CN104675044A - 负离子环保壁纸及其制备方法 - Google Patents

负离子环保壁纸及其制备方法 Download PDF

Info

Publication number
CN104675044A
CN104675044A CN201510019277.3A CN201510019277A CN104675044A CN 104675044 A CN104675044 A CN 104675044A CN 201510019277 A CN201510019277 A CN 201510019277A CN 104675044 A CN104675044 A CN 104675044A
Authority
CN
China
Prior art keywords
negative ion
terbium
anion
kilograms
environmental protection
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201510019277.3A
Other languages
English (en)
Other versions
CN104675044B (zh
Inventor
袁娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Maya Forest (Beijing) International Technology Co., Ltd.
Original Assignee
NINGBO FREE TRADE ZONE TAOHONG CHEMICAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NINGBO FREE TRADE ZONE TAOHONG CHEMICAL TECHNOLOGY Co Ltd filed Critical NINGBO FREE TRADE ZONE TAOHONG CHEMICAL TECHNOLOGY Co Ltd
Priority to CN201510019277.3A priority Critical patent/CN104675044B/zh
Publication of CN104675044A publication Critical patent/CN104675044A/zh
Application granted granted Critical
Publication of CN104675044B publication Critical patent/CN104675044B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种负离子环保壁纸及其制备方法。所述负离子环保壁纸的制备方法，包括如下步骤和工艺条件：(1)制备负离子涂料：将12-20wt％聚丙烯酸酯、1-3wt％聚丙烯酸、5-15wt％铁镁电气石、2-6wt％铽氧化物、2-6wt％氧化十二钙十四铝和50-80wt％水，混合搅拌均匀，制得负离子涂料；(2)将上述负离子涂料涂覆在涤纶纤维基布上，烘烤。本发明制备的负离子环保壁纸不需要外界能量激发永久释放负离子，且释放负离子数量较高。

