CN104725967A - Preparation method of water-soluble varnish containing Ag-carrying sepiolite - Google Patents
Preparation method of water-soluble varnish containing Ag-carrying sepiolite Download PDFInfo
- Publication number
- CN104725967A CN104725967A CN201510069560.7A CN201510069560A CN104725967A CN 104725967 A CN104725967 A CN 104725967A CN 201510069560 A CN201510069560 A CN 201510069560A CN 104725967 A CN104725967 A CN 104725967A
- Authority
- CN
- China
- Prior art keywords
- water
- sepiolite
- colored
- resin liquid
- silver
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of water-soluble varnish and discloses a preparation method of water-soluble varnish containing Ag-carrying sepiolite. The preparation method comprises the following steps: (1) preparing Ag-carrying sepiolite; (2) compounding silane coupling agent modified Ag-carrying sepiolite with a water-soluble resin liquid A and a water-soluble resin liquid B and then compounding a mixed resin liquid with deionized water, ethanol, tea saponin, water-soluble wax emulsion, a defoaming agent, a levelling agent and a buffer agent, thus preparing the water-soluble varnish containing Ag-carrying sepiolite. The preparation method has the beneficial effects that containing various antibacterial components, such as nano-silver, titanium dioxide and tea saponin, the water-soluble varnish prepared by the preparation method has strong bactericidal broad-spectrum property; the bactericidal components have synergistic effects, so that the bactericidal effects are greatly enhanced; the dispersibility of the bactericidal components in the water-soluble varnish is quite outstanding.
Description
Technical field
The present invention relates to technical field of water-base varnish, particularly relate to a kind of preparation method of the water-based gloss oil containing year silver-colored sepiolite.
Background technology
Water-based gloss oil is as a kind of emerging environmental protection printing material, be widely used in the printings such as food product pack, medical packaging, tobacco bale, books and periodicals, wall calendar, water-based gloss oil has outstanding surface gloss, because its solvent is mainly water, the volatile gases that can not be harmful to airborne release, relatively environmental protection, meets the current theory advocating environment protection health.Therefore water-based gloss oil is having wide development space from now on.
For the water-based gloss oil for higher fields of hygienic requirements such as tobacco bale, medical packaging, food product pack printings, require that water-based gloss oil self is nontoxic.Although but water-based gloss oil self has done harm to human non-toxic, tobacco bale, medical packaging and food pack easily grow germ, if water-based gloss oil has antibacterial, can effectively address this problem.
Wang Can just waits in " the Tipping Paper Antibacterial Water-based Ink research " delivered at " Packaging Engineering " and discloses a kind of antibacterial aqueous ink, and its formula is: diarylide yellow 5%, titanium dioxide 25%, water-borne acrylic resin liquid 45%, ethanol 15% and deionized water 10%.This water color ink has good printability on cork paper, and has good antibacterial effect.
Chinese invention patent CN 102477238B discloses a kind of water-based gloss oil, its formula comprises water, acrylate copolymer, titanium dioxide, a huge sum of money stone flour, water-ground limestone, kaolin, Yu Mufen, wetting dispersing agent, defoamer, flow agent, thickening material, multifunctional assistant, film coalescence aid and biocide mildewcide, this water-based gloss oil environment-protecting asepsis, alkali resistant mildew-resistant, protection against the tide.
Above two kinds of products but weak point be: antimicrobial component and other compositions are only physical mixed, although serve anti-microbial effect, dispersed and effect is all general.
Chinese invention patent CN 102952431A discloses a kind of cigarette cork paper water color ink and preparation method thereof, comprises one or more 0.5-1 parts in aqueous emulsifying sylvic oil 50-60 part+iron oxide pigment 10-20 part+deionized water 10-20 part+defoamer, anti-sedimentation agent, flow agent, wetting agent, antiseptic-germicide, wetting dispersing agent, surface tension agent aid.It is little that the cigarette cork paper water color ink of this invention has fineness, and rate of drying is fast, and denseness is high, viscosity is low, and dispersion stabilization is good, without scleroma property precipitation, without cohesion, the advantages such as noresidue peculiar smell, sterilant is directly allocated in water color ink by this invention, although this sterilant can play germicidal action, but the broad-spectrum of single sterilant is little, sterilization effect is limited, in addition may also can be harmful, causes side effect.
Summary of the invention
In order to solve the problems of the technologies described above, the invention provides a kind of preparation method of the cork paper water-based gloss oil containing year silver-colored sepiolite composite antibacterial material, water-based gloss oil sterilant dispersion effect prepared by the method is good, broad-spectrum is strong, antibacterial effect is strong.
