CN104761247A - Production method of polished tiles having jade stone texture - Google Patents
Production method of polished tiles having jade stone texture Download PDFInfo
- Publication number
- CN104761247A CN104761247A CN201510110731.6A CN201510110731A CN104761247A CN 104761247 A CN104761247 A CN 104761247A CN 201510110731 A CN201510110731 A CN 201510110731A CN 104761247 A CN104761247 A CN 104761247A
- Authority
- CN
- China
- Prior art keywords
- content
- powder
- production method
- jade
- super
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
A production method of polished tiles having a jade stone texture, wherein the polished tiles is prepared from following raw materials: high-whiteness albite powder being 5-10 wt% in the content of sodium, feldspar, clay, talcum being 28-32 wt% in the content of MgO, anorthite being 2.0-4.0 wt% in the content of CaO and bone ash being 45-50 wt% in the content of CaO. The production method includes following steps: powder producing, blank body moulding, high-temperature sintering and polishing. During the blank body moulding, firstly more than more than one stacks of a granular powder material is randomly arranged on a material arranging trolley in the form of a large-granular materials, and then a layer of mixed powder material is arranged at the periphery of the granular powder material. The powder materials are press-compacted by a press roller and then are cracked naturally, wherein the cracks are filled with a super-transparent jade material. Finally the prepared materials are fed into a die cavity for being compression-moulded. Compared with a method in the prior art, the production method is free of addition of a reinforcing agent and a whitening agent (such as zirconium silicate) which are harmful to environment. The polished tile has a super-transparent sense just like jade stone, is fine-and-smooth and has a layered sense, is clear in bottom pattern, and has such an excellent jade-like texture.
Description
Technical field
The present invention relates to a kind of ceramic tile and production method thereof.
Background technology
The micro powder polished brick of existing market is all utilize Na2O, K2O, MgO three-part system structure, add certain zirconium silicate to make, whiteness is generally at about 40 degree, transparence is poor, texture is inadequate, do not reach the texture of beautiful matter stone material, moreover the toughener added, whitening agent (as zirconium silicate) are hostile environments.
Summary of the invention
Goal of the invention of the present invention is to provide a kind of toughener without the need to adding hostile environment, whitening agent (as zirconium silicate), it is clear to have that beautiful matter stone material surpasses transparence, exquisiteness has levels, the end is spent, the production method with the polished tile of beautiful matter stone texture of good jade sense.
The present invention realizes like this, comprise sodium content at the high white sodium stone flour of 5-10wt%, feldspar, clay, content of MgO is at the talcum of 28-32wt%, CaO content at the calcium stone of 2.0-4.0wt% and CaO content at the bone ash of 45-50wt% through powder manufacture, blank forming, high-temperature firing, polishing forms, during blank forming, first with the form of macrobead powder random particle powder laying more than a pile on charge car, then one deck mixed powder is laid toward particle powder periphery, through roller compaction, its season crack is made again with instrument, then in crackle, fill super jade material, finally send into die cavity compression moulding, wherein
Macrobead material component content is (unit is: weight part):
A, material usage:
B, chemical composition:
The component content of mixed powder is (unit is: weight part):
A, material usage:
B, chemical composition:
The component content of super jade material is (unit is: weight part):
A, material usage:
B, chemical composition:
The present invention adopts the super jade material of the formula of high calcium content to embody the super sense of jade, the stereoscopic sensation of beautiful matter stone material is embodied by macrobead powder, produced like this ceramic tile is just provided with natural beautiful matter stone material stereoscopic sensation, super sense, well arranged, the natural beautiful matter stone material features such as clear are spent at the end, adopt content of MgO at the talcum of 28-32wt%, CaO content is in the calcium stone of 2.0-4.0wt% and the CaO content high whiteness at 45-50wt% bone ash, transmittance reaches the formula of 80-90%, both improved ceramic tile colouring after gorgeous, transparence, turn avoid simultaneously and use zirconium silicate to brighten the brought harm to environment.Suitable potassium felspar sand is introduced in formula, and fully natural green
Ceramics reinforcing agent-the wilkinite (clay) of environmental protection, overcomes the firing range due to sodium, formula that calcium contents is high
Narrow, in sintering procedure, easily there is distortion and defect; In compression moulding, damaged low in course of conveying, burn till oxidation well, be conducive to expanding firing range, thus effectively control the beautiful texture of pin hole, fusion hole and raising, and can fire by common brick output.
The present invention compared with the prior art, there is the toughener without the need to adding hostile environment, whitening agent (as zirconium silicate), there is natural beautiful matter stone material stereoscopic sensation, that super sense, exquisiteness have levels, particle clearly demarcated, the end is spent is clear, the advantage such as good beautiful sense.
Embodiment:
Now in conjunction with example, the present invention is described in further detail:
The present invention realizes like this, comprise sodium content at the high white sodium stone flour of 5-10wt%, feldspar, clay, content of MgO is at the talcum of 28-32wt%, CaO content at the calcium stone of 2.0-4.0wt% and CaO content at the bone ash of 45-50wt% through powder manufacture, blank forming, high-temperature firing, polishing forms, during blank forming, first with the form of macrobead powder random particle powder laying more than a pile on charge car, then one deck mixed powder is laid toward particle powder periphery, through roller compaction, its season crack is made again with instrument, then in crackle, fill super jade material, finally send into die cavity compression moulding, wherein
Macrobead material component content is (unit is: weight part):
A, material usage:
B, chemical composition:
The component content of mixed powder is (unit is: weight part):
A, material usage:
B, chemical composition:
The component content of super jade material is (unit is: weight part):
A, material usage:
B, chemical composition:
Here in order to overcome slurry fluidity difference, causing the problem that grinding efficiency is low, being added with in formula and subtracting jelly.
The feature of above-mentioned enforcement is:
On the basis of stone polishing brick space of a whole page effect, be bumped into super jade material (transmittance 80-90%) having very much sense.Its this brick is made to highlight closely the fine and smooth texture of super crackle of " Khotan jade ".This brick is fine and smooth in beautiful well arranged, and the end is spent clear, and super material transmittance is high, naturally true to nature, and be of moderate size very strong stereoscopic sensation.
Claims (2)
1. one kind has the production method of the polished tile of beautiful matter stone texture, it is characterized in that comprising sodium content at the high white sodium stone flour of 5-10wt%, feldspar, clay, content of MgO is at the talcum of 28-32wt%, CaO content at the calcium stone of 2.0-4.0wt% and CaO content at the bone ash of 45-50wt% through powder manufacture, blank forming, high-temperature firing, polishing forms, during blank forming, first with the form of macrobead powder random particle powder laying more than a pile on charge car, then one deck mixed powder is laid toward particle powder periphery, through roller compaction, make its season crack again, then in crackle, fill super jade material, finally send into die cavity compression moulding, wherein
Macrobead material component content is (unit is: weight part):
A, material usage:
B, chemical composition:
The component content of mixed powder is (unit is: weight part):
A, material usage:
B, chemical composition:
The component content of super jade material is (unit is: weight part):
A, material usage:
B, chemical composition:
。
2. the production method with the polished tile of beautiful matter stone texture according to claim 1, is characterized in that being added with in formula subtracting jelly.