is the FeO of 0.5-1.5%, weight percent content is the MnO of 0.1-0.3%;
(3) the pellet lost pressure cooling will collected, screens;
(4) pellet after screening is carried out coating, packaging shipment, obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate.
Waste resource bamboo is obtained bamboo quality of biomass charcoal by preparation method of the present invention, the composite obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate with fused(calcium magnesium)phosphate again, greatly reduce production cost, decrease environmental pollution, the value good economic results in society can brought He apply; And this preparation method's technique is simple, convenient operation and control, steady quality, production efficiency is high, can large-scale industrial production.
Preferably, described step (1) is specially: bamboo is crushed to particle diameter 1-2mm, the bamboo after pulverizing is dried to water ratio and is less than 5%, obtain biomass material; Catalyst for cracking and biomass material are put into the cracking of high temperature pyrolysis stove by weight 0.5-1.5:100 and carries out Pintsch process, obtain bamboo quality of biomass charcoal and inflammable gas; Wherein, the temperature of Pintsch process is 500-700 DEG C, and the time of Pintsch process is 60-120min.
Biomass can produce biomass charcoal, tar and inflammable gas through Pintsch process, adding of catalyst for cracking can catalytic tar cracking, catalyst for cracking can obtain higher tar clearance at a lower reaction temperature, and can also improve gas heating value and output.
Preferably, described catalyst for cracking comprises the raw material of following weight part: support of the catalyst 20-60 part, Primary Catalysts 6-10 part and promotor 12-30 part, and wherein, described support of the catalyst is peridotites; Primary Catalysts is NiO; Promotor comprises: MgO 5-15 part, CeO
21-5 part, WO
36-10 part.
The preparation method of described catalyst for cracking comprises the steps:
Step 1, synthesizing mesoporous silicon dioxide material, described Metaporous silicon dioxide material is the template in this preparation method;
Step 2, the precursor of described Metaporous silicon dioxide material, Fe and the precursor of Ni being stirred in ethanol or acetone, it is air-dry to be placed in ventilating kitchen, obtains the first powder;
Step 3, after described first powder and described lipid acid fully being ground in mortar, is placed in tube furnace high-temperature calcination under nitrogen atmosphere, obtains the second powder;
Step 4, soaks described second powder in NaOH solution, and etching removes described Metaporous silicon dioxide material, obtains the 3rd powder;
Step 5, filtration, washing, dry described 3rd powder, be the described biomass gasification tar cracking catalyst prepared by present method.
Wherein, described Metaporous silicon dioxide material is the mixture of any one or at least two kinds in the wide-aperture SBA-15 of six sides, the SBA-3 of six side small-bores, KIT-6, the FDU-5 of bicontinuous cubic structure of three-dimensional cubic macroporous structure and the FDU-12 of face-centred cubic structure.
Wherein, described lipid acid is the mixture of any one or at least two kinds in soybean oil, Semen Maydis oil, peanut oil, sunflower seed oil, rapeseed oil.
Wherein, the precursor of described iron is FeCl
36H
2o or Fe (NO
3)
39H
2the mixture of any one or both in O; The precursor of described nickel is NiCl
26H
2o or Ni (NO
3)
26H
2the mixture of any one or both in O.
Wherein, the time of described grinding is 0.5-8h, and the mass ratio of described SiO 2 mesoporous materials and described lipid acid is 0.2-2, and the mol ratio of the precursor of described Fe and the precursor of described Ni is 0.05-15.
Wherein, the temperature of described high-temperature calcination is 500-1200 DEG C, and the hold-time is 1-12h, and temperature rise rate is 1-15 DEG C of min
-1.
Wherein, the concentration of described NaOH solution is 1-6molL
-1, the time of etching is 10-30h.
Catalyst for cracking specific surface area and the pore volume of the present invention's employing are larger, uniform pore diameter, iron-nickel alloy as active ingredient is, the synergy of metal catalyst can be played, efficiently solve the problem of easy inactivation during nickel Individual existence, iron-nickel alloy is embedded in greying mesoporous carbon, wrapped by greying mesoporous carbon, along with the carrying out of reaction, ever-increasing carbon distribution drops in graphite mesoporous carbon, directly do not contact active ingredient, make active ingredient avoid being covered by carbon distribution, thus improve the work-ing life of catalyzer.The catalyst for cracking that the present invention adopts can obtain higher tar clearance at a lower reaction temperature, and can also improve gas heating value and output, can reach more than 99% to the transformation efficiency of tar.
Biomass charcoal has shown huge application potential at everyways such as raising crop yield, enhancing soil nutrient, increase soil fertility, soil structure improved addictive reparation, contaminated environment reparation and reductions of greenhouse gas discharge, causes extensive concern as a class novel environmental functional materials at society.
Charcoal has huge surface-area and various small structure, this pore space structure more easily assembles absorption nutrition nutrient thing, promotes beneficial microorganism growth, thus makes soil become more fertile, be conducive to the growth of plant, realize the green agriculture of Sustainable development.So, biomass charcoal can not only reduce greenhouse gases, as the effect of methane, Nitrous Oxide and Carbon emission, and to improving soil health, reduce nutrient loss, recover soil fertility, improve the utilising efficiency of fertilizer, improve soil productivity there is active effect.
Containing abundant space and organic macromolecule structure in biomass charcoal, when with fertilizer join execute, in soil, more easily form macro aggregate, promote absorption and the maintenance of the nutrient ion of soil, the NH in soil
4 +absorption and fixing effect are able to obvious enhancing, improve the utilization ratio of crop to nitrogen, thus nitrogen loss is reduced.In addition, there is certain hour rear face portion branch and formed carbonyl, phenolic group etc. by mild oxidation in biomass charcoal in soil, and this contributes to the cation exchange capacity increasing soil.Biomass charcoal is to NH
4 +and N0
3 -there is stronger characterization of adsorption, thus the nitrogen stayed in soil can be held, the volatilization of effective reduction agricultural land soil ammonia and the pouring drop of control Soil Nitrogen nutrient run off, these characteristics enable biomass charcoal effectively reduce the loss of agricultural land soil nitrogen nutrient, improve crop yield, decrease the pollution of area source that applying quantity of chemical fertilizer and farmland nitrogen nutrient loss cause simultaneously.
