CN104692749B - Anion heat-insulating construction material - Google Patents
Anion heat-insulating construction material Download PDFInfo
- Publication number
- CN104692749B CN104692749B CN201510020517.1A CN201510020517A CN104692749B CN 104692749 B CN104692749 B CN 104692749B CN 201510020517 A CN201510020517 A CN 201510020517A CN 104692749 B CN104692749 B CN 104692749B
- Authority
- CN
- China
- Prior art keywords
- anion
- terbium
- construction material
- parts
- insulating construction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of anion heat-insulating construction material, including the raw material of following weight parts: expanded perlite 30 50 parts；10 30 parts of magnesia；Portland cement 10 30 parts；Lauxite 10 30 parts；Neopelex 0.5 1.5 parts；Anionic additive 46 parts.The anion heat-insulating construction material thermal and insulating performance of the present invention is preferable, it is possible to effectively anion releasing, it is possible to purifies air, eliminate foreign flavor indoors and various pernicious gas.
Description
Technical field
The present invention relates to a kind of construction material, particularly relate to a kind of anion heat-insulating construction material.
Background technology
Insulation material generally refers to the thermal conductivity factor material less than or equal to 0.2.Insulation material Materials
Quickly, in industry and building, use good heat preservation technology and material, often can play and get twice the result with half the effort
Effect.Building often uses one ton of mineral wool insulating product, one ton of oil within 1 year, can be saved.
Insulation material can collect waste heat, the most steadily release, and graded is little, effectively reduces loss
Amount, room temperature can become, Winter protection all can play balanced action.In new building decoration and old building transforming, gram
Take the inadequate natural endowment disadvantages such as cracking of wall surface, condensation, mouldy, peeling；And it is safe and reliable overall with substrate
Bonding is random good, without cavity, it is to avoid negative blast tears and comes off.Effectively overcome board material splice back
The problems such as deformation Tile falling are stuck up outside rib, external corner.The free acid that in material, organic matter exists with main wall substrate
Reaction forms compound, penetrates in main wall micropore, forms community, it is ensured that dry state caking property, and change
Kind hygrometric state bonding value preserving rate, has fabulous caking property.Select floating bead, brucite fiber (tubular fiber) etc.
Raw material, form the hydrophobic microporous gap cavity structure of closing in its structure, as phase-change material carrier,
Can ensure that the long-term practicality of phase-change material.
Anion, to the health of people, long-lived and ecological significant impact, has been that domestic and international medical circle expert is led to
Cross clinical practice to be verified.Contemporary science has opened bioelectric secret, and each cell of organism is just
It is a micro cell, inside and outside cell membrane, has the potential difference of 50-90mv, if " cell battery " can not get
Sufficiently electric charge supplements, and the electric process of body is difficult to continue to, thus has influence on the normal of body and live
Dynamic, produce aging and early ageing.
Anion can not only facilitate human body synthesis and vitamin storage, strengthening and the physiological activity of human activin,
Therefore it is otherwise known as " air vitamin ", it is believed that it is as the vitamin of food, to human body and other
Biological vital movement has highly important impact, and after thunderstorm, the anion of air increases, people
Feel happy.And at air-conditioned room, because in air, anion processes through a series of air conditioning purges
Disappear with almost all after very long ventilation shaft, people's extended stationary periods wherein can feel uncomfortable in chest, dizzy,
Weak, operating efficiency and health status decline, and are referred to as " air conditioner comprehensive disease ".In medical circle, negative
Ion is identified it is to have kill germ and purify the effective means of air.Its mechanism essentially consists in anion
After being combined with bacterium, make bacterium produce change or the transfer of energy of structure, cause bacterial death, finally
Fall is sunken to ground.Medical research shows, in air, electronegative particulate makes oxygen content in blood increase, favorably
In the conveying of blood oxygen, absorb and utilize, there is promotion human metabolism, improving human immunological competence, increasing
Strong man's body flesh energy, the effect of regulation human body function balance.According to textual criticism, anion to 7 systems of human body,
Nearly more than 30 kinds of diseases have suppression, alleviate and auxiliary therapeutic action, especially to the health-care effect of human body more
Substantially.
In prior art, there is not a kind of heat-insulating construction material, it is possible to effectively anion releasing.
