CN104760441A - Laser printed wallpaper and processing method thereof - Google Patents
Laser printed wallpaper and processing method thereof Download PDFInfo
- Publication number
- CN104760441A CN104760441A CN201510143810.7A CN201510143810A CN104760441A CN 104760441 A CN104760441 A CN 104760441A CN 201510143810 A CN201510143810 A CN 201510143810A CN 104760441 A CN104760441 A CN 104760441A
- Authority
- CN
- China
- Prior art keywords
- wallpaper
- laser
- target
- coating
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a laser printed wallpaper and processing method thereof. The laser printed wallpaper comprises a base wallpaper, and a coating and a coating figure arranged on the base wallpaper. The laser printed wallpaper is characterized in that the coating is a metal coating or metal oxide coating plated by adopting a magnetron sputtering method; the coating figure is the coating figure realized by adopting an open-width dynamic continuous laser; four and more metal target positions are adopted by plating adopting the magnetron sputtering method to perform sputtering, the metal targets are respectively as follows: a copper target, a titanium target, a stainless steel target and a silver target; the plated coating is monolayer or multi-layer. The metal or the metal oxide is plated on the surface of the wallpaper through the adoption of the magnetron sputtering, and the laser printing is performed; the wallpaper is simple in process, high in efficiency, uniform and compact in film, and good in adhesiveness; the process is fast in construction and perfect in joint, the character that the pattern is clear is guaranteed, the printing efficiency is greatly improved, and the problem of pollution in the prior art is completely eradicated.
Description
Technical field:
The present invention relates to a kind of laser decoration printing wallpaper and processing method thereof, it belongs to indoor wall ornament materials environment-friendly type anhydrous printing metal coloring technical field, on wallpaper, particularly adopt the fashion decoration wallpaper laser decoration printing technology of magnetic-control sputtering coiling metal lining or metal oxide film.
Background technology:
Wallpaper is a kind of application indoor wall ornament materials quite widely, so that pattern is abundant, color is various, decorative effect elegant, environmental protection and superior, more and more by the favor of people.Wallpaper kind is many, adapts to different spaces or place, different hobbies and different price levels.According to appearance classification, the basis mask technique on wallpaper surface can divide stamp, embossing and three kinds, embossment, and three kinds of techniques can be combined to again printing and embossing wallpaper, embossing anaglyptic wallpaper, stamp anaglyptic wallpaper.Following a few class can be divided into: (1) resinae wallpaper: namely surface layer is made up of glue, and water resistance is excellent according to surface material; (2) pure paper class wallpaper: be base material with paper, after stamp, embossing forms, naturally comfortable, good permeability, but of long duration may show slightly yellowing; (3) non-woven fabrics wallpaper: with pure non-woven fabrics for base material, special material is not coated after adopting water color ink printing in surface, processes through special, sound-absorbing, yielding; (4) dry goods wallpaper: fabric is through processing, and print color decorative pattern and the novel wall covering material of one that formed, with braids such as silk, fiber crops, cotton for raw material, its physical behavior is highly stable, and after wet water, color changes also little; (5) mica sheet class wallpaper: this series products is graceful, and have reflecting feel, good electrical insulating property, electric conductivity is weak, and safety coefficient is high, both beautiful and practical; (6) gold and silver aluminium foil wallpaper, as utility model patent discloses a kind of metallized wall paper (patent No.: CN91203830), it is the metallized wall paper that a kind of transfer method is produced, utility model discloses a kind of multilayer metal color foil wall paper (patent No.: CN201320245482.8), has the magnificent effect of metal polish.New patent discloses a kind of Multifunctional wallpaper (patent No.: CN200520105012), by antistatic wallpaper and aluminum foil material compound, has the performances such as antistatic, heat insulation, moistureproof, anti-electromagnetic radiation.Its technics comparing is complicated, and cost is high, expensive, and fastness is undesirable, easily occurs disadvantages such as flaking.Also there is the problems such as pattern is old, printed color is not bright-coloured, crease easily in current domestic wallpaper.
