CN104697833A - 一种焦炭热态强度检验的标准试样及其制备方法 - Google Patents

一种焦炭热态强度检验的标准试样及其制备方法 Download PDF

Info

Publication number
CN104697833A
CN104697833A CN201510097386.7A CN201510097386A CN104697833A CN 104697833 A CN104697833 A CN 104697833A CN 201510097386 A CN201510097386 A CN 201510097386A CN 104697833 A CN104697833 A CN 104697833A
Authority
CN
China
Prior art keywords
coke
preparation
standard sample
described step
method described
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510097386.7A
Other languages
English (en)
Inventor
魏玉玲
贺秀丽
胡建军
孟科
任校丹
齐婳
段河良
张智
孙建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shandong Iron and Steel Group Co Ltd SISG
Original Assignee
Shandong Iron and Steel Group Co Ltd SISG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shandong Iron and Steel Group Co Ltd SISG filed Critical Shandong Iron and Steel Group Co Ltd SISG
Priority to CN201510097386.7A priority Critical patent/CN104697833A/zh
Publication of CN104697833A publication Critical patent/CN104697833A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种焦炭热态强度检验的标准试样及其制备方法，本发明通过试样的采取及大样挑选，试样的破碎、制备及储存等步骤制备标准试样，试样可评价测定结果的准确度，具有快捷、准确的优点，降低了比对成本，大大提高了测定结果的准确度和精密度，重复性误差由国家标准规定的反应性(CRI)＜2.4％，反应后强度(CSR)＜3.2％降低到反应性(CRI)＜1％，反应后强度(CSR)＜1.5％，为高炉和煤焦提供了精准数据。