Concrete technical scheme of the present invention is: a kind of preparation method of the water-based gloss oil containing year silver-colored sepiolite, and carry out as follows, wherein following material number is parts by weight,
(1) preparation of silver-colored sepiolite is carried:
Get 10 parts of sepiolites and to be made an addition to 100 parts of deionized water for stirring even, 10 parts of Silver Nitrates are added again in sepiolite solution, diluted nitric acid aqueous solution is dripped until pH value of solution is 3-4 after stirring, then 60 DEG C of stirring heating 3h are bathed at lucifuge Water Under, again by suspension first after through centrifugation, get solid matter washing, after vacuum-drying, get 10 parts of above-mentioned solid matters and 0.5 part of sodium borohydride joins in the aqueous sodium hydroxide solution of 0.01mol/L, add deionized water and regulate pH to 7.5-8, finally by stirring, solid is got in centrifugation, washing, dry, grind and obtain carrying silver-colored sepiolite.
Nanometer silver has very strong sterilizing ability, and broad-spectrum is strong.Sepiolite self structure is with trickle duct, there is stronger adsorptive power, to silver ions, there is stronger complex ability, after sepiolite carries out complexing to silver ions, again silver ion reduction is become more stable nano-Ag particles, thus on nano-silver loaded and sepiolite matrix.
(2) preparation of silane coupler modified year silver-colored sepiolite:
The silver-colored sepiolite that carries of above-mentioned gained is joined in aqueous ethanolic solution, and at 60 DEG C of temperature, carry out ultrasonic wave dispersion 0.5-1h, then silane coupling agent is added, continue insulation and ultrasonic wave dispersion 1-1.5h, suction filtration, washing, drying afterwards obtains silane coupler modified sepiolite, and the weight consumption ratio of above-mentioned year silver-colored sepiolite, aqueous ethanolic solution, silane coupling agent is: 1:20-30:3-5.
By silane coupling agent, modification is carried out to sepiolite, the consistency of sepiolite in water-base resin can be increased with dispersed.
(3) preparation of water-based gloss oil:
Silane coupler modified year silver-colored sepiolite of above-mentioned gained to be added in the mixed resin liquid of water-base resin liquid A and water-base resin liquid B and to stir, in mixed resin liquid, adding deionized water, ethanol, water-borne wax emulsion, tea saponin, defoamer, flow agent and buffer reagent again, obtaining the water-based gloss oil containing carrying silver-colored sepiolite finally by grinding distribution;
In wherein said water-based gloss oil, each component concentration is as follows:
40-50wt% water-base resin liquid A;
15-25 wt% water-base resin liquid B;
3-5%wt% silane coupler modified year silver-colored sepiolite;
1-2wt% tea saponin;
5-10 wt% deionized water;
5-15 wt% ethanol;
5-10 wt% water-borne wax emulsion;
1-2wt% defoamer;
1-2 wt% flow agent;
1-2 wt% buffer reagent.
Described water-base resin liquid A is water-borne acrylic resin liquid,
Described water-base resin liquid B is selected from the one in water-compatible amino resin liquid, maleic acid resin liquid, waterborne polyurethane resin liquid.
As preferably, described sepiolite is front through acid activation process in step (1), and acid activation method is as follows:
Get 20 parts of sepiolites, 200 parts of mass concentrations are that 2-5% hydrochloric acid soln successively joins in 200 parts of deionized waters, stir 3-5 hour at 40-50 DEG C of temperature after, filtration drying obtains acid activation sepiolite.
As preferably, described sepiolite is also through thermal activation treatment after acid activation, and process of thermal activation is as follows:
By the sepiolite after acid activation at 300-400 DEG C of roasting temperature 2-4 hour, obtain thermal activation sepiolite.
Acid activation and thermal activation can promote the adsorptive power of sepiolite, make the carrying capacity of sepiolite to nanometer silver stronger.
As preferably, described sepiolite crosses 500 mesh sieve.
As preferably, the water-borne acrylic resin liquid in described step (2) is nano-titanium dioxide modified water-borne acrylic resin liquid, and method of modifying is as follows:
A, nano titanium oxide, ethanol, deionized water and silane coupling agent are mixed after at 60 DEG C of water-bath back flow reaction 8-16h, then room temperature is down to, product is through centrifugation and washing, obtain silane coupler modified inorganic nano-particle, the weight consumption of described nano titanium oxide, ethanol, deionized water and silane coupling agent is than being 1:30-50:5-15:1-3.
