CN104630550A - 高精度h65黄铜带生产工艺 - Google Patents

高精度h65黄铜带生产工艺 Download PDF

Info

Publication number
CN104630550A
CN104630550A CN201310549891.1A CN201310549891A CN104630550A CN 104630550 A CN104630550 A CN 104630550A CN 201310549891 A CN201310549891 A CN 201310549891A CN 104630550 A CN104630550 A CN 104630550A
Authority
CN
China
Prior art keywords
rolling
high precision
annealing
casting
process annealing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310549891.1A
Other languages
English (en)
Inventor
李保成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QINGDAO HONGTAI COPPER INDUSTRY Co Ltd
Original Assignee
QINGDAO HONGTAI COPPER INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QINGDAO HONGTAI COPPER INDUSTRY Co Ltd filed Critical QINGDAO HONGTAI COPPER INDUSTRY Co Ltd
Priority to CN201310549891.1A priority Critical patent/CN104630550A/zh
Publication of CN104630550A publication Critical patent/CN104630550A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高精度H65黄铜带生产工艺，工艺流程为：熔炼→铸造→加热→热轧→铣面→初轧→中间退火→中轧→切边→中间退火→预精轧→中间退火→精轧→成品退火→清洗→成品剪切→检查、包装。色泽美观、耐磨、耐蚀，表面光滑，无擦划伤，硬度一致性好。操作简单方便，工序流程易于控制。

Description

高精度H65黄铜带生产工艺
 
技术领域
本发明属于黄铜带生产工艺，具体涉及一种高精度H65黄铜带生产工艺。
 
背景技术
H65黄铜带因其色泽美观、耐磨、耐蚀，并具有良好的塑性加工性能而被广泛应用于五金、电子电讯等行业，拥有广阔的市场前景。由于技术进步及市场的发展，对H65黄铜带的产品精度要求逐步提高，高精度H65黄铜带的生产向着大锭坯、大卷重方向发展。目前多采用热轧法生产，但生产工艺及生产中常出现质量问题。
 
发明内容
为了克服现有技术领域存在的上述缺陷，本发明的目的在于，提供一种高精度H65黄铜带生产工艺，操作方便。
本发明提供的高精度H65黄铜带生产工艺，工艺流程为：熔炼→铸造→加热→热轧→铣面→初轧→中间退火→中轧→切边→中间退火→预精轧→中间退火→精轧→成品退火→清洗→成品剪切→检查、包装。其中，配料为T2一、二级，Cu-2，紫杂铜，H65一级，Zn；采用半连续铸造，硼砂覆盖，铸造速度8-15m/h，水压40-125KPa；在步进式煤气加热炉中加热，加热温度820-840℃；每面铣削量为0.25-0.35mm；酸洗剂8-15％的硫酸，温度为50-70℃；钝化剂为0.1-0.5％的BTA，钝化温度50-90℃。
本发明提供的高精度H65黄铜带生产工艺，其有益效果在于，色泽美观、耐磨、耐蚀，表面光滑，无擦划伤，硬度一致性好。操作简单方便，工序流程易于控制。
 
具体实施方式
下面结合一个实施例，对本发明提供的高精度H65黄铜带生产工艺进行详细的说明。
 
实施例
工艺流程为：熔炼→铸造→加热→热轧→铣面→初轧→中间退火→中轧→切边→中间退火→预精轧→中间退火→精轧→成品退火→清洗→成品剪切→检查、包装。其中，配料为T2一、二级，Cu-2，紫杂铜，H65一级，Zn；采用半连续铸造，硼砂覆盖，铸造速度8-15m/h，水压40-125KPa；在步进式煤气加热炉中加热，加热温度820-840℃；每面铣削量为0.25-0.35mm；酸洗剂8-15％的硫酸，温度为50-70℃；钝化剂为0.1-0.5％的BTA，钝化温度50-90℃。

Claims (1)

1.一种高精度H65黄铜带生产工艺，其特征在于，工艺流程为：熔炼→铸造→加热→热轧→铣面→初轧→中间退火→中轧→切边→中间退火→预精轧→中间退火→精轧→成品退火→清洗→成品剪切→检查、包装；其中，配料为T2一、二级，Cu-2，紫杂铜，H65一级，Zn；采用半连续铸造，硼砂覆盖，铸造速度8-15m/h，水压40-125KPa；在步进式煤气加热炉中加热，加热温度820-840℃；每面铣削量为0.25-0.35mm；酸洗剂8-15％的硫酸，温度为50-70℃；钝化剂为0.1-0.5％的BTA，钝化温度50-90℃。
CN201310549891.1A 2013-11-08 2013-11-08 高精度h65黄铜带生产工艺 Pending CN104630550A (zh)