Description

一种焦炭热态强度检验的标准试样及其制备方法
技术领域
本发明涉及一种焦炭热态强度检验的标准试样及制备方法，具体涉及一种适用于钢铁冶金行业的焦炭热态强度检验的标准试样剂制备方法，属于焦炭热态强度检验领域。
背景技术
焦炭热态强度是反应焦炭质量的关键指标，随着高炉冶炼程度的强化和操作水平的不断提高，对焦炭热态性能指标的要求更加严格，每增加或降低1-1.5％的热性能指标，高炉就要调整配料结构。此项指标的测定时间长，测定方法复杂，仪器多样，系统误差大，是钢铁企业关注的焦点，也是生产方、使用方和检验方争议的焦点。许多钢铁企业之间经常进行反应炉的比对检测，但都没有取得好的效果，因此焦炭热态强度检验的精准度对指导高炉生产起着举足轻重的作用。如何评价焦炭热态强度检验的精准度，国家标准GB/4000-2008规定了重复性测定误差反应性(CRI)＜2.4％，反应后强度(CSR)＜3.2％,这只是规定了热态强度检测的精密度，不能准确反应检验的准确度，容易造成系统误差，这样的规定根本满足不了高炉生产的需求。由于焦炭本身质量均匀性差的特点，检验一次需要200克试样，所以，目前国内还没有焦炭热态强度的标准试样。
发明内容
本发明针对现有技术中的不足，提供了一种焦炭热态强度检验的标准试样及制备方法，本发明大幅提高了工作效率，降低了检验成本，标定方法达到国内领先水平。本发明的技术方案如下：
一种焦炭热态强度检验的标准试样，制备方法如下：
(1)采用取样器在运输皮带上刮取焦炉焦炭；
(2)剔除泡焦和炉头焦，挑选颜色灰亮、致密性好的粒度为的焦炭；优选的，焦炭粒度为更优选的，焦炭粒度为
(3)用颚式破碎机将焦炭破碎到用的样筛进行筛分， 保留筛上物，同时，去掉片状焦炭和条状焦炭；优选的，用颚式破碎机将焦炭破碎到更优选的，用颚式破碎机将焦炭破碎到
(4)采用焦炭制球机将破碎焦炭制成一粒粒圆球状，用的样筛进行筛分，取筛上物；优选的，焦炭制球机破碎的粒度为
(5)分两次置于Ⅰ型转鼓中，以20r/min的转速，转2-3min，取出后再用圆孔筛筛分，取筛上物；优选的，以20r/min的转速，转2.5min。
(6)将制好的焦炭放入干燥箱，在160℃-180℃下烘干1.5-3h，取出冷却至室温，用圆孔筛筛分；优选的，在175℃下烘干2h。
通过本发明制备的焦炭热态强度检验的标准试样也在本发明的保护范围之内。
本发明与现有技术相比具有以下优点：
本发明用于校准热态反应装置的精度，及时发现影响测定结果的各种因素，可评价测定结果的准确度，具有快捷、准确的优点，降低了比对成本，用于与同行企业共同比对反应装置的稳定性，大大提高了测定结果的准确度和精密度，重复性误差由国家标准规定的反应性(CRI)＜2.4％，反应后强度(CSR)＜3.2％降低到反应性(CRI)＜1％，反应后强度(CSR)＜1.5％，为高炉和煤焦提供了精准数据。
具体实施方式
下面结合具体实施例来进一步描述本发明，本发明的优点和特点将会随着描述而更为清楚。但实施例仅是范例性的，并不对本发明的范围构成任何限制。本领域技术人员应该理解的是，在不偏离本发明的精神和范围下可以对本发明技术方案的细节和形式进行修改或替换，但这些修改和替换均落入本发明的保护范围内。
实施例1一种焦炭热态强度检验的标准试样，制备方法如下：
(1)采用取样器在运输皮带上刮取质量比较稳定的焦炉焦炭300Kg；
(2)剔除泡焦和炉头焦，挑选颜色灰亮、致密性好的粒度为的焦炭约100Kg；
(3)用颚式破碎机将100Kg焦炭破碎到左右，用的样 筛进行筛分，保留筛上物，同时，去掉片状焦炭和条状焦炭；
(4)采用焦炭制球机(粒度)将破碎焦炭制成一粒粒圆球状，用 的样筛进行筛分，取筛上物；
(5)分两次置于Ⅰ型转鼓中，以20r/min的转速，转50转，取出后再用 圆孔筛筛分，取筛上物；
(6)将制好的焦炭放入干燥箱，在175℃温度下烘干2h，取出冷却至室温，用圆孔筛筛分，由于量比较大，每次烘干1Kg。
实施例2一种焦炭热态强度检验的标准试样，制备方法如下：
(1)采用取样器在运输皮带上刮取焦炉焦炭；
(2)剔除泡焦和炉头焦，挑选颜色灰亮、致密性好的粒度为的焦炭；
(3)用颚式破碎机将焦炭破碎到用的样筛进行筛分，保留筛上物，同时，去掉片状焦炭和条状焦炭；
(4)采用焦炭制球机(粒度为)将破碎焦炭制成一粒粒圆球状，用的样筛进行筛分，取筛上物；
(5)分两次置于Ⅰ型转鼓中，以20r/min的转速，转3min，取出后再用 圆孔筛筛分，取筛上物；
(6)将制好的焦炭放入干燥箱，在165℃下烘干3h，取出冷却至室温，用圆孔筛筛分。
实施例3一种焦炭热态强度检验的标准试样，制备方法如下：
(1)采用取样器在运输皮带上刮取焦炉焦炭；
(2)剔除泡焦和炉头焦，挑选颜色灰亮、致密性好的粒度为的焦炭；
(3)用颚式破碎机将焦炭破碎到用的样筛进行筛分，保留筛上物，同时，去掉片状焦炭和条状焦炭；
(4)采用焦炭制球机(粒度为)将破碎焦炭制成一粒粒圆球状，用的样筛进行筛分，取筛上物；
(5)分两次置于Ⅰ型转鼓中，以20r/min的转速，转2min，取出后再用 圆孔筛筛分，取筛上物。
(6)将制好的焦炭放入干燥箱，在180℃下烘干1.5h，取出冷却至室温，用圆孔筛筛分。 
试验例1
对本发明制备的焦炭热态强度检验的标准试样的反应性(CRI)、反应后强度(CSR)的检测
检测步骤如下：
(1)从大样中缩分并称取200g±0.5g待用(焦炭质量记为m)。
(2)打开反应器上盖，先铺一层高约100mm的高铝球()，上面平放筛板。然后再装入已烘干的焦炭200g±0.5g(焦炭质量记为m)，再放上反应器上盖，应使反应器上盖上的电偶套管位于焦炭试样料层的中心，否则应调整放入高铝球的高度。然后用螺丝将上盖与反应筒体固定。将反应器放入电炉内，在反应器法兰四周围上炉顶砖，以减少散热。
(3)将反应器的进气管与气路柜连接好，排气管伸到室外，再插入热电偶。
(4)依次合上配电箱电源开关→仪器电源开关→显示器开关→计算机主机开关，双击计算机桌面上<焦炭反应性控制系统>图标，打开焦炭反应性测试系统窗口，点击“开始试验”按钮，仪器开始加热升温，升温速度一般控制在8-16℃/min之内。当焦炭料层中的温度达到400℃时，打开氮气瓶，自动调节氮气流量为0.8L/min，保护焦炭，防止其烧损。
(5)当料层中心温度达到1050℃时，仪器自动预热CO2气瓶出口处，当温度达到1100℃时，稳定10min后仪器自动切断氮气，打开CO2气瓶，自动调节CO2流量为5.0L/min，焦炭开始进行反应，反应时间为2h。通CO2后，料层中的温度应在5-10min内恢复1100℃±5℃，并在反应过程中一直保持在1100℃±5℃。
(6)反应2h后，CO2自动切断，反应终止，关闭CO2气瓶；仪器自动接通氮气，自动调节氮气流量为2L/min，使焦炭冷却。将反应器从反应炉中取出，放在支架上继续冷却。当焦炭冷却到100℃以下时，关闭氮气气瓶， 拔掉进气管，打开反应器上盖，倒出焦炭，进行称量,记为m1。
(7)反应后的焦炭全部倒入Ⅰ型转鼓，以20r/min转速转600转，然后取出焦炭，用10mm圆孔筛过筛，并称量筛上焦炭质量,记为m2。
(8)结果计算
焦炭反应性:
CRI(％)＝(m-m1)/m×100………………⑴
式中：m—焦炭试样质量，单位为克(g)；
m1—反应后残余焦炭质量，单位为克(g)。
反应后强度:
CSR(％)＝m2/m1×100……………………⑵
式中：m2—转鼓后大于10mm粒级焦炭质量，单位为克(g)；
m1—反应后残余焦炭的质量，单位为克(g)。
(9)结果分析，确定标准值
从大样中缩分出12份试样，分别用三台反应炉测定四次平行样，测定数据如1所示：
表1