B, 30-60 part deionized water and 1-3 part emulsifying agent are put into reactor and is heated to 80 DEG C, again by 20-40 part acrylic monomer, the silane coupler modified inorganic nano-particle of 15-25 part step a gained, stir after 3-5 part polyoxyethylene glycol and 0.25-0.5 part water soluble starter put into reactor, be incubated after 0.5-1 hour, 0.25-0.5 part water soluble starter is at the uniform velocity added in 2 hours, and then be incubated 4-8 hour, stir while add ammoniacal liquor and neutralize afterwards, pH value of solution is made to maintain between 7.5-8.5, vacuumize again and remove free ammoniacal liquor, finally filter and obtain nano-titanium dioxide modified water-borne acrylic resin liquid, above material number is parts by weight.
As preferably, the particle diameter of described nano titanium oxide is at 10-20nm.
As preferably, described acrylic monomer is selected from least two kinds in methyl methacrylate, methyl acrylate, vinylbenzene, β-dimethyl-aminoethylmethacrylate, hydroxyethyl methylacrylate, acrylamide.
Silane coupling agent is adopted to carry out modification to nano titanium oxide, can with acrylic monomer copolymerization, nano titanium oxide and hydroxyalkyl are incorporated on water-borne acrylic resin, nano titanium oxide after modified participates in polymerization directly, being evenly distributed in resin, better to the modified effect of water-borne acrylic resin.Nano titanium oxide has outstanding light aging resisting property and antibacterial and mouldproof performance.
The invention has the beneficial effects as follows: the present invention carries out complexing by sepiolite to silver ions, again silver ion reduction is become more stable nano-Ag particles, make nano-silver loaded on sepiolite, after year silver-colored sepiolite after silane coupler modified and water-base resin compound, nanometer silver can play its outstanding bacteriostasis.
Water-borne acrylic resin liquid and water-compatible amino resin liquid, maleic acid resin liquid or waterborne polyurethane resin liquid are carried out composite, has merged the advantage of various resin, compensate for the shortcoming of each genus resin.
Tea saponin is with the addition of in the formula of water-based gloss oil, tea saponin has outstanding emulsification, wetting, dispersing property, the effect of dispersion agent can be played in water-based gloss oil, moreover, tea saponin also has certain sterilizing function, to streptococcus aureus, intestinal bacteria etc., there is good rejection ability, tea saponin solvability in alcohol solution is good, as the dispersion agent of water-based gloss oil and antiseptic-germicide, there are bright prospects, although tea saponin has the problem of bubbling under oscillatory condition, just can be solved by defoamer.
Containing antimicrobial components such as nanometer silver, titanium dioxide and tea saponins in the present invention, water-based gloss oil is made to have very strong broad-spectrum, various sterilization component synergy, sterilization effect is also strengthened greatly, and the dispersiveness of each sterilization component in water-based gloss oil is very outstanding.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
A preparation method for water-based gloss oil containing year silver-colored sepiolite, carry out as follows, wherein following material number is parts by weight,
(1) preparation of silver-colored sepiolite is carried:
Get the sepiolite of 10 parts of mistake 500 mesh sieves and to be made an addition to 100 parts of deionized water for stirring even, 10 parts of Silver Nitrates are added again in sepiolite solution, diluted nitric acid aqueous solution is dripped until pH value of solution is 3-4 after stirring, then 60 DEG C of stirring heating 3h are bathed at lucifuge Water Under, again by suspension first after through centrifugation, get solid matter washing, after vacuum-drying, get 10 parts of above-mentioned solid matters and 0.5 part of sodium borohydride joins in the aqueous sodium hydroxide solution of 0.01mol/L, add deionized water and regulate pH to 7.5-8, finally by stirring, solid is got in centrifugation, washing, dry, grind and obtain carrying silver-colored sepiolite.
(2) preparation of silane coupler modified year silver-colored sepiolite
The silver-colored sepiolite that carries of above-mentioned gained is joined in aqueous ethanolic solution, and at 60 DEG C of temperature, carry out ultrasonic wave dispersion 0.75h, then silane coupling agent is added, continue insulation and ultrasonic wave dispersion 1.25h, suction filtration, washing, drying afterwards obtains silane coupler modified sepiolite, and the weight consumption ratio of above-mentioned year silver-colored sepiolite, aqueous ethanolic solution, silane coupling agent is: 1:25:4.
