CN104744749A - Rubber water stop and making method thereof - Google Patents
Rubber water stop and making method thereof Download PDFInfo
- Publication number
- CN104744749A CN104744749A CN201310735476.5A CN201310735476A CN104744749A CN 104744749 A CN104744749 A CN 104744749A CN 201310735476 A CN201310735476 A CN 201310735476A CN 104744749 A CN104744749 A CN 104744749A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- sbr
- styrene
- composite reinforcing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a rubber water stop and a making method thereof. The rubber water stop comprises, by mass, 100 parts of styrene butadiene rubber, 40-80 parts of a composite strengthening agent, 2-5 parts of a vulcanizing agent and 1-3 parts of a vulcanizing promoter. The rubber water stop is made through mixing, vulcanizing and molding processes. The rubber water stop has the characteristics of high tensile strength, aging resistance and corrosion resistance, and is suitable for being used in capital construction engineering, underground facilities, tunnels, sewage treatment plants, water conservancy projects and metros.
Description
Technical field
The present invention relates to a kind of rubber fastening band and preparation method thereof.
Background technology
Along with the quickening of urbanization process, traffic congestion, environmental pollution and energy dilemma have become current problem demanding prompt solution.Ground railway capable underground traffic process can be avoided the crowded of urban pavement and make full use of outside the underground space, also has fast, advantage easily, has become the prefered method of big and medium-sized cities solving urban traffic blocking problem.
In the construction process of some underground workss, due to can not continuous placing be carried out, or starve the reasons such as the concrete member caused expands with heat and contract with cold due to the distortion of ground and the numbering of temperature, construction joint, settlement joint, movement joint need be left, need that at these gap places sealing is installed and bring the seepage preventing water.Meanwhile, domestic and international metro construction mainly adopts shield technique to construct, and shield tunnel is spliced by paying section of jurisdiction in advance, and segment joint uses rubber packing material.Rubber packing material utilizes the rubber of rubber and the feature of compression set, produces elastic deformation, thus play effective fit sealing under various load, prevents the effect that Architectural Construction is seeped water, leaked.The ability that styrene-butadiene rubber(SBR) waterstop is suitable for segment joint distortion is comparatively strong, and the ageing-resistant performance of material is good, has been widely used in the seam waterproof of the piecing assembly such as railway, subway underground works as a kind of rubber packing material of excellent property.But, in recent years, in some underground construction processes, to the requirement of the tensile strength of waterstop etc., more and more higher.Common rubber fastening band cannot meet the requirement of high-speed railway to its performance.Add that the underground condition in some constructions is complicated, stronger to the corrosive nature of rubber fastening band, make rubber fastening band in the present context performance have and decline significantly, greatly have impact on its hermetic seal performance, cause the leaking of Architectural Construction, deep water thus cause sealing unsuccessfully.
Summary of the invention
The object of the present invention is to provide a kind of rubber fastening band and preparation method thereof, this rubber fastening band has excellent mechanical property.
To achieve these goals, technical scheme of the present invention is: a kind of rubber fastening band and preparation method thereof, it is characterized in that it is made up of styrene-butadiene rubber(SBR), composite reinforcing agent, sulphur, vulcanization accelerator, the massfraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 40 ~ 80 parts, vulcanizing agent 2 ~ 5 parts, vulcanization accelerator 1 ~ 3 part.
Described composite reinforcing agent is carbon black: mica powder=1:1.
Described vulcanization leveller is zinc oxide.
Described vulcanizing agent is sulphur.
Described vulcanization accelerator is Methasam.
The preparation method of above-mentioned a kind of rubber water-proof, is characterized in that carrying out as follows:
(1) mass fraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 40 ~ 80 parts, vulcanizing agent 2 ~ 5 parts, vulcanization accelerator 1 ~ 3 part;
(2) take raw material according to the above ratio, the banburying in Banbury mixer by styrene-butadiene rubber(SBR) and composite reinforcing agent, keep temperature to be 140 ± 5 DEG C, batch mixing 5-15 minute;
(3) then in Banbury mixer, add vulcanizing agent, vulcanization accelerator successively, keep temperature to be 140 ± 5, batch mixing 5 ~ 10 minutes, then discharging, is pressed into thin slice through mill;
(4) thin slice is put into mould, in vulcanizer, carry out sulfuration, curing temperature is 160 ~ 180 DEG C, and sulfide stress is 10 ~ 15MPa, and curing time is 5 ~ 20 minutes, and sulfuration terminates to be cooled to room temperature, takes out cross-linked rubber, obtained rubber fastening band.
Beneficial effect of the present invention is as follows:
1. the present invention is by being undertaken mixing by composite reinforcing agent and styrene-butadiene rubber(SBR), forms nano composite structure, to improve the stopping property of styrene-butadiene rubber(SBR), thus effectively improves the stagnant water effect of waterstop.
2. the present invention selects composite reinforcing agent and styrene-butadiene rubber(SBR) blending and modifying, thus makes polymkeric substance have high strength and rubber.
Embodiment
In order to the present invention is understood at the better end, further illustrate content of the present invention below in conjunction with embodiment.
