CN104806870A - 一种耐磨型铝合金管材 - Google Patents
一种耐磨型铝合金管材 Download PDFInfo
- Publication number
- CN104806870A CN104806870A CN201510138655.XA CN201510138655A CN104806870A CN 104806870 A CN104806870 A CN 104806870A CN 201510138655 A CN201510138655 A CN 201510138655A CN 104806870 A CN104806870 A CN 104806870A
- Authority
- CN
- China
- Prior art keywords
- powder
- aluminum alloy
- alloy pipe
- aluminium alloy
- tubular product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐磨型铝合金管材,该铝合金管材包括基材层和表层,所述的表层采用等离子热喷涂工艺成型于基材层外部,所述的基材层为铝合金管套,所述的表层原料的主要成分及其百分含量配比为:Al2O3粉末55%-65%、TiO2粉末2%-4%、SiO2粉末8%-10%、ZnO粉末10%-12%、镍粉12%-15%、铬粉4%-8%。本发明揭示了一种耐磨型铝合金管材,该铝合金管材采用双层复合结构设计,层间结合性能稳定、强度高,表层由多种合金材料组成,其成分配制合理,成本适中,可有效的提高铝合金管材的耐磨性能及使用寿命,扩展铝合金管材的适用范围。
Description
技术领域
本发明涉及一种铝合金管材,尤其涉及一种耐磨型铝合金管材,属于铝合金制品技术领域。
背景技术
铝合金管材是有色金属管的一种,它是将铝合金型材经挤压、拉拔等工艺加工成沿其纵向全长中空的金属管状材料。铝合金管材可以有一个或多个封闭的通孔,壁厚、横截面均匀一致,按外形可分为:方管、圆管、花纹管、异型管等;按挤压方式可分为:无缝铝管和普通挤压管;按精度可分为:普通铝管和精密铝管,其中精密铝管一般需要在挤压后进行再加工,如冷拉精抽;按轧制厚度可分为:普通铝管和薄壁铝管。由于铝合金管材具有密度小、质量轻、强度高以及优良的导热性、可焊性、可锻型、低电阻性及机加工等性能,铝合金管材被广泛用于各行各业,如:汽车、轮船、航天、航空、电器、农业、机电、家居等。铝合金管材在我们的生活已经无处不在,在很多场合已代替钢铁、铜材、木材和塑料,成为人类社会的一种重要的基础材料。
为了提高铝合金管材的使用寿命和耐用度,人们采取了多种工艺对铝合金管材进行表面强度,如:热喷涂,物理、化学气相沉积、复合电镀法、激光熔覆法等。上述工艺可在铝合金管材表面形成强化层,以提高其耐磨性能,但其强化层的性能层次不齐、表面质量不高,且成本偏高,因此,铝合金管材的表面强化工艺还有待进一步研发和完善。
发明内容
针对上述需求,本发明提供了一种耐磨型铝合金管材,该铝合金管材采用双层复合结构设计,表层成分配制合理,成本适中,在基材层上的附着性能稳定,赋予了铝合金管材突出的耐磨性能,有效的提升了铝合金管材的使用寿命。
本发明是一种耐磨型铝合金管材,该铝合金管材包括基材层和表层,所述的表层采用等离子热喷涂工艺成型于基材层外部,所述的基材层为铝合金管套,所述的表层原料的主要成分及其百分含量配比为:Al2O3粉末 55%-65%、TiO2粉末 2%-4%、SiO2粉末 8%-10%、ZnO粉末 10%-12%、镍粉 12%-15%、铬粉 4%-8%。
在本发明一较佳实施例中,所述的表层原料的主要成分及其百分含量配比为:Al2O3粉末 58%-60%、TiO2粉末 2.5%-3%、SiO2粉末 8.5%-9%、ZnO粉末 10%-11%、镍粉 14%-15%、铬粉 5%-6%。
在本发明一较佳实施例中,所述的表层原料的平均颗粒直径为8-10um。
在本发明一较佳实施例中,所述的表层的成型厚度控制在20-35um。
本发明揭示了一种耐磨型铝合金管材,该铝合金管材采用双层复合结构设计,层间结合性能稳定、强度高,表层由多种合金材料组成,其成分配制合理,成本适中,可有效的提高铝合金管材的耐磨性能及使用寿命,扩展铝合金管材的适用范围。