Laser technology is along with CAD and graphics and industrial automation blending with multidiscipline, expand laser engraving range of application, laser science and technology and Art Imagination power, effectively be combined with traditional wallpaper surface basis mask technique and printed design, for laser carving technology provides new approaches in the application of indoor wall decoration wallpaper.For solving the limitation of laser decoration printing wallpaper in gradation, again in conjunction with magnetron sputtering plating metal or metal oxide, it can be made to appear various metal color and gloss in one's mind, there is brilliant fashion and unique functional, comprise antistatic, uvioresistant, radiation proof, waterproof, automatically cleaning, antibacterial etc.
Along with making rapid progress of domestic and international vacuum technique, magnetron sputtering technique has become the green environmental protection technique of a lot of industry value chain.Modification and the arrangement of the flexible parent metal such as non-woven fabrics and fabric foundation wall paper can be applied in theory, especially on decorative effect and practicality, have new development space.But with regard to prior art, wallpaper surface yet there are no report by the industrial applications of magnetron sputtering continuous reeling formula plating, because wallpaper is with existing to utilize magnetron sputtering mode to carry out the hard materials such as the glass of plating different, first its both different hard glass, also flexible simple fabric is different from, so when carrying out magnetron sputtering, technological design and state modulator are required from above-mentioned material will be completely different, the determination of process design parameter and program, directly have influence on magnetron sputtering technique and obtain multicolour decorative quality and effect, particularly wallpaper laser decoration printing or magnetron sputtering plating process easily deformable, the post processing processing not being easy to do complicated, therefore also need to protect according to reasonable easy corrosion-resistant anti-oxidant coating layers of factor design such as the heat-resisting of base material and physical and mechanical properties are stable.Otherwise not only plating effect does not reach expection, exterior quality and the physical and mechanical properties of wallpaper script also can be had influence on.
For above-mentioned reasons, existing laser decoration printing and magnetron sputtering technique directly can not realize separately the multi-level pattern decorative effect of wallpaper multicolour, supporting new process design parameter must be had, could under guarantee change the original outward appearance kind of wallpaper and physical and mechanical properties situation, utilize vacuum magnetron sputtering coil film coating machine and environment-friendly type open width dynamic continous way galvanometer laser focusing carving machine, realize the decorative effect of the multi-level pattern of wallpaper surface multicolour metallochrome.
Summary of the invention:
The object of the present invention is to provide a kind of pollution-free, easy to process, and can large-scale production be realized, wallpaper intensity is good, outward appearance is indeformable and have a kind of laser decoration printing wallpaper and the processing method thereof of all kinds of different-style effects such as metal sense, reflecting feel, color sense, aerial perspective.
The object of the present invention is achieved like this:
A kind of laser decoration printing wallpaper and processing method thereof, is characterized in that it comprises following step:
A: first, gets out metal targets and working gas; Target and warehouse dust catcher are cleaned out, the wall thickness>=2 ~ 3mm of target, cooling water flow 50 ~ 100m
3/ h, the return valve of hydraulic pressure>=0.2MPa, half-open return duct, then opening power and source of the gas, JPL-650 magnetic-control sputtering coiling film coating machine is adopted to carry out plating, plating temperature arranges scope 180 ~ 280 DEG C, adopts DC/ magnetron sputtering deposition pattern plating, arranges more than 4 or 4 metal target position, the metal targets of described metal target position is respectively: copper target, titanium target, stainless steel target, silver-colored target, carries out the sputtering of many target position elemental metals or the sputtering of many target position various metals; Wherein the magnetic control plating current of copper target, titanium target and stainless steel target is: 0.1 ~ 10A, and the magnetic control plating current of silver-colored target is: 0.1 ~ 4A; Described working gas is the mist of argon gas or oxygen or argon gas and oxygen, and argon working gas flow is 60 ~ 320Sccm, and oxygen flow is 30 ~ 200Sccm; Vacuum coating pressure is 8 × 10
-4pa ~ 8 × 10
-3pa, plated film operating pressure is 1 × 10
-1pa ~ 2 × 10
-1pa; Operating pressure is:>=2 × 10
-1pa; The plated film speed of a motor vehicle is 0.1 ~ 15 m/min, wallpaper plating fabric width 0.1 ~ 0.65 meter, adopts synchronous ion source electric current: 0.03 ~ 0.5A; For ensureing wallpaper plated film fastness, metastable plasma source current strength is larger, and plated base material surface is more easily activated and roughening, is more conducive to the plating fastness improving wallpaper surface.
