CN104761223B - A kind of ardealite base material jade slabstone and preparation method thereof - Google Patents
A kind of ardealite base material jade slabstone and preparation method thereof Download PDFInfo
- Publication number
- CN104761223B CN104761223B CN201510104767.3A CN201510104767A CN104761223B CN 104761223 B CN104761223 B CN 104761223B CN 201510104767 A CN201510104767 A CN 201510104767A CN 104761223 B CN104761223 B CN 104761223B
- Authority
- CN
- China
- Prior art keywords
- ardealite
- base material
- temperature
- jade
- slabstone
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to chemical building material technical field, especially a kind of ardealite base material jade slabstone and preparation method thereof, pass through ardealite, sand, cement, flyash, glass fibre, the design of the appropriate match ratio of the raw materials such as jade stone coating, make ardealite, flyash the like waste can be at glass fibre, cement, activate in the presence of sand etc., enhance the activity of discarded object, especially reduce the relative amount of soluble impurity in ardealite, promote ardealite more excellent with the solidifiability of cement, improve intensity and the quality of product, reduce the radioactivity of product, strengthen corrosion resistance, reduce the production cost of jade slabstone product.
Description
Technical field
The present invention relates to chemical building material technical field, especially a kind of ardealite base material jade slabstone and preparation method thereof.
Background technology
Continuous expansion with ardealite volume of cargo in storage, there is numerous studies person that ardealite is applied to construction material manufacture technology field, especially ardealite is used for construction and decoration field progressively opened up, and then ardealite is more wide in the application prospect of finishing building field.
But, at present ardealite is mainly ardealite as additive as what building field was applied, is added on the making field such as cement, coating more, be exactly additionally that ardealite is used for being incubated the manufacture technology field of fragment of brick, insulation blocks；These application are all some advantages utilizing ardealite itself to exist, and the product itself making such as ardealite has lightweight and preferably heat-insulating property.Can be also relatively fewer directly as the production in finishing field by ardealite.Meanwhile, finishing material is copied current also in being promoted and applying progressively, especially the imitated more tradition and common of imitation wood, parian, artificial granite etc. decorating and renovating material；But ardealite is carried out the imitated also relatively fewer of finishing material as base material.And traditional imitated process is all at substrate surface by spray painting, then after maintenance is carried out to it, obtained；And these technology are all difficult to substantial amounts of for the ardealite building field that is applied to, cause storing up in a large number of ardealite, and then cause serious pollution to environment.Simultaneously, imitated for ardealite application building materials field is also faced with more severe technical barrier also do not solved by prior art, the content and the sodium content that are exactly i.e. soluble impurity in ardealite are higher, and soluble impurity content is higher, the solidifiability that will cause ardealite is affected, sodium content is too high will cause ardealite substrate surface generation efflorescence, in turn results in coming off of top layer, and then affects imitation effect.
Based on this, ardealite, through long-term exploration and research, is made jade slabstone technical field as base material and provides a kind of the newly selected by this researcher.
Content of the invention
In order to solve above-mentioned technical problem present in prior art, the present invention provides a kind of ardealite base material jade slabstone, the imitative jade effect of this sheet material is more excellent, have bending and compressive strength height, radioactivity is low, resistance to corrosion is strong, weatherability is strong, heat insulation effect is more excellent, and discarded object saturation is relatively big, and top layer is not susceptible to powder phenomenon-tion.
And, the present invention also provides the preparation method of a kind of ardealite base material jade slabstone, the performance of ardealite can be strengthened completely by the activity maximization of ardealite, improves the quality of ardealite, strengthen the intensity of ardealite product, reduce ardealite the like waste and produce the radioactivity of building products, reduce the content of soluble impurity, improve the solidifiability of ardealite, avoid top layer powder phenomenon-tion to produce, improve the quality of product.
It is achieved particular by techniques below scheme:
A kind of ardealite base material jade slabstone, its material composition, is ardealite 30-40 part, sand 10-20 part, cement 1-3 part, flyash 1-5 part, glass fibre 1-3 part, jade stone coating 10-20 part in parts by weight.
