CN104807892A - 低压电器电触头超声波无损检测用直角型狭缝测试工件 - Google Patents
低压电器电触头超声波无损检测用直角型狭缝测试工件 Download PDFInfo
- Publication number
- CN104807892A CN104807892A CN201510170296.6A CN201510170296A CN104807892A CN 104807892 A CN104807892 A CN 104807892A CN 201510170296 A CN201510170296 A CN 201510170296A CN 104807892 A CN104807892 A CN 104807892A
- Authority
- CN
- China
- Prior art keywords
- slit
- width
- depth
- degree
- perpendicular type
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明提供一种低压电器电触头超声波无损检测用直角型狭缝测试工件，包括测试块，所述测试块为声学分辨力测试块，所述声学分辨力测试块上分别设置有12组不同宽度、不同间距的相互垂直的直角型狭缝。本发明可以标定超声探头分辨水平间距、垂直间距相隔为0.05mm、0.08mm、0.10mm、0.13mm、0.15mm、0.18mm、0.20mm、0.23mm、0.25mm、0.28mm、0.30mm、0.35mm的水平、垂直及倾斜缺陷的能力，完成对超声探头声学分辨力的标定；同时能够检测出低压电器电触点焊接面上的裂纹、孔状以及条状的各类缺陷，并能对缺陷的大小做出定量标定，提高工作效率，具有很高的推广应用价值。
Description
技术领域
本发明属于超声波探伤装备技术领域，更具体地说，是涉及一种低压电器电触头超声波无损检测用直角型狭缝测试工件。
背景技术
超声波检测是目前应用最为广泛的无损检测方法之一。它具有穿透力强、设备轻便、检测成本低、检测效率高，并可以即时知道检测结果等优点。在实际检测中，被检测部件不同，而需要采用不同的超声波探伤标准。但是目前，在低压电器行业中，没有专用试块进行超声检测中超声探头的声学分辨力的性能指标的标定，给检测工作带来了不便。
发明内容
针对上述现有技术中的缺陷，本发明的目的是设计一种低压电器电触头超声波无损检测用直角型狭缝测试工件，能快速准确检测探头的声学分辨力指标。
为实现上述的目的，本发明采用的技术方案是，
本发明提供一种低压电器电触头超声波无损检测用直角型狭缝测试工件，包括测试块，所述测试块为声学分辨力测试块，所述声学分辨力测试块上分别设置有多组不同宽度、不同间距的相互垂直的直角型狭缝。
优选地，所述声学分辨力测试块为长方体，所述长方体的长为300mm、宽为100mm、厚度为5.0mm。
优选地，所述声学分辨力测试块的长方体上表面从上到下，依次设置有12组直角型狭缝。
优选地，12组直角型狭缝的宽度范围是：0.02～0.5mm，各组宽度差值可以为0.02mm,0.03mm，0.05mm；12组直角型狭缝的狭缝间距范围是：0.05mm～0.35mm，各组狭缝中狭缝间距的差值可以为0.02mm，0.03mm,0.05mm；12组直角型狭缝的深度相等并可取1.0mm，2.0mm，或者3.0mm。
更优选地，12组所述直角型狭缝深度是一定的，具体的：
设置有宽度为0.35mm、狭缝间距为0.35mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.05mm、狭缝间距为0.05mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.08mm、狭缝间距为0.08mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.30mm、狭缝间距为0.30mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.28mm、狭缝间距为0.28mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.10mm、狭缝间距为0.10mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.13mm、狭缝间距为0.13mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.25mm、狭缝间距为0.25mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.23mm、狭缝间距为0.23mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.15mm、狭缝间距为0.15mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.18mm、狭缝间距为0.18mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.20mm、狭缝间距为0.20mm、深度为2.0mm的狭缝共3条。
更优选地，各组所述直角型狭缝之间保持0.6～1.5mm的间距。
优选地，所述直角型狭缝的靠近长方体块边缘一条直角边距离长方体块边缘为1.0mm。
由于采用了上述技术方案，本发明的有益效果是：
本发明测试工件是检验焊接区域不同位置的条状缺陷的专用试块；可以标定超声探头分辨水平间距、垂直间距相隔为0.05mm、0.08mm、0.10mm、0.13mm、0.15mm、0.18mm、0.20mm、0.23mm、0.25mm、0.28mm、0.30mm、0.35mm等的水平、垂直及倾斜缺陷的能力，完成对超声探头声学分辨力的标定；同时能够检测出低压电器电触点焊接面上的裂纹、孔状以及条状的各类缺陷，并能对缺陷的大小做出定量的标定，提高工作效率，具有很高的推广应用价值。
附图说明
图1为本发明一实施例的低压电器电触头超声波探伤测试工件俯视图；
图2为本发明一实施例的低压电器电触头超声波探伤测试工件前视图。
具体实施方式