According to the Color Scheme requirement being plated base material, specifically sputter the operating energy loss of target position, if need color complicated, just need to use many target position to sputter, both run plural target position simultaneously and sputtered.As copper target and titanium target sputter simultaneously, then can produce the effect of copper-titanium alloy sputtering; If stainless steel target, titanium target and silver-colored target sputter simultaneously, then produce the sputtering effect of titanium stainless steel silver alloy.Therefore adopt many target position combination sputterings of four target position, multiple alloy sputter effect can be completed.If need metal lining oxide, just need to use hybrid working gas, when namely running, be connected with the different working gas of at least two-way.If argon gas and oxygen are with the mixed proportion of 1:2-5, copper target or stainless steel target sputter, then can produce cupric oxide or be oxidized stainless sputtering effect; If argon gas and oxygen are with the mixed proportion of 2-5:1, titanium target sputters, then can produce the sputtering effect of titanium oxide.Also can online according to the different time space changing plating speed of a motor vehicle or change the plating that the magnetic controlled current of metallic target carries out gradual change color.Above-mentioned metal lining and metal oxide film can also carry out two-layer and two-layer above chromatograph structural design, namely carry out the plating of two-layer and two-layer above multiple layer metal and metal oxide, thus obtain abundant metallochrome color effect.As: bronze-colored, golden yellow, shallow orange red, apricot, light yellow, light grey, champagne is yellow, shallow blackish green, color and the color-grading effect such as dusty blue, purple cyan.Usually the online plating speed of a motor vehicle is slower, and the magnetic controlled current of sputtering target is larger, and plated thickness is thicker, and plating color also can be more deeply.Otherwise the online plating speed of a motor vehicle is faster, and the magnetic controlled current of sputtering target is less, can be zero, plated thickness be thinner, and plating color also can be more shallow.
B, the wallpaper open width of magnetron sputtering plating film is placed on the cloth roll frame of the dynamic continous way laser carving machine of open width; Processing Surrounding Temperature 22 DEG C-26 DEG C, humidity 60%-80%; Door width is :≤1.8m; The carving speed of a motor vehicle is: 0.01-5.4m/min; The pattern of laser carving is set: design the pattern needing laser ablation first in a computer, to derive 8 gray-scale maps of BMP form after Photoshop software process picture; And BMP formatted image is saved as .OTB file automatically; The dynamic continous way laser carving machine of open width arranges technological parameter: laser speed V is set to: 1000-1500m/min; Laser vertical direction spacing Y is: 0.45-0.60mm; Whiteness W is: 0-100%; Blackness B is: 0-100%; Door width is :≤1.8m; Run the dynamic continous way laser carving machine of open width and carry out continous way carving;
Wherein: R=0-100%, L=0-100%, P=0-100%, C=0-100%, Q=0-100%.
The described plated film speed of a motor vehicle is 0.1 ~ 15 m/min, the electric current summation≤40A of each described sputtering target; Described working gas is argon gas, and the flow of argon gas is 60 ~ 320Sccm.
The described plated film speed of a motor vehicle is 0.1 ~ 15 m/min, described working gas is the mist of argon gas and oxygen, and described argon gas and Yang Qi Alto mixed proportion are: 1:2 ~ 5, and argon flow amount is 60 ~ 320Sccm, oxygen flow is 30 ~ 200Sccm, and air pressure is>=2 × 10
-1pa.
The described plated film speed of a motor vehicle is 0.1 ~ 15 m/min, described working gas is the mist of argon gas and oxygen, and described argon gas and Yang Qi Alto mixed proportion are: 2 ~ 5:1, and argon flow amount is 60 ~ 320Sccm, oxygen flow is 30 ~ 200Sccm, and air pressure is>=2 × 10
-1pa.