Described material composition, is ardealite 35 parts, 15 parts of sand, cement 2 parts, 3 parts of flyash, 2 parts of glass fibre, jade stone coating 15 parts in parts by weight.
nullThe described sodium content in ardealite is≤0.9%，Its preparation method be by ardealite with water according to (1-3): after (2-4) mixes，Mixing speed is used to be 100-200r/min stir process 10-20min again，And to be warmed up to temperature be 50-60 DEG C，After end to be mixed，Its constant temperature standing is processed 1-2h，It is added thereto to the quick lime of 0.3-0.5 times of ardealite consumption again，And after using mixing speed to be 50-60r/min stir process 30-60min，Standing processes 3-5h，It is added thereto to aluminum oxide again，Addition is made a living 1-2 times of lime consumption，And use mixing speed to be 30-50r/min stir process，And take to add while stirring calcirm-fluoride，The addition of calcirm-fluoride is and aluminum oxide equivalent，After continuously stirred process 20-30min，Adjusting its temperature again is 30-50 DEG C，Still aging process 1-3h，?.
Soluble impurity content≤6% in described ardealite.
Described sand is 80-130 mesh.
The intensity of described cement is 42.5-52.5RMPa.
nullDescribed jade stone coating is for by titanium dioxide 1.5-1.7 part in parts by weight、Polyvinyl alcohol 0.08-0.15 part、Ethanol 0.1-0.7 part、Clear water 3-3.5 part，Its preparation method is to put into clear water to carry out hyperthermic treatment in heating bath，When temperature reaches 40 DEG C，It is added thereto to polyvinyl alcohol again，And maintain programming rate constant，And use mixing speed to be 120-150r/min stir process，When temperature is warmed up to 88-92 DEG C，Stop heating up，Maintain temperature constant state stirring，Polyvinyl alcohol is all dissolved，Stop again heating，When making temperature be reduced to 80 DEG C，Titanium dioxide is added thereto，And take the mode stirring while adding，When continuing stirring until temperature and be reduced to 40 DEG C，Stop stir process，After carrying out filtration treatment with gauze again，Obtain filtrate，And after filtrate is mixed with ethanol，Obtain jade stone coating.
The a length of 0.1-2mm of described glass fibre.
The preparation method of this ardealite base material jade slabstone, comprises the following steps:
(1) prepared by base material: by ardealite, sand, cement, flyash, glass fibre is sequentially added in mixing channel, the clarification limewash of the 10-15% of total inventory is sprayed again in mixing channel, mixing speed is used to be 80-90r/min stir process 3-5h again, after again the temperature in mixing channel being warming up to 50-60 DEG C, constant temperature still aging process 10-12h, obtain mixing slurry, and after being placed in mixing slurry in roller and carrying out rolling 10-20min, it is cast in jade slabstone mould again, and the mould by good for cast mixing slurry moves on shake table, vibration frequency is used to be 70-90Hz vibration processing 10-30min, and move it to the environment that temperature is 40-50 DEG C is placed 20-30min again, again by mould removal, just base can be obtained；Again first base being placed in vapor (steam) temperature is 40-60 DEG C, and pressure is in the steam-pressure maintaining device of 1.4-1.6MPa, and steam press maintenance processes 40-50s, can obtain semi-finished product base material；
(2) base material polishing: semi-finished product base material uses clarification limewash spray once, the consumption of clarification limewash is 1/10th of semi-finished product substrate weight, after sprinkling completes, it is placed in the environment that temperature is 40-50 DEG C placement 10-30min, it is drawn off using sand papering process again, make smooth surface, finished product base material can be obtained；
(3) scrape the end to spray paint: use jade stone coating first to carry out to finished product base material scraping bottom reason, scraping base thickness degree is 0.1-0.3mm, after the end to be doctored, completes, temperature is used to be 20-30 DEG C of drying and processing 10-20min, spray gun is used to carry out two layers of spraying of jade stone coating again, coating thickness is 1.1-2.3mm, after spraying completes, use varnish sprayed surface 0.3-0.5mm thick again, move it to the drying baker that temperature is 30-40 DEG C again and carry out drying and processing 20-30min, it is drawn off, is positioned in natural environment, ardealite base material jade slabstone can be obtained.
The a diameter of 1-7mm of described spray gun muzzle.
Compared with prior art, the technique effect of the present invention is embodied in:
1. the design by the appropriate match ratio of the raw materials such as ardealite, sand, cement, flyash, glass fibre, jade stone coating, ardealite, flyash the like waste can be activated in the presence of glass fibre, cement, sand etc., enhance the activity of discarded object, especially reduce the relative amount of soluble impurity in ardealite, promote ardealite more excellent with the solidifiability of cement, improve intensity and the quality of product, reduce the radioactivity of product, strengthen corrosion resistance, reduce the production cost of jade slabstone product.
