CN104804462A - Plastic wood material - Google Patents

Abstract

The invention relates to a plastic wood material which comprises the following raw materials in parts by weight: 6 to 10 parts of cupric acetate, 3 to 6 parts of urea, 2 to 4 parts of urotropine, 7 to 11 parts of waste plastic, 6 to 8 parts of talcum powder, 6 to 10 parts of titanate, 4 to 11 parts of HMDS (hexamethyl-disilazane), 1 to 4 parts of an antioxidant DLTP, 3 to 6 parts of a composite lubricant, 4 to 7 parts of wood meal, 1 to 3 parts of a mould inhibitor, 8 to 11 parts of zinc stearate, 4 to 9 parts of iron oxide red, 3 to 8 parts of carbon black, 6 to 10 parts of chlorinated polyethylene, 2 to 5 parts of a plasticizer and 4 to 11 parts of maleic anhydride. The plastic wood material provided by the invention has the benefits as follows: the plastic wood material is excellent in intensity, and is acid and alkali resistant and corrosion-proof, waste plastics are adopted for use, environment pollution caused by plastic is reduced, and a far-reaching influence can be produced.

Description

A kind of plastic-wood material

Technical field

The present invention relates to a kind of plastic-wood material.

Background technology

Mould wood, as the term suggests be exactly the combination of solid wood and plastics, it had both maintained the affinity sensation of solid wood, had again good protection against the tide water-fast, acid and alkali-resistance, antifungal, antistatic, the performances such as Anti-moth-eating.Have the Waterproof corrosion of plastics and texture two kinds of characteristics of timber concurrently owing to moulding wood, make it become a kind of excellent property and very durable outdoor building materials; The also Wood member of the use such as alternative harbour, harbour.And along with people are to the raising of environmental resources attention degree, become the trend of development of world economy with the circular-type economy Development patterns that waste and old material reclaims and comprehensive utilization of resources is core.Devoting Major Efforts To Developing resource circulation utilization technology, will exert far reaching influence to the national economic development and environment sustainable development.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provides a kind of plastic-wood material, has good intensity and acid and alkali-resistance and etch-proof performance, adopts waste or used plastics simultaneously, decrease the pollution of plastics to environment, have a far reaching influence.

For solving prior art problem, technical scheme provided by the invention is, a kind of plastic-wood material, and it is made up of the raw material of following parts by weight:

Neutralized verdigris 6-10 part, urea 3-6 part, urotropine 2-4 part, waste or used plastics 7-11 part, talcum powder 6-8 part, titanic acid ester 6-10 part, hexamethyldisilazane 4-11 part, anti-oxidant DLTP 1-4 part, compounded lubricant 3-6 part, wood powder 4-7 part, mould inhibitor 1-3 part, Zinic stearas 8-11 part, iron oxide red 4-9 part, carbon black 3-8 part, chlorinatedpolyethylene 6-10 part, softening agent 2-5 part, maleic anhydride 4-11 part.

The invention has the beneficial effects as follows: plastic-wood material of the present invention to there is good intensity and acid and alkali-resistance and etch-proof performance, adopt waste or used plastics simultaneously, decrease the pollution of plastics to environment, have a far reaching influence.

Embodiment

embodiment 1

A kind of plastic-wood material, it is made up of the raw material of following parts by weight:

Neutralized verdigris 6-10 part, urea 3-6 part, urotropine 2-4 part, waste or used plastics 7-11 part, talcum powder 6-8 part, titanic acid ester 6-10 part, hexamethyldisilazane 4-11 part, anti-oxidant DLTP 1-4 part, compounded lubricant 3-6 part, wood powder 4-7 part, mould inhibitor 1-3 part, Zinic stearas 8-11 part, iron oxide red 4-9 part, carbon black 3-8 part, chlorinatedpolyethylene 6-10 part, softening agent 2-5 part, maleic anhydride 4-11 part.

Claims (1)

1. a plastic-wood material, is characterized in that: it is made up of the raw material of following parts by weight:

Neutralized verdigris 6-10 part, urea 3-6 part, urotropine 2-4 part, waste or used plastics 7-11 part, talcum powder 6-8 part, titanic acid ester 6-10 part, hexamethyldisilazane 4-11 part, anti-oxidant DLTP 1-4 part, compounded lubricant 3-6 part, wood powder 4-7 part, mould inhibitor 1-3 part, Zinic stearas 8-11 part, iron oxide red 4-9 part, carbon black 3-8 part, chlorinatedpolyethylene 6-10 part, softening agent 2-5 part, maleic anhydride 4-11 part.