Biomass charcoal contains various abundant ash element, as soluble nutrient utilization absorbed by crops in soil, thus can improve soil organic matter content and soil carbon maintenance capacity, and biomass charcoal itself also can improve upper earth fertility as fertilizer.What biomass charcoal contained enriches ash element such as K, Ca, Mg etc. is all soluble state, the soluble base ion in solution is become after entering soil, improve the degree of base saturation of soil, reduce its Exchange alkalinity and exchangeable aluminum content, be conducive to improving other cation exchange capacity, and reduce aluminum ion activation, reduce the saturation ratio of aluminium in acid soil, thus improve the pH value of soil.Aluminium in Soil ion too much can produce detrimentally affect to plant-growth and soil microbial activity.
The surface of biomass charcoal has a large amount of negative charges, there is a large amount of pore space structures and huge specific surface area, there is impact in various degree to the chemical property of soil and physical behavior, to the mineral ion in soil polarity or nonpolar organic compound, soil available water, soil nutritive element or settling, all there is very strong adsorptive power.After being manured into soil by biomass charcoal, its cellular structure is conducive to the maintenance of the soil water, and the water-retentivity of soil is enhanced, and after applying a large amount of biomass charcoals in soil, its field capacity can be higher by 18% than contrasting soil around.Biomass charcoal add soil to after, soil aeration and porosity are improved, and make soil have good farming structure.For microorganism provides more living space, be conducive to the growth of aerobic microbiological in soil, improve Mineralization process organic in earth, increase soil fertility and Content of available nutrient element, be conducive to promoting the absorption of Plant To Nutrient element and the formation of soil agreegate.
Biomass charcoal has good chemical property, physical structure and nutrient Regulation effect, has strong adsorption effect to the Nutrients of exchangeable species in soil.The Reasonable of biomass charcoal and fertilizer is executed, and can strengthen absorption and the fixing of soil ammonium-state, improves plant to the utilising efficiency of nutrient element, particularly improves crop to the utilization ratio of nitrogen, reduces the volatile quantity of nitrogen in field.The soil applying black wood charcoal more easily forms larger coacervate, and makes nutrient ion more easily be adsorbed in biomass charcoal surface and hole, is particularly conducive to the adsorptivity of ammonium nitrogen ion.The adsorption of black wood charcoal is conducive to the utilization of plant to absorption nutrient, significantly can promote Seed Germination and growth, thus promote plant growth.
Biomass charcoal contains abundant organic matter, applies biomass charcoal in soil, can improve the organic content in soil, and the positively charged ion finally making its plant utilize and exchangeable species cations improve.The interpolation of biomass charcoal plays excitation to the soil organism, is conducive to the decomposition of original organic matter in soil, improves the fertility of soil further, has coordinated fertilizer and the fertilizer-preserving ability of soil, ensure that plant has sufficient nutrient supply.
In sum, the characteristics such as the porousness of biomass charcoal, huge specific surface area, surface negative charge and electric density can be adsorbed and nutrient in fixing fertilizer, realize its slow release effect, remarkable reduction soil N number of dropouts, increase soil fertility, promote the effect of crop yield and maintenance soil ecosystem balance.
At present, the activation method of biomass charcoal mainly adopts chemical activation method, and chemical activation is divided into: acid activation (mainly phosphoric acid, sulfuric acid activated), alkali activation (mainly potassium hydroxide, sodium hydroxide activation), salt activation (mainly zinc chloride activation).Salt activation has the low and simple advantage of technique of activation temperature.
Preferably, also comprise step (1 ') between described step (1) and step (2): by bamboo quality of biomass charcoal and activator mix, be warming up to activation temperature in an inert atmosphere and carry out activation treatment, be then cooled to room temperature, pickling is carried out to product, then is washed to neutral rear dry; Described activator is at least one in salt of wormwood, dipotassium hydrogen phosphate, potassium primary phosphate, Potassium ethanoate, Secondary ammonium phosphate, primary ammonium phosphate and ammonium acetate; The weight ratio of described biomass charcoal and described activator is 100:1-5; Inert atmosphere used is nitrogen, and flow is 100-400mL/min; Temperature rise rate is 2-10 DEG C/min; Activation temperature is 300-600 DEG C; Activation treatment soaking time is 1-3h; Pickling acid used is dilute hydrochloric acid.
Gac is obtained after being activated by biomass charcoal, gac is the loose porous property material with high-specific surface area, high characterization of adsorption, its pore texture is more flourishing than biomass charcoal, make the penetrating gas of soil better, be conducive to microorganism aerobic respiration, promote beneficial microorganism growth, thus make soil become more fertile, be conducive to the growth of plant.Gac is imposed in soil, physical structure and the chemical constitution of soil can be improved, adjustable fertilizer agricultural chemicals execute effect, thus promote the growth of plant.Gac can increase biological fixation nitrogen in soil, and makes organonitrogen comparatively fast change ammonia and nitrate into, thus plays fertilizer.
Preferably, in described step (2), the temperature of melting is 125-128 DEG C; In described step (3), the particle diameter of the pellet after screening is 1-4.75mm; In described step (4), packaging net weight >=25Kg, and≤50Kg.