(3) preparation of water-based gloss oil:
Silane coupler modified year silver-colored sepiolite of above-mentioned gained to be added in the mixed resin liquid of water-borne acrylic resin liquid and water-compatible amino resin liquid and to stir, in mixed resin liquid, adding deionized water, ethanol, water-borne wax emulsion, tea saponin, defoamer, flow agent and buffer reagent again, obtaining the water-based gloss oil containing carrying silver-colored sepiolite finally by grinding distribution.
In wherein said water-based gloss oil, each component concentration is as follows:
45wt% water-borne acrylic resin liquid;
20 wt% water-compatible amino resin liquid;
4%wt% silane coupler modified year silver-colored sepiolite;
1.5wt% tea saponin;
7.5wt% deionized water;
10wt% ethanol;
7.5wt% water-borne wax emulsion;
1.5wt% defoamer;
1.5wt% flow agent;
1.5 wt% buffer reagents.
Embodiment 2
A preparation method for water-based gloss oil containing year silver-colored sepiolite, carry out as follows, wherein following material number is parts by weight,
(1) preparation of silver-colored sepiolite is carried:
Get the sepiolite of 20 parts of mistake 500 mesh sieves, 200 parts of mass concentrations are that 3% hydrochloric acid soln successively joins in 200 parts of deionized waters, at 45 DEG C of temperature, stir filtration drying after 4 hours obtain acid activation sepiolite.
Get 10 parts of acid activation sepiolites and to be made an addition to 100 parts of deionized water for stirring even, 10 parts of Silver Nitrates are added again in sepiolite solution, diluted nitric acid aqueous solution is dripped until pH value of solution is 3-4 after stirring, then 60 DEG C of stirring heating 3h are bathed at lucifuge Water Under, again by suspension first after through centrifugation, get solid matter washing, after vacuum-drying, get 10 parts of above-mentioned solid matters and 0.5 part of sodium borohydride joins in the aqueous sodium hydroxide solution of 0.01mol/L, add deionized water and regulate pH to 7.5-8, finally by stirring, solid is got in centrifugation, washing, dry, grind and obtain carrying silver-colored sepiolite.
(2) preparation of silane coupler modified year silver-colored sepiolite:
The silver-colored sepiolite that carries of above-mentioned gained is joined in aqueous ethanolic solution, and at 60 DEG C of temperature, carry out ultrasonic wave dispersion 0.75h, then silane coupling agent is added, continue insulation and ultrasonic wave dispersion 1.25h, suction filtration, washing, drying afterwards obtains silane coupler modified sepiolite, and the weight consumption ratio of above-mentioned year silver-colored sepiolite, aqueous ethanolic solution, silane coupling agent is: 1:25:4.
(3) preparation of water-based gloss oil:
Be at 60 DEG C of water-bath back flow reaction 12h by particle diameter after the nano titanium oxide of 15nm, ethanol, deionized water and silane coupling agent mix, then room temperature is down to, product is through centrifugation and washing, obtain silane coupler modified inorganic nano-particle, the weight consumption of described nano titanium oxide, ethanol, deionized water and silane coupling agent is than being 1:40:10:2.
B, 45 parts of deionized waters and 2 parts of emulsifying agents are put into reactor and is heated to 80 DEG C, again by 15 parts of methyl methacrylates, 15 parts of hydroxyethyl methylacrylates, the silane coupler modified inorganic nano-particle of 20 parts of step a gained, stir after 4 parts of polyoxyethylene glycol and 0.4 part of water soluble starter put into reactor, be incubated after 0.75 hour, 0.4 part of water soluble starter is at the uniform velocity added in 2 hours, and then be incubated 6 hours, stir while add ammoniacal liquor and neutralize afterwards, pH value of solution is made to maintain between 7.5-8.5, vacuumize again and remove free ammoniacal liquor, finally filter and obtain nano-titanium dioxide modified water-borne acrylic resin liquid, above material number is parts by weight.
C, silane coupler modified year silver-colored sepiolite of above-mentioned gained added in the mixed resin liquid of nano-titanium dioxide modified water-borne acrylic resin liquid and water-compatible amino resin liquid and stir, in mixed resin liquid, adding deionized water, ethanol, water-borne wax emulsion, tea saponin, defoamer, flow agent and buffer reagent again, obtaining the water-based gloss oil containing carrying silver-colored sepiolite finally by grinding distribution.
In wherein said water-based gloss oil, each component concentration is as follows:
The nano-titanium dioxide modified water-borne acrylic resin liquid of 45wt%;
20 wt% water-compatible amino resin liquid;
4%wt% silane coupler modified year silver-colored sepiolite;
1.5wt% tea saponin;
7.5wt% deionized water;
10wt% ethanol;
7.5wt% water-borne wax emulsion;
1.5wt% defoamer;
1.5wt% flow agent;
1.5 wt% buffer reagents.
