CN104745128A - 一种脲醛树脂胶黏剂及其在胶合板中的应用 - Google Patents

一种脲醛树脂胶黏剂及其在胶合板中的应用 Download PDF

Info

Publication number
CN104745128A
CN104745128A CN201510168689.3A CN201510168689A CN104745128A CN 104745128 A CN104745128 A CN 104745128A CN 201510168689 A CN201510168689 A CN 201510168689A CN 104745128 A CN104745128 A CN 104745128A
Authority
CN
China
Prior art keywords
parts
urea
resin adhesive
formaldehyde
formaldehyde resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510168689.3A
Other languages
English (en)
Other versions
CN104745128B (zh
Inventor
徐伟鹏
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Jingmao Technology Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510168689.3A priority Critical patent/CN104745128B/zh
Publication of CN104745128A publication Critical patent/CN104745128A/zh
Application granted granted Critical
Publication of CN104745128B publication Critical patent/CN104745128B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及胶黏剂领域，特别涉及一种脲醛树脂胶黏剂及其在胶合板中的应用。一种脲醛树脂胶黏剂，包含有如下重量份数的组分：脲醛树脂80~120份；填充剂8~15份；防老剂3~6份；甲醛捕获剂0.1~0.5份；其中，所述甲醛捕获剂的化学分子式为C16H18N2O4Zn。本发明的脲醛树脂胶黏剂能够利用甲醛捕获剂在胶合板热压过程中有效吸附游离的甲醛，有效降低甲醛的释放量，较好的从根本上解决现有技术中甲醛释放量过高的问题。而且，本发明的甲醛捕获剂不单能够吸附甲醛，还能使得胶黏剂的粘结强度不但不会下降，还有所上升。