Preferably, described fused(calcium magnesium)phosphate also comprises the raw material of following weight part: urea 5-15 part, sodium polyacrylate 5-15 part, poly-aspartic-acid 1-5 part, Castor seed Meal 8-12 part, straw powder 10-14 part, rare earth nitrate 2-6 part, sodium selenate 1-5 part, humic acids 4-8 part, medical stone 6-10 part, rhombspar 5-9 part.
Fused(calcium magnesium)phosphate of the present invention is by adopting above-mentioned raw materials and the strict weight proportion controlling each raw material, and obtained fused(calcium magnesium)phosphate can promote the growth of plant fiber tissue, plant is had prevent preferably the ability of lodging and disease and pest; Can improve acid soil, fine as base fertilizer effect during cultivating large seedling, plant can slowly absorb required nutrient; Be that a kind of nutrition is complete, function is many, comprehensive fertility is high, yield potential is large, soil physical chemistry state can be improved, quick-actingly to combine with slow, the fertilizer variety of water, fertile regulation and control integration.
Preferably, described mixing Adlerika is the Adlerika containing carboxymethyl cellulose, and the massfraction of carboxymethyl cellulose is 0.5-1.5%.
The present invention by adding mixing Adlerika in fused(calcium magnesium)phosphate, is prepared into particulate state, and make contact with water after application soluble, effective ingredient easily discharges, and soon, easy to use, fertilizer efficiency is lasting for Crop.The magnesium sulfate addition added is few, and do not change the original component ratio of fused(calcium magnesium)phosphate and structure, have synergy with fused(calcium magnesium)phosphate, quality standard is easily grasped, and implements easily.
Preferably, described composite fungus agent comprises the raw material of following weight part: phosphorus bacteria 10-20 part, vinelandii 20-30 part, silicate bacteria 10-20 part, nitrifier 20-30 part and antibiotic bacteria 5-15 part.
Composite fungus agent of the present invention is by adopting above-mentioned raw materials and the strict weight proportion controlling each raw material; obtained composite fungus agent not only has the effect increasing water-soluble phosphorus in fused(calcium magnesium)phosphate; also there is fixed nitrogen, potassium decomposing effect; also vitamin substances is secreted in its life movement process; crop increase yield can be promoted, improve quality; The antibiotic bacteria added is to preventing rotten kind, stimulating crop to take root, to germinate and prevention and elimination of disease and pests also has good effect.So biological calcium magnesium phosphorius fertilizer of the present invention had both improved water-soluble phosphorus content in fused(calcium magnesium)phosphate, turn increased the organic matter in soil, improved Soil structure, crop had been had to the multiple effects such as fixed nitrogen, phosphorus decomposing, potassium decomposing, growth-promoting, diseases prevention.
Preferably, described soil improvement agent comprises the raw material of following weight part: Iron-ore Slag 10-20 part, Starso 1-5 part, anilinomethyl triethoxysilane 6-10 part, selenium enriched yeast 2-4 part, Zinc Gluconate 1-3 part, boric acid 1-3 part, double pentaerythritol methacrylate 2-6 part, vinegar 30-40 part, ferrous sulfate 1-3 part, Oil of Eucalyptus 0.5-1.5 part, jade powder 1-5 part and 3-aminopropyl trimethoxysilane 1-3 part.
Soil improvement agent of the present invention is by adopting above-mentioned raw materials and the strict weight proportion controlling each raw material, and obtained soil improvement agent has synergy, promotes the effect of plant absorption nutrition; Adopt the urea coated of melting, slow release effect is remarkable, and fertility is lasting, reaches the effect increasing income volume increase.
Another object of the present invention is achieved through the following technical solutions: a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, and described bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate obtains according to above-mentioned preparation method.
Bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate of the present invention utilizes the physicals of bamboo quality of biomass charcoal, achieve the effective slowly-releasing to fused(calcium magnesium)phosphate, extend the action time of fused(calcium magnesium)phosphate, improve the utilization ratio of fused(calcium magnesium)phosphate, for crop long-time sufficient nutrient supply in vegetative period, and for crop alimentary strengthening provide good technical support.
Bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate of the present invention is used in the plurality of cereals crops such as corn, soybean, paddy rice and vegetables, fruit tree, can realize the single-dose application later stage need not topdress, the level of effective raising soil effective constituent, content and the output of crop kernel nutritive ingredient obviously promote, fertilizer efficiency is lasting, increasing both production and income.
Beneficial effect of the present invention is: waste resource bamboo is obtained bamboo quality of biomass charcoal by preparation method of the present invention, the composite obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate with fused(calcium magnesium)phosphate again, greatly reduce production cost, decrease environmental pollution, the value good economic results in society can brought He apply.
Preparation method's technique of the present invention is simple, and convenient operation and control, steady quality, production efficiency is high, can large-scale industrial production.
Bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate of the present invention is by adding biomass charcoal, biomass charcoal is slight alkalinity, porous, loose and be rich in the carbonaceous mixture of organic matter fraction of various different structure, there is good physical properties and nutrient Regulation effect, increase the validity of the particularly nitrogenous fertilizer of nutrient in soil, the discharge of the sub-nitrogen of effective reduction Soil oxidation, effectively can improve the storage capacity of organic carbon in soil simultaneously.
Bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate of the present invention utilizes the physicals of bamboo quality of biomass charcoal, achieve the effective slowly-releasing to fused(calcium magnesium)phosphate, extend the action time of fused(calcium magnesium)phosphate, improve the utilization ratio of fused(calcium magnesium)phosphate, for crop long-time sufficient nutrient supply in vegetative period, and for crop alimentary strengthening provide good technical support.
Bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate nutritive substance of the present invention enriches, it is lasting that nutritive element release is coordinated, and fertilizer nutrient utilising efficiency is high, can effectively improve and fertilizing soil, improve utilization rate of fertilizer, increase soil organic matter content, reduce the soil weight, improve soil water-reataining fertilizer-keeping ability, promote plant growth, and can crop yield be significantly improved, improve crop quality, there is obvious economic benefit.
Bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate of the present invention is used in the plurality of cereals crops such as corn, soybean, paddy rice and vegetables, fruit tree, can realize the single-dose application later stage need not topdress, the level of effective raising soil effective constituent, content and the output of crop kernel nutritive ingredient obviously promote, fertilizer efficiency is lasting, increasing both production and income.
Biomass charcoal is combined with fused(calcium magnesium)phosphate and produces bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate by the present invention, can either realize utilization of waste as resource, can reach again energy-saving and emission-reduction, increase the doulbe-sides' victory effect of soil carbon sink and raising crop yield and quality.
Embodiment
For the ease of the understanding of those skilled in the art, below in conjunction with embodiment, the present invention is further illustrated, and the content that embodiment is mentioned not is limitation of the invention.
Embodiment 1
A preparation method for bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, comprises step:
(1) by bamboo Pintsch process, bamboo quality of biomass charcoal and inflammable gas is obtained;
(2) by the raw material of fused(calcium magnesium)phosphate and the rear melting of bamboo quality of biomass charcoal mixing, the granulation that account for fused(calcium magnesium)phosphate total raw material weight 20%, pellet is collected; Wherein, the heat needed for melting is burnt by described inflammable gas to be provided;
Described fused(calcium magnesium)phosphate comprises the raw material of following weight part: 20 parts, base manure, mixing Adlerika 0.11 part, composite fungus agent 0.5 part and soil improvement agent 0.5 part; Wherein, described base manure contains the P that weight percent content is 12%
2o
5, the weight percent content MgO that is 8%, the weight percent content CaO that is 25%, weight percent content be the SiO of 20%
2, weight percent content be 0.5% FeO, weight percent content be the MnO of 0.1%;
(3) the pellet lost pressure cooling will collected, screens;
(4) pellet after screening is carried out coating, packaging shipment, obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate.
Described step (1) is specially: bamboo is crushed to particle diameter 1mm, the bamboo after pulverizing is dried to water ratio and is less than 5%, obtain biomass material; Catalyst for cracking and biomass material are put into the cracking of high temperature pyrolysis stove by weight 0.5:100 and carries out Pintsch process, obtain bamboo quality of biomass charcoal and inflammable gas; Wherein, the temperature of Pintsch process is 500 DEG C, and the time of Pintsch process is 60min.
Described catalyst for cracking with greying mesoporous carbon for support of the catalyst, take iron-nickel alloy as active ingredient, wherein, the quality of described iron-nickel alloy accounts for 30% of described catalyst quality, the pattern of described catalyst for cracking is that described iron-nickel alloy is embedded in described greying mesoporous carbon, and the specific surface area of described catalyst for cracking is 400m
2.g
-1, aperture is 5nm, and pore volume is 0.5cm
3.g
-1.
Step (1 ') is also comprised: by bamboo quality of biomass charcoal and activator mix between described step (1) and step (2), be warming up to activation temperature in an inert atmosphere and carry out activation treatment, then be cooled to room temperature, pickling is carried out to product, then be washed to neutral rear dry; Described activator is salt of wormwood; The weight ratio of described biomass charcoal and described activator is 100:1; Inert atmosphere used is nitrogen, and flow is 100mL/min; Temperature rise rate is 4 DEG C/min; Activation temperature is 300 DEG C; Activation treatment soaking time is 3h; Pickling acid used is dilute hydrochloric acid.
In described step (2), the temperature of melting is 125 DEG C; In described step (3), the particle diameter of the pellet after screening is 1mm; In described step (4), packaging net weight >=25Kg, and≤50Kg.
Described fused(calcium magnesium)phosphate also comprises the raw material of following weight part: 5 parts, urea, sodium polyacrylate 5 parts, poly-aspartic-acid 1 part, Castor seed Meal 8 parts, straw powder 10 parts, rare earth nitrate 2 parts, sodium selenate 1 part, humic acids 4 parts, medical stone 6 parts, rhombspar 5 parts.
Described mixing Adlerika is the Adlerika containing carboxymethyl cellulose, and the massfraction of carboxymethyl cellulose is 0.5%.
Described composite fungus agent comprises the raw material of following weight part: phosphorus bacteria 10 parts, 20 parts, vinelandii, silicate bacteria 10 parts, nitrifier 20 parts and antibiotic bacteria 5 parts.
Described soil improvement agent comprises the raw material of following weight part: Iron-ore Slag 10 parts, Starso 1 part, anilinomethyl triethoxysilane 6 parts, selenium enriched yeast 2 parts, Zinc Gluconate 1 part, boric acid 1 part, double pentaerythritol methacrylate 2 parts, vinegar 30 parts, 1 part, ferrous sulfate, Oil of Eucalyptus 0.5 part, jade powder 1 part and 3-aminopropyl trimethoxysilane 1 part.
A kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, obtains according to above-mentioned preparation method.
The bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate obtained by the present embodiment and conventional fused(calcium magnesium)phosphate are applied in corn field respectively and test, under the equal condition of fertilizer amount, bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate is than conventional every mu, fused(calcium magnesium)phosphate volume increase corn 160 kilograms, volume increase 20%, through nutritive ingredient, monitoring center is detected, and the nutrient composition content in corn improves about 3%.
