CN104805709A - 一种改进的无纺布涂布用颜料 - Google Patents

一种改进的无纺布涂布用颜料 Download PDF

Info

Publication number
CN104805709A
CN104805709A CN201510225310.8A CN201510225310A CN104805709A CN 104805709 A CN104805709 A CN 104805709A CN 201510225310 A CN201510225310 A CN 201510225310A CN 104805709 A CN104805709 A CN 104805709A
Authority
CN
China
Prior art keywords
parts
pigment
ethylene glycol
nonwoven fabric
coating pigment
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510225310.8A
Other languages
English (en)
Inventor
沈向红
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huzhou Zhe Hao Silk Co Ltd
Original Assignee
Huzhou Zhe Hao Silk Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Huzhou Zhe Hao Silk Co Ltd filed Critical Huzhou Zhe Hao Silk Co Ltd
Priority to CN201510225310.8A priority Critical patent/CN104805709A/zh
Publication of CN104805709A publication Critical patent/CN104805709A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种改进的无纺布涂布用颜料，原料为：乙醇、溶纤剂、颜料、水、高岭土、碳酸钙、淀粉酶、乙二醇单乙醚醋酸酯、炭黑和醋酸丁酯；产品固含量39-45％，粘度75-95s；pH6.5-8.5，贮存15-19个月不变质；原料简单易得，光泽95-99.9％，耐磨性160-320次，可以广泛生产并不断代替现有材料。

Description

一种改进的无纺布涂布用颜料
技术领域
本发明涉及纺织品用材料技术领域，尤其涉及一种改进的无纺布涂布用颜料。
背景技术
无纺布属于纺织品的一种；纺织纤维经过加工织造而成的产品称之为纺织品。中国是世界上最早生产纺织品的国家之一。丙烯颜料是用一种化学合成胶乳剂(含丙烯酸酯、甲基丙烯酸酯、丙烯酸、甲基丙烯酸，以及增稠剂、填充剂等)与颜色微粒混合而成的新型绘画颜料。纺织颜料附着力相对小些，操作不当极易掉色。用来手绘绘画工序麻烦，相对费时费力。纺织颜料系列：例如珍珠笔，植绒胶，爱得乐金属纺织色，ABS防滑胶，纺织亮粉胶等。六色牌是专门在纺织材料上制作的颜料。此产品是随着个性手绘DIY的流行，出现的一种新型颜料，广泛应用于手绘鞋，手绘T恤，手绘服装，手绘钱包，手绘帽子，手绘涂鸦，服装修色，墙体绘画等领域。其性能突出，使用简单，得到手绘店、手绘工厂以及DIY爱好者的喜爱和广泛使用。
从国内经济环境看，国内需求将成为行业增长的重要驱动力。80％左右的中国纺织品在国内消费。随着国内经济的持续快速增长，居民收入的稳定提升，将拉动内需市场的进一步发展。从生产制造角度来分类又可分为钛系颜料、铁系颜料、铬系颜料、铅系颜料、锌系颜料、金属颜料、有机合成颜料，这种分类方法有实用意义，往往一个系统就能代表一个颜料专业生产行业。丙烯颜料可用于手绘墙画的绘制上，以及其他的装饰绘画，丙烯颜料不溶于水，又可以方便的溶于油画，是一种非常好的手绘颜料。
发明内容
本发明提供一种纺织品涂布用颜料，解决现有纺织品涂布用颜料光泽度和粘度低等技术问题。
本发明采用以下技术方案：一种改进的无纺布涂布用颜料，其原料按质量份数配比如下：乙醇100份，溶纤剂40-60份，颜填料1-10份，水40-80份，高岭土10-30份，碳酸钙5-25份，淀粉酶3-17份，乙二醇单乙醚醋酸酯15-35份，炭黑0.1-1份，醋酸丁酯10-50份。
作为本发明的一种优选技术方案：所述纺织品涂布用颜料的原料按质量份数配比如下：乙醇100份，溶纤剂45-55份，颜填料2-8份，水50-70份，高岭土15-25份，碳酸钙10-20份，淀粉酶4-16份，乙二醇单乙醚醋酸酯20-30份，炭黑0.3-0.7份，醋酸丁酯20-40份。
作为本发明的一种优选技术方案：所述纺织品涂布用颜料的原料按质量份数配比如下：乙醇100份，溶纤剂50份，颜填料5份，水60份，高岭土20份，碳酸钙15份，淀粉酶10份，乙二醇单乙醚醋酸酯25份，炭黑0.5份，醋酸丁酯30份。
作为本发明的一种优选技术方案：所述溶纤剂采用二甲基溶纤剂或乙二醇单乙醚。
作为一种优选技术方案：所述颜填料采用酞菁蓝或氧化铁黄。
有益效果
本发明所述一种纺织品涂布用颜料采用以上技术方案与现有技术相比，具有以下技术效果：1、产品固含量39-45％，粘度75-95s；2、pH6.5-8.5，贮存15-19个月不变质；3、原料简单易得，光泽95-99.9％，耐磨性160-320次，可以广泛生产并不断代替现有材料。
具体实施方式
以下结合实例对本发明作进一步的描述，实施例仅用于对本发明进行说明，并不构成对权利要求范围的限制，本领域技术人员可以想到的其他替代手段，均在本发明权利要求范围内。
实施例1：
按照质量份数配比称取乙醇100份，乙二醇单乙醚40份，氧化铁黄1份，水40份，高岭土10份，碳酸钙5份，淀粉酶3份，乙二醇单乙醚醋酸酯15份，炭黑0.1份，醋酸丁酯10份，在反应釜中搅拌混合均匀既可。
产品固含量39％，粘度75s；pH6.5，贮存15个月不变质；原料简单易得，光泽95％，耐磨性160次。
实施例2：
按照质量份数配比称取乙醇100份，乙二醇单乙醚60份，氧化铁黄10份，水80份，高岭土30份，碳酸钙25份，淀粉酶17份，乙二醇单乙醚醋酸酯35份，炭黑1份，醋酸丁酯50份，在反应釜中搅拌混合均匀既可。。
产品固含量40％，粘度80s；pH7，贮存16个月不变质；原料简单易得，光泽96％，耐磨性160-200次。
实施例3：
按照质量份数配比称取乙醇100份，二甲基溶纤剂45份，酞菁蓝2份，水50份，高岭土15份，碳酸钙10份，淀粉酶4份，乙二醇单乙醚醋酸酯20份，炭黑0.3份，醋酸丁酯20份，在反应釜中搅拌混合均匀既可。
产品固含量42％，粘度85s；pH7.5，贮存17个月不变质；原料简单易得，光泽98％，耐磨性220次。
实施例4：
按照质量份数配比称取乙醇100份，二甲基溶纤剂55份，酞菁蓝8份，水70份，高岭土25份，碳酸钙20份，淀粉酶16份，乙二醇单乙醚醋酸酯30份，炭黑0.7份，醋酸丁酯40份，在反应釜中搅拌混合均匀既可。
产品固含量44％，粘度90s；pH8，贮存18个月不变质；原料简单易得，光泽99％，耐磨性300次。
实施例5：
按照质量份数配比称取乙醇100份，二甲基溶纤剂50份，酞菁蓝5份，水60份，高岭土20份，碳酸钙15份，淀粉酶10份，乙二醇单乙醚醋酸酯25份，炭黑0.5份，醋酸丁酯30份，在反应釜中搅拌混合均匀既可。
产品固含量45％，粘度95s；pH8.5，贮存19个月不变质；原料简单易得，光泽99.9％，耐磨性320次。

