CN104789168B - Composited aluminum and plastic decking adhesive resin composition - Google Patents
Composited aluminum and plastic decking adhesive resin composition Download PDFInfo
- Publication number
- CN104789168B CN104789168B CN201510183331.8A CN201510183331A CN104789168B CN 104789168 B CN104789168 B CN 104789168B CN 201510183331 A CN201510183331 A CN 201510183331A CN 104789168 B CN104789168 B CN 104789168B
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic decking
- composited aluminum
- resin composition
- adhesive resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The open a kind of composited aluminum and plastic decking adhesive resin composition of the present invention, belongs to resin art.The present invention is by arranging in pairs or groups ethylene acrylic graft, terpene resin, rosin ester, cyanate, BMI, silicon powder, hindered phenol, liquid paraffin and acetic acid, so that the composited aluminum and plastic decking adhesive resin composition prepared reaches to may insure that prepared composited aluminum and plastic decking has good weatherability and persistent purpose.
Description
Technical field
The invention belongs to resin art, particularly relate to a kind of composited aluminum and plastic decking adhesive resin composition.
Background technology
Composited aluminum and plastic decking be with through chemically treated application aluminium sheet as skin-material, be core with vinyon, the composite processed on special aluminium-plastic panel production equipment.The special performance that composited aluminum and plastic decking itself is had, determines its extensive use: it may be used for building exposed wall, curtain wallboard, old building transforming renovation, indoor wall and ceiling finishing, advertising signboard, exhibition bench frame, purification dustproof engineering.Composited aluminum and plastic decking uses the most in a large number, belongs to a kind of new decorative material for building.
Owing to composited aluminum and plastic decking is made up of metal and nonmetal two kinds of distinct materials of character, there is adhesion problem, need to select specific binder resin, just can ensure that prepared composited aluminum and plastic decking has good weatherability and persistency.
Summary of the invention
The present invention provides a kind of composited aluminum and plastic decking adhesive resin composition, and this composited aluminum and plastic decking adhesive resin composition may insure that prepared composited aluminum and plastic decking has good weatherability and persistency.
In order to solve above-mentioned technical problem, the technical solution adopted in the present invention is:
It is made up of the component of following parts by weight:
Ethylene-acrylic acid graft 100 parts, terpene resin 5 parts～10 parts, rosin ester 1 part～5 parts, cyanate 1 part～5 parts, BMI 5 parts～8 parts, silicon powder 1 part～5 parts, hindered phenol 8 parts～15 parts, liquid paraffin 1 part～3 parts and acetic acid 6 parts～10 parts.
In technique scheme, more specifically technical scheme is: ethylene-acrylic acid graft 100 parts, terpene resin 5 parts, rosin ester 1 part, cyanate 3 parts, BMI 8 parts, silicon powder 3 parts, hindered phenol 15 parts, liquid paraffin 1 part and acetic acid 8 parts；
Further, ethylene-acrylic acid graft 100 parts, terpene resin 10 parts, rosin ester 5 parts, cyanate 1 part, BMI 5 parts, silicon powder 1 part, hindered phenol 8 parts, liquid paraffin 2 parts and acetic acid 6 parts；
Further, ethylene-acrylic acid graft 100 parts, terpene resin 8 parts, rosin ester 3 parts, cyanate 5 parts, BMI 6 parts, silicon powder 5 parts, hindered phenol 12 parts, liquid paraffin 3 parts and acetic acid 10 parts.
Owing to using technique scheme, there is advantages that
The present invention is by arranging in pairs or groups ethylene-acrylic acid graft, terpene resin, rosin ester, cyanate, BMI, silicon powder, hindered phenol, liquid paraffin and acetic acid, so that the composited aluminum and plastic decking adhesive resin composition prepared reaches to may insure that prepared composited aluminum and plastic decking has good weatherability and persistent purpose.
Detailed description of the invention
Below in conjunction with instantiation, the invention will be further described:
Embodiment 1
This composited aluminum and plastic decking adhesive resin composition is made up of following components:
Ethylene-acrylic acid graft 1000g, terpene resin 50g, rosin ester 10g, cyanate 30g, BMI 80g, silicon powder 30g, hindered phenol 150g, liquid paraffin 10g and acetic acid 80g.
Its preparation method is: said components is stirred at 150 DEG C～155 DEG C, to obtain final product.
The present embodiment composited aluminum and plastic decking adhesive resin composition reaches 7.5N/mm to the adhesive strength of metallic aluminium, when it is used for preparing composited aluminum and plastic decking, it can be ensured that prepared composited aluminum and plastic decking has good weatherability and persistency.
Embodiment 2
This composited aluminum and plastic decking adhesive resin composition is made up of following components:
Ethylene-acrylic acid graft 1000g, terpene resin 100g, rosin ester 50g, cyanate 10g, BMI 50g, silicon powder 10g, hindered phenol 80g, liquid paraffin 20g and acetic acid 60g.
Its preparation method is: said components is stirred at 150 DEG C～155 DEG C, to obtain final product.
The present embodiment composited aluminum and plastic decking adhesive resin composition reaches 7.6N/mm to the adhesive strength of metallic aluminium, when it is used for preparing composited aluminum and plastic decking, it can be ensured that prepared composited aluminum and plastic decking has good weatherability and persistency.
Embodiment 3
This composited aluminum and plastic decking adhesive resin composition is made up of following components:
Ethylene-acrylic acid graft 1000g, terpene resin 80g, rosin ester 30g, cyanate 50g, BMI 60g, silicon powder 50g, hindered phenol 120g, liquid paraffin 30g and acetic acid 100g.
Its preparation method is: said components is stirred at 150 DEG C～155 DEG C, to obtain final product.
The present embodiment composited aluminum and plastic decking adhesive resin composition reaches 8.0N/mm to the adhesive strength of metallic aluminium, when it is used for preparing composited aluminum and plastic decking, it can be ensured that prepared composited aluminum and plastic decking has good weatherability and persistency.
Claims (4)
1. a composited aluminum and plastic decking adhesive resin composition, it is characterised in that be made up of the component of following parts by weight:
Ethylene-acrylic acid graft 100 parts, terpene resin 5 parts～10 parts, rosin ester 1 part～5 parts, cyanate 1 part～5 parts, BMI 5 parts～8 parts, silicon powder 1 part～5 parts, hindered phenol 8 parts～15 parts, liquid paraffin 1 part～3 parts and acetic acid 6 parts～10 parts.
Composited aluminum and plastic decking adhesive resin composition the most according to claim 1, it is characterised in that: ethylene-acrylic acid graft 100 parts, terpene resin 5 parts, rosin ester 1 part, cyanate 3 parts, BMI 8 parts, silicon powder 3 parts, hindered phenol 15 parts, liquid paraffin 1 part and acetic acid 8 parts.
Composited aluminum and plastic decking adhesive resin composition the most according to claim 1, it is characterised in that: ethylene-acrylic acid graft 100 parts, terpene resin 10 parts, rosin ester 5 parts, cyanate 1 part, BMI 5 parts, silicon powder 1 part, hindered phenol 8 parts, liquid paraffin 2 parts and acetic acid 6 parts.
Composited aluminum and plastic decking adhesive resin composition the most according to claim 1, it is characterised in that: ethylene-acrylic acid graft 100 parts, terpene resin 8 parts, rosin ester 3 parts, cyanate 5 parts, BMI 6 parts, silicon powder 5 parts, hindered phenol 12 parts, liquid paraffin 3 parts and acetic acid 10 parts.