A kind of laser decoration printing wallpaper, it comprises basic wallpaper and the coating be arranged on basic wallpaper and coating decorative pattern, and described coating is the metal coating adopting magnetically controlled sputter method plating; Described coating decorative pattern is the coating decorative pattern adopting the dynamic continous way laser of open width to realize.
Described coating is the monometallic coating of monometallic target realization or the composite metal coated of many metallic targets realization.
Described basic wallpaper is non-woven fabrics or yarn fabric and other flexible parent metal wallpaper.
Present invention employs vacuum magnetron sputtering coil film coating combine with technique open width dynamic continous way laser carving machine printing technology, process can not produce three waste discharge problem.The present invention solves Problems existing in existing metallized wall paper.First utilize magnetron sputtering technique at the film of wallpaper coating surface different metal or metal oxide component, metalized is carried out to fabric, because its plated coating thickness is only between 15 ~ 300 nanometers, therefore do not change the original feature of wallpaper, provide a kind of good decorating effect, there is the manufacture method enriching clear pattern metal wallpaper, increase the new function of wallpaper, as antibacterial, antistatic, radiation proof, automatically cleaning etc. at imparting wallpaper metallic luster simultaneously.Magnetron sputtering membrane process is simple, efficiency is high, even film layer is fine and close, tack is good, environmental protection, is easy to realize large-scale industrial production.
On magnetron sputtering plating metal or metal oxide wallpaper surface, carry out laser decoration printing, user can according to the interest of oneself, hobby, artistic wallpaper and the ancient painting such as landscape scenery with hills and waters, cartoon, personage of selecting oneself to like, only need to provide picture concerned, by computer graphics Software for Design image, carry out stamp through laser technology on metal coating wallpaper surface, there is rapid construction, seam is perfect, the characteristic of clear patterns, improves stamp efficiency greatly, and environmental protection.
Accompanying drawing illustrates:
Fig. 1 is the embodiment of the present invention 1 picturesque landscape picture group carving flower pattern .BMP file
Fig. 2 is the embodiment of the present invention 1 picturesque landscape picture group laser carving gray scale adjustment conic section
Fig. 3 is the embodiment of the present invention 1 picturesque landscape picture group laser decoration printing wallpaper design sketch
Fig. 4 is the embodiment of the present invention 2 cashew nut flower picture group carving flower pattern .BMP file
Fig. 5 is the embodiment of the present invention 2 cashew nut flower picture group laser carving gray scale adjustment conic section
Fig. 6 is the embodiment of the present invention 2 cashew nut flower picture group laser decoration printing wallpaper design sketch
Fig. 7 is the embodiment of the present invention 3 auspicious cloud picture group carving flower pattern .BMP file
Fig. 8 is the embodiment of the present invention 3 auspicious cloud picture group laser carving gray scale adjustment conic section
Fig. 9 is the embodiment of the present invention 3 auspicious cloud laser decoration printing wallpaper design sketch
Detailed description of the invention:
Concrete operations technological process of the present invention is as follows:
The technological process of magnetron sputtering plating metal or metal oxide
First: prepare
Prepare copper target, titanium target, stainless steel target and silver-colored target as target of the present invention, then clean all targets, target wall thickness>=2 ~ 3mm; Cooling water flow: 50 ~ 10m
3/ h, hydraulic pressure>=0.2MPa; Half-open cooling tower return valve, ensures that water pipe is unimpeded, opens electricity gentle; Preheating: drive holding pump after about 2 ~ 3 minutes, drives diffusion pump and is heated to about 250 DEG C after about 2 hours
Second: adopt JPL-650 magnetic-control sputtering coiling film coating machine to carry out plating; Unload and prepare sputtered wallpaper volume, upper wallpaper volume, enters to sputter storehouse;
3rd: vacuumize
Slightly vacuumize: diffusion pump cushioning is to 250 DEG C, and cryogenic refrigeration temperature≤-120 DEG C start sliding vane rotary pump, pull open and slightly take out valve, and open vacuum meter power supply, after vacuum pressure reaches 70Pa, drive lobe pump and continue slightly to take out.
