CN104743992A - Anti-drop vitrified tile adhesive and preparation method thereof - Google Patents
Anti-drop vitrified tile adhesive and preparation method thereof Download PDFInfo
- Publication number
- CN104743992A CN104743992A CN201510083399.9A CN201510083399A CN104743992A CN 104743992 A CN104743992 A CN 104743992A CN 201510083399 A CN201510083399 A CN 201510083399A CN 104743992 A CN104743992 A CN 104743992A
- Authority
- CN
- China
- Prior art keywords
- vitrified tile
- tile adhesive
- weight percent
- powder
- adhesive special
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-drop vitrified tile adhesive which is characterized in that the adhesive comprises a powder formula and a slurry formula which are stirred and mixed, wherein the powder formula is prepared by mixing the following components in percentage by weight: 50-60% of inorganic silicate cement, 30-40% of washed-out sands (80 meshes), 0.8-1.2% of bentonite, 0.4-0.6% of (hydroxypropyl) cellulose, 0.4-0.6% of redispersible latex powder, 0.2-0.4% of macromolecular nanopowder, 0.2-0.3% of guar gum powder, 0.2-0.3% of 801 rubber powder, 0.1-0.15% of honeyed starch and 0.1-0.2% of lignocellulose, and the ratio of the powder formula and the slurry formula in percentage by weight is 1: 1. Compared with a conventional adhesive, the performance indexes of the physical bite force of the anti-drop vitrified tile adhesive are superior to those of similar products and the anti-drop vitrified tile adhesive has the advantages of being free of toxicity and harmlessness, low in cost, low in manufacturing cost and the like.
Description
Technical field
The present invention relates to a kind of tackiness agent of vitrified tile, belong to a kind of powder composition and building material field, particularly relate to a kind of asepsis environment-protecting, the vitrified tile tackiness agent that viscosity is strong.
Background technology
Vitrified tile is the brick of surface through a kind of light of polishing of all-body tile base substrate, belongs to the one of all-body tile.Because water-intake rate is low, hardness is high, not easily having cut, be widely used in indoor decoration design, show luxurious, air fully, is that modern Interior is decorate preferred wall tile.
Current field of constructional ornament tradition vitrified tile binding agent is generally raw material and cement class tackiness agent with natural rubber, and the former is usually containing formaldehyde, and cost is high; toxicity is high, and preparation condition also has corresponding requirement in addition, economical and practical not; latter is a kind of response type polymer cement sill; there is advantage with low cost, but bounding force decreases, easily occur hollowing phenomenon; brick body is caused to come off; especially in vibration and temperature variation, very easily flake and peel off, causing potential safety hazard.Therefore, existing existing defects, is further improved.The invention provides a kind of vitrified tile adhesive special, be all better than product of the same type compared to the property indices of its physics snap-in force of traditional binding agent, and there is the advantages such as nontoxic, with low cost, low cost of manufacture.
Summary of the invention
One is the object of the present invention is to provide to have toxicity low; environmental protection and cheap for manufacturing cost; cohesive strength is better than the adhesive special for vitrified tile of national like product, causes hollowing phenomenon for solving due to various factors, and then produces vitrified tile and flake and the technical problem such as stripping.
In order to solve the problem, a kind of vitrified tile adhesive special of the present invention, it is characterized in that being uniformly mixed by powder formulation and liquid material formula forming, wherein: described powder formulation is mixed by weight percentage by following component: inorganic silicic acid salt cement 50% ~ 60%, washed-out sand 80 orders ~ 30%-40%, wilkinite 0.8% ~ 1.2%, Mierocrystalline cellulose (hydroxypropyl) 0.4%-0.6%, can at dispersed latex powder 0.4% ~ 0.6% high molecular nanometer powder, 0.2% ~ 0.4%, guar gum flour 0.2% ~ 0.3%, 801 rubber powders 0.2% ~ 0.3%, starch honey, 0.1% ~ 0.15%, lignocellulose 0.1% ~ 0.2%, described powder formulation and liquid material formula are powder formulation according to weight percent: liquid material formula=1: 1.
