CN104790121B - A kind of multifunctional non-woven fabric and production technology - Google Patents
A kind of multifunctional non-woven fabric and production technology Download PDFInfo
- Publication number
- CN104790121B CN104790121B CN201510153304.6A CN201510153304A CN104790121B CN 104790121 B CN104790121 B CN 104790121B CN 201510153304 A CN201510153304 A CN 201510153304A CN 104790121 B CN104790121 B CN 104790121B
- Authority
- CN
- China
- Prior art keywords
- fiber
- woven fabric
- parts
- terylene
- multifunctional non
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of multifunctional non-woven fabric and production technology, including multifunctional non-woven fabric fiber, a diameter of 26.2~30 μm of single fiber in the multifunctional non-woven fabric fiber, the fiber number of the multifunctional non-woven fabric fiber is 311~331dtex, the multifunctional non-woven fabric fiber is by Pearl Cellulose Polyblend Fiber, hygroscopic, perspiratory and antibacterial terylene or nylon fibre and principal fiber composition, nano-glass pearl powder is added in fiber in viscose rayon spinning Pearl Cellulose Polyblend Fiber is made, inorganic antiseptic is added in fiber in moisture absorption sweat-releasing terylene or nylon fibre spinning hygroscopic, perspiratory and antibacterial terylene or nylon fibre is made, compared with prior art, the present invention has anti-ultraviolet function；Antibacterial functions；Far infrared emission function；Moisture absorption sweat discharging functions, can be widely applied for hygiene article sector or other fields such as skin-material, the mask carriers of disposable adsorption object of top grade.
Description
【Technical field】
The present invention relates to the technical field of cloth, the technical field of particularly a kind of multifunctional non-woven fabric and production technology.
【Background technology】
Non-woven fabrics is widely used in the hygiene article sectors such as the skin-material of disposable adsorption object, mask carriers or other
Association area.But its functional embodiment, mainly with chemical agent, such as to be sterilized, the function such as antibacterial, or addition phase
Physical material is closed, certain simple function is obtained.The features of the present invention, is not use chemical agent or additive, with different things
Reason material is mixed, so as to obtain a kind of multi-functional non-woven fabrics, is possessed：Antibacterial functions, moisture absorption sweat discharging functions, far infrared transmitting
Function, and anti-ultraviolet function.Technical process is simple, and manufacturing cost is low, mixes a variety of functions, because it is physical work(
Can, can't be washed off, the excitant of no chemical agent, can be widely applied to the high-grade demand part of these appropriate arts.
【The content of the invention】
The purpose of the present invention is exactly to solve the problems of the prior art, proposes a kind of multifunctional non-woven fabric and production technology,
There can be anti-ultraviolet function；Antibacterial functions；Far infrared emission function；Moisture absorption sweat discharging functions, can be widely applied for height
Hygiene article sector or other fields such as skin-material, the mask carriers of disposable adsorption object of shelves.
To achieve the above object, the present invention proposes a kind of multifunctional non-woven fabric, including multifunctional non-woven fabric fiber, described
Single fiber in a diameter of 26.2~30 μm of single fiber, the multifunctional non-woven fabric fiber in multifunctional non-woven fabric fiber
A diameter of 26.2~30 μm, the fiber number of the multifunctional non-woven fabric fiber is 311~331dtex, and the multifunctional non-woven fabric is fine
Dimension is made up of Pearl Cellulose Polyblend Fiber, hygroscopic, perspiratory and antibacterial terylene or nylon fibre and principal fiber.
Preferably, a diameter of 28 μm of single fiber in the multifunctional non-woven fabric fiber, the multifunctional non-woven fabric
The fiber number of fiber is 322dtex.
To achieve the above object, the invention also provides a kind of multifunctional non-woven fabric production technology, it is characterised in that：Including
Following steps：
(a) Raw material processing：Nano-glass pearl powder is added in fiber in viscose rayon spinning pearl blended fiber is made
The quality proportioning of cellulose fiber, Nano pearl powder and viscose rayon is：3-7 parts of Nano pearl powder, 97-93 parts of viscose rayon；By nothing
Machine antiseptic is added in moisture absorption sweat-releasing terylene or nylon fibre spinning is made hygroscopic, perspiratory and antibacterial terylene or polyamide fibre fibre in fiber
Tie up, the quality proportioning of inorganic antiseptic and moisture absorption sweat-releasing terylene or nylon fibre is：1.5-3 parts of inorganic antiseptic, moisture absorbing and sweat releasing
98.5-97 parts of terylene or nylon fibre；
(b) Pearl Cellulose Polyblend Fiber, hygroscopic, perspiratory and antibacterial terylene or nylon fibre and principal fiber are mixed many
Functional non-woven fabric fiber, raw material mass mixture ratio is：Pearl Cellulose Polyblend Fiber：13~17 parts, hygroscopic, perspiratory and antibacterial terylene or
Nylon fibre：23~27 parts, principal fiber：55~65 parts；
(c) multifunctional non-woven fabric fiber is subjected to shredding combing and forms non-woven fabrics fiber net；
(d) acupuncture is carried out to folding web, the syringe needle of pricker used is to have hangnail on cone, syringe needle, and pricker is fixed
On needle plate；Pricker density be 6500~7000 every square metre, puncture frequency be 150~190 times per minute, obtain acupuncture without
Spin cloth；
(e) needle punched non-woven fabrics are subjected to thermal finalization under 201~220 degrees Celsius.
