CN104761237A - A shale light solid brick - Google Patents
A shale light solid brick Download PDFInfo
- Publication number
- CN104761237A CN104761237A CN201510103804.9A CN201510103804A CN104761237A CN 104761237 A CN104761237 A CN 104761237A CN 201510103804 A CN201510103804 A CN 201510103804A CN 104761237 A CN104761237 A CN 104761237A
- Authority
- CN
- China
- Prior art keywords
- parts
- shale
- solid brick
- brick
- light solid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A shale light solid brick is disclosed. The solid brick is prepared from following raw materials by weight: 35-45 parts of shale, 25-30 parts of gangue, 10-14 parts of straw, 2-4 parts of silica, 1-3 parts of magnesium oxide, 4-6 parts of ferrous ferric oxide, 5-7 parts of corundum, 3-6 parts of chromic oxide, 2-5 parts of silicon carbide and 5-8 parts of titanium dioxide. The beneficial effects of the solid brick are that: after being fired, the solid brick can be effectively resistant to heat and corrosion, fracture phenomena are prevented, and heat resistance is improved by 2-3 times.
Description
Technical field
The present invention relates to the light body solid brick of a kind of shale.
Background technology
Shale brick utilizes shale and coal gangue to carry out the fragment of brick of high-temperature firing for raw material.Existing shale brick is heat-resisting, corrosion-resistant mostly, easily produces phenomenon of rupture of turning.
Summary of the invention
Object of the present invention is exactly for above-mentioned defect of the prior art, provides the light body solid brick of a kind of shale.
To achieve these goals, technical scheme provided by the invention is: the light body solid brick of a kind of shale, is prepared by the following raw material according to parts by weight: shale 35-45 part, coal gangue 25-30 part, stalk 10-14 part, silicon-dioxide 2-4 part, magnesium oxide 1-3 part, Z 250 4-6 part, corundum 5-7 part, chromium sesquioxide 3-6 part, silicon carbide 2-5 part, titanium dioxide 5-8 part.
Beneficial effect of the present invention is: the light body solid brick of a kind of shale provided by the invention, can be effectively heat-resisting, corrosion-resistant after sintering, prevents the generation of phenomenon of rupture, and thermotolerance improves 2-3 doubly.
Embodiment
embodiment 1:
The light body solid brick of a kind of shale is prepared by the following raw material according to parts by weight: shale 35-45 part, coal gangue 25-30 part, stalk 10-14 part, silicon-dioxide 2-4 part, magnesium oxide 1-3 part, Z 250 4-6 part, corundum 5-7 part, chromium sesquioxide 3-6 part, silicon carbide 2-5 part, titanium dioxide 5-8 part.
Last it is noted that the foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to previous embodiment to invention has been detailed description, for a person skilled in the art, it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (1)
1. the light body solid brick of shale, it is characterized in that, be prepared by the following raw material according to parts by weight: shale 35-45 part, coal gangue 25-30 part, stalk 10-14 part, silicon-dioxide 2-4 part, magnesium oxide 1-3 part, Z 250 4-6 part, corundum 5-7 part, chromium sesquioxide 3-6 part, silicon carbide 2-5 part, titanium dioxide 5-8 part.