Preferably, described inorganic silicate cement weight degree 60%.
Preferably, described washed-out sand 80 order weight percent content is 37%.
Preferably, described wilkinite weight percent content is 1.0%.
Preferably, described Mierocrystalline cellulose (hydroxypropyl) weight percent content is 0.5%.
Preferably, described can be 0.6% at dispersed latex powder weight percent content.
Preferably, described high molecular nanometer powder weight percent content is 0.2%.
Preferably, described guar gum flour weight percent content is 0.2%.
Preferably, described 801 rubber powder weight percent contents are 0.2%.
Preferably, described starch honey weight percent content is 0.1%.
Preferably, lignocellulose weight percent content is 0.2%.
Prepare the vitrified tile caking agent method that comes off that prevents of the present invention to be made up of following steps:
A, aforementioned powder formulation poured into Special agitating machinery tank;
B, pour liquid material formula into, mix according to 1: 1 ratio with the powder formulation described in step a;
C, mixture in step b is heated to 40 DEG C after uniform stirring 15 minutes, pack and get final product.
In order to more firmly be fixed on body of wall by vitrified tile, preferably adopt following steps:
A, first use 1: 2 sand-cement slurry will to construct the levelling correction of metope;
B, again preparation is completed after vitrified tile binding agent uniform application in the vitrified tile back side;
C, finally vitrified tile block-by-block is attached at metope by concora crush is real.
The present invention, for a kind of vitrified tile adhesive special, is all better than product of the same type compared to the property indices of its physics snap-in force of traditional binding agent, and has the advantages such as nontoxic, with low cost, low cost of manufacture.
Embodiment
The present invention is further illustrated below by embodiment and comparative example.
The specific embodiment of the invention is to provide a kind of vitrified tile binding agent, by powder formulation and liquid material formula according to the ratio of weight percent 1: 1, within 15 minutes, packs and get final product after being heated to 40 DEG C with professional stirrer uniform stirring.
Embodiment one:
Described powder formulation is that multiple special high molecular polymer and inorganic silicate are formulated, specifically mixed by weight percentage by following component: inorganic silicic acid salt cement 50% ~ 60%, washed-out sand 80 order 30% ~ 40%, wilkinite 0.8% ~ 1.2%, Mierocrystalline cellulose (hydroxypropyl) 0.4% ~ 0.6%, can at dispersed latex powder 0.4% ~ 0.6% high molecular nanometer powder, 0.2% ~ 0.4%, guar gum flour 0.2% ~ 0.3%, 801 rubber powders 0.2% ~ 0.3%, starch honey, 0.1% ~ 0.15%, lignocellulose 0.1% ~ 0.2%; Wherein, described liquid material formula is ordinary tap water.
Furthermore, the using method of vitrified tile adhesive special, is preferably completed by following steps: a, first use 1: 2 sand-cement slurry will to construct the levelling correction of metope; B, again preparation is completed after vitrified tile binding agent uniform application in the vitrified tile back side, smearing thickness is arranged on 3 ~ 5cm; C, finally vitrified tile block-by-block is attached at metope by concora crush is real.This using method is applicable to degree of plainness for wall surface usually within the scope of 1 ~ 2.5cm.
Embodiment two:
This powder formulation preferably includes: inorganic silicic acid salt cement 60%, washed-out sand 80 order 37%, wilkinite 1.0%, Mierocrystalline cellulose (hydroxypropyl) 0.5%, can in dispersed latex powder 0.6%, high molecular nanometer powder 0.2%, guar gum flour 0.2%, 801 rubber powders 0.2%, starch honey 0.1%, lignocellulose 0.2%.Wherein, described liquid material formula is ordinary tap water.
Furthermore, the using method of vitrified tile adhesive special, is preferably completed by following steps: a, first use 1: 2 sand-cement slurry will to construct the levelling correction of metope; B, again preparation is completed after vitrified tile binding agent uniform application in the vitrified tile back side, smearing thickness is arranged on 3 ~ 5cm; C, finally vitrified tile block-by-block is attached at metope by concora crush is real.This using method is applicable to degree of plainness for wall surface usually within the scope of 1 ~ 2.5cm.