Preferably, the quality proportioning of the Nano pearl powder and viscose rayon in the step (a) is：Nano pearl powder 5
Part, 95 parts of viscose rayon.
Preferably, the inorganic antiseptic in the step (a) includes silver, copper and zinc oxide, inorganic antiseptic and moisture absorption
The quality proportioning of sweat-releasing terylene or nylon fibre is：98 parts of 2 parts of inorganic antiseptic, moisture absorption sweat-releasing terylene or nylon fibre.
Preferably, the principal fiber in the step (b) includes cotton fiber and nylon.
Preferably, the principal fiber in the step (b) includes cotton fiber and acrylic fiber.
Preferably, the raw material mass mixture ratio in the step (b) is：Pearl Cellulose Polyblend Fiber：14 parts, moisture absorption row
Sweat antibacterial dacron or nylon fibre：25 parts, principal fiber：58 parts.
Preferably, the pricker density in the step (d) is 6800 every square metre, it is per minute 180 to puncture frequency
It is secondary, obtain needle punched non-woven fabrics.
Preferably, in the step (e), gained grid non-woven fabrics is carried out into thermal finalization at 200 degrees celsius.
Beneficial effects of the present invention：The present invention passes through Pearl Cellulose Polyblend Fiber and hygroscopic, perspiratory and antibacterial terylene or polyamide fibre
The combination application of fiber, with anti-ultraviolet function；Antibacterial functions；Far infrared emission function；Moisture absorption sweat discharging functions, Neng Gouguang
It is general to be applied to hygiene article sector or other fields such as high-grade skin-material, the mask carriers of disposable adsorption object.
【Embodiment】
It is single in a kind of multifunctional non-woven fabric of the present invention, including multifunctional non-woven fabric fiber, the multifunctional non-woven fabric fiber
A diameter of 26.2~30 μm of single fiber, institute in a diameter of 26.2~30 μm of root fiber, the multifunctional non-woven fabric fiber
The fiber number for stating multifunctional non-woven fabric fiber is 311~331dtex, and the multifunctional non-woven fabric fiber is fine by pearl blended fiber element
Single fiber is straight in dimension, hygroscopic, perspiratory and antibacterial terylene or nylon fibre and principal fiber composition, the multifunctional non-woven fabric fiber
Footpath is 28 μm, and the fiber number of the multifunctional non-woven fabric fiber is 322dtex.
A kind of multifunctional non-woven fabric production technology, it is characterised in that：Comprise the following steps：
(a) Raw material processing：Nano-glass pearl powder is added in fiber in viscose rayon spinning pearl blended fiber is made
The quality proportioning of cellulose fiber, Nano pearl powder and viscose rayon is：3-7 parts of Nano pearl powder, 97-93 parts of viscose rayon；By nothing
Machine antiseptic is added in moisture absorption sweat-releasing terylene or nylon fibre spinning is made hygroscopic, perspiratory and antibacterial terylene or polyamide fibre fibre in fiber
Tie up, the quality proportioning of inorganic antiseptic and moisture absorption sweat-releasing terylene or nylon fibre is：1.5-3 parts of inorganic antiseptic, moisture absorbing and sweat releasing
98.5-97 parts of terylene or nylon fibre；
(b) Pearl Cellulose Polyblend Fiber, hygroscopic, perspiratory and antibacterial terylene or nylon fibre and principal fiber are mixed many
Functional non-woven fabric fiber, raw material mass mixture ratio is：Pearl Cellulose Polyblend Fiber：13~17 parts, hygroscopic, perspiratory and antibacterial terylene or
Nylon fibre：23~27 parts, principal fiber：55~65 parts；
(c) multifunctional non-woven fabric fiber is subjected to shredding combing and forms non-woven fabrics fiber net；
(d) acupuncture is carried out to folding web, the syringe needle of pricker used is to have hangnail on cone, syringe needle, and pricker is fixed
On needle plate；Pricker density be 6500~7000 every square metre, puncture frequency be 150~190 times per minute, obtain acupuncture without
Spin cloth；
(e) needle punched non-woven fabrics are subjected to thermal finalization under 201~220 degrees Celsius.