Description

负离子环保壁纸及其制备方法
技术领域
本发明涉及一种壁纸及其制备方法，尤其涉及一种负离子环保壁纸及其制备方法。
背景技术
负离子对人的健康、长寿及生态的重大影响，已为国内外医学界专家通过临床实践所验证。当代科学揭开了生物电的奥秘，生物体的每一个细胞就是一个微电池，细胞膜内外有50-90mv的电位差，如果“细胞电池”得不到充分的电荷补充，机体的电过程就难于继续维持，因而影响到机体的正常活动，产生老化和早衰。
负离子不仅能促成人体合成和储存维生素，强化和激活人体的生理活动，因此它又被称为"空气维生素"，认为它像食物的维生素一样，对人体及其他生物的生命活动有着十分重要的影响，如雷雨过后，空气的负离子增多，人们感到心情舒畅。而在空调房间，因空气中负离子经过一系列空调净化处理和漫长通风管道后几乎全部消失，人们在其中长期停留会感到胸闷、头晕、乏力、工作效率和健康状况下降，被称之为“空调综合症”。在医学界，负离子被确认是具有杀灭病菌及净化空气的有效手段。其机理主要在于负离子与细菌结合后，使细菌产生结构的改变或能量的转移，导致细菌死亡，最终降沉于地面。医学研究表明，空气中带负电的微粒使血中含氧量增加，有利于血氧输送、吸收和利用，具有促进人体新陈代谢，提高人体免疫能力，增强人体肌能，调节肌体功能平衡的作用。据考证，负离子对人体7个系统，近30多种疾病具有抑制、缓解和辅助治疗作用，尤其对人体的保健作用更为明显。
墙纸具有色彩多样，图案丰富，豪华气派、安全环保、施工方便、价格适宜等多种其它室内装饰材料所无法比拟的特点，是一种应用相当广泛的室内装修材料。在环境评价中，空气中负离子浓度被列为衡量空气质量的一个重要参数。
现有技术中，并未有一种壁纸，能够有效释放负离子。
发明内容
针对现有技术的不足，本发明所要解决的技术问题之一是提供一种负离子环保壁纸的制备方法。
本发明所要解决的技术问题之二是提供一种负离子环保壁纸。
本发明提供了一种负离子环保壁纸的制备方法，包括如下步骤和工艺条件：
(1)制备负离子涂料：将12-20wt％聚丙烯酸酯、1-3wt％聚丙烯酸、5-15wt％铁镁电气石、2-6wt％铽氧化物、2-6wt％氧化十二钙十四铝和50-80wt％水，混合搅拌均匀，制得负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，烘烤。
优选地，
所述聚丙烯酸酯，CAS号：57828-93-0。
所述聚丙烯酸，英文名称：SFoly(aSFryliSF aSFid)，CAS号：9003-01-4。
所述铁镁电气石的Fe2O3含量为12-16wt％、MgO含量为12-16wt％，平均粒径为1-2微米。
所述铽氧化物为三氧化二铽和/或七氧化四铽。最优地，所述铽氧化物为三氧化二铽和七氧化四铽的混合物，三氧化二铽和七氧化四铽的质量比为4:1-1:4。
所述氧化十二钙十四铝，化学式：12CaO·7Al2O3，简称：C12A7，CaO与Al2O3的摩尔比12:7。
本发明制备的负离子环保壁纸不需要外界能量激发永久释放负离子，且释放负离子数量较高。
具体实施方式
实施例中，铁镁电气石中Fe2O3含量12％(重量百分比)、MgO含量12％(重量百分比)，平均粒径为2微米。
实施例1：
负离子环保壁纸的制备方法，包括如下步骤和工艺条件：
(1)制备负离子涂料：将16公斤聚丙烯酸酯、2公斤聚丙烯酸、10公斤铁镁电气石、2公斤三氧化二铽、2公斤七氧化四铽、4公斤氧化十二钙十四铝，再加64公斤水至总重量到100公斤，混合搅拌均匀，制得负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，控制基布上涂料密度为150克/平方米，烘烤。
实施例2：
负离子环保壁纸的制备方法，包括如下步骤和工艺条件：
(1)制备负离子涂料：将16公斤聚丙烯酸酯、2公斤聚丙烯酸、10公斤铁镁电气石、4公斤三氧化二铽、4公斤氧化十二钙十四铝，再加64公斤水至总重量到100公斤，混合搅拌均匀，制得负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，控制基布上涂料密度为150克/平方米，烘烤。
实施例3：
负离子环保壁纸的制备方法，包括如下步骤和工艺条件：
(1)制备负离子涂料：将16公斤聚丙烯酸酯、2公斤聚丙烯酸、10公斤铁镁电气石、4公斤七氧化四铽、4公斤氧化十二钙十四铝，再加64公斤水至总重量到100公斤，混合搅拌均匀，制得负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，控制基布上涂料密度为150克/平方米，烘烤。
对比例1：
负离子环保壁纸的制备方法，包括如下步骤和工艺条件：
(1)制备负离子涂料：将16公斤聚丙烯酸酯、2公斤聚丙烯酸、14公斤铁镁电气石、2公斤三氧化二铽、2公斤七氧化四铽，再加64公斤水至总重量到100公斤，混合搅拌均匀，制得负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，控制基布上涂料密度为150克/平方米，烘烤。
对比例2：
负离子环保壁纸的制备方法，包括如下步骤和工艺条件：
(1)制备负离子涂料：将16公斤聚丙烯酸酯、2公斤聚丙烯酸、14公斤铁镁电气石、2公斤三氧化二铽、2公斤七氧化四铽，再加64公斤水至总重量到100公斤，混合搅拌均匀，制得负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，控制基布上涂料密度为150克/平方米，烘烤。
测试例：
采用《GBT 30128-2013纺织品负离子发生量的检测和评价》测定负离子发生量，见表1。
表1：负离子发生量测试数据表
  负离子发生量(个/cm3)
实施例1 875
实施例2 810
实施例3 795
对比例1 750
对比例2 595
可见，本发明能够有效释放负离子，能够净化空气。
比较实施例1与实施例2-3，采用三氧化二铽和七氧化四铽复配的铽氧化物比采用单一铽氧化物产生负离子效果明显要好，二者协同增效。
比较实施例1与对比例1-2，氧化十二钙十四铝和铁镁电气石复配的负离子环保壁纸配方产生负离子效果要好于单独氧化十二钙十四铝/铁镁电气石的产生负离子效果。
上述实施例，应理解为仅用于说明本发明而不用于限制本发明的保护范围。在阅读了本发明记载的内容之后，本领域技术人员可以对本发明作各种改动或修改，这些等效变化和修饰同样落入本发明权利要求所限定的范围。

Claims (5)

1.一种负离子环保壁纸的制备方法，其特征在于，包括如下步骤和工艺条件：
(1)制备负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，烘烤。
2.一种负离子环保壁纸的制备方法，其特征在于，包括如下步骤和工艺条件：
(1)制备负离子涂料：将12-20wt％聚丙烯酸酯、1-3wt％聚丙烯酸、5-15wt％铁镁电气石、2-6wt％铽氧化物、2-6wt％氧化十二钙十四铝和50-80wt％水，混合搅拌均匀，制得负离子涂料；
(2)将上述负离子涂料涂覆在涤纶纤维基布上，烘烤。
3.如权利要求2所述的负离子环保壁纸的制备方法，其特征在于，所述铽氧化物为三氧化二铽和/或七氧化四铽。
4.如权利要求3所述的负离子环保壁纸的制备方法，其特征在于，所述铽氧化物为三氧化二铽和七氧化四铽的混合物，三氧化二铽和七氧化四铽质量比为4:1-1:4。
5.一种负离子环保壁纸，其特征在于，采用权利要求2-4中任一项所述方法制备而成。
CN201510019277.3A 2015-01-15 2015-01-15 负离子环保壁纸及其制备方法 Active CN104675044B (zh)