Embodiment 2
A preparation method for bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, comprises step:
(1) by bamboo Pintsch process, bamboo quality of biomass charcoal and inflammable gas is obtained;
(2) by the raw material of fused(calcium magnesium)phosphate and the rear melting of bamboo quality of biomass charcoal mixing, the granulation that account for fused(calcium magnesium)phosphate total raw material weight 21%, pellet is collected; Wherein, the heat needed for melting is burnt by described inflammable gas to be provided;
Described fused(calcium magnesium)phosphate comprises the raw material of following weight part: 30 parts, base manure, mixing Adlerika 0.12 part, composite fungus agent 0.7 part and soil improvement agent 0.7 part; Wherein, described base manure contains the P that weight percent content is 14%
2o
5, the weight percent content MgO that is 10%, the weight percent content CaO that is 27%, weight percent content be the SiO of 22%
2, weight percent content be 0.7% FeO, weight percent content be the MnO of 0.15%;
(3) the pellet lost pressure cooling will collected, screens;
(4) pellet after screening is carried out coating, packaging shipment, obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate.
Described step (1) is specially: bamboo is crushed to particle diameter 1.2mm, the bamboo after pulverizing is dried to water ratio and is less than 5%, obtain biomass material; Catalyst for cracking and biomass material are put into the cracking of high temperature pyrolysis stove by weight 0.7:100 and carries out Pintsch process, obtain bamboo quality of biomass charcoal and inflammable gas; Wherein, the temperature of Pintsch process is 550 DEG C, and the time of Pintsch process is 75min.
Described catalyst for cracking with greying mesoporous carbon for support of the catalyst, take iron-nickel alloy as active ingredient, wherein, the quality of described iron-nickel alloy accounts for 32% of described catalyst quality, the pattern of described catalyst for cracking is that described iron-nickel alloy is embedded in described greying mesoporous carbon, and the specific surface area of described catalyst for cracking is 450m
2.g
-1, aperture is 6nm, and pore volume is 0.7cm
3.g
-1.
Step (1 ') is also comprised: by bamboo quality of biomass charcoal and activator mix between described step (1) and step (2), be warming up to activation temperature in an inert atmosphere and carry out activation treatment, then be cooled to room temperature, pickling is carried out to product, then be washed to neutral rear dry; Described activator is dipotassium hydrogen phosphate; The weight ratio of described biomass charcoal and described activator is 100:2; Inert atmosphere used is nitrogen, and flow is 200mL/min; Temperature rise rate is 5 DEG C/min; Activation temperature is 350 DEG C; Activation treatment soaking time is 2.5h; Pickling acid used is dilute hydrochloric acid.
In described step (2), the temperature of melting is 126 DEG C; In described step (3), the particle diameter of the pellet after screening is 2mm; In described step (4), packaging net weight >=25Kg, and≤50Kg.
Described fused(calcium magnesium)phosphate also comprises the raw material of following weight part: 7 parts, urea, sodium polyacrylate 7 parts, poly-aspartic-acid 2 parts, Castor seed Meal 9 parts, straw powder 11 parts, rare earth nitrate 3 parts, sodium selenate 2 parts, humic acids 5 parts, medical stone 7 parts, rhombspar 6 parts.
Described mixing Adlerika is the Adlerika containing carboxymethyl cellulose, and the massfraction of carboxymethyl cellulose is 0.7%.
Described composite fungus agent comprises the raw material of following weight part: phosphorus bacteria 12 parts, 22 parts, vinelandii, silicate bacteria 12 parts, nitrifier 22 parts and antibiotic bacteria 7 parts.
Described soil improvement agent comprises the raw material of following weight part: Iron-ore Slag 12 parts, Starso 2 parts, anilinomethyl triethoxysilane 7 parts, selenium enriched yeast 2.5 parts, Zinc Gluconate 1.5 parts, boric acid 1.5 parts, double pentaerythritol methacrylate 3 parts, vinegar 32 parts, 1.5 parts, ferrous sulfate, Oil of Eucalyptus 0.7 part, jade powder 2 parts and 3-aminopropyl trimethoxysilane 1.5 parts.
A kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, obtains according to above-mentioned preparation method.
The bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate obtained by the present embodiment and conventional fused(calcium magnesium)phosphate are applied in Soybean Field respectively and test, under the equal condition of fertilizer amount, bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate is than conventional every mu, fused(calcium magnesium)phosphate volume increase soybean 55 kilograms, volume increase 22%, through nutritive ingredient, monitoring center is detected, and the nutrient composition content in soybean improves about 5%.
Embodiment 3
A preparation method for bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, comprises step:
(1) by bamboo Pintsch process, bamboo quality of biomass charcoal and inflammable gas is obtained;
(2) by the raw material of fused(calcium magnesium)phosphate and the rear melting of bamboo quality of biomass charcoal mixing, the granulation that account for fused(calcium magnesium)phosphate total raw material weight 22%, pellet is collected; Wherein, the heat needed for melting is burnt by described inflammable gas to be provided;
Described fused(calcium magnesium)phosphate comprises the raw material of following weight part: 40 parts, base manure, mixing Adlerika 0.13 part, composite fungus agent 1 part and soil improvement agent 1 part; Wherein, described base manure contains the P that weight percent content is 16%
2o
5, the weight percent content MgO that is 12%, the weight percent content CaO that is 29%, weight percent content be the SiO of 25%
2, weight percent content be 1% FeO, weight percent content be the MnO of 0.2%;
(3) the pellet lost pressure cooling will collected, screens;
(4) pellet after screening is carried out coating, packaging shipment, obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate.
Described step (1) is specially: bamboo is crushed to particle diameter 1.5mm, the bamboo after pulverizing is dried to water ratio and is less than 5%, obtain biomass material; Catalyst for cracking and biomass material are put into the cracking of high temperature pyrolysis stove by weight 1:100 and carries out Pintsch process, obtain bamboo quality of biomass charcoal and inflammable gas; Wherein, the temperature of Pintsch process is 600 DEG C, and the time of Pintsch process is 90min.