Essence vacuumizes: after vacuum pressure reaches 4Pa, opens foreline valve, closes and slightly takes out valve, open essence and take out valve after reaching 3Pa.Reach predetermined vacuum coating pressure, working gas can be filled with to vacuum chamber, after operating pressure is stable, starts home roll and make rolling, unreel and water cooled rolls low-speed running.
4th: magnetron sputtering plating
Open target power supply refining target one by one about 3 ~ 5 minutes, voltage stabilization aura no-spark can finely tune increase electric current, suitably accelerates, and after being transferred to required operating current, according to designing requirement, determines the sputtering of single target position or the sputtering of many target position, can carry out magnetron sputtering plating.
5th: shut down
Close magnetic control power supply, slowing down allows speed back to zero, closes vacuum measurement meter; Close working gas and host power supply; Close essence to take out and foreline valve, close lobe pump, close roughing vacuum pump after about 60 seconds, by the defrosting of deep cooling cabinet, water chiller-heater unit is heated to 40 DEG C; After defrosting, inflation listening delivers from godown to can't hear, and unloads warehouse entry after yardage roll, closes and increases pump and diffusion pump; After spending 2 hours, close holding pump, close general supply, close gas and close water.
The technological process of laser decoration printing:
Laser parameter table
The operating process of the dynamic continous way laser carving machine of open width:
Power-up sequence is: open general supply → open facility switching (computer is automatically opened and opened XM software) → wait inflation → blue indicator light bright → inflating complete → blue indicator light goes out → by the green button → open laser (green indicating lamp is bright can use laser).
Open width dynamic continous way laser carving machine design computer aided design software system:
BMP is bitmap format, to derive 8 gray-scale maps after Photoshop software process picture.In this software .BMP saves as .OTB file automatically, and Fig. 2 is BMP format operation interface.When using .BMP form, laser speed is up to 2400m/min.This part is designed to the application of prior art, is in the present invention to utilize computer aided design software system to complete the design of design.
Embodiment is the processing for three kinds of different base colors dry goods wallpapers.
Embodiment adopts JPL-650 magnetic-control sputtering coiling film coating machine, uses above-mentioned concrete operations technological process.
Embodiment is by metallic targets different for comprehensive utilization four: copper target, titanium palladium, stainless steel target and silver-colored target, on vacuum magnetic-control sputtering continous way winding film coating machine, according to technological design, under the hybrid working gas condition of argon gas or argon gas and oxygen, carry out vacuum magnetic-control sputtering plating with certain working vacuum degree and the speed of a motor vehicle that reels, concrete technology Selecting parameter is in table 1 and table 2.
Table 1 magnetic-control sputtering coiling plating wallpaper essential information
Table 2 magnetic-control sputtering coiling plating basic technological parameters
Wallpaper color after above-mentioned processing has the metallochrome effect such as steel gray, color purple ash, champagne, golden yellow.
Embodiment 1:1# picturesque landscape picture group laser decoration printing wallpaper work flow:
A: the open width that faced up by 1# magnetic control metal lining film wallpaper volume is placed on laser carving machine;
B: the pattern on adjustment laser carving machine is set
I. design:
1. pattern texture has meticulousr landscape painting transparent effect;
2. there is black, white, grey adjustable in pattern line region, seemingly has gradual change aerial perspective;
3. fall powerful because considering that laser decoration printing easily draws, therefore the carving area of pattern is as far as possible little.
Obtain picturesque landscape picture group carving flower pattern .BMP file as shown in Figure 1 based on above design thinking, and obtain to should pattern laser carving gray scale adjustment conic section, as shown in Figure 2.
C: technological parameter is set on the dynamic continous way laser carving machine of open width:
While the clear fade effect the best of guarantee carved pattern and high production speed, allow wallpaper on average fall and control by force within 30%.
Based on above processing parameter arrange thinking obtain as depicted in figs. 1 and 2 1# through plating wallpaper laser carving production technology: namely, laser speed V is 1400m/min, laser vertical direction spacing Y is 0.45mm, whiteness W is 10, blackness B is 90, etching effect R=100, L=0, P=10, C=0, Q=0, the speed of a motor vehicle is 0.92m, and stamp fabric width is 0.53/0.50m.
