A kind of manufacture craft of notebook touch-control glass cover board
Technical field
The present invention relates to a kind of glass cover-plate production technology, and in particular to a kind of making of notebook touch-control glass cover board
Technique.
Background technology
The Trackpad that the control mouse used at present in laptop is directed toward is made of plastic sheet more, i.e., by touching
Stick on the sheet plastic of one layer of protection on control electronic circuit board, be assembled into Trackpad.When our hand moves on the touch pad
It can accurately sense computer screen, move to desired position, and sequence of operations work(can be achieved by actions such as clicks
Energy.But the Trackpad of this kind of structure, found during use, its sense of touch is not good enough, and hardness is low, easy to wear and deformation, long
Its touch controllable function easily fails after time contact, brings inconvenience to user, it is impossible to meet requirement.
In addition, the Trackpad whole region used at present in notebook is all made for the material of identical frosted degree, touching
Region can not recognize left click and right click, therefore left click button and right click key area are set below touch area, still
Button has service life, and long period of operation easily causes the damage of button, and is not easy to operate with, and in manufacture craft
On will a point three parts process, complex process, cost of manufacture is high.
The content of the invention
For above-mentioned technical problem, the purpose of the present invention is:It is simple to propose a kind of manufacture craft, cost of manufacture
It is low so that user can obtain the manufacture craft of the notebook touch-control glass cover board of more preferably user experience.
What the technical solution of the present invention was realized in:A kind of manufacture craft of notebook touch-control glass cover board,
Comprise the following steps that:
(1), former material glass cleaning is clean;
(2), sawing sheet:Square glass cover board A by the former material glass-cutting after cleaning into multiple required apparent sizes;
(3), numerically-controlled machine tool finishing impression edging profiling:Glass cover-plate A is carried out to finishing impression edging profiling processing on numerically-controlled machine tool
Afterwards, glass cover-plate B is obtained;
(4), cleaning, drying:Drying operation after glass cover-plate B is cleaned;
(5), surface etching frosted processing:The central region of glass cover-plate B is smeared into protective layer first, then by glass cover
The areas at both sides of plate carries out surface etching frosted processing;Cleaned and dried afterwards;Then middle part protective layer is removed, and will
Areas at both sides smears protective layer, and surface etching frosted processing is carried out to middle part, is dried after finally cleaning, obtains glass cover-plate C;
(6), tempering:Glass cover-plate C is subjected to chemical tempering processing, its hardness is reached more than 6H, glass cover-plate is made
D;
(7), ultrasonic cleaning;
(8), silk-screen printing:Ink is printed on glass cover-plate D lower surfaces using with screen process press, obtains touch-control glass
Glass cover board E, by controlling ink thickness to control the conductive voltage of glass touch panel E, the ink thickness control arrives 30um 15;
(9), drying:Touch-control glass cover board E is placed in baking machine and is dried;
(10), ultrasonic cleaning.
Preferably, in the surface etching frosted treatment process, using anti-hydrofluoric acid coating as protective layer.
Preferably, in the surface etching frosted treatment process, the Ra values of central region are controlled in 0.2~0.8um;It is left
The Ra values of border region are controlled in 1.2~2.0 um;The Ra values of right area are controlled in 1.2~2.0 um.
Preferably, in the silkscreen process, using not below corresponding central region, left area and right area
Ink with color prints, and can also use same ink to print.
Due to the utilization of above-mentioned technical proposal, the present invention has following advantages compared with prior art:
The manufacture craft of the notebook touch-control glass cover board of the present invention, passes through touch-control glass lid made from the manufacture craft
Plate instead of the Trackpad that conventionally employed plastic sheet assembles, and eliminates former mechanical left click key and right click key, effectively carries
The service life of high notebook touch area now, and the glass materials of different frosted degree is fabricated to divide glass cover-plate
Using area, makes it have a variety of operating functions so that user can obtain more preferably user experience, and can support more
Complicated touch control operation, provides a user more various operation application, again improves its hardness and wearability, make it not
It is yielding, and the precision and touch-control performance of Trackpad are improved, reliability is high.
Brief description of the drawings
Technical solution of the present invention is described further below in conjunction with the accompanying drawings:
Attached drawing 1 is the structure of touch-control glass cover board made from the manufacture craft of the notebook touch-control glass cover board of the present invention
Figure;
Wherein, 1, glass touch control layer;2nd, decorative ink layer;3rd, left area;4th, central region;5th, right area.
Embodiment
Illustrate the present invention below in conjunction with the accompanying drawings.
It is as shown in Figure 1 touch-control glass made from the manufacture craft of notebook touch-control glass cover board of the present invention
The structure chart of cover board, is mainly made of glass touch control layer 1 and the decorative ink layer 2 being arranged on below glass touch control layer 1;The glass
Glass touch control layer 1 is made of left area 3, central region 4 and the region of right area 5 three, and left area 3 is the left list of mouse pointer
Region is hit, right area 5 is mouse pointer right click region.
The notebook manufacture craft of touch-control glass cover board, comprises the following steps that:
(1), former material glass cleaning is clean;
(2), sawing sheet:Square glass cover board A by the former material glass-cutting after cleaning into multiple required apparent sizes;
(3), numerically-controlled machine tool finishing impression edging profiling:Glass cover-plate A is carried out to finishing impression edging profiling processing on numerically-controlled machine tool
Afterwards, glass cover-plate B is obtained;
(4), cleaning, drying:Drying operation after glass cover-plate B is cleaned;
(5), surface etching frosted processing:The central region of glass cover-plate B is smeared into protective layer first, then by glass cover
The areas at both sides of plate carries out surface etching frosted processing;Cleaned and dried afterwards;Then middle part protective layer is removed, and will
Areas at both sides smears protective layer, and surface etching frosted processing is carried out to middle part, is dried after finally cleaning, obtains glass cover-plate C;
(6), tempering:Glass cover-plate C is subjected to chemical tempering processing, its hardness is reached more than 6H, glass cover-plate is made
D;
(7), ultrasonic cleaning;
(8), silk-screen printing:Ink is printed on glass cover-plate D lower surfaces using with screen process press, obtains touch-control glass
Glass cover board E, by controlling ink thickness to control the conductive voltage of glass touch panel E, the ink thickness control arrives 30um 15;
(9), drying:Touch-control glass cover board E is placed in baking machine and is dried;
(10), ultrasonic cleaning.
In etching frosted treatment process on surface, using anti-hydrofluoric acid coating as protective layer.
In etching frosted treatment process on surface, the Ra values of central region are controlled in 0.6um;The Ra values control of left area
System is in 1.5 um;The Ra values of right area are controlled in 2.0 um.
In silkscreen process, the oil of different colours is used below corresponding central region, left area and right area
Ink print, can also use same ink to print
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar can understand present disclosure and be carried out, and it is not intended to limit the scope of the present invention, it is all according to the present invention
The equivalent change or modification that Spirit Essence is made, should all cover within the scope of the present invention.