Claims (5)

1.一种改进的无纺布涂布用颜料，其特征在于，所述纺织品涂布用颜料的原料按质量份数配比如下：乙醇100份，溶纤剂40-60份，颜填料1-10份，水40-80份，高岭土10-30份，碳酸钙5-25份，淀粉酶3-17份，乙二醇单乙醚醋酸酯15-35份，炭黑0.1-1份，醋酸丁酯10-50份。
2.根据权利要求1所述的一种改进的无纺布涂布用颜料，其特征在于，所述纺织品涂布用颜料的原料按质量份数配比如下：乙醇100份，溶纤剂45-55份，颜填料2-8份，水50-70份，高岭土15-25份，碳酸钙10-20份，淀粉酶4-16份，乙二醇单乙醚醋酸酯20-30份，炭黑0.3-0.7份，醋酸丁酯20-40份。
3.根据权利要求2所述的一种改进的无纺布涂布用颜料，其特征在于，所述纺织品涂布用颜料的原料按质量份数配比如下：乙醇100份，溶纤剂50份，颜填料5份，水60份，高岭土20份，碳酸钙15份，淀粉酶10份，乙二醇单乙醚醋酸酯25份，炭黑0.5份，醋酸丁酯30份。
4.根据权利要求1所述的一种改进的无纺布涂布用颜料，其特征在于：所述溶纤剂采用二甲基溶纤剂或乙二醇单乙醚。
5.根据权利要求1所述的一种改进的无纺布涂布用颜料，其特征在于：所述颜填料采用酞菁蓝或氧化铁黄。
CN201510225310.8A 2015-05-05 2015-05-05 一种改进的无纺布涂布用颜料 Pending CN104805709A (zh)