2. by base material in preparation technology prepare, base material polishing, scrape end painting process, various piece in ardealite base material jade slabstone is perfectly combined together, the intensity making ardealite base material is higher, bending and compressive strength is higher, and resistance to corrosion is strong, and radioactivity is relatively low, process in conjunction with follow-up technique, jade stone coating perfectly can be merged with ardealite base material, and then reduce the probability that comes off of jade stone coating, improve the quality of the jade slabstone of ardealite base material；Meanwhile, in preparation technology, sodium content in ardealite is reduced so that ardealite avoids surface and produces the defect that the intensity of the brought product of crystalline substance flower reduces, and improves intensity and the quality of ardealite substrate product.
Furthermore 3., the whole technological process of production is short, and technical parameter is easily controllable, and waste containment amount is higher, reduces the cost of manufacture of jade slabstone product, reduces environmental pollution probability.
Detailed description of the invention
Below in conjunction with specific embodiment, technical scheme is further limited, but claimed scope is not only limited to description.
Embodiment 1
A kind of ardealite base material jade slabstone, its material composition is ardealite 30kg, sand 10kg, cement 1kg, flyash 1kg, glass fibre 1kg, jade stone coating 10kg.
Sodium content in ardealite is 0.9%, its preparation method be ardealite is mixed according to 1:2 with water after, mixing speed is used to be 100r/min stir process 10min again, and to be warmed up to temperature be 50 DEG C, after end to be mixed, its constant temperature standing is processed 1h, it is added thereto to the quick lime of 0.3 times of ardealite consumption again, and after using mixing speed to be 50r/min stir process 30min, standing processes 3h, it is added thereto to aluminum oxide again, addition is made a living 1 times of lime consumption, and use mixing speed to be 30r/min stir process, and take to add while stirring calcirm-fluoride, the addition of calcirm-fluoride is and aluminum oxide equivalent, after continuously stirred process 20min, adjusting its temperature again is 30 DEG C, still aging process 1h, ?.
Soluble impurity content 6% in ardealite.
Sand is 80 mesh.
The intensity of cement is 42.5MPa.
Jade stone coating is for by titanium dioxide 1.5kg in parts by weight, polyvinyl alcohol 0.08kg, ethanol 0.1kg, clear water 3kg, its preparation method is to put into clear water to carry out hyperthermic treatment in heating bath, when temperature reaches 40 DEG C, it is added thereto to polyvinyl alcohol again, and maintain programming rate constant, and use mixing speed to be 120r/min stir process, when temperature is warmed up to 88 DEG C, stop heating up, maintain temperature constant state stirring, polyvinyl alcohol is all dissolved, stop again heating, when making temperature be reduced to 80 DEG C, titanium dioxide is added thereto, and take to stir while adding
Mode, when continuing stirring until temperature and be reduced to 40 DEG C, stop stir process, then after carrying out filtration treatment with gauze, it is thus achieved that filtrate, and after filtrate is mixed with ethanol, it is thus achieved that jade stone coating.
The a length of 0.1mm of glass fibre.
The preparation method of this ardealite base material jade slabstone, comprises the following steps:
(1) prepared by base material: by ardealite, sand, cement, flyash, glass fibre is sequentially added in mixing channel, spray in mixing channel more total inventory 10% clarification limewash, mixing speed is used to be 80r/min stir process 3h again, after again the temperature in mixing channel being warming up to 50 DEG C, constant temperature still aging process 10h, obtain mixing slurry, and after being placed in mixing slurry in roller and carrying out rolling 10min, it is cast in jade slabstone mould again, and the mould by good for cast mixing slurry moves on shake table, vibration frequency is used to be 70Hz vibration processing 10min, and move it to the environment that temperature is 40 DEG C is placed 20min again, again by mould removal, just base can be obtained；It is 40 DEG C that first base is placed in vapor (steam) temperature again, and pressure is in the steam-pressure maintaining device of 1.4MPa, and steam press maintenance processes 40s, can obtain semi-finished product base material；
(2) base material polishing: semi-finished product base material uses clarification limewash spray once, the consumption of clarification limewash is 1/10th of semi-finished product substrate weight, after sprinkling completes, it is placed in the environment that temperature is 40 DEG C placement 10min, it is drawn off using sand papering process again, make smooth surface, finished product base material can be obtained；
(3) scrape the end to spray paint: use jade stone coating first to carry out to finished product base material scraping bottom reason, scraping base thickness degree is 0.1mm, after the end to be doctored, completes, temperature is used to be 20 DEG C of drying and processing 10min, spray gun is used to carry out two layers of spraying of jade stone coating again, coating thickness is 1.1mm, after spraying completes, use varnish sprayed surface 0.3mm thick again, move it to the drying baker that temperature is 30 DEG C again and carry out drying and processing 20min, it is drawn off, is positioned in natural environment, ardealite base material jade slabstone can be obtained.
