Negative ion heat-insulating construction material
Technical field
The present invention relates to a kind of material of construction, particularly relate to a kind of negative ion heat-insulating construction material.
Background technology
Lagging material generally refers to that thermal conductivity is less than or equal to the material of 0.2.Lagging material Materials is very fast, adopts good heat preservation technology and material, often can play a multiplier effect in industry and building.Often use one ton of mineral wool insulating product in building, one ton of oil within 1 year, can be saved.
Lagging material can collect waste heat, in good time steadily release, and graded is little, effectively the amount of reducing the wastage, and room temperature can become, Winter protection all can play poising action.In new building decoration and old building transforming, overcome the congenital defect disadvantages such as cracking of wall surface, condensation, mouldy, peeling; And safe and reliable entirety bond with substrate, randomness is good, without cavity, avoids negative blast tear and come off.Effectively overcome outside board material splice back rib, external corner and stick up the problems such as distortion Tile falling.The free acid that in material, organism and main wall substrate exist reacts and forms compound, infiltrates in main wall microporosity, forms community, guarantee dry state cohesiveness, and improves hygrometric state bonding value preserving rate, has fabulous cohesiveness.Select starting material such as drift pearl, brucite fiber (tubular fiber) etc., form closed hydrophobic microporous gap cavity structure in its structure, as phase change material carrier, the long-term practicality of phase change material can be guaranteed.
Negative ion to the health of people, longevity and ecological great effect, by domestic and international medical circle expert is verified by clinical practice.Contemporary science has opened bioelectric secret; each cell of organism is exactly a microbattery; the potential difference of 50-90mv is had inside and outside cytolemma; " cell battery " supplement if can not get sufficient electric charge; the electric process of body is just difficult to continue to maintain; thus have influence on the normal activity of body, produce aging and early ageing.
Negative ion can not only facilitate human body to synthesize and vitamin storage, the physiological activity of strengthening and human activin, therefore it is otherwise known as " air VITAMIN ", think that it is as the VITAMIN of food, very important impact is had on the vital movement of human body and other biological, after thunderstorm, the negative ion of air increases, and people feel happy.And at air-conditioned room, because negative ion in air almost all disappears after a series of air conditioning purge process and very long ventilator trunk, extended stationary periods can feel uncomfortable in chest, dizzy, weak to people wherein, working efficiency and healthy state declines, and is referred to as " air conditioner comprehensive disease ".In medical circle, it is the effective means having killing pathogenic bacteria and purify air that negative ion is identified.After its mechanism is mainly that negative ion is combined with bacterium, makes bacterium produce the change of structure or the transfer of energy, cause bacterial death, most final decline is sunken to ground.Medical research shows, in air, electronegative particulate makes oxygen level in blood increase, and is conducive to blood Oxygen deliver, absorption and utilization, has promotion human metabolism, improve human immunological competence, strengthens human body flesh energy, regulates the effect of human body function balance.According to textual criticism, negative ion is to human body 7 systems, and nearly 30 various diseases have suppression, alleviate and auxiliary therapeutic action, especially more obvious to the health-care effect of human body.
In prior art, there is not a kind of heat-insulating construction material, can effective anion releasing.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is to provide a kind of negative ion heat-insulating construction material.
A kind of negative ion heat-insulating construction material, comprises the raw material of following weight parts:
Preferably,
Described anionic additive, is made up of following materials by weight percentage: terbium oxide 3-5%, and surplus is tourmalinite.
Described anionic additive, is made up of following materials by weight percentage: terbium oxide 3-5%, zirconium white 1-2%, and surplus is tourmalinite.
Preferably, described terbium oxide is terbium sesquioxide and/or terbium peroxide.Optimally, described terbium oxide is the mixture of terbium sesquioxide and terbium peroxide, and the mass ratio of terbium sesquioxide and terbium peroxide is 2:1-1:2.
Described negative ion heat-insulating construction material can adopt industry universal method to be prepared, and such as, by each raw material mixing and stirring, can obtain negative ion heat-insulating construction material of the present invention.
Negative ion heat-insulating construction material of the present invention, can add the water that 0.5-1.5 doubly weighs, and is in harmonious proportion evenly, is coated on metope.
Negative ion heat-insulating construction material thermal and insulating performance of the present invention is better, can effective anion releasing, can purify air, eliminate foreign flavor indoors and various obnoxious flavour.
Embodiment
By each raw material mixing and stirring, pulverize, negative ion heat-insulating construction material of the present invention can be obtained.
Table 1: negative ion heat-insulating construction material formula table unit: kilogram
In table 1, tourmalinite selects the single crystal tourmaline powder of the new mineral products process plants of Lingshou County swallow.
Test case:
" the JCT 2040-2010 anion function indoor decoration material " standard of employing, carry out negative aeroion and induce measurement examination, concrete test data is in table 2.
Table 2: negative aeroion induces and measures examination data sheet
|
The negative aeroion amount of inducing, individual/s.cm
2 |
Embodiment 1 |
905 |
Embodiment 2 |
885 |
Embodiment 3 |
870 |
Embodiment 4 |
930 |
Embodiment 5 |
895 |
Embodiment 6 |
880 |
Comparative example 1 |
65 |
Visible, negative ion heat-insulating construction material of the present invention, can effective anion releasing, can purify air, eliminate foreign flavor indoors and various obnoxious flavour.
Comparing embodiment 1 and embodiment 2-3, comparing embodiment 4 and embodiment 5-6, adopt terbium sesquioxide and the composite terbium oxide of terbium peroxide to produce negative ion successful than the single terbium oxide of employing good, the two synergy.
Comparing embodiment 1 and embodiment 4, embodiment 2 and embodiment 5, embodiment 3 and embodiment 6, be surprised to find that, produces negative ion effect and be better than containing not adding zirconium white in the negative ion heat-insulating construction material formula of terbium oxide on the contrary and with the addition of zirconic effect.
The negative ion heat-insulating construction material of embodiment 1: thermal conductivity 0.095W/ (m.K), wet apparent density 405kg/m
3.The negative ion heat-insulating construction material of embodiment 4: thermal conductivity 0.097W/ (m.K), wet apparent density 410kg/m
3.
Above-described embodiment, is interpreted as only being not used in for illustration of the present invention limiting the scope of the invention.After the content of having read the present invention's record, those skilled in the art can make various changes or modifications the present invention, and these equivalence changes and modification fall into the scope of the claims in the present invention equally.