D: run the dynamic continous way laser carving machine of open width, starts continous way carving.Effect is shown in Fig. 3.Be disclosed in the terms such as R, L, P, C, Q of described etching effect No. 201410004302.6 Chinese patent application disclosed in.
Embodiment 2:2# cashew nut flower picture group laser decoration printing wallpaper work flow:
A: the open width that faced up by 2# magnetic control metal lining film wallpaper volume is placed on laser carving machine;
B: the pattern on adjustment laser carving machine is set
I. design:
1. pattern texture has comparatively fine pattern flowers profile and to continue in all directions effect;
2. there is black, white, grey adjustable in pattern line region, seemingly has gradual change stereovision;
3. fall powerful because considering that laser decoration printing easily draws, therefore the carving area of pattern is as far as possible little.
Obtain cashew nut flower picture group carving flower pattern .BMP file as shown in Figure 4 based on above design thinking, and obtain should the laser carving gray scale adjustment conic section of pattern, as shown in Figure 5.
C: technological parameter is set on the dynamic continous way laser carving machine of open width:
While the clear fade effect the best of guarantee carved pattern and high production speed, allow wallpaper on average fall and control by force within 30%.
Based on above processing parameter arrange thinking obtain as shown in Figure 4 and Figure 5 2# through plating wallpaper laser carving production technology: namely, laser speed V is 1400m/min, laser vertical direction spacing Y is 0.5mm, whiteness W is 75, blackness B is 25, etching effect R=100, L=0, P=5, C=0, Q=0, the speed of a motor vehicle is 1.02m, and stamp fabric width is 0.53/0.241m.
D: run the dynamic continous way laser carving machine of open width, starts continous way carving.Effect is shown in Fig. 6.
Embodiment 3:3# auspicious cloud picture group laser decoration printing wallpaper work flow:
A: the open width that faced up by 3# magnetic control metal lining film wallpaper volume is placed on laser carving machine;
B: the pattern on adjustment laser carving machine is set
I. design:
1. pattern texture has meticulousr auspicious cloud profile and to continue in all directions effect;
2. there is black, white, grey adjustable in pattern line region, seemingly has gradual change stereovision;
3. fall powerful because considering that laser decoration printing easily draws, therefore the carving area of pattern is as far as possible little.
Obtain auspicious cloud picture group carving flower pattern .BMP file as shown in Figure 7 based on above design thinking, and obtain to should pattern laser carving gray scale adjustment conic section, as shown in Figure 8.
C: technological parameter is set on the dynamic continous way laser carving machine of open width:
While the clear fade effect the best of guarantee carved pattern and high production speed, allow wallpaper on average fall and control by force within 30%.
Based on above processing parameter arrange thinking obtain as shown in Figure 7 and Figure 8 3# through plating wallpaper laser carving production technology: namely, laser speed V is 1500m/min, laser vertical direction spacing Y is 0.5mm, whiteness W is 10, blackness B is 100, etching effect R=100, L=0, P=5, C=0, Q=0, the speed of a motor vehicle is 1.08m, and stamp fabric width and cell height are 0.53/0.108m.
D: run the dynamic continous way laser carving machine of open width, starts continous way carving.Effect is shown in Fig. 9.
1#, 2#, 3# laser decoration printing wallpaper, through the test of overdrying fastness to wet rubbing, compared with conventional wallpaper plating, can make some difference, and shows in table 3 data.