下面结合附图及具体实施例对本发明的具体实施方式如所涉及的工作原理等作进一步的详细说明。
如图1、图2所示，本实施例为一种低压电器电触头超声波无损检测用直角型狭缝测试工件，包括测试块，所述测试块为声学分辨力测试块；所述声学分辨力测试块为长方体，该长方体的长为300mm、宽为100mm、厚度为5.0mm。长方体上表面从上到下，依次设置有12组直角型狭缝；12组直角型狭缝的宽度范围是：0.02～0.5mm，各组宽度差值可以为0.02mm,0.03mm，0.05mm。12组直角型狭缝的狭缝间距范围是：0.05mm～0.35mm，各组狭缝中狭缝间距的差值可以为0.02mm，0.03mm,0.05mm。12组直角型狭缝的深度相等并可取1.0mm，2.0mm，或者3.0mm。
具体的，本实施例中12组直角型狭缝的参数为：
宽度为0.35mm，狭缝间距为0.35mm，深度为2.0mm的狭缝共3条；
宽度为0.05mm,狭缝间距为0.05mm，深度为2.0mm的狭缝共3条；
宽度为0.08mm,狭缝间距为0.08mm，深度为2.0mm的狭缝共3条；
宽度为0.30mm,狭缝间距为0.30mm，深度为2.0mm的狭缝共3条；
宽度为0.28mm,狭缝间距为0.28mm，深度为2.0mm的狭缝共3条；
宽度为0.10mm,狭缝间距为0.10mm，深度为2.0mm的狭缝共3条；
宽度为0.13mm,狭缝间距为0.13mm，深度为2.0mm的狭缝共3条；
宽度为0.25mm,狭缝间距为0.25mm，深度为2.0mm的狭缝共3条；
宽度为0.23mm,狭缝间距为0.23mm，深度为2.0mm的狭缝共3条；
宽度为0.15mm,狭缝间距为0.15mm，深度为2.0mm的狭缝共3条；
宽度为0.18mm,狭缝间距为0.18mm，深度为2.0mm的狭缝共3条；
宽度为0.20mm,狭缝间距为0.20mm，深度为2.0mm的狭缝共3条。
本实施例中，各组所述直角型狭缝之间应保持1.0mm的间距。
本实施例中，所述直角型狭缝的靠近长方体块边缘一条直角边距离长方体块边缘为1.0mm。
本实施例所述测试工件，是检验焊接区域不同位置的条状缺陷的专用试块，可以标定超声探头分辨水平间距、垂直间距相隔为0.05mm、0.08mm、0.10mm、0.13mm、0.15mm、0.18mm、0.20mm、0.23mm、0.25mm、0.28mm、0.30mm、0.35mm的水平、垂直及倾斜缺陷的能力，完成对超声探头声学分辨力的标定；同时能够检测出低压电器电触点焊接面上的裂纹、孔状以及条状的各类缺陷，并能对缺陷的大小做出定量的标定，提高工作效率，具有很高的推广应用价值。
尽管本发明的内容已经通过上述优选实施例作了详细介绍，但应当认识到上述的描述不应被认为是对本发明的限制。在本领域技术人员阅读了上述内容后，对于本发明的多种修改和替代都将是显而易见的。因此，本发明的保护范围应由所附的权利要求来限定。
Claims (7)
1.一种低压电器电触头超声波无损检测用直角型狭缝测试工件，其特征在于，包括测试块，所述测试块为声学分辨力测试块，所述声学分辨力测试块上分别设置有多组不同宽度、不同间距的相互垂直的直角型狭缝。
2.如权利要求1所述的一种低压电器电触头超声波无损检测用直角型狭缝测试工件，其特征在于，所述声学分辨力测试块为长方体，所述长方体的长为300mm、宽为100mm、厚度为5.0mm。
3.如权利要求2所述的一种低压电器电触头超声波无损检测用直角型狭缝测试工件，其特征在于，所述声学分辨力测试块的长方体上表面从上到下，依次设置有12组直角型狭缝。
4.如权利要求3所述的一种低压电器电触头超声波无损检测用直角型狭缝测试工件，其特征在于，12组直角型狭缝的宽度范围是：0.02～0.5mm，各组宽度差值为0.02mm,0.03mm，0.05mm；12组直角型狭缝的狭缝间距范围是：0.05mm～0.35mm，各组狭缝中狭缝间距的差值为0.02mm，0.03mm,0.05mm；12组直角型狭缝的深度相等并取1.0mm，2.0mm，或者3.0mm。
5.如权利要求4所述的一种低压电器电触头超声波无损检测用直角型狭缝测试工件，其特征在于，12组所述直角型狭缝深度是一定的，具体的：
设置有宽度为0.35mm、狭缝间距为0.35mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.05mm、狭缝间距为0.05mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.08mm、狭缝间距为0.08mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.30mm、狭缝间距为0.30mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.28mm、狭缝间距为0.28mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.10mm、狭缝间距为0.10mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.13mm、狭缝间距为0.13mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.25mm、狭缝间距为0.25mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.23mm、狭缝间距为0.23mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.15mm、狭缝间距为0.15mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.18mm、狭缝间距为0.18mm、深度为2.0mm的狭缝共3条；
设置有宽度为0.20mm、狭缝间距为0.20mm、深度为2.0mm的狭缝共3条。
6.如权利要求2-5任一项所述的一种低压电器电触头超声波无损检测用直角型狭缝测试工件，其特征在于，所述直角型狭缝的靠近长方体块边缘一条直角边距离长方体块边缘为1.0mm。
7.如权利要求1-5任一项所述的一种低压电器电触头超声波无损检测用直角型狭缝测试工件，其特征在于，各组所述直角型狭缝之间保持0.6～1.5mm的间距。