Claims (9)

1.一种焦炭热态强度检验的标准试样的制备方法，其特征在于，具体步骤如下：
(1)采用取样器在运输皮带上刮取焦炉焦炭；
(2)剔除泡焦和炉头焦，挑选颜色灰亮、致密性好的粒度为的焦炭；
(3)用颚式破碎机将焦炭破碎到用的样筛进行筛分，保留筛上物，同时，去掉片状焦炭和条状焦炭；
(4)采用焦炭制球机将破碎焦炭制成一粒粒圆球状，用的样筛进行筛分，取筛上物；
(5)分两次置于Ⅰ型转鼓中，以20r/min的转速，转2-3min，取出后再用圆孔筛筛分，取筛上物；
(6)将制好的焦炭放入干燥箱，在160℃-180℃下烘干1.5-3h，取出冷却至室温，用圆孔筛筛分。
2.根据权利要求1中所述的制备方法，所述步骤(2)中焦炭粒度为
3.根据权利要求1中所述的制备方法，所述步骤(2)中焦炭粒度为
4.根据权利要求1中所述的制备方法，所述步骤(3)中用颚式破碎机将焦炭破碎到
5.根据权利要求1中所述的制备方法，所述步骤(3)中用颚式破碎机将焦炭破碎到
6.根据权利要求1中所述的制备方法，所述步骤(4)中焦炭制球机破碎的粒度为
7.根据权利要求1中所述的制备方法，所述步骤(5)中分两次置于Ⅰ型转鼓中，以20r/min的转速，转2.5min。
8.根据权利要求1中所述的制备方法，所述步骤(6)中将制好的焦炭放入干燥箱，在175℃下烘干2h。
9.如权利要求1-8任一项所述的制备方法制备的焦炭热态强度检验的标准试样。
CN201510097386.7A 2015-03-05 2015-03-05 一种焦炭热态强度检验的标准试样及其制备方法 Pending CN104697833A (zh)