The test of the dry fastness to wet rubbing of table 3 laser decoration printing magnetron sputtering plating wallpaper
Claims (7)
1. a processing method for laser decoration printing wallpaper, is characterized in that it comprises following step:
A: first, gets out metal targets and working gas; Target and warehouse dust catcher are cleaned out, the wall thickness>=2 ~ 3mm of target, cooling water flow 50 ~ 100m
3/ h, the return valve of hydraulic pressure>=0.2MPa, half-open return duct, then opening power and source of the gas, JPL-650 magnetic-control sputtering coiling film coating machine is adopted to carry out plating, plating temperature arranges scope 180 ~ 280 DEG C, adopts DC/ magnetron sputtering deposition pattern plating, arranges the metal target position of more than 4 or 4, the metal targets of described metal target position is respectively: copper target, titanium target, stainless steel target, silver-colored target, carries out the sputtering of many target position elemental metals or the sputtering of many target position various metals; Wherein the magnetic control plating current of copper target, titanium target and stainless steel target is: 0.1 ~ 10A, and the magnetic control plating current of silver-colored target is: 0.1 ~ 4A; Described working gas is the mist of argon gas or oxygen or argon gas and oxygen, and argon working gas flow is 60 ~ 320Sccm, and oxygen flow is 30 ~ 200Sccm; Vacuum coating pressure is 8 × 10
-4pa ~ 8 × 10
-3pa, plated film operating pressure is 1 × 10
-1pa ~ 2 × 10
-1pa; Operating pressure is:>=2 × 10
-1pa; The plated film speed of a motor vehicle is 0.1 ~ 15 m/min, wallpaper plating fabric width 0.1 ~ 0.65 meter, adopts synchronous ion source electric current: 0.03 ~ 0.5A.
B, the wallpaper open width of magnetron sputtering plating film is placed on the cloth roll frame of the dynamic continous way laser carving machine of open width; Processing Surrounding Temperature 22 DEG C-26 DEG C, humidity 60%-80%; Door width is :≤1.8m; The carving speed of a motor vehicle is: 0.01-5.4m/min; The pattern of laser carving is set: design the pattern needing laser ablation first in a computer, to derive 8 gray-scale maps of BMP form after Photoshop software process picture; And BMP formatted image is saved as .OTB file automatically; The dynamic continous way laser carving machine of open width arranges technological parameter: laser speed V is set to: 1000-1500m/min; Laser vertical direction spacing Y is: 0.45-0.60mm; Whiteness W is: 0-100%; Blackness B is: 0-100%; Door width is :≤1.8m; Run the dynamic continous way laser carving machine of open width and carry out continous way carving;
Wherein: R=0-100%, L=0-100%, P=0-100%, C=0-100%, Q=0-100%.
2. the processing method of laser decoration printing wallpaper as described in claim 1, is characterized in that the described plated film speed of a motor vehicle is 0.1 ~ 15 m/min, the electric current summation≤40A of each described sputtering target; Described working gas is argon gas, and the flow of argon gas is 60 ~ 320Sccm.
3. the processing method of laser decoration printing wallpaper as described in claim 1, it is characterized in that the described plated film speed of a motor vehicle is 0.1 ~ 15 m/min, described working gas is the mist of argon gas and oxygen, described argon gas and Yang Qi Alto mixed proportion are: 1:2 ~ 5, argon flow amount is 60 ~ 320Sccm, oxygen flow is 30 ~ 200Sccm, and air pressure is>=2 × 10
-1pa.
4. the processing method of laser decoration printing wallpaper as described in claim 1, it is characterized in that the described plated film speed of a motor vehicle is 0.1 ~ 15 m/min, described working gas is the mist of argon gas and oxygen, described argon gas and Yang Qi Alto mixed proportion are: 2 ~ 5:1, argon flow amount is 60 ~ 320Sccm, oxygen flow is 30 ~ 200Sccm, and air pressure is>=2 × 10
-1pa.
5. a laser decoration printing wallpaper, it comprises basic wallpaper and the coating be arranged on basic wallpaper and coating decorative pattern, it is characterized in that described coating is the metal coating or the coating of metal oxides that adopt magnetically controlled sputter method plating; Described coating decorative pattern is the coating decorative pattern adopting the dynamic continous way laser of open width to realize.
6. laser decoration printing wallpaper as described in claim 5, is characterized in that described coating is the monometallic coating of the single or multiple lift that monometallic target realizes or the composite metal coated of many metallic targets realization.
7. the laser decoration printing wallpaper as described in claim 5 or 6, is characterized in that described basic wallpaper is non-woven fabrics or yarn fabric and other flexible parent metal wallpaper.