Embodiment 3
A preparation method for water-based gloss oil containing year silver-colored sepiolite, carry out as follows, wherein following material number is parts by weight,
(1) preparation of silver-colored sepiolite is carried:
Get the sepiolite of 20 parts of mistake 500 mesh sieves, 200 parts of mass concentrations are that 2% hydrochloric acid soln successively joins in 200 parts of deionized waters, at 40 DEG C of temperature, stir filtration drying after 5 hours obtain acid activation sepiolite; By the sepiolite after acid activation 350 DEG C of roasting temperatures 3 hours, obtain thermal activation sepiolite.
Get 10 parts of thermal activation sepiolites and to be made an addition to 100 parts of deionized water for stirring even, 10 parts of Silver Nitrates are added again in sepiolite solution, diluted nitric acid aqueous solution is dripped until pH value of solution is 3-4 after stirring, then 60 DEG C of stirring heating 3h are bathed at lucifuge Water Under, again by suspension first after through centrifugation, get solid matter washing, after vacuum-drying, get 10 parts of above-mentioned solid matters and 0.5 part of sodium borohydride joins in the aqueous sodium hydroxide solution of 0.01mol/L, add deionized water and regulate pH to 7.5-8, finally by stirring, solid is got in centrifugation, washing, dry, grind and obtain carrying silver-colored sepiolite.
(2) preparation of silane coupler modified year silver-colored sepiolite:
The silver-colored sepiolite that carries of above-mentioned gained is joined in aqueous ethanolic solution, and at 60 DEG C of temperature, carry out ultrasonic wave dispersion 0.5h, then silane coupling agent is added, continue to be incubated also ultrasonic wave and disperse 1 h, suction filtration, washing, drying afterwards obtains silane coupler modified sepiolite, and the weight consumption ratio of above-mentioned year silver-colored sepiolite, aqueous ethanolic solution, silane coupling agent is: 1:20:3.
(3) preparation of water-based gloss oil:
Be at 60 DEG C of water-bath back flow reaction 8h by particle diameter after the nano titanium oxide of 10nm, ethanol, deionized water and silane coupling agent mix, then room temperature is down to, product is through centrifugation and washing, obtain silane coupler modified inorganic nano-particle, the weight consumption of described nano titanium oxide, ethanol, deionized water and silane coupling agent is than being 1:30:5:1.
B, 30 parts of deionized waters and 1 part of emulsifying agent are put into reactor and is heated to 80 DEG C, again by 7 parts of hydroxyethyl methylacrylates, 7 parts of vinylbenzene, 7 parts of Rocryl 410s, the silane coupler modified inorganic nano-particle of 15 parts of step a gained, stir after 3 parts of polyoxyethylene glycol and 0.25 part of water soluble starter put into reactor, be incubated after 0.5 hour, 0.25 part of water soluble starter is at the uniform velocity added in 2 hours, and then be incubated 4 hours, stir while add ammoniacal liquor and neutralize afterwards, pH value of solution is made to maintain between 7.5-8.5, vacuumize again and remove free ammoniacal liquor, finally filter and obtain nano-titanium dioxide modified water-borne acrylic resin liquid, above material number is parts by weight.
C, silane coupler modified year silver-colored sepiolite of above-mentioned gained added in the mixed resin liquid of nano-titanium dioxide modified water-borne acrylic resin liquid and waterborne polyurethane resin liquid and stir, in mixed resin liquid, adding deionized water, ethanol, water-borne wax emulsion, tea saponin, defoamer, flow agent and buffer reagent again, obtaining the water-based gloss oil containing carrying silver-colored sepiolite finally by grinding distribution.
In wherein said water-based gloss oil, each component concentration is as follows:
The nano-titanium dioxide modified water-borne acrylic resin liquid of 40wt%;
24 wt% waterborne polyurethane resin liquid;
3%wt% silane coupler modified year silver-colored sepiolite;
1wt% tea saponin;
10 wt% deionized waters;
10wt% ethanol;
10 wt% water-borne wax emulsions;
1wt% defoamer;
1wt% flow agent;
1 wt% buffer reagent.
Embodiment 4
A preparation method for water-based gloss oil containing year silver-colored sepiolite, carry out as follows, wherein following material number is parts by weight,
(1) preparation of silver-colored sepiolite is carried:
Get the sepiolite of 20 parts of mistake 500 mesh sieves, 200 parts of mass concentrations are that 5% hydrochloric acid soln successively joins in 200 parts of deionized waters, at 50 DEG C of temperature, stir filtration drying after 3 hours obtain acid activation sepiolite; By the sepiolite after acid activation 400 DEG C of roasting temperatures 2 hours, obtain thermal activation sepiolite.