Described catalyst for cracking with greying mesoporous carbon for support of the catalyst, take iron-nickel alloy as active ingredient, wherein, the quality of described iron-nickel alloy accounts for 35% of described catalyst quality, the pattern of described catalyst for cracking is that described iron-nickel alloy is embedded in described greying mesoporous carbon, and the specific surface area of described catalyst for cracking is 500m
2.g
-1, aperture is 7nm, and pore volume is 1cm
3.g
-1.
Step (1 ') is also comprised: by bamboo quality of biomass charcoal and activator mix between described step (1) and step (2), be warming up to activation temperature in an inert atmosphere and carry out activation treatment, then be cooled to room temperature, pickling is carried out to product, then be washed to neutral rear dry; Described activator is potassium primary phosphate; The weight ratio of described biomass charcoal and described activator is 100:3; Inert atmosphere used is nitrogen, and flow is 300mL/min; Temperature rise rate is 6 DEG C/min; Activation temperature is 400 DEG C; Activation treatment soaking time is 2h; Pickling acid used is dilute hydrochloric acid.
In described step (2), the temperature of melting is 126 DEG C; In described step (3), the particle diameter of the pellet after screening is 3mm; In described step (4), packaging net weight >=25Kg, and≤50Kg.
Described fused(calcium magnesium)phosphate also comprises the raw material of following weight part: 10 parts, urea, sodium polyacrylate 10 parts, poly-aspartic-acid 3 parts, Castor seed Meal 10 parts, straw powder 12 parts, rare earth nitrate 4 parts, sodium selenate 3 parts, humic acids 6 parts, medical stone 8 parts, rhombspar 7 parts.
Described mixing Adlerika is the Adlerika containing carboxymethyl cellulose, and the massfraction of carboxymethyl cellulose is 1%.
Described composite fungus agent comprises the raw material of following weight part: phosphorus bacteria 15 parts, 25 parts, vinelandii, silicate bacteria 15 parts, nitrifier 25 parts and antibiotic bacteria 10 parts.
Described soil improvement agent comprises the raw material of following weight part: Iron-ore Slag 15 parts, Starso 3 parts, anilinomethyl triethoxysilane 8 parts, selenium enriched yeast 3 parts, Zinc Gluconate 2 parts, boric acid 2 parts, double pentaerythritol methacrylate 4 parts, vinegar 35 parts, 2 parts, ferrous sulfate, Oil of Eucalyptus 1 part, jade powder 3 parts and 3-aminopropyl trimethoxysilane 2 parts.
A kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, obtains according to above-mentioned preparation method.
The bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate obtained by the present embodiment and conventional fused(calcium magnesium)phosphate are applied in rice terrace respectively and test, under the equal condition of fertilizer amount, bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate is than conventional every mu, fused(calcium magnesium)phosphate volume increase 144 kilograms, paddy rice, volume increase 24%, through nutritive ingredient, monitoring center is detected, and the nutrient composition content in paddy rice improves about 7%.
Embodiment 4
A preparation method for bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, comprises step:
(1) by bamboo Pintsch process, bamboo quality of biomass charcoal and inflammable gas is obtained;
(2) by the raw material of fused(calcium magnesium)phosphate and the rear melting of bamboo quality of biomass charcoal mixing, the granulation that account for fused(calcium magnesium)phosphate total raw material weight 23%, pellet is collected; Wherein, the heat needed for melting is burnt by described inflammable gas to be provided;
Described fused(calcium magnesium)phosphate comprises the raw material of following weight part: 50 parts, base manure, mixing Adlerika 0.14 part, composite fungus agent 1.3 parts and soil improvement agent 1.3 parts; Wherein, described base manure contains the P that weight percent content is 18%
2o
5, the weight percent content MgO that is 13%, the weight percent content CaO that is 31%, weight percent content be the SiO of 28%
2, weight percent content be 1.3% FeO, weight percent content be the MnO of 0.25%;
(3) the pellet lost pressure cooling will collected, screens;
(4) pellet after screening is carried out coating, packaging shipment, obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate.
Described step (1) is specially: bamboo is crushed to particle diameter 1.8mm, the bamboo after pulverizing is dried to water ratio and is less than 5%, obtain biomass material; Catalyst for cracking and biomass material are put into the cracking of high temperature pyrolysis stove by weight 1.3:100 and carries out Pintsch process, obtain bamboo quality of biomass charcoal and inflammable gas; Wherein, the temperature of Pintsch process is 650 DEG C, and the time of Pintsch process is 105min.
Described catalyst for cracking with greying mesoporous carbon for support of the catalyst, take iron-nickel alloy as active ingredient, wherein, the quality of described iron-nickel alloy accounts for 38% of described catalyst quality, the pattern of described catalyst for cracking is that described iron-nickel alloy is embedded in described greying mesoporous carbon, and the specific surface area of described catalyst for cracking is 550m
2.g
-1, aperture is 8nm, and pore volume is 1.3cm
3.g
-1.
Step (1 ') is also comprised: by bamboo quality of biomass charcoal and activator mix between described step (1) and step (2), be warming up to activation temperature in an inert atmosphere and carry out activation treatment, then be cooled to room temperature, pickling is carried out to product, then be washed to neutral rear dry; Described activator is Potassium ethanoate; The weight ratio of described biomass charcoal and described activator is 100:4; Inert atmosphere used is nitrogen, and flow is 400mL/min; Temperature rise rate is 7 DEG C/min; Activation temperature is 450 DEG C; Activation treatment soaking time is 1.5h; Pickling acid used is dilute hydrochloric acid.
In described step (2), the temperature of melting is 127 DEG C; In described step (3), the particle diameter of the pellet after screening is 4mm; In described step (4), packaging net weight >=25Kg, and≤50Kg.
