CN104725914A - 一种金色美术涂料 - Google Patents

一种金色美术涂料 Download PDF

Info

Publication number
CN104725914A
CN104725914A CN201510171697.3A CN201510171697A CN104725914A CN 104725914 A CN104725914 A CN 104725914A CN 201510171697 A CN201510171697 A CN 201510171697A CN 104725914 A CN104725914 A CN 104725914A
Authority
CN
China
Prior art keywords
golden
artistic coating
emulsion
artistic
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510171697.3A
Other languages
English (en)
Inventor
叶光明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201510171697.3A priority Critical patent/CN104725914A/zh
Publication of CN104725914A publication Critical patent/CN104725914A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种金色美术涂料，包括如下组分：聚氯乙烯乳液，邻苯二甲酸二异辛酯，磷酸二甲酚酯，1:2型金属络合染料，氯化石蜡，聚有机硅氧烷乳液，去离子水，闪亮镭射粉，羟基聚丙烯酸酯乳液，硬脂酸钡，热熔胶粉，二氧化硅，改性鳞石英，消泡剂，pH调节剂，紫外吸收剂，乳化润湿剂，变性氨基有机硅，甘油松香酯。有益效果是：为水性浆料，原料易得，环保，制作方便，不产生对环境有毒害物质；添加氯化石蜡使烫金胶具有手感柔软；添加硬脂酸钡使烫金浆牢度坚固，耐溶剂性能和透光度好，抗拉裂性能出众，应用方式多样化。