Get 10 parts of thermal activation sepiolites and to be made an addition to 100 parts of deionized water for stirring even, 10 parts of Silver Nitrates are added again in sepiolite solution, diluted nitric acid aqueous solution is dripped until pH value of solution is 3-4 after stirring, then 60 DEG C of stirring heating 3h are bathed at lucifuge Water Under, again by suspension first after through centrifugation, get solid matter washing, after vacuum-drying, get 10 parts of above-mentioned solid matters and 0.5 part of sodium borohydride joins in the aqueous sodium hydroxide solution of 0.01mol/L, add deionized water and regulate pH to 7.5-8, finally by stirring, solid is got in centrifugation, washing, dry, grind and obtain carrying silver-colored sepiolite.
(2) preparation of silane coupler modified year silver-colored sepiolite:
The silver-colored sepiolite that carries of above-mentioned gained is joined in aqueous ethanolic solution, and at 60 DEG C of temperature, carry out ultrasonic wave disperse 1 h, then silane coupling agent is added, continue insulation and ultrasonic wave dispersion 1.5h, suction filtration, washing, drying afterwards obtains silane coupler modified sepiolite, and the weight consumption ratio of above-mentioned year silver-colored sepiolite, aqueous ethanolic solution, silane coupling agent is: 1:30:5.
(3) preparation of water-based gloss oil:
Be at 60 DEG C of water-bath back flow reaction 16h by particle diameter after the nano titanium oxide of 20nm, ethanol, deionized water and silane coupling agent mix, then room temperature is down to, product is through centrifugation and washing, obtain silane coupler modified inorganic nano-particle, the weight consumption of described nano titanium oxide, ethanol, deionized water and silane coupling agent is than being 1:50:15:3.
B, 60 parts of deionized waters and 3 parts of emulsifying agents are put into reactor and is heated to 80 DEG C, again by 20 parts of methyl methacrylates, 10 parts of β-dimethyl-aminoethylmethacrylates, 10 parts of acrylamides, the silane coupler modified inorganic nano-particle of 25 parts of step a gained, stir after 5 parts of polyoxyethylene glycol and 0.5 part of water soluble starter put into reactor, be incubated after 1 hour, 0.5 part of water soluble starter is at the uniform velocity added in 2 hours, and then be incubated 8 hours, stir while add ammoniacal liquor and neutralize afterwards, pH value of solution is made to maintain between 7.5-8.5, vacuumize again and remove free ammoniacal liquor, finally filter and obtain nano-titanium dioxide modified water-borne acrylic resin liquid, above material number is parts by weight.
C, silane coupler modified year silver-colored sepiolite of above-mentioned gained added in the mixed resin liquid of nano-titanium dioxide modified water-borne acrylic resin liquid and water-compatible amino resin liquid and stir, in mixed resin liquid, adding deionized water, ethanol, water-borne wax emulsion, tea saponin, defoamer, flow agent and buffer reagent again, obtaining the water-based gloss oil containing carrying silver-colored sepiolite finally by grinding distribution.
In wherein said water-based gloss oil, each component concentration is as follows:
The nano-titanium dioxide modified water-borne acrylic resin liquid of 50wt%;
15 wt% maleic acid resin liquid;
5%wt% silane coupler modified year silver-colored sepiolite;
2wt% tea saponin;
10wt% deionized water;
10 wt% ethanol;
5 wt% water-borne wax emulsions;
1wt% defoamer;
1wt% flow agent;
1 wt% buffer reagent.
Embodiment 5
A preparation method for cork paper water-based gloss oil containing year silver-colored sepiolite composite antibacterial material, carry out as follows, wherein following material number is parts by weight,
(1) preparation of silver-colored sepiolite is carried:
Get the sepiolite of 20 parts of mistake 500 mesh sieves, 200 parts of mass concentrations are that 4% hydrochloric acid soln successively joins in 200 parts of deionized waters, at 45 DEG C of temperature, stir filtration drying after 4 hours obtain acid activation sepiolite; By the sepiolite after acid activation 300 DEG C of roasting temperatures 4 hours, obtain thermal activation sepiolite.