The a diameter of 1mm of spray gun muzzle.
Embodiment 2
A kind of ardealite base material jade slabstone, its material composition is ardealite 40kg, sand 20kg, cement 3kg, flyash 5kg, glass fibre 3kg, jade stone coating 20kg.
Sodium content in ardealite is 0.1%, its preparation method be ardealite is mixed according to 1:4 with water after, mixing speed is used to be 200r/min stir process 20min again, and to be warmed up to temperature be 60 DEG C, after end to be mixed, its constant temperature standing is processed 2h, it is added thereto to the quick lime of 0.5 times of ardealite consumption again, and after using mixing speed to be 60r/min stir process 60min, standing processes 5h, it is added thereto to aluminum oxide again, addition is made a living 2 times of lime consumption, and use mixing speed to be 50r/min stir process, and take to add while stirring calcirm-fluoride, the addition of calcirm-fluoride is and aluminum oxide equivalent, after continuously stirred process 30min, adjusting its temperature again is 50 DEG C, still aging process 3h, ?.
Soluble impurity content 1% in ardealite.
Sand is 130 mesh.
The intensity of cement is 52.5RMPa.
nullJade stone coating is for by titanium dioxide 1.7kg in parts by weight、Polyvinyl alcohol 0.15kg、Ethanol 0.7kg、Clear water 3.5kg，Its preparation method is to put into clear water to carry out hyperthermic treatment in heating bath，When temperature reaches 40 DEG C，It is added thereto to polyvinyl alcohol again，And maintain programming rate constant，And use mixing speed to be 150r/min stir process，When temperature is warmed up to 92 DEG C，Stop heating up，Maintain temperature constant state stirring，Polyvinyl alcohol is all dissolved，Stop again heating，When making temperature be reduced to 80 DEG C，Titanium dioxide is added thereto，And take the mode stirring while adding，When continuing stirring until temperature and be reduced to 40 DEG C，Stop stir process，After carrying out filtration treatment with gauze again，Obtain filtrate，And after filtrate is mixed with ethanol，Obtain jade stone coating.
The a length of 2mm of glass fibre.
The preparation method of this ardealite base material jade slabstone, comprises the following steps:
(1) prepared by base material: by ardealite, sand, cement, flyash, glass fibre is sequentially added in mixing channel, spray in mixing channel more total inventory 15% clarification limewash, mixing speed is used to be 90r/min stir process 5h again, after again the temperature in mixing channel being warming up to 60 DEG C, constant temperature still aging process 12h, obtain mixing slurry, and after being placed in mixing slurry in roller and carrying out rolling 20min, it is cast in jade slabstone mould again, and the mould by good for cast mixing slurry moves on shake table, vibration frequency is used to be 90Hz vibration processing 30min, and move it to the environment that temperature is 50 DEG C is placed 30min again, again by mould removal, just base can be obtained；It is 60 DEG C that first base is placed in vapor (steam) temperature again, and pressure is in the steam-pressure maintaining device of 1.6MPa, and steam press maintenance processes 50s, can obtain semi-finished product base material；
(2) base material polishing: semi-finished product base material uses clarification limewash spray once, the consumption of clarification limewash is 1/10th of semi-finished product substrate weight, after sprinkling completes, it is placed in the environment that temperature is 50 DEG C placement 30min, it is drawn off using sand papering process again, make smooth surface, finished product base material can be obtained；
(3) scrape the end to spray paint: use jade stone coating first to carry out to finished product base material scraping bottom reason, scraping base thickness degree is 0.3mm, after the end to be doctored, completes, temperature is used to be 30 DEG C of drying and processing 20min, spray gun is used to carry out two layers of spraying of jade stone coating again, coating thickness is 2.3mm, after spraying completes, use varnish sprayed surface 0.5mm thick again, move it to the drying baker that temperature is 40 DEG C again and carry out drying and processing 30min, it is drawn off, is positioned in natural environment, ardealite base material jade slabstone can be obtained.
The a diameter of 7mm of spray gun muzzle.
Embodiment 3
A kind of ardealite base material jade slabstone, its material composition is ardealite 35kg, sand 15kg, cement 2kg, flyash 3kg, glass fibre 2kg, jade stone coating 15kg.