Embodiment 1:
A preparation method for rubber fastening band, carries out as follows:
1. the mass fraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 40 parts, vulcanizer 2 parts, vulcanization accelerator 1 part;
2. take raw material according to the above ratio, by styrene-butadiene rubber(SBR) stripping and slicing, mixing in Banbury mixer with composite reinforcing agent, keep temperature to be 135 DEG C, mixing 5 minutes;
3. then in Banbury mixer, add vulcanizing agent and vulcanization accelerator successively, keep temperature to be 135 DEG C, continue mixing 8 minutes, then discharging, be pressed into thin slice through two roller mill;
4. above-mentioned thin slice is put into mould, in vulcanizing press, carry out sulfuration, curing temperature is 160 DEG C, and sulfide stress is 10MPa, and curing time is 20 minutes, is cooled to room temperature after sulfuration terminates, and takes out cross-linked rubber, namely obtains rubber fastening band.
Embodiment 2:
A preparation method for rubber fastening band, carries out as follows:
1. the mass fraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 80 parts, vulcanizing agent 5 parts, vulcanization accelerator 2 parts;
2. take raw material according to the above ratio, by styrene-butadiene rubber(SBR) stripping and slicing, mixing in Banbury mixer with composite reinforcing agent, keep temperature to be 135 DEG C, mixing 5 minutes;
3. then in Banbury mixer, add vulcanizing agent, vulcanization accelerator successively, keep temperature to be 135 DEG C, continue mixing 8 minutes, then discharging, be pressed into thin slice through two roller mill;
4. above-mentioned thin slice is put into mould, in vulcanizing press, carry out sulfuration, curing temperature is 160 DEG C, and sulfide stress is 13MPa, and curing time is 20 minutes, is cooled to room temperature after sulfuration terminates, and takes out cross-linked rubber, namely obtains rubber fastening band.
Embodiment 3:
A preparation method for rubber fastening band, carries out as follows:
1. the mass fraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 80 parts, vulcanizing agent 4 parts, vulcanization accelerator 3 parts;
2. take raw material according to the above ratio, by styrene-butadiene rubber(SBR) stripping and slicing, mixing in Banbury mixer with composite reinforcing agent, keep temperature to be 135 DEG C, mixing 5 minutes;
3. then in Banbury mixer, add vulcanizing agent, vulcanization accelerator successively, keep temperature to be 135 DEG C, continue mixing 8 minutes, then discharging, be pressed into thin slice through two roller mill;
4. above-mentioned thin slice is put into mould, in vulcanizing press, carry out sulfuration, curing temperature is 160 DEG C, and sulfide stress is 13MPa, and curing time is 20 minutes, is cooled to room temperature after sulfuration terminates, and takes out cross-linked rubber, namely obtains rubber fastening band.
Embodiment 4:
A preparation method for rubber fastening band, carries out as follows:
1. the mass fraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 80 parts, vulcanizing agent 4 parts, vulcanization accelerator 2 parts;
2. take raw material according to the above ratio, by styrene-butadiene rubber(SBR) stripping and slicing, mixing in Banbury mixer with composite reinforcing agent, keep temperature to be 135 DEG C, mixing 5 minutes;
3. then in Banbury mixer, add vulcanizing agent, vulcanization accelerator successively, keep temperature to be 135 DEG C, continue mixing 8 minutes, then discharging, be pressed into thin slice through two roller mill;
4. above-mentioned thin slice is put into mould, in vulcanizing press, carry out sulfuration, curing temperature is 160 DEG C, and sulfide stress is 13MPa, and curing time is 20 minutes, is cooled to room temperature after sulfuration terminates, and takes out cross-linked rubber, namely obtains rubber fastening band.
Performance comparision table
Project | Embodiment 1 | Embodiment 2 | Embodiment 3 | Embodiment 4 |
Tensile strength MPa | 16.05 | 17.04 | 18.52 | 18.92 |
Elongation at break % | 375 | 405 | 513 | 498 |
The above, it is only preferred embodiment of the present invention, not any pro forma restriction is done to the present invention, every above embodiment is done according to technical spirit of the present invention any simple modification, equivalent variations and modification, all still belong in the scope of technical solution of the present invention.
Claims (3)
1. a rubber fastening band, it is characterized in that being made up of styrene-butadiene rubber(SBR), composite reinforcing agent, sulphur, vulcanization accelerator, the massfraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 40 ~ 80 parts, vulcanizing agent 2 ~ 5 parts, vulcanization accelerator 1 ~ 3 part.
2. require described a kind of rubber fastening band according to right 1, it is characterized in that: described composite reinforcing agent is carbon black: mica powder=1:1.
3. require the preparation method of described a kind of rubber fastening band according to right 1, it is characterized in that, carry out as follows:
1. the mass fraction of each raw material is: 100 parts, styrene-butadiene rubber(SBR), composite reinforcing agent 40 ~ 80 parts, vulcanizing agent 2 ~ 5 parts, vulcanization accelerator 1 ~ 3 part;
2. take raw material according to the above ratio, the banburying in Banbury mixer by styrene-butadiene rubber(SBR) and composite reinforcing agent, keep temperature to be 140 ± 5 DEG C, batch mixing 5-15 minute;
3. then in Banbury mixer, add vulcanizing agent, vulcanization accelerator successively, keep temperature to be 140 ± 5, batch mixing 5 ~ 10 minutes, then discharging, is pressed into thin slice through mill;
4. thin slice is put into mould, in vulcanizer, carry out sulfuration, curing temperature is 160 ~ 180 DEG C, and sulfide stress is 10 ~ 15MPa, and curing time is 5 ~ 20 minutes, and sulfuration terminates to be cooled to room temperature, takes out cross-linked rubber, obtained rubber fastening band.