Get 10 parts of thermal activation sepiolites and to be made an addition to 100 parts of deionized water for stirring even, 10 parts of Silver Nitrates are added again in sepiolite solution, diluted nitric acid aqueous solution is dripped until pH value of solution is 3-4 after stirring, then 60 DEG C of stirring heating 3h are bathed at lucifuge Water Under, again by suspension first after through centrifugation, get solid matter washing, after vacuum-drying, get 10 parts of above-mentioned solid matters and 0.5 part of sodium borohydride joins in the aqueous sodium hydroxide solution of 0.01mol/L, add deionized water and regulate pH to 7.5-8, finally by stirring, solid is got in centrifugation, washing, dry, grind and obtain carrying silver-colored sepiolite.
(2) preparation of silane coupler modified year silver-colored sepiolite:
The silver-colored sepiolite that carries of above-mentioned gained is joined in aqueous ethanolic solution, and at 60 DEG C of temperature, carry out ultrasonic wave disperse 0.5 h, then silane coupling agent is added, continue insulation and ultrasonic wave dispersion 1h, suction filtration, washing, drying afterwards obtains silane coupler modified sepiolite, and the weight consumption ratio of above-mentioned year silver-colored sepiolite, aqueous ethanolic solution, silane coupling agent is: 1:28:4.
(3) preparation of water-based gloss oil:
Be at 60 DEG C of water-bath back flow reaction 11h by particle diameter after the nano titanium oxide of 10nm, ethanol, deionized water and silane coupling agent mix, then room temperature is down to, product is through centrifugation and washing, obtain silane coupler modified inorganic nano-particle, the weight consumption of described nano titanium oxide, ethanol, deionized water and silane coupling agent is than being 1:35:8:2.
B, 50 parts of deionized waters and 2 parts of emulsifying agents are put into reactor and is heated to 80 DEG C, again by 10 parts of β-dimethyl-aminoethylmethacrylates, 10 parts of Rocryl 410s, 8 parts of vinylbenzene, the silane coupler modified inorganic nano-particle of 18 parts of step a gained, stir after 3 parts of polyoxyethylene glycol and 0.4 part of water soluble starter put into reactor, after being incubated 0. 5 hours, 0.4 part of water soluble starter is at the uniform velocity added in 2 hours, and then be incubated 5 hours, stir while add ammoniacal liquor and neutralize afterwards, pH value of solution is made to maintain between 7.5-8.5, vacuumize again and remove free ammoniacal liquor, finally filter and obtain nano-titanium dioxide modified water-borne acrylic resin liquid, above material number is parts by weight.
C, silane coupler modified year silver-colored sepiolite of above-mentioned gained added in the mixed resin liquid of nano-titanium dioxide modified water-borne acrylic resin liquid and waterborne polyurethane resin liquid and stir, in mixed resin liquid, adding deionized water, ethanol, water-borne wax emulsion, tea saponin, defoamer, flow agent and buffer reagent again, obtaining the water-based gloss oil containing carrying silver-colored sepiolite finally by grinding distribution.
In wherein said water-based gloss oil, each component concentration is as follows:
The nano-titanium dioxide modified water-borne acrylic resin liquid of 41wt%;
23wt% waterborne polyurethane resin liquid;
3%wt% silane coupler modified year silver-colored sepiolite;
1wt% tea saponin;
10wt% deionized water;
10wt% ethanol;
9wt% water-borne wax emulsion;
1wt% defoamer;
1wt% flow agent;
1 wt% buffer reagent.
The above; it is only preferred embodiment of the present invention; not the present invention is imposed any restrictions, every above embodiment is done according to the technology of the present invention essence any simple modification, change and equivalent transformation, all still belong to the protection domain of technical solution of the present invention.