Sodium content in ardealite is 0.7%, its preparation method be ardealite is mixed according to 3:2 with water after, then use mixing speed to be 150r/min stir process 15min, and to be warmed up to temperature be 55 DEG C, after end to be mixed, by its constant temperature standing process 1.5h, more wherein
The quick lime of 0.4 times of addition ardealite consumption, and after using mixing speed to be 55r/min stir process 40min, standing processes 4h, then is added thereto to aluminum oxide, addition is made a living 1.5 times of lime consumption, and use mixing speed to be 40r/min stir process, and take to add while stirring calcirm-fluoride, the addition of calcirm-fluoride is and aluminum oxide equivalent, after continuously stirred process 25min, adjusting its temperature again is 40 DEG C, still aging process 2h,.
Soluble impurity content 3% in ardealite.
Sand is 110 mesh.
The intensity of cement is 52.5MPa.
nullJade stone coating is for by titanium dioxide 1.6kg in parts by weight、Polyvinyl alcohol 0.13kg、Ethanol 0.3kg、Clear water 3.3kg，Its preparation method is to put into clear water to carry out hyperthermic treatment in heating bath，When temperature reaches 40 DEG C，It is added thereto to polyvinyl alcohol again，And maintain programming rate constant，And use mixing speed to be 130r/min stir process，When temperature is warmed up to 90 DEG C，Stop heating up，Maintain temperature constant state stirring，Polyvinyl alcohol is all dissolved，Stop again heating，When making temperature be reduced to 80 DEG C，Titanium dioxide is added thereto，And take the mode stirring while adding，When continuing stirring until temperature and be reduced to 40 DEG C，Stop stir process，After carrying out filtration treatment with gauze again，Obtain filtrate，And after filtrate is mixed with ethanol，Obtain jade stone coating.
The a length of 1mm of glass fibre.
The preparation method of this ardealite base material jade slabstone, comprises the following steps:
(1) prepared by base material: by ardealite, sand, cement, flyash, glass fibre is sequentially added in mixing channel, spray in mixing channel more total inventory 13% clarification limewash, mixing speed is used to be 85r/min stir process 4h again, after again the temperature in mixing channel being warming up to 55 DEG C, constant temperature still aging process 11h, obtain mixing slurry, and after being placed in mixing slurry in roller and carrying out rolling 15min, it is cast in jade slabstone mould again, and the mould by good for cast mixing slurry moves on shake table, vibration frequency is used to be 80Hz vibration processing 20min, and move it to the environment that temperature is 45 DEG C is placed 25min again, again by mould removal, just base can be obtained；It is 50 DEG C that first base is placed in vapor (steam) temperature again, and pressure is in the steam-pressure maintaining device of 1.5MPa, and steam press maintenance processes 45s, can obtain semi-finished product base material；
(2) base material polishing: semi-finished product base material uses clarification limewash spray once, the consumption of clarification limewash is 1/10th of semi-finished product substrate weight, after sprinkling completes, it is placed in the environment that temperature is 45 DEG C placement 20min, it is drawn off using sand papering process again, make smooth surface, finished product base material can be obtained；
(3) scrape the end to spray paint: use jade stone coating first to carry out to finished product base material scraping bottom reason, scraping base thickness degree is 0.2mm, after the end to be doctored, completes, temperature is used to be 25 DEG C of drying and processing 15min, spray gun is used to carry out two layers of spraying of jade stone coating again, coating thickness is 1.7mm, after spraying completes, use varnish sprayed surface 0.4mm thick again, move it to the drying baker that temperature is 35 DEG C again and carry out drying and processing 25min, it is drawn off, is positioned in natural environment, ardealite base material jade slabstone can be obtained.
The a diameter of 5mm of spray gun muzzle.
It is important to point out at this; above-described embodiment is only limitted to be further elaborated technical scheme and illustrate; it is not the further restriction to technical scheme; the essential characteristics of the non-protruding that those skilled in the art make on this basis and non-significant progress, belong to the protection category of the present invention.