The quality proportioning of Nano pearl powder and viscose rayon in the step (a) is：5 parts of Nano pearl powder, viscose glue is fine
95 parts of dimension；Inorganic antiseptic in the step (a) includes silver, copper and zinc oxide, inorganic antiseptic and moisture absorption sweat-releasing terylene or
The quality proportioning of nylon fibre is：98 parts of 2 parts of inorganic antiseptic, moisture absorption sweat-releasing terylene or nylon fibre；In the step (b)
Principal fiber includes cotton fiber and nylon；Principal fiber in the step (b) includes cotton fiber and acrylic fiber；The step (b)
In raw material mass mixture ratio be：Pearl Cellulose Polyblend Fiber：14 parts, hygroscopic, perspiratory and antibacterial terylene or nylon fibre：25 parts, master
Fiber：58 parts；Pricker density in the step (d) is 6800 every square metre, and it is 180 times per minute to puncture frequency, is obtained
Needle punched non-woven fabrics；In the step (e), gained grid non-woven fabrics is subjected to thermal finalization at 200 degrees celsius.
A kind of multifunctional non-woven fabric of the present invention and production technology, pass through Pearl Cellulose Polyblend Fiber and hygroscopic, perspiratory and antibacterial
The combination application of terylene or nylon fibre, with anti-ultraviolet function；Antibacterial functions；Far infrared emission function；Moisture absorbing and sweat releasing
Function, can be widely applied for top grade the hygiene article sector such as skin-material, the mask carriers of disposable adsorption object or its
Its field.
Above-described embodiment is the description of the invention, is not limitation of the invention, it is any to simple transformation of the present invention after
Scheme belong to protection scope of the present invention.
Claims (8)
1. a kind of multifunctional non-woven fabric production technology, it is characterised in that：Comprise the following steps：
(a) Raw material processing：Nano pearl powder is added in fiber in viscose rayon spinning Pearl Cellulose Polyblend Fiber is made,
The quality proportioning of Nano pearl powder and viscose rayon is：3~7 parts of Nano pearl powder, 97~93 parts of viscose rayon；By inorganic antibacterial
Agent adds in fiber in moisture absorption sweat-releasing terylene or nylon fibre spinning and hygroscopic, perspiratory and antibacterial terylene or nylon fibre is made, inorganic
The quality proportioning of antiseptic and moisture absorption sweat-releasing terylene or nylon fibre is：1.5~3 parts of inorganic antiseptic, moisture absorption sweat-releasing terylene or
98.5~97 parts of nylon fibre；
(b) Pearl Cellulose Polyblend Fiber, hygroscopic, perspiratory and antibacterial terylene or nylon fibre and principal fiber are mixed multi-functional
Non-woven fabrics fiber, raw material mass mixture ratio is：Pearl Cellulose Polyblend Fiber：13~17 parts, hygroscopic, perspiratory and antibacterial terylene or polyamide fibre
Fiber：23~27 parts, principal fiber：55~65 parts；
(c) multifunctional non-woven fabric fiber is subjected to shredding combing and forms non-woven fabrics fiber net；
(d) the laggard hand-manipulating of needle of non-woven fabrics fiber net folding is pierced, the syringe needle of pricker used is to have hangnail on cone, syringe needle, thorn
Pin is fixed on needle plate；Pricker density is 6500~7000 every square metre, and it is 150~190 times per minute to puncture frequency, is obtained
Needle punched non-woven fabrics；
(e) needle punched non-woven fabrics are subjected to thermal finalization under 201~220 degrees Celsius.
2. a kind of multifunctional non-woven fabric production technology as claimed in claim 1, it is characterised in that：Receiving in the step (a)
Rice pearl powder and the quality proportioning of viscose rayon are：5 parts of Nano pearl powder, 95 parts of viscose rayon.
3. a kind of multifunctional non-woven fabric production technology as claimed in claim 1, it is characterised in that：Nothing in the step (a)
Machine antiseptic includes silver, copper and zinc oxide, and the quality proportioning of inorganic antiseptic and moisture absorption sweat-releasing terylene or nylon fibre is：It is inorganic
98 parts of 2 parts of antiseptic, moisture absorption sweat-releasing terylene or nylon fibre.
4. a kind of multifunctional non-woven fabric production technology as claimed in claim 1, it is characterised in that：Master in the step (b)
Fiber includes cotton fiber and nylon.
5. a kind of multifunctional non-woven fabric production technology as claimed in claim 1, it is characterised in that：Master in the step (b)
Fiber includes cotton fiber and acrylic fiber.
6. a kind of multifunctional non-woven fabric production technology as claimed in claim 1, it is characterised in that：Original in the step (b)
Expect that quality proportioning is：Pearl Cellulose Polyblend Fiber：14 parts, hygroscopic, perspiratory and antibacterial terylene or nylon fibre：25 parts, principal fiber：
58 parts.
7. a kind of multifunctional non-woven fabric production technology as claimed in claim 1, it is characterised in that：Thorn in the step (d)
Pin density is 6800 every square metre, and it is 180 times per minute to puncture frequency, obtains needle punched non-woven fabrics.
8. a kind of multifunctional non-woven fabric production technology as any one of claim 1 to 7, it is characterised in that：The step
Suddenly in (e), gained needle punched non-woven fabrics are subjected to thermal finalization at 200 degrees celsius.