Description

一种金色美术涂料
技术领域
本发明涉及一种金色美术涂料。
背景技术
美术涂料是涂料的众多品种之一，其中在现代装饰装潢、美术作品中，金色美术涂料的使用频率和使用量大幅增加。
以往的金色涂料大多数以铜、锌及铝等组成的合金，进过球磨粉碎，风选分级，抛光处理而成。这种金色涂料易燃易爆，不耐酸碱，耐候性差，容易氧化失色。并且色彩保护度较低，生产升本高，不易广泛使用。
发明内容
针对上述现有技术存在的不足，本发明的目的是提供一种手感柔软，牢度坚固，耐溶剂性能和透光度好，耐候性好的金色美术涂料。
为了实现上述目的，本发明所采用的技术方案是：一种金色美术涂料，由包括以下重量份数的原料制成：
聚氯乙烯乳液                    60-75，
邻苯二甲酸二异辛酯    22-30，
磷酸二甲酚酯          11-16，
1:2型金属络合染料     4-10，
氯化石蜡              3-5，
聚有机硅氧烷乳液      10-16，
去离子水                          5-10，
闪亮镭射粉            5-15，
羟基聚丙烯酸酯乳液    10-25，
硬脂酸钡                           1-5，
热熔胶粉                          10-20，
二氧化硅                          0.5-3，
改性鳞石英            5-10，
硅油乳液                           0.2-0.5，
pH调节剂                         0.8-1.5，
紫外吸收剂                        1-2，
乳化润湿剂                       0.3-1，
变性氨基有机硅        1-4
甘油松香酯                        0.5-2。
优选地，热熔胶粉内含有MI为700-900的EVA和20-28%的丙烯酸正丁酯。
优选地，所述紫外吸收剂为水杨酸苯酯或紫外线吸收剂UV-9。
优选地，所述乳化润湿剂为聚环氧乙烷酚醚或聚乙二醇甘油缩聚物。
本发明的有益效果是：
得到的涂料为水性浆料，原料易得，环保，制作方便，不产生对环境有毒害物质；添加氯化石蜡使烫金胶具有手感柔软；添加硬脂酸钡使烫金浆牢度坚固，耐溶剂性能和透光度好，抗拉裂性能出众，应用方式多样化；可赋予纺织品烫金优良的洗水牢度及闪亮的外观，体现纺织高贵的品质。
本发明的涂料，具有耐溶剂性好的优点，使得烫金产品遇溶剂其颜色不会析出，而且，烫金产品在生产和使用的过程中，不会出现色彩变淡的问题，从而也保证了涂料在涂布后的表面品质比较好。
    本发明的涂料，透光度好，并能够增强画作的耐热性和耐候性。
本发明的涂料，由于是通过特殊类型的金属络合染料和有机树脂进行搭配共同作为该烫金涂料的调色剂，能够调配出更多色彩，而且所调配出的色彩更加鲜艳，从而大大提高产品竞争力。
鳞石英表面被聚甲基丙烯酸甲酯改性后，将其用于涂料中改性后的鳞石英表面的聚合物与羟基聚丙烯酸酯和聚有机硅氧烷中各基团相互作用，进一步增加了涂膜的硬度、强度和耐刮擦性，延长了涂膜的使用寿命。
具体实施方式
以下结合具体实施例对本发明作进一步的说明。
实施例1
一种金色美术涂料，由包括以下重量份数的原料制成：
聚氯乙烯乳液                    60，
邻苯二甲酸二异辛酯    22，
磷酸二甲酚酯          11，
1:2型金属络合染料     4，
氯化石蜡              3，
聚有机硅氧烷乳液      10，
去离子水                          5，
闪亮镭射粉            5，
羟基聚丙烯酸酯乳液    10，
硬脂酸钡                           1，
热熔胶粉                          10，
二氧化硅                          0.5，
改性鳞石英            5，
硅油乳液                           0.2，
pH调节剂                         0.8，
紫外吸收剂                        1，
乳化润湿剂                       0.3，
变性氨基有机硅        1，
甘油松香酯                        0.5。
所述热熔胶粉内含有MI为700-900的EVA和20-28%的丙烯酸正丁酯。所述消泡剂为硅油乳液。所述紫外吸收剂为水杨酸苯酯或紫外线吸收剂UV-9。所述乳化润湿剂为聚环氧乙烷酚醚或聚乙二醇甘油缩聚物。
实施例2：
一种金色美术涂料，由包括以下重量份数的原料制成：
聚氯乙烯乳液                   70，
邻苯二甲酸二异辛酯    28，
磷酸二甲酚酯          13，
1:2型金属络合染料     8，
氯化石蜡              4，
聚有机硅氧烷乳液      13，
去离子水                          8，
闪亮镭射粉            10，
羟基聚丙烯酸酯乳液    18，
硬脂酸钡                           3，
热熔胶粉                          15，
二氧化硅                          2，
改性鳞石英            7，
硅油乳液                           0.3，
pH调节剂                         1，
紫外吸收剂                        1.5，
乳化润湿剂                       0.6，
变性氨基有机硅        2，
甘油松香酯                      1。
所述热熔胶粉内含有MI为700-900的EVA和20-28%的丙烯酸正丁酯。所述消泡剂为硅油乳液。所述紫外吸收剂为水杨酸苯酯或紫外线吸收剂UV-9。所述乳化润湿剂为聚环氧乙烷酚醚或聚乙二醇甘油缩聚物。
实施例3：
一种金色美术涂料，由包括以下重量份数的原料制成：
聚氯乙烯乳液                    75，
邻苯二甲酸二异辛酯    30，
磷酸二甲酚酯          16，
1:2型金属络合染料     10，
氯化石蜡              5，
聚有机硅氧烷乳液      16，
去离子水                          10，
闪亮镭射粉            15，
羟基聚丙烯酸酯乳液    25，
硬脂酸钡                           5，
热熔胶粉                          20，
二氧化硅                          3，
改性鳞石英            10，
硅油乳液                           0.5，
pH调节剂                         1.5，
紫外吸收剂                        2，
乳化润湿剂                       1，
变性氨基有机硅        4
甘油松香酯                        2。
所述热熔胶粉内含有MI为700-900的EVA和20-28%的丙烯酸正丁酯。所述消泡剂为硅油乳液。所述紫外吸收剂为水杨酸苯酯或紫外线吸收剂UV-9。所述乳化润湿剂为聚环氧乙烷酚醚或聚乙二醇甘油缩聚物。

Claims (4)

1.一种金色美术涂料，其特征在于，由包括以下重量份数的原料制成：
聚氯乙烯乳液                    60-75，
邻苯二甲酸二异辛酯    22-30，
磷酸二甲酚酯          11-16，
1:2型金属络合染料     4-10，
氯化石蜡              3-5，
聚有机硅氧烷乳液      10-16，
去离子水                          5-10，
闪亮镭射粉            5-15，
羟基聚丙烯酸酯乳液    10-25，
硬脂酸钡                           1-5，
热熔胶粉                          10-20，
二氧化硅                          0.5-3，
改性鳞石英            5-10，
硅油乳液                           0.2-0.5，
pH调节剂                         0.8-1.5，
紫外吸收剂                        1-2，
乳化润湿剂                       0.3-1，
变性氨基有机硅        1-4
甘油松香酯                        0.5-2。
2.根据权利要求1所述的金色美术涂料，其特征在于：热熔胶粉内含有MI为700-900的EVA和20-28%的丙烯酸正丙酯。
3.根据权利要求1所述的金色美术涂料，其特征在于：所述紫外吸收剂为水杨酸苯酯、紫外线吸收剂UV-9等。
4.根据权利要求1所述的金色美术涂料，其特征在于：所述乳化润湿剂为聚环氧乙烷酚醚或聚乙二醇甘油缩聚物。
CN201510171697.3A 2015-04-13 2015-04-13 一种金色美术涂料 Pending CN104725914A (zh)