CN104730612A - Polarized lens coiled material manufacturing technology - Google Patents
Polarized lens coiled material manufacturing technology Download PDFInfo
- Publication number
- CN104730612A CN104730612A CN201510128678.2A CN201510128678A CN104730612A CN 104730612 A CN104730612 A CN 104730612A CN 201510128678 A CN201510128678 A CN 201510128678A CN 104730612 A CN104730612 A CN 104730612A
- Authority
- CN
- China
- Prior art keywords
- sheet material
- sheet
- glue
- enter
- cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a polarized lens coiled material manufacturing technology. The manufacturing technology is characterized by including the following working procedures of 1cutting, wherein an enhanced sheet, a thickened colorless sheet, a polarized sheet, a colored sheet and a protective film sheet are cut in a laser cutting mode, and the lengths of the cut sheets are 520-600 mm; 2 cleaning, wherein all the sheets enter an alkaline bath from the unreeling end to be cleaned in an alkaline mode, then enter a hot water bath to be cleaned through circulating hot water and ultrasonic waves, enter three circulating cold water flushing tanks to be cleaned and finally enter a tunnel-type drying oven to dry the surfaces of the sheets, and then the sheets are reeled; 3 compositing. The polarized lens coiled material manufacturing technology has the advantages that heat expansion and cold contraction deformation among all layers is small, and the yield of polarized lens coiled materials is high.
Description
Technical field
The invention belongs to the preparation field of polarized lenses, specifically refer to a kind of coiled material preparation technology of polarized lenses.
Background technology
Polarized lenses, only allows the eyeglass that the light of a certain particular polarization in natural light passes exactly.Due to its filter action, put on it and see that thing can be dimmed.Impinging upon the glare in the equality direction on the water surface, land or snowfield in order to filter the sun, eyeglass adding the special coating of Vertical dimension, is just called polarized lenses, the most applicable outdoor exercises or use when driving.
The sheet materials such as colored pellets sheet material, polaroid sheet material, the colourless sheet material thickened, surface enhanced sheet sheet material are composited by the preparation technology of existing polarized lenses mutually.But in prior art, materials for each sheet material select and work flow has unreasonable part, cause the end product quality of coiled material poor, its reason is: the rate of expanding with heat and contract with cold of each sheet material all has larger difference, occur that the deformation force expanded with heat and contract with cold involves between the composite surface causing mutual compound tense to occur between each sheet material, cause shaping after coiled material local shrinkage, rejection rate is higher.
Summary of the invention
The object of the invention is the shortcoming and defect existed to overcome prior art, and provide reasonable, each sheet material composite surface of a kind of preparation technology to expand with heat and contract with cold to involve the coiled material preparation technology of the polarized lenses that impact is little, yield rate is high.
For achieving the above object, technical scheme of the present invention is
(1) cut, all adopt cut mode to cut into 520mm-600mm strengthening sheet sheet material, the colourless sheet material, polaroid sheet material, colored pellets sheet material and the diaphragm sheet material that thicken;
(2) clean, above-mentioned each sheet material is entered alkali groove respectively from unreeling end and carries out alkali cleaning, then reenter hot water storgae carry out circulating hot water cleaning and Ultrasonic Cleaning, then enter three circulate cold water flush grooves clean, finally enter tunnel type baking oven the water of sheet surface is dried, and then rolling
(3) compound, by the strengthening sheet sheet material after cleaning, the colourless sheet material thickened, polaroid sheet material, colored pellets sheet material and diaphragm sheet material are arranged from top to bottom successively, then glue wheel is imported into from unreeling end, open the glue outlet of glue wheel, make the composite surface of composite glue between each synusia material evenly applies, wherein the composite glue temperature strengthened between sheet sheet material and the colourless sheet material thickened controls at 60-62 DEG C, glue temperature between the colourless sheet material thickened and polaroid sheet material controls at 61-63 DEG C, glue temperature between polaroid sheet material and colored pellets sheet material controls at 42-43 DEG C, glue temperature between colored pellets sheet material and diaphragm sheet material controls at 67-68 DEG C, by glue pressure roller by mutual for each sheet material compound, and enter baking oven maintenance 40-45 DEG C of oven dry 1-2 hour, obtain finished product.
