CN104711094A - Novel emulsion cutting oil and production method thereof - Google Patents
Novel emulsion cutting oil and production method thereof Download PDFInfo
- Publication number
- CN104711094A CN104711094A CN201310678354.7A CN201310678354A CN104711094A CN 104711094 A CN104711094 A CN 104711094A CN 201310678354 A CN201310678354 A CN 201310678354A CN 104711094 A CN104711094 A CN 104711094A
- Authority
- CN
- China
- Prior art keywords
- oil
- novel emulsion
- sodium sulfonate
- raw materials
- production method
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a novel emulsion cutting oil. The novel emulsion cutting oil comprises following raw materials, by mass, 10 to 13% of petroleum sodium sulfonate, 5 to 7% of a soak degreasing unoiling special-purpose surfactant, 20 to 30% of chlorinated paraffin, 4 to 6% of lead naphthenate, 4 to 6% of triethanolamine oleic soap, 0.5 to 1% of a cleaning agent, 0.5 to 1% of a bactericide, and the balance No.45 transformer oil. A production method comprises following steps: weighed water is delivered into a reaction vessel, and is heated to 70 to 80 DEG C; a stirrer is turned on, and rotating speed is controlled to be 40r/min; weighed petroleum sodium sulfonate, the soak degreasing unoiling special-purpose surfactant, chlorinated paraffin, lead naphthenate, triethanolamine oleic soap, the cleaning agent, the bactericide, and the balance No.45 transformer oil are delivered into a reaction vessel successively and slowly, wherein after adding of each of the raw materials, stirring is carried out for 30min, and after adding of all the raw materials, stirring is carried out for another 3 to 4h; and an obtained mixture is cooled to room temperature, and is collected, filtered, and packaged.
Description
Technical field
The present invention relates to a kind of metal working fluid, especially a kind of novel emulsion machining oil and production method with good cooling performance, lubricity, cleaning performance and rustless property.
Background technology
In metal cutting process, the frictional force between cutter and workpiece can make work pieces process regional temperature rise to more than 1000 DEG C, and the portion faces load that cutter contacts with the uneven place of workpiece surface can reach 5000N/mm
2, so workpiece can cause local Welding Phenomena when cutting.In order to reduce cutting temperature and cutting force, just cutting fluid must be used in metal cutting process, water-base cutting fluid is conventional one, but the greatest problem existing for water-base cutting fluid used in current cutting process is exactly that antirust ability is poor, and workpiece surface easily corrosion occurs.
Summary of the invention
The present invention is the above-mentioned technical problem in order to solve existing for prior art, provides a kind of novel emulsion machining oil and the production method with good cooling performance, lubricity, cleaning performance and rustless property.
Technical solution of the present invention is: a kind of novel emulsion machining oil, it is characterized in that raw materials used and mass percent is as follows:
Petroleum sodium sulfonate 10 ~ 13%
Soak degreasing oil removing special surfactant 5 ~ 7%
Clorafin 20 ~ 30%
Lead naphthenate 4 ~ 6%
Trihydroxy ethylamine oleate soap 4 ~ 6%
Clean-out system 0.5 ~ 1%
Sterilant 0.5 ~ 1%
45# transformer oil surplus.
A kind of production method of above-mentioned novel emulsion machining oil, it is characterized in that carrying out as follows: join in reactor by calculating the water weighed, be heated to 70 ~ 80 DEG C and start agitator, control rotating speed 40 turns/min, then the petroleum sodium sulfonate weighed will be calculated, soak degreasing oil removing special surfactant, clorafin, lead naphthenate, trihydroxy ethylamine oleate soap, clean-out system, sterilant and 45# transformer oil join in reactor successively slowly, often add a kind of raw material and need stir 30min, whole raw material adds rear continuation stirring 3 ~ 4H, when temperature drops to room temperature, blowing filters and packages.
The high-quality raw material that optimum combination of the present invention is relevant, the mutual compatibility effect of each component, compared with the existing technology, have good cooling performance, lubricity, cleaning performance and rustless property.
Embodiment:
Embodiment 1:
Raw materials used and mass percent is as follows:
Petroleum sodium sulfonate 10 ~ 13%
Soak degreasing oil removing special surfactant 5 ~ 7%
Clorafin 20 ~ 30%
Lead naphthenate 4 ~ 6%
Trihydroxy ethylamine oleate soap 4 ~ 6%
Clean-out system 0.5 ~ 1%
Sterilant 0.5 ~ 1%
45# transformer oil surplus.
Production method is carried out as follows: join in reactor by calculating the water weighed, be heated to 70 ~ 80 DEG C and start agitator, control rotating speed 40 turns/min, then slowly join calculating the petroleum sodium sulfonate, soak degreasing oil removing special surfactant, clorafin, lead naphthenate, trihydroxy ethylamine oleate soap, clean-out system, sterilant and the 45# transformer oil that weigh successively in reactor, often add a kind of raw material and need stir 30min, whole raw material adds rear continuation stirring 3 ~ 4H, when temperature drops to room temperature, blowing filters and packages.
Soak degreasing oil removing special surfactant in above-mentioned raw materials is Qi Yanglong Science and Technology Ltd. of Shenzhen product, and product type is QYL-10F.
Embodiment 2:
Raw materials used and mass percent is as follows:
Petroleum sodium sulfonate 13%
Soak degreasing oil removing special surfactant 5%
Clorafin 20%
Lead naphthenate 4%
Trihydroxy ethylamine oleate soap 6%
Clean-out system 0.5%
Sterilant 1%
45# transformer oil surplus.
Production method is with embodiment 1.
During use, the embodiment of the present invention 1,2 is prepared the working fluid of mass percent 5 ~ 30%, respectively as metal works processing etc. such as carbon steel, cast iron, copper, steel, stainless steels, cooling performance, lubricity, cleaning performance and rustless property obtain significant raising, and rust-proof life was more than two weeks.
Claims (2)
1. a novel emulsion machining oil, is characterized in that raw materials used and mass percent is as follows:
Petroleum sodium sulfonate 10 ~ 13%
Soak degreasing oil removing special surfactant 5 ~ 7%
Clorafin 20 ~ 30%
Lead naphthenate 4 ~ 6%
Trihydroxy ethylamine oleate soap 4 ~ 6%
Clean-out system 0.5 ~ 1%
Sterilant 0.5 ~ 1%
45# transformer oil surplus.
2. the production method of a novel emulsion machining oil as claimed in claim 1, it is characterized in that carrying out as follows: join in reactor by calculating the water weighed, be heated to 70 ~ 80 DEG C and start agitator, control rotating speed 40 turns/min, then the petroleum sodium sulfonate weighed will be calculated, soak degreasing oil removing special surfactant, clorafin, lead naphthenate, trihydroxy ethylamine oleate soap, clean-out system, sterilant and 45# transformer oil join in reactor successively slowly, often add a kind of raw material and need stir 30min, whole raw material adds rear continuation stirring 3 ~ 4H, when temperature drops to room temperature, blowing filters and packages.