CN104743894A - 一种增强型玻璃纤维浸润剂的制备工艺 - Google Patents
一种增强型玻璃纤维浸润剂的制备工艺 Download PDFInfo
- Publication number
- CN104743894A CN104743894A CN201410839646.9A CN201410839646A CN104743894A CN 104743894 A CN104743894 A CN 104743894A CN 201410839646 A CN201410839646 A CN 201410839646A CN 104743894 A CN104743894 A CN 104743894A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- agent
- preparation technology
- membrane
- forming agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种增强型玻璃纤维浸润剂的制备工艺，涉及玻璃纤维生产技术领域，本发明中首先要准备原料，然后开启混合釜搅拌，按偶联剂、成膜剂、润滑剂、抗静电剂的顺序加入，再加入余量的水，充分搅匀，即可制得所需浸润剂，采用本发明方法制备出的浸润剂浸润性好，能够显著提高原丝的浸透性，性能稳定，经过该种浸润剂浸润后的原丝经拉丝工艺后，原丝基本保持良好的集束性、切割性和分散性，可快速浸透，短切丝光滑，不分叉，成毡性好，毡面均匀，不松散，毡的浸透性也好，且制备工艺简单，可操作性强，适于大批量生产。
Description
技术领域
本发明涉及玻璃纤维生产技术领域，具体涉及一种增强型玻璃纤维浸润剂的制备工艺。
背景技术
增强型浸润剂的组成主要包括成膜剂、润滑剂、抗静电剂和偶联剂。成膜剂对玻璃纤维原丝的性能起着决定性的作用，如原丝的集束性、切割性、分散性等，润滑剂主要用于改善浸润剂的拉丝作业性能，如阳离子型润滑剂虽然可以降低玻璃纤维的静摩擦系数，但会给原丝的浸透性带来负效应，抗静电剂可使玻璃纤维难以产生静电，常见的无机抗静电剂有氯化锂、硝酸锂、氯化铵。使用偶联剂是为了改善玻璃纤维聚合物的界面状态，提高复合材料性能如强度、耐水性和耐老化性，延长使用寿命。
采光板用玻璃纤维增强性浸润剂除了要具备良好的稳定性，满足拉丝等一系列作业性能外，还必须赋予原丝以下性能：良好的集束性、均匀的分散性、快速的浸透性、浸透无白丝透明性好、硬挺度在110～130mm之间为宜，因此研制出性能符合要求的浸润剂是当下研究人员需要解决的问题。
发明内容
本发明所要解决的问题是提供一种性能优异的增强型玻璃纤维浸润剂的制备工艺。
为了实现上述目的，本发明采取的技术方案为：所提供的一种增强型玻璃纤维浸润剂的制备工艺，包括如下步骤：
（1）称一定量的软化水，加入冰醋酸，调节好pH=3.0～4.0，在搅拌下缓缓加入偶联剂，搅拌至溶液澄清透明备用；
（2）称量好润滑剂，加入10倍热水（70～80℃），搅拌使其充分溶解，自然冷却至室温备用；
（3）称量好抗静电剂，加入10倍的软化水，搅拌使其充分溶解并过滤杂质，备用；
（4）将成膜剂1，2分别称量好，加入3倍的软化水充分搅匀备用；称好成膜剂3，加入3倍的软化水充分搅拌，使其溶解至溶液透明；
（5）开启混合釜搅拌，按偶联剂、成膜剂、润滑剂、抗静电剂的顺序加入，再加入余量的水，充分搅匀。
优选的，所述步骤（4）中所用的成膜剂1，2分别为聚氨酯成膜剂和环氧脂成膜剂。
优选的，所述步骤（4）中所用的偶联剂具体为A-174偶联剂。
采用本发明的技术方案，采用该种制备工艺制备出的浸润剂浸润性好，能够显著提高原丝的浸透性，性能稳定，经过该种浸润剂浸润后的原丝经拉丝工艺后，原丝基本保持良好的集束性、切割性和分散性，可快速浸透，短切丝光滑，不分叉，成毡性好，毡面均匀，不松散，毡的浸透性也好，且制备工艺简单，可操作性强，适于大批量生产。
具体实施方式
为使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面结合具体实施方式，进一步阐述本发明。
实施例1：
一种增强型玻璃纤维浸润剂的制备工艺，包括如下步骤：
（1）称一定量的软化水，加入冰醋酸，调节好pH=3.0，在搅拌下缓缓加入A-174偶联剂，搅拌至溶液澄清透明备用；
（2）称量好润滑剂，加入10倍热水（75℃），搅拌使其充分溶解，自然冷却至室温备用；
（3）称量好抗静电剂，加入10倍的软化水，搅拌使其充分溶解并过滤杂质，备用；
（4）将成膜剂1，2分别称量好，加入3倍的软化水充分搅匀备用；称好成膜剂3，加入3倍的软化水充分搅拌，使其溶解至溶液透明，其中，所述成膜剂1，2分别为聚氨酯成膜剂和环氧脂成膜剂；
（5）开启混合釜搅拌，按偶联剂、成膜剂、润滑剂、抗静电剂的顺序加入，再加入余量的水，充分搅匀。
基于上述，采用该种制备工艺制备出的浸润剂浸润性好，能够显著提高原丝的浸透性，性能稳定，经过该种浸润剂浸润后的原丝经拉丝工艺后，原丝基本保持良好的集束性、切割性和分散性，可快速浸透，短切丝光滑，不分叉，成毡性好，毡面均匀，不松散，毡的浸透性也好，且制备工艺简单，可操作性强，适于大批量生产。
显然本发明具体实现并不受上述方式的限制，只要采用了本发明的方法构思和技术方案进行的各种非实质性的改进，或未经改进将本发明的构思和技术方案直接应用于其它场合的，均在本发明的保护范围之内。
Claims (3)
1.一种增强型玻璃纤维浸润剂的制备工艺，其特征在于：包括如下步骤：
（1）称一定量的软化水，加入冰醋酸，调节好pH=3.0～4.0，在搅拌下缓缓加入偶联剂，搅拌至溶液澄清透明备用；
（2）称量好润滑剂，加入10倍热水（70～80℃），搅拌使其充分溶解，自然冷却至室温备用；
（3）称量好抗静电剂，加入10倍的软化水，搅拌使其充分溶解并过滤杂质，备用；
（4）将成膜剂1，2分别称量好，加入3倍的软化水充分搅匀备用；称好成膜剂3，加入3倍的软化水充分搅拌，使其溶解至溶液透明；
（5）开启混合釜搅拌，按偶联剂、成膜剂、润滑剂、抗静电剂的顺序加入，再加入余量的水，充分搅匀。
2.根据权利要求1所述的一种增强型玻璃纤维浸润剂的制备工艺，其特征在于：所述步骤（4）中所用的成膜剂1，2分别为聚氨酯成膜剂和环氧脂成膜剂。
3.根据权利要求1所述的一种增强型玻璃纤维浸润剂的制备工艺，其特征在于：所述步骤（4）中所用的偶联剂具体为A-174偶联剂。