Summary of the invention
For the deficiencies in the prior art, the technical problem to be solved is to provide a kind of anion and protects
Temperature construction material.
A kind of anion heat-insulating construction material, including the raw material of following weight parts:
Preferably,
Described anionic additive, is made up of following materials by weight percentage: terbium oxide 3-5%, surplus
For tourmaline.
Described anionic additive, is made up of following materials by weight percentage: terbium oxide 3-5%, oxidation
Zirconium 1-2%, surplus is tourmaline.
Preferably, described terbium oxide is terbium sesquioxide and/or terbium peroxide.Optimally, described terbium
Oxide is the matter of the mixture of terbium sesquioxide and terbium peroxide, terbium sesquioxide and terbium peroxide
Amount ratio is 2:1-1:2.
Described anion heat-insulating construction material can use industry universal method to be prepared, such as will be each
Raw material mixing and stirring, can be prepared by the anion heat-insulating construction material of the present invention.
The anion heat-insulating construction material of the present invention, can add the 0.5-1.5 times of water weighed, and is in harmonious proportion uniformly, is coated with
It is overlying on metope.
The anion heat-insulating construction material thermal and insulating performance of the present invention is preferable, it is possible to effectively anion releasing,
Air can be purified, eliminate foreign flavor indoors and various pernicious gas.
Detailed description of the invention
By each raw material mixing and stirring, pulverize, can be prepared by the anion heat-insulating construction material of the present invention.
Table 1: anion heat-insulating construction material formula table unit: kilogram
In table 1, tourmaline selects the monocrystal tourmaline powder of Lingshou County swallow new mineral products process plants.
Test case:
" the JCT 2040-2010 anion function indoor decoration material " standard of employing, carries out air
Anion induces measurement examination, and concrete test data are shown in Table 2.
Table 2: negative aeroion induces measurement examination tables of data
| The negative aeroion amount of inducing, individual/s.cm2 | |
| Embodiment 1 | 905 |
| Embodiment 2 | 885 |
| Embodiment 3 | 870 |
| Embodiment 4 | 930 |
| Embodiment 5 | 895 |
| Embodiment 6 | 880 |
| Comparative example 1 | 65 |
Visible, the anion heat-insulating construction material of the present invention, it is possible to effectively anion releasing, it is possible to purify
Air, elimination foreign flavor indoors and various pernicious gas.
Comparing embodiment 1 and embodiment 2-3, comparing embodiment 4 and embodiment 5-6, use three oxidations two
The terbium oxide that terbium and terbium peroxide compound produces anion effect than the single terbium oxide of employing and substantially wants
Good, the two Synergistic.
Comparing embodiment 1 and embodiment 4, embodiment 2 and embodiment 5, embodiment 3 and embodiment 6,
It was unexpectedly observed that the anion heat-insulating construction material containing terbium oxide produces negative without zirconium oxide in filling a prescription
Ion effect is better than on the contrary and with the addition of zirconic effect.
The anion heat-insulating construction material of embodiment 1: thermal conductivity factor 0.095W/ (m.K), wet apparent close
Degree 405kg/m3.The anion heat-insulating construction material of embodiment 4: thermal conductivity factor 0.097W/ (m.K),
Wet apparent density 410kg/m3。
Above-described embodiment, it is thus understood that be merely to illustrate the present invention rather than limit the protection model of the present invention
Enclose.After having read the content that the present invention records, the present invention can be made various by those skilled in the art
Changing or amendment, these equivalence changes and modification fall into the scope of the claims in the present invention equally.
Claims (2)
1. an anion heat-insulating construction material, it is characterised in that include the raw material of following weight parts:
Described anionic additive, is made up of following materials by weight percentage: terbium oxide 3-5%, surplus
For tourmaline；
Described terbium oxide is the mixture of terbium sesquioxide and terbium peroxide, terbium sesquioxide and seven oxygen
The mass ratio changing four terbiums is 2:1-1:2.
2. an anion heat-insulating construction material, it is characterised in that include the raw material of following weight parts:
Described anionic additive, is made up of following materials by weight percentage: terbium oxide 3-5%, oxidation
Zirconium 1-2%, surplus is tourmaline；
Described terbium oxide is the mixture of terbium sesquioxide and terbium peroxide, terbium sesquioxide and seven oxygen
The mass ratio changing four terbiums is 2:1-1:2.