Described fused(calcium magnesium)phosphate also comprises the raw material of following weight part: 13 parts, urea, sodium polyacrylate 13 parts, poly-aspartic-acid 4 parts, Castor seed Meal 11 parts, straw powder 13 parts, rare earth nitrate 5 parts, sodium selenate 4 parts, humic acids 7 parts, medical stone 9 parts, rhombspar 8 parts.
Described mixing Adlerika is the Adlerika containing carboxymethyl cellulose, and the massfraction of carboxymethyl cellulose is 1.3%.
Described composite fungus agent comprises the raw material of following weight part: phosphorus bacteria 18 parts, 28 parts, vinelandii, silicate bacteria 18 parts, nitrifier 28 parts and antibiotic bacteria 13 parts.
Described soil improvement agent comprises the raw material of following weight part: Iron-ore Slag 18 parts, Starso 4 parts, anilinomethyl triethoxysilane 9 parts, selenium enriched yeast 3.5 parts, Zinc Gluconate 2.5 parts, boric acid 2.5 parts, double pentaerythritol methacrylate 5 parts, vinegar 38 parts, 2.5 parts, ferrous sulfate, Oil of Eucalyptus 1.3 parts, jade powder 4 parts and 3-aminopropyl trimethoxysilane 2.5 parts.
A kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, obtains according to above-mentioned preparation method.
The bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate obtained by the present embodiment and conventional fused(calcium magnesium)phosphate are applied in Rapeseed Field respectively and test, under the equal condition of fertilizer amount, bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate is than conventional every mu, fused(calcium magnesium)phosphate volume increase rape 34.5 kilograms, volume increase 23%, through nutritive ingredient, monitoring center is detected, and the nutrient composition content in rape improves about 6%.
Embodiment 5
A preparation method for bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, comprises step:
(1) by bamboo Pintsch process, bamboo quality of biomass charcoal and inflammable gas is obtained;
(2) by the raw material of fused(calcium magnesium)phosphate and the rear melting of bamboo quality of biomass charcoal mixing, the granulation that account for fused(calcium magnesium)phosphate total raw material weight 24%, pellet is collected; Wherein, the heat needed for melting is burnt by described inflammable gas to be provided;
Described fused(calcium magnesium)phosphate comprises the raw material of following weight part: 60 parts, base manure, mixing Adlerika 0.15 part, composite fungus agent 1.5 parts and soil improvement agent 1.5 parts; Wherein, described base manure contains the P that weight percent content is 20%
2o
5, the weight percent content MgO that is 15%, the weight percent content CaO that is 32%, weight percent content be the SiO of 30%
2, weight percent content be 1.5% FeO, weight percent content be the MnO of 0.3%;
(3) the pellet lost pressure cooling will collected, screens;
(4) pellet after screening is carried out coating, packaging shipment, obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate.
Described step (1) is specially: bamboo is crushed to particle diameter 2mm, the bamboo after pulverizing is dried to water ratio and is less than 5%, obtain biomass material; Catalyst for cracking and biomass material are put into the cracking of high temperature pyrolysis stove by weight 1.5:100 and carries out Pintsch process, obtain bamboo quality of biomass charcoal and inflammable gas; Wherein, the temperature of Pintsch process is 700 DEG C, and the time of Pintsch process is 120min.
Described catalyst for cracking with greying mesoporous carbon for support of the catalyst, take iron-nickel alloy as active ingredient, wherein, the quality of described iron-nickel alloy accounts for 40% of described catalyst quality, the pattern of described catalyst for cracking is that described iron-nickel alloy is embedded in described greying mesoporous carbon, and the specific surface area of described catalyst for cracking is 600m
2.g
-1, aperture is 10nm, and pore volume is 1.5cm
3.g
-1.
Step (1 ') is also comprised: by bamboo quality of biomass charcoal and activator mix between described step (1) and step (2), be warming up to activation temperature in an inert atmosphere and carry out activation treatment, then be cooled to room temperature, pickling is carried out to product, then be washed to neutral rear dry; Described activator is Secondary ammonium phosphate; The weight ratio of described biomass charcoal and described activator is 100:5; Inert atmosphere used is nitrogen, and flow is 500mL/min; Temperature rise rate is 8 DEG C/min; Activation temperature is 500 DEG C; Activation treatment soaking time is 1h; Pickling acid used is dilute hydrochloric acid.
In described step (2), the temperature of melting is 128 DEG C; In described step (3), the particle diameter of the pellet after screening is 4.75mm; In described step (4), packaging net weight >=25Kg, and≤50Kg.
Described fused(calcium magnesium)phosphate also comprises the raw material of following weight part: 15 parts, urea, sodium polyacrylate 15 parts, poly-aspartic-acid 5 parts, Castor seed Meal 12 parts, straw powder 14 parts, rare earth nitrate 6 parts, sodium selenate 5 parts, humic acids 8 parts, medical stone 10 parts, rhombspar 9 parts.
Described mixing Adlerika is the Adlerika containing carboxymethyl cellulose, and the massfraction of carboxymethyl cellulose is 1.5%.
Described composite fungus agent comprises the raw material of following weight part: phosphorus bacteria 20 parts, 30 parts, vinelandii, silicate bacteria 20 parts, nitrifier 30 parts and antibiotic bacteria 15 parts.
Described soil improvement agent comprises the raw material of following weight part: Iron-ore Slag 20 parts, Starso 5 parts, anilinomethyl triethoxysilane 10 parts, selenium enriched yeast 4 parts, Zinc Gluconate 3 parts, boric acid 3 parts, double pentaerythritol methacrylate 6 parts, vinegar 40 parts, 3 parts, ferrous sulfate, Oil of Eucalyptus 1.5 parts, jade powder 5 parts and 3-aminopropyl trimethoxysilane 3 parts.
A kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, obtains according to above-mentioned preparation method.
The bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate obtained by the present embodiment and conventional fused(calcium magnesium)phosphate are applied in apple orchard respectively and test, under the equal condition of fertilizer amount, bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate is than conventional every mu, fused(calcium magnesium)phosphate volume increase apple 420 kilograms, volume increase 21%, through nutritive ingredient, monitoring center is detected, and the nutrient composition content in apple improves about 4%.
Bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate of the present invention can realize the single-dose application later stage and need not topdress, and effectively improve the level of soil effective constituent, content and the output of crop kernel nutritive ingredient obviously promote, and fertilizer efficiency is lasting, increasing both production and income.
Above-described embodiment is the present invention's preferably implementation, and in addition, the present invention can also realize by alternate manner, and any apparent replacement is all within protection scope of the present invention without departing from the inventive concept of the premise.
Claims (10)
1. a preparation method for bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, is characterized in that: comprise the steps:
(1) by bamboo Pintsch process, bamboo quality of biomass charcoal and inflammable gas is obtained;
(2) by the raw material of fused(calcium magnesium)phosphate and the rear melting of bamboo quality of biomass charcoal mixing, the granulation that account for fused(calcium magnesium)phosphate total raw material weight 20-24%, pellet is collected; Wherein, the heat needed for melting is burnt by described inflammable gas to be provided;
Described fused(calcium magnesium)phosphate comprises the raw material of following weight part: base manure 20-60 part, mixing Adlerika 0.11-0.15 part, composite fungus agent 0.5-1.5 part and soil improvement agent 0.5-1.5 part; Wherein, described base manure contains the P that weight percent content is 12-20%
2o
5, the weight percent content MgO that is 8-15%, the weight percent content CaO that is 25-32%, weight percent content be the SiO of 20-30%
2, weight percent content is the FeO of 0.5-1.5%, weight percent content is the MnO of 0.1-0.3%;
(3) the pellet lost pressure cooling will collected, screens;
(4) pellet after screening is carried out coating, packaging shipment, obtained bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate.
2. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 1, it is characterized in that: described step (1) is specially: bamboo is crushed to particle diameter 1-2mm, bamboo after pulverizing is dried to water ratio and is less than 5%, obtain biomass material; Catalyst for cracking and biomass material are put into the cracking of high temperature pyrolysis stove by weight 0.5-1.5:100 and carries out Pintsch process, obtain bamboo quality of biomass charcoal and inflammable gas; Wherein, the temperature of Pintsch process is 500-700 DEG C, and the time of Pintsch process is 60-120min.
3. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 2, it is characterized in that: described catalyst for cracking with greying mesoporous carbon for support of the catalyst, take iron-nickel alloy as active ingredient, wherein, the quality of described iron-nickel alloy accounts for the 30-40% of described catalyst quality, the pattern of described catalyst for cracking is that described iron-nickel alloy is embedded in described greying mesoporous carbon, and the specific surface area of described catalyst for cracking is 400m
2.g
-1-600m
2.g
-1, aperture is 5-10nm, and pore volume is 0.5cm
3.g
-1-1.5cm
3.g
-1.
4. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 1, it is characterized in that: also comprise step (1 ') between described step (1) and step (2): by bamboo quality of biomass charcoal and activator mix, be warming up to activation temperature in an inert atmosphere and carry out activation treatment, then room temperature is cooled to, pickling is carried out to product, then is washed to neutral rear dry; Described activator is at least one in salt of wormwood, dipotassium hydrogen phosphate, potassium primary phosphate, Potassium ethanoate, Secondary ammonium phosphate, primary ammonium phosphate and ammonium acetate; The weight ratio of described biomass charcoal and described activator is 100:1-5; Inert atmosphere used is nitrogen, and flow is 100-500mL/min; Temperature rise rate is 4-8 DEG C/min; Activation temperature is 300-500 DEG C; Activation treatment soaking time is 1-3h; Pickling acid used is dilute hydrochloric acid.
5. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 1, it is characterized in that: in described step (2), the temperature of melting is 125-128 DEG C; In described step (3), the particle diameter of the pellet after screening is 1-4.75mm; In described step (4), packaging net weight >=25Kg, and≤50Kg.
6. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 1, is characterized in that: described fused(calcium magnesium)phosphate also comprises the raw material of following weight part: urea 5-15 part, sodium polyacrylate 5-15 part, poly-aspartic-acid 1-5 part, Castor seed Meal 8-12 part, straw powder 10-14 part, rare earth nitrate 2-6 part, sodium selenate 1-5 part, humic acids 4-8 part, medical stone 6-10 part, rhombspar 5-9 part.
7. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 1, it is characterized in that: described mixing Adlerika is the Adlerika containing carboxymethyl cellulose, the massfraction of carboxymethyl cellulose is 0.5-1.5%.
8. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 1, is characterized in that: described composite fungus agent comprises the raw material of following weight part: phosphorus bacteria 10-20 part, vinelandii 20-30 part, silicate bacteria 10-20 part, nitrifier 20-30 part and antibiotic bacteria 5-15 part.
9. the preparation method of a kind of bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to claim 1, is characterized in that: described soil improvement agent comprises the raw material of following weight part: Iron-ore Slag 10-20 part, Starso 1-5 part, anilinomethyl triethoxysilane 6-10 part, selenium enriched yeast 2-4 part, Zinc Gluconate 1-3 part, boric acid 1-3 part, double pentaerythritol methacrylate 2-6 part, vinegar 30-40 part, ferrous sulfate 1-3 part, Oil of Eucalyptus 0.5-1.5 part, jade powder 1-5 part and 3-aminopropyl trimethoxysilane 1-3 part.
10. a bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate, is characterized in that: the preparation method of described bamboo quality of biomass charcoal base fused(calcium magnesium)phosphate according to any one of claim 1-9 obtains.