By this setting, in conjunction with the feature of expanding with heat and contract with cold of each layer material, the glue temperature of mutual for each sheet material compound accurately controlled, by this setting, the deformation of expanding with heat and contract with cold between each layer can be made little, and finished product rate is high.
Embodiment is described further the present invention below.
Embodiment
Below by embodiment, the present invention is specifically described; only be used to further illustrate the present invention; can not be interpreted as limiting the scope of the present invention, the technician in this field can make some nonessential improvement and adjustment according to the content of foregoing invention to the present invention.
Technique of the present invention comprises following operation:
(1) cut, all adopt cut mode to cut into 520mm-600mm strengthening sheet sheet material, the colourless sheet material, polaroid sheet material, colored pellets sheet material and the diaphragm sheet material that thicken; What the present embodiment strengthening sheet was chosen is the strengthening sheet that company is strengthened in Taiwan, guarantees skin hardness and wearing quality; Thicken without color chips choose be Lekai, Hebei Materials Co., Ltd without color chips, guarantee material sharpness; The polaroid of the Shi Shengbao Lay company that polaroid is chosen, guarantees that finished product degree of polarization anti-ultraviolet function strengthens; The colored pellets of what colored pellets was chosen is Wuxi A Ermei company, guarantees the homogeneity of colour system; What diaphragm was chosen is day east material diaphragm, guarantee the temperature tolerance of finished product and the noresidue of film.
(2) clean, above-mentioned each sheet material is entered alkali groove respectively from unreeling end and carries out alkali cleaning, then reenter hot water storgae carry out circulating hot water cleaning and Ultrasonic Cleaning, then enter three circulate cold water flush grooves clean, finally enter tunnel type baking oven the water of sheet surface is dried, and then rolling; This cleaning step of the present embodiment in conjunction with the sheet material cleaning drying device of a kind of polarized lenses of 201420484429.8 of the applicant's earlier application, can have extraordinary cleaning performance.
(3) compound, by the strengthening sheet sheet material after cleaning, the colourless sheet material thickened, polaroid sheet material, colored pellets sheet material and diaphragm sheet material are arranged from top to bottom successively, then glue wheel is imported into from unreeling end, open the glue outlet of glue wheel, make the composite surface of composite glue between each synusia material evenly applies, wherein the composite glue temperature strengthened between sheet sheet material and the colourless sheet material thickened controls at 60-62 DEG C, glue temperature between the colourless sheet material thickened and polaroid sheet material controls at 61-63 DEG C, glue temperature between polaroid sheet material and colored pellets sheet material controls at 42-43 DEG C, glue temperature between colored pellets sheet material and diaphragm sheet material controls at 67-68 DEG C, by glue pressure roller by mutual for each sheet material compound, and enter baking oven maintenance 40-45 DEG C of oven dry 1-2 hour, obtain finished product.Composite glue described in the present embodiment adopts the bonding glue of commercially available optical sheet, as 705 transparent glue.
Claims (1)
1. a coiled material preparation technology for polarized lenses, is characterized in that comprising following operation:
Cut, all adopt cut mode to cut into 520mm-600mm strengthening sheet sheet material, the colourless sheet material, polaroid sheet material, colored pellets sheet material and the diaphragm sheet material that thicken;
Cleaning, above-mentioned each sheet material is entered alkali groove respectively from unreeling end and carries out alkali cleaning, then reenter hot water storgae carry out circulating hot water cleaning and Ultrasonic Cleaning, then enter three circulate cold water flush grooves clean, finally enter tunnel type baking oven the water of sheet surface is dried, and then rolling
Compound, by the strengthening sheet sheet material after cleaning, the colourless sheet material thickened, polaroid sheet material, colored pellets sheet material and diaphragm sheet material are arranged from top to bottom successively, then glue wheel is imported into from unreeling end, open the glue outlet of glue wheel, make the composite surface of composite glue between each synusia material evenly applies, wherein the composite glue temperature strengthened between sheet sheet material and the colourless sheet material thickened controls at 60-62 DEG C, glue temperature between the colourless sheet material thickened and polaroid sheet material controls at 61-63 DEG C, glue temperature between polaroid sheet material and colored pellets sheet material controls at 42-43 DEG C, glue temperature between colored pellets sheet material and diaphragm sheet material controls at 67-68 DEG C, by glue pressure roller by mutual for each sheet material compound, and enter baking oven maintenance 40-45 DEG C of oven dry 1-2 hour, obtain finished product.