Claims (7)
1. a preparation method for the water-based gloss oil containing year silver-colored sepiolite, it is characterized in that carrying out as follows, wherein following material number is parts by weight,
(1) preparation of silver-colored sepiolite is carried:
Get 10 parts of sepiolites and to be made an addition to 100 parts of deionized water for stirring even, 10 parts of Silver Nitrates are added again in sepiolite solution, diluted nitric acid aqueous solution is dripped until pH value of solution is 3-4 after stirring, then 60 DEG C of stirring heating 3h are bathed at lucifuge Water Under, again by suspension first after through centrifugation, get solid matter washing, after vacuum-drying, get 10 parts of above-mentioned solid matters and 0.5 part of sodium borohydride joins in the aqueous sodium hydroxide solution of 0.01mol/L, add deionized water and regulate pH to 7.5-8, finally by stirring, solid is got in centrifugation, washing, dry, grind and obtain carrying silver-colored sepiolite,
(2) preparation of silane coupler modified year silver-colored sepiolite:
The silver-colored sepiolite that carries of above-mentioned gained is joined in aqueous ethanolic solution, and at 60 DEG C of temperature, carry out ultrasonic wave dispersion 0.5-1h, then silane coupling agent is added, continue insulation and ultrasonic wave dispersion 1-1.5h, suction filtration, washing, drying afterwards obtains silane coupler modified sepiolite, and the weight consumption ratio of above-mentioned year silver-colored sepiolite, aqueous ethanolic solution, silane coupling agent is: 1:20-30:3-5;
(3) preparation of water-based gloss oil:
Silane coupler modified year silver-colored sepiolite of above-mentioned gained to be added in the mixed resin liquid of water-base resin liquid A and water-base resin liquid B and to stir, in mixed resin liquid, adding deionized water, ethanol, water-borne wax emulsion, tea saponin, defoamer, flow agent and buffer reagent again, obtaining the water-based gloss oil containing carrying silver-colored sepiolite finally by grinding distribution;
In wherein said water-based gloss oil, each component concentration is as follows:
40-50wt% water-base resin liquid A;
15-25 wt% water-base resin liquid B;
3-5%wt% silane coupler modified year silver-colored sepiolite;
1-2wt% tea saponin;
5-10 wt% deionized water;
5-15 wt% ethanol;
5-10 wt% water-borne wax emulsion;
1-2wt% defoamer;
1-2 wt% flow agent;
1-2 wt% buffer reagent;
Described water-base resin liquid A is water-borne acrylic resin liquid,
Described water-base resin liquid B is selected from the one in water-compatible amino resin liquid, maleic acid resin liquid, waterborne polyurethane resin liquid.
2. the preparation method of the water-based gloss oil containing year silver-colored sepiolite as claimed in claim 1, it is characterized in that, described sepiolite is front through acid activation process in step (1), and acid activation method is as follows:
Get 20 parts of sepiolites, 200 parts of mass concentrations are that 2-5% hydrochloric acid soln successively joins in 200 parts of deionized waters, stir 3-5 hour at 40-50 DEG C of temperature after, filtration drying obtains acid activation sepiolite.
3. the preparation method of the water-based gloss oil containing year silver-colored sepiolite as claimed in claim 2, it is characterized in that, described sepiolite is also through thermal activation treatment after acid activation, and process of thermal activation is as follows:
By the sepiolite after acid activation at 300-400 DEG C of roasting temperature 2-4 hour, obtain thermal activation sepiolite.
4. the preparation method of the water-based gloss oil containing year silver-colored sepiolite as described in one of claim 1-3, it is characterized in that, described sepiolite crosses 500 mesh sieve.
5. the preparation method of the water-based gloss oil containing year silver-colored sepiolite as claimed in claim 1, it is characterized in that, the water-borne acrylic resin liquid in described step (2) is nano-titanium dioxide modified water-borne acrylic resin liquid, and method of modifying is as follows:
A, nano titanium oxide, ethanol, deionized water and silane coupling agent are mixed after at 60 DEG C of water-bath back flow reaction 8-16h, then room temperature is down to, product is through centrifugation and washing, obtain silane coupler modified inorganic nano-particle, the weight consumption of described nano titanium oxide, ethanol, deionized water and silane coupling agent is than being 1:30-50:5-15:1-3;
B, 30-60 part deionized water and 1-3 part emulsifying agent are put into reactor and is heated to 80 DEG C, again by 20-40 part acrylic monomer, the silane coupler modified inorganic nano-particle of 15-25 part step a gained, stir after 3-5 part polyoxyethylene glycol and 0.25-0.5 part water soluble starter put into reactor, be incubated after 0.5-1 hour, 0.25-0.5 part water soluble starter is at the uniform velocity added in 2 hours, and then be incubated 4-8 hour, stir while add ammoniacal liquor and neutralize afterwards, pH value of solution is made to maintain between 7.5-8.5, vacuumize again and remove free ammoniacal liquor, finally filter and obtain nano-titanium dioxide modified water-borne acrylic resin liquid, above material number is parts by weight.
6. the preparation method of the water-based gloss oil containing year silver-colored sepiolite as claimed in claim 5, it is characterized in that, the particle diameter of described nano titanium oxide is at 10-20nm.
7. the preparation method of the water-based gloss oil containing year silver-colored sepiolite as claimed in claim 5, it is characterized in that, described acrylic monomer is selected from least two kinds in methyl methacrylate, methyl acrylate, vinylbenzene, β-dimethyl-aminoethylmethacrylate, hydroxyethyl methylacrylate, acrylamide.