The industry standard that vitrified tile adhesive special of the present invention is selected: 1JCT547-2005 " floor tile tackiness agent ", respective specified should not be less than 0.4MPa for often organizing sample mean cohesive strength, and often group can have a sample cohesive strength to be less than 0.4MPa, Dan Buying is less than the standard of 0.3MPa; After tested; result shows; three groups of vitrified tile adhesive strengths (units MPa) that face area (unit mm2) is respectively 4136,4092,4230 are followed successively by 1.0,1.0,1.0, and mean value 0.9, all considerably beyond industry standard regulation relevant parameter.
Table 1
Another test industry standard that the present invention selectes: " construction work cohesive strength of decorative tile examination criteria " JGJ110-2008, as shown in table 2, trier range (5KN) is all exceeded to cohesive strength, thermal ageing cohesive strength detected result after its former cohesive strength, immersion, and bonding strength 0.50MPa after freeze-thaw cycle, performance is due to like product.
The present invention is all better than product (see table 1 and table 2) of the same type compared to the property indices of its physics snap-in force of traditional binding agent, not easily occur that hollowing causes peeling off with metope, and hot environment stability, and have nontoxic with low cost, the advantages such as low cost of manufacture.
As known by the technical knowledge, the present invention is realized by other the embodiment not departing from its spirit or essential feature.Therefore, above-mentioned disclosed embodiment, with regard to each side, all just illustrates, is not only.Within the scope of the present invention all or be all included in the invention being equal to the change in scope of the present invention.
Claims (14)
1. vitrified tile adhesive special, it is characterized in that being uniformly mixed by powder formulation and liquid material formula forming, wherein: described powder formulation comprises following component to mix by weight percentage:
Described powder formulation and liquid material formula are powder formulation according to weight percent: liquid material formula=1: 1.
2. vitrified tile adhesive special according to claim 1, is characterized in that, described inorganic silicate cement weight degree 60%.
3. vitrified tile adhesive special according to claim 1, is characterized in that, described washed-out sand 80 order weight percent content is 37%.
4. vitrified tile adhesive special according to claim 1, is characterized in that, described wilkinite weight percent content is 1.0%.
5. vitrified tile adhesive special according to claim 1, is characterized in that, described Mierocrystalline cellulose (hydroxypropyl) weight percent content is 0.5%.
6. vitrified tile adhesive special according to claim 1, is characterized in that, described can be 0.6% at dispersed latex powder weight percent content.
7. vitrified tile adhesive special according to claim 1, is characterized in that, described high molecular nanometer powder weight percent content is 0.2%.
8. vitrified tile adhesive special according to claim 1, is characterized in that, described guar gum flour weight percent content is 0.2%.
9. vitrified tile adhesive special according to claim 1, is characterized in that, described 801 rubber powder weight percent contents are 0.2%.
10. vitrified tile adhesive special according to claim 1, is characterized in that, described starch honey weight percent content is 0.1%.
11. vitrified tile adhesive specials according to claim 1, is characterized in that, described lignocellulose weight percent content is 0.2%.
12. 1 kinds of vitrified tile adhesive special preparation methods, is characterized in that, prepare described vitrified tile adhesive special method and are made up of following steps:
A, powder formulation described in claim 1 ~ 11 poured into Special agitating machinery tank;
B, pour liquid material formula into, mix according to 1: 1 ratio with the powder formulation described in step a;
C, mixture in step b is heated to 40 DEG C after uniform stirring 15 minutes, pack and get final product.
The using method of 13. 1 kinds of vitrified tile adhesive specials, is characterized in that: using method is made up of following steps:
A, first use 1: 2 sand-cement slurry will to construct the levelling school of metope;
B, again preparation is completed after vitrified tile binding agent uniform application in the vitrified tile back side;
C, vitrified tile block-by-block is being compacted at construction metope by flat.
The using method of 14. a kind of vitrified tile adhesive specials according to claim 13, is characterized in that in described use step b, smearing thickness is 3 ~ 5cm.