A kind of manufacture craft of notebook touch-control glass cover-plate
Technical field
The present invention relates to a kind of glass cover-plate production technology, be specifically related to a kind of manufacture craft of notebook touch-control glass cover-plate.
Background technology
Trackpad many employings plastic sheet that the mouse beacon used in current notebook computer points to is made, and namely by sticking on the sheet plastic of one deck protection on touch-control electronic wiring board, is assembled into Trackpad.When our hand moves on the touch pad, it can sense computer screen accurately, moves to desired position, can realize sequence of operations function by actions such as clicks.But the Trackpad of this kind of structure, finds in use procedure, its sense of touch is not good enough, and hardness is low, easily wearing and tearing and distortion, and after Long contact time, its touch controllable function easily lost efficacy, and brought inconvenience to user, can not meet request for utilization.
In addition, the whole region of the Trackpad used in current notebook is all that the material of identical frosted degree is made, cannot identification left click and right click in touch area, therefore below touch area, arrange left click button and right click key area, but button has serviceable life, long period of operation easily causes the damage of button, and be not easy to operation use, and three part processing will be divided in manufacture craft, complex process, cost of manufacture is high.
Summary of the invention
For the technical matters of above-mentioned existence, the object of the invention is: propose a kind of manufacture craft simple, cost of manufacture is low, makes user can obtain the manufacture craft of the notebook touch-control glass cover-plate of better Consumer's Experience.
Technical solution of the present invention is achieved in that a kind of manufacture craft of notebook touch-control glass cover-plate, comprises following making step:
(1), by clean for former material glass cleaning;
(2), sawing sheet: the square glass cover plate A former material glass-cutting after cleaning being become multiple required apparent size;
(3), numerically-controlled machine finishing impression edging profiling: after glass cover-plate A being carried out on numerically-controlled machine finishing impression edging profiling process, obtain glass cover-plate B;
(4), cleaning, drying: glass cover-plate B is carried out the operation of cleaning post-drying;
(5), surface etching frosted process: first the central region of glass cover-plate B is smeared protective seam, then the areas at both sides of glass cover-plate is carried out surface etching frosted process; Carry out afterwards cleaning and drying; Then removing middle part protective seam, and areas at both sides is smeared protective seam, surface etching frosted process is carried out to middle part, finally cleans post-drying, obtain glass cover-plate C;
(6), tempering: glass cover-plate C is carried out chemical tempering process, makes its hardness reach more than 6H, obtained glass cover-plate D;
(7), Ultrasonic Cleaning;
(8), serigraphy: ink printing on glass cover-plate D lower surface, is obtained touch-control glass cover-plate E by employing screen process press, controls the conductive voltage of glass touch panel E by controlling ink thickness, and described ink thickness controls 15 to 30um;
(9), dry: touch-control glass cover-plate E is placed in baking machine and dries;
(10), Ultrasonic Cleaning.
Preferably, in described surface etching frosted treatment process, adopt anti-hydrofluorite coating as protective seam.
Preferably, in described surface etching frosted treatment process, the Ra value of central region is controlled at 0.2 ~ 0.8um; The Ra value of left area controls at 1.2 ~ 2.0 um; The Ra value of right area controls at 1.2 ~ 2.0 um.
Preferably, in described silkscreen process, below corresponding central region, left area and right area, adopt the ink printing of different colours, also can adopt same ink printing.
Due to the utilization of technique scheme, the present invention compared with prior art has following advantages:
The manufacture craft of notebook touch-control glass cover-plate of the present invention, the touch-control glass cover-plate obtained by this manufacture craft instead of the Trackpad that tradition adopts plastic sheet to assemble, eliminate former mechanical left click key and right click key, the serviceable life of effective raising notebook touch area now, and be made into the glass material of different frosted degree to divide the use region of glass cover-plate, make it have multiple operating function, make user can obtain better Consumer's Experience, and more complicated touch control operation can be supported, more various operational applications is provided to user, again improve its hardness and wearing quality, make it not yielding, and improve precision and the touch-control performance of Trackpad, reliability is high.
Accompanying drawing explanation
Below in conjunction with accompanying drawing, technical solution of the present invention is described further:
Accompanying drawing 1 is the structural drawing of the touch-control glass cover-plate that the manufacture craft of notebook touch-control glass cover-plate of the present invention obtains;
Wherein, 1, glass touch control layer; 2, decorative ink layer; 3, left area; 4, central region; 5, right area.
Embodiment
Below in conjunction with accompanying drawing, the present invention is described.
The structural drawing of the touch-control glass cover-plate obtained for the manufacture craft of notebook touch-control glass cover-plate of the present invention as shown in Figure 1, is formed primarily of glass touch control layer 1 and the decorative ink layer 2 be arranged on below glass touch control layer 1; Described glass touch control layer 1 is made up of left area 3, central region 4 and region, 5 three, right area, and left area 3 is mouse pointer left click region, and right area 5 is mouse pointer right click region.
The notebook manufacture craft of touch-control glass cover-plate, comprises following making step:
(1), by clean for former material glass cleaning;
(2), sawing sheet: the square glass cover plate A former material glass-cutting after cleaning being become multiple required apparent size;
(3), numerically-controlled machine finishing impression edging profiling: after glass cover-plate A being carried out on numerically-controlled machine finishing impression edging profiling process, obtain glass cover-plate B;
(4), cleaning, drying: glass cover-plate B is carried out the operation of cleaning post-drying;
(5), surface etching frosted process: first the central region of glass cover-plate B is smeared protective seam, then the areas at both sides of glass cover-plate is carried out surface etching frosted process; Carry out afterwards cleaning and drying; Then removing middle part protective seam, and areas at both sides is smeared protective seam, surface etching frosted process is carried out to middle part, finally cleans post-drying, obtain glass cover-plate C;
(6), tempering: glass cover-plate C is carried out chemical tempering process, makes its hardness reach more than 6H, obtained glass cover-plate D;
(7), Ultrasonic Cleaning;
(8), serigraphy: ink printing on glass cover-plate D lower surface, is obtained touch-control glass cover-plate E by employing screen process press, controls the conductive voltage of glass touch panel E by controlling ink thickness, and described ink thickness controls 15 to 30um;
(9), dry: touch-control glass cover-plate E is placed in baking machine and dries;
(10), Ultrasonic Cleaning.
In surface etching frosted treatment process, adopt anti-hydrofluorite coating as protective seam.
In surface etching frosted treatment process, the Ra value of central region is controlled at 0.6um; The Ra value of left area controls at 1.5 um; The Ra value of right area controls at 2.0 um.
In silkscreen process, below corresponding central region, left area and right area, adopt the ink printing of different colours, also can adopt same ink printing
Above-described embodiment is only for illustrating technical conceive of the present invention and feature; its object is to person skilled in the art can be understood content of the present invention and be implemented; can not limit the scope of the invention with this; all equivalences done according to Spirit Essence of the present invention change or modify, and all should be encompassed in protection scope of the present invention.