附图说明
下面结合附图和具体实施方式对本发明作进一步详细的说明:
图1是本发明实施例耐磨型铝合金管材的结构示意图;
附图中各部件的标记如下: 1、基材层,2、表层。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
图1是本发明实施例耐磨型铝合金管材的结构示意图;该铝合金管材包括基材层1和表层2,所述的表层2采用等离子热喷涂工艺成型于基材层1外部,所述的基材层1为铝合金管套,所述的表层2原料的主要成分及其百分含量配比为:Al2O3粉末 55%-65%、TiO2粉末 2%-4%、SiO2粉末 8%-10%、ZnO粉末 10%-12%、镍粉 12%-15%、铬粉 4%-8%。
本发明提及的耐磨型铝合金管材中,表层2原料的主要成分及其百分含量配比为:Al2O3粉末 58%-60%、TiO2粉末 2.5%-3%、SiO2粉末 8.5%-9%、ZnO粉末 10%-11%、镍粉 14%-15%、铬粉 5%-6%;表层2原料的平均颗粒直径为8-10um;表层2的成型厚度控制在20-35um。
本发明提及的耐磨型铝合金管材的具体制备方法如下:
a)选材备料,基材选用为铝合金管套,外径为35mm,厚度约为2mm,合金成分控制在3%以下;表层原料的主要成分及其百分含量配比为:Al2O3粉末 58%%、TiO2粉末 3%、SiO2粉末9%、ZnO粉末 10%%、镍粉 15%、铬粉 5%;
b)材料前处理,该工序包括表层原料的球磨及干燥处理、基材的粗化及预热处理;表层原料的处理设备选用干式球磨机,球磨机转速控制在55r/min,球料比为3:1,处理时间约为8小时,制得的表层原料的平均颗粒直径为9-10um;表层原料的干燥温度控制在60℃,时间为1.5小时;
基材的粗化处理方式为喷砂处理,原料选用白刚玉砂,颗粒度约为400目,喷砂压力控制在0.1-0.12MPa,距离为15mm,粗化处理后的基材的表面粗糙度约为25um;预热设备使用烘箱,基材的预热温度控制在120℃左右;
c)热喷涂处理,该工序使用等离子喷涂设备,其主要参数如下:主电源的最大输出功率为80KW,喷枪的工作电流控制在200-220A,工作电压为60V,工作气体选用氮气和氢气,压力约为1.2MPa,喷枪与基材的距离控制在68-70mm,角度为70°,移动速度控制在300mm/s;送粉器的送粉速度控制在20g/min,辅助气体选用氮气;上述热喷涂操作往复执行3次,制得的表层厚度约为30-35um;
d)后处理,该工序包括去应力退火处理和封孔处理;去应力退火的温度控制在200℃-210℃,处理时间为2.5小时;期间,待管材温度降至60℃-70℃左右时,进行封孔处理,封孔材料使用微晶石蜡。
本发明揭示了一种耐磨型铝合金管材,其特点是:该铝合金管材采用双层复合结构设计,层间结合性能稳定、强度高,表层由多种合金材料组成,其成分配制合理,成本适中,可有效的提高铝合金管材的耐磨性能及使用寿命,扩展铝合金管材的适用范围。
以上所述,仅为本发明的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本领域的技术人员在本发明所揭露的技术范围内,可不经过创造性劳动想到的变化或替换,都应涵盖在本发明的保护范围之内。因此,本发明的保护范围应该以权利要求书所限定的保护范围为准。
Claims (4)
1.一种耐磨型铝合金管材,其特征在于,该铝合金管材包括基材层和表层,所述的表层采用等离子热喷涂工艺成型于基材层外部,所述的基材层为铝合金管套,所述的表层原料的主要成分及其百分含量配比为:Al2O3粉末 55%-65%、TiO2粉末 2%-4%、SiO2粉末 8%-10%、ZnO粉末 10%-12%、镍粉 12%-15%、铬粉 4%-8%。
2.根据权利要求1所述的耐磨型铝合金管材,其特征在于,所述的表层原料的主要成分及其百分含量配比为:Al2O3粉末 58%-60%、TiO2粉末 2.5%-3%、SiO2粉末 8.5%-9%、ZnO粉末 10%-11%、镍粉 14%-15%、铬粉 5%-6%。
3.根据权利要求1所述的耐磨型铝合金管材,其特征在于,所述的表层原料的平均颗粒直径为8-10um。
4.根据权利要求1所述的耐磨型铝合金管材,其特征在于,所述的表层的成型厚度控制在20-35um。