CN104786318A - Mildew-proof modification treatment agent of wood - Google Patents

Abstract

A mildew-proof modification treatment agent of wood is prepared from the following raw materials in parts by weight: 6-9 parts of silicon dioxide particle, 3-9 parts of polyethylene glycol, 4-9 parts of 60% boric acid solution, 3-8 parts of trichloroisocyanuric acid, 6-10 parts of 50% silicone acrylic emulsion, 3-11 parts of 5-aminolevulinic acid, 6-8 parts of furfuryl alcohol, 7-9 parts of cashew nut oil, 3-7 parts of phytic acid, 4-10 parts of xylitol, 3-10 parts of ethoxyl urea, 4-7 parts of lithium silicate, 1-5 parts of sodium oleate and 4-6 parts of eugenol. The mildew-proof modification treatment agent of the wood has the benefits that the treatment agent has a good mildew-proof effect, improves overall performance of the wood and prolongs the service life at the same time.

Description

The agent of a kind of wood mould modification

Technical field

The present invention relates to the agent of a kind of wood mould modification.

Background technology

Timber and goods thereof are widely used in interior decoration, Furniture manufacture, building construction and extraneous adornment, but the forest reserves that China can fell use are very limited.Based on domestic, make full use of existing resource, walk Sustainable Development Road.Modifier can improve or change physics or the chemical process processing method of the physics of timber, mechanics, chemical property and structural feature.Its objective is the natural decay resistance, acid resistance, alkali resistance, anti-flammability, mechanical strength and the dimensional stability that improve timber.Therefore, modifier is widely applied.

Summary of the invention

For the deficiencies in the prior art, the problem to be solved in the present invention is, provides the agent of a kind of wood mould modification, has good anti-mold effect, improve the overall performance of timber simultaneously, improve service life.

For solving prior art problem, technical scheme provided by the invention is, the agent of a kind of wood mould modification, and it is made up of the raw material of following parts by weight:

Silicon dioxide granule 6-9 part, polyethylene glycol 3-9 part, 60% BAS 4-9 part, sym-closene 3-8 part, Silicone acrylic emulsion 6-10 part of 50%, 5-ALA 3-11 part, furfuryl alcohol 6-8 part, cashew nut oil 7-9 part, phytic acid 3-7 part, xylitol 4-10 part, ethoxy urea 3-10 part, lithium metasilicate 4-7 part, enuatrol 1-5 part, Eugenol 4-6 part.

The invention has the beneficial effects as follows: wood mould modification of the present invention agent, has good anti-mold effect, improves the overall performance of timber simultaneously, improves service life.

Detailed description of the invention

embodiment 1

The agent of a kind of wood mould modification, it is made up of the raw material of following parts by weight:

Silicon dioxide granule 6-9 part, polyethylene glycol 3-9 part, 60% BAS 4-9 part, sym-closene 3-8 part, Silicone acrylic emulsion 6-10 part of 50%, 5-ALA 3-11 part, furfuryl alcohol 6-8 part, cashew nut oil 7-9 part, phytic acid 3-7 part, xylitol 4-10 part, ethoxy urea 3-10 part, lithium metasilicate 4-7 part, enuatrol 1-5 part, Eugenol 4-6 part.

Claims (1)

1. a wood mould modification agent, is characterized in that: it is made up of the raw material of following parts by weight:

Silicon dioxide granule 6-9 part, polyethylene glycol 3-9 part, 60% BAS 4-9 part, sym-closene 3-8 part, Silicone acrylic emulsion 6-10 part of 50%, 5-ALA 3-11 part, furfuryl alcohol 6-8 part, cashew nut oil 7-9 part, phytic acid 3-7 part, xylitol 4-10 part, ethoxy urea 3-10 part, lithium metasilicate 4-7 part, enuatrol 1-5 part, Eugenol 4-6 part.