Description

一种脲醛树脂胶黏剂及其在胶合板中的应用
技术领域
本发明涉及胶黏剂领域，特别涉及一种脲醛树脂胶黏剂及其在胶合板中的应用。
背景技术
脲醛树脂是市场需求量最大的树脂之一，由于其原料价廉易得、制造工艺简单、初黏度大、黏结强度高等优点，被广泛应用于木器加工、人造板材的生产及室内装修等行业。但是，但随着人们对室内环境意识的日益提高及胶黏剂应用领域的扩大，胶粘剂存在的主要问题也暴露了出来：如粘结性能较差，游离甲醛含量偏高，导致环境污染，损害人体健康。
发明内容
本发明所要解决的技术问题是提供一种游离甲醛含量低，粘结性能好的脲醛树脂胶黏剂。
本发明的另一个目的是提供上述胶黏剂在胶合板中的应用。
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂80~120份；填充剂8~15份；防老剂3~6份；甲醛捕获剂0.1~0.5份；其中，所述甲醛捕获剂的化学分子式为C16H18N2O4Zn。
进一步的，所述甲醛捕获剂为单斜晶系，C2/c空间群，晶胞参数为a=13.293(2) Å，b=14.147(3) Å，c=9.258(3) Å，α=γ =90º，β= 102.035(5)º，V=1741.02(3) Å 3。
进一步的，所述填充剂为碳酸钙、高岭土、淀粉中的至少一种。
进一步的，所述防老剂为氢氧化钙、聚乙烯醇中的至少一种。
上述脲醛树脂胶黏剂在胶合板中的应用。
本发明具有如下有益效果：
本发明的脲醛树脂胶黏剂能够利用甲醛捕获剂在胶合板热压过程中有效吸附游离的甲醛，有效降低甲醛的释放量，较好的从根本上解决现有技术中甲醛释放量过高的问题。而且，本发明的甲醛捕获剂不单能够吸附甲醛，还能使得胶黏剂的粘结强度不但不会下降，还有所上升。
具体实施方式
下面结合实施例对本发明进行详细的说明，实施例仅是本发明的优选实施方式，不是对本发明的限定。
本发明的甲醛捕获剂如无特别说明，均按下述方法制备。
将0.1 mmol2,3,5,6-四甲基对苯二甲酸、0.1 mmol4-甲基-1H-吡唑和0.1 mmol的硝酸锌溶于10 mL乙腈和5 mL甲醇的混合溶剂当中，在室温下搅拌形成混合液A，然后将上述混合液A在35℃下静置7天得到混合液B。
然后将所述混合液B置入25 mL水热反应釜中在溶剂热135℃条件下加热反应48小时后以5℃/小时降至室温得到所述的甲醛捕获剂。
然后将甲醛捕获剂进行结构表征。
该甲醛捕获剂的X射线衍射数据是在Bruker Smart Apex CCD面探衍射仪上，用MoKα辐射(λ = 0.71073 Å)，以ω扫描方式收集并进行Lp因子校正，吸收校正使用SADABS程序。用直接法解结构，然后用差值傅立叶法求出全部非氢原子坐标，并用理论加氢法得到氢原子位置(C−H 1.083 Å)，用最小二乘法对结构进行修正。计算工作在PC机上用SHELXTL程序包完成。
经测试解析可知，该甲醛捕获剂化学分子式为C16H18N2O4Zn，单斜晶系，C2/c空间群，晶胞参数为a=13.293(2) Å，b=14.147(3) Å，c=9.258(3) Å，α=γ =90º，β= 102.035(5)º，V=1741.02(3) Å 3，Z=2。
最后将上述所得的甲醛捕获剂研磨成200-300目的粉末后待用。
本发明所用的脲醛树脂、填充剂和防老剂等如无特别说明，均为市面常用产品。
本发明的胶黏剂利用为本技术领域常用的制备方法均可实现本发明，在此不再详细描述。
实施例 1
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂80份，淀粉10份，碳酸钙3份，氢氧化钙4份，甲醛捕获剂0.3份。
实施例 2
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂120份，碳酸钙8份，高岭土3份，聚乙烯醇3份，氢氧化钙3份，甲醛捕获剂0.1份。
实施例 3
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂95份，碳酸钙9份，聚乙烯醇2份，氢氧化钙4份，甲醛捕获剂0.5份。
实施例 4
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂110份，高岭土15份，聚乙烯醇5份，甲醛捕获剂0.4份。
实施例 5
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂85份，淀粉12份，聚乙烯醇3份，甲醛捕获剂0.2份。
实施例 6
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂100份，淀粉5份，高岭土6份，碳酸钙2份，聚乙烯醇2份，氢氧化钙2份，甲醛捕获剂0.3份。
对比例 1
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂100份，淀粉5份，高岭土6份，碳酸钙2份，聚乙烯醇2份，氢氧化钙2份。
对比例 2
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂110份，高岭土15份，聚乙烯醇5份。
对比例 3
一种脲醛树脂胶黏剂，包含有如下重量份数的组分：
脲醛树脂80份，淀粉10份，碳酸钙3份，氢氧化钙4份。
然后将上述实施例和对比例的胶黏剂用于胶合板的涂胶拼板，此过程为本技术领域的常用手段，在此不再详细说明。
最终得到商品胶合板，产品质量及胶合板中释放出的游离甲醛的含量指标按照国家标准GB/T 9846.1～9846.8-2004《胶合板》中的各项性能指标的要求进行检测。测试结果如下表1所示。
表 1 胶合板的甲醛释放量与胶合强度
从上表可知本发明所得的胶黏剂通过新型的甲醛捕获剂在制备的胶合板中能够显著降低甲醛释放量。此外，从表1我们可以看出通过增加甲醛捕获剂，胶接制品的胶合强度不但没有下降，反而有所提高。
以上所述实施例仅表达了本发明的实施方式，其描述较为具体和详细，但并不能因此而理解为对本发明专利范围的限制，但凡采用等同替换或等效变换的形式所获得的技术方案，均应落在本发明的保护范围之内。

Claims (5)

1.一种脲醛树脂胶黏剂，其特征在于，包含有如下重量份数的组分：
脲醛树脂80~120份；填充剂8~15份；防老剂3~6份；甲醛捕获剂0.1~0.5份；其中，所述甲醛捕获剂的化学分子式为C16H18N2O4Zn。
2.根据权利要求1所述的一种脲醛树脂胶黏剂，其特征在于，所述甲醛捕获剂为单斜晶系，C2/c空间群，晶胞参数为a=13.293(2) Å，b=14.147(3) Å，c=9.258(3) Å，α=γ=90º，β= 102.035(5)º，V=1741.02(3) Å 3。
3.根据权利要求1所述的一种脲醛树脂胶黏剂，其特征在于，所述填充剂为碳酸钙、高岭土、淀粉中的至少一种。
4.根据权利要求1所述的一种脲醛树脂胶黏剂，其特征在于，所述防老剂为氢氧化钙、聚乙烯醇中的至少一种。
5.权利要求1所述的脲醛树脂胶黏剂在胶合板中的应用。
CN201510168689.3A 2015-04-10 2015-04-10 一种脲醛树脂胶黏剂及其在胶合板中的应用 Expired - Fee Related CN104745128B (zh)