Claims (6)
1. an ardealite base material jade slabstone, it is characterised in that its material composition, is ardealite 30-40 part, sand 10-20 part, cement 1-3 part, flyash 1-5 part, glass fibre 1-3 part, jade stone coating 10-20 part in parts by weight；
nullThe described sodium content in ardealite is≤0.9%，Its preparation method be by ardealite with water according to (1-3): after (2-4) mixes，Mixing speed is used to be 100-200r/min stir process 10-20min again，And to be warmed up to temperature be 50-60 DEG C，After end to be mixed，Its constant temperature standing is processed 1-2h，It is added thereto to the quick lime of 0.3-0.5 times of ardealite consumption again，And after using mixing speed to be 50-60r/min stir process 30-60min，Standing processes 3-5h，It is added thereto to aluminum oxide again，Addition is made a living 1-2 times of lime consumption，And use mixing speed to be 30-50r/min stir process，And take to add while stirring calcirm-fluoride，The addition of calcirm-fluoride is and aluminum oxide equivalent，After continuously stirred process 20-30min，Adjusting its temperature again is 30-50 DEG C，Still aging process 1-3h，?；
nullDescribed jade stone coating is for by titanium dioxide 1.5-1.7 part in parts by weight、Polyvinyl alcohol 0.08-0.15 part、Ethanol 0.1-0.7 part、Clear water 3-3.5 part，Its preparation method is to put into clear water to carry out hyperthermic treatment in heating bath，When temperature reaches 40 DEG C，It is added thereto to polyvinyl alcohol again，And maintain programming rate constant，And use mixing speed to be 120-150r/min stir process，When temperature is warmed up to 88-92 DEG C，Stop heating up，Maintain temperature constant state stirring，Polyvinyl alcohol is all dissolved，Stop again heating，When making temperature be reduced to 80 DEG C，Titanium dioxide is added thereto，And take the mode stirring while adding，When continuing stirring until temperature and be reduced to 40 DEG C，Stop stir process，After carrying out filtration treatment with gauze again，Obtain filtrate，And after filtrate is mixed with ethanol，Obtain jade stone coating；
Preparation method, comprises the following steps:
null(1) prepared by base material: by ardealite、Sand、Cement、Flyash、Glass fibre is sequentially added in mixing channel，The clarification limewash of the 10-15% of total inventory is sprayed again in mixing channel，Mixing speed is used to be 80-90r/min stir process 3-5h again，After again the temperature in mixing channel being warming up to 50-60 DEG C，Constant temperature still aging process 10-12h，Obtain mixing slurry，And after being placed in mixing slurry in roller and carrying out rolling 10-20min，It is cast in jade slabstone mould again，And the mould by good for cast mixing slurry moves on shake table，Vibration frequency is used to be 70-90Hz vibration processing 10-30min，And move it to the environment that temperature is 40-50 DEG C is placed 20-30min again，Again by mould removal，Just base can be obtained；Again first base being placed in vapor (steam) temperature is 40-60 DEG C, and pressure is in the steam-pressure maintaining device of 1.4-1.6MPa, and steam press maintenance processes 40-50s, can obtain semi-finished product base material；
(2) base material polishing: semi-finished product base material uses clarification limewash spray once, the consumption of clarification limewash is 1/10th of semi-finished product substrate weight, after sprinkling completes, it is placed in the environment that temperature is 40-50 DEG C placement 10-30min, it is drawn off using sand papering process again, make smooth surface, finished product base material can be obtained；
(3) scrape the end to spray paint: use jade stone coating first to carry out to finished product base material scraping bottom reason, scraping base thickness degree is 0.1-0.3mm, after the end to be doctored, completes, temperature is used to be 20-30 DEG C of drying and processing 10-20min, spray gun is used to carry out two layers of spraying of jade stone coating again, coating thickness is 1.1-2.3mm, after spraying completes, use varnish sprayed surface 0.3-0.5mm thick again, move it to the drying baker that temperature is 30-40 DEG C again and carry out drying and processing 20-30min, it is drawn off, is positioned in natural environment, ardealite base material jade slabstone can be obtained.
2. ardealite base material jade slabstone as claimed in claim 1, it is characterised in that described material composition, is ardealite 35 parts, 15 parts of sand, cement 2 parts, 3 parts of flyash, 2 parts of glass fibre, jade stone coating 15 parts in parts by weight.
3. ardealite base material jade slabstone as claimed in claim 1, it is characterised in that soluble impurity content≤6% in described ardealite.
4. ardealite base material jade slabstone as claimed in claim 1, it is characterised in that described sand is 80-130 mesh.
5. ardealite base material jade slabstone as claimed in claim 1, it is characterised in that a length of 0.1-2mm of described glass fibre.
6. ardealite base material jade slabstone as claimed in claim 1, it is characterised in that a diameter of 1-7mm of described spray gun muzzle.