CN104629552A - Environment-friendly type aqueous fireproof paint used for building - Google Patents
Environment-friendly type aqueous fireproof paint used for building Download PDFInfo
- Publication number
- CN104629552A CN104629552A CN201310555664.XA CN201310555664A CN104629552A CN 104629552 A CN104629552 A CN 104629552A CN 201310555664 A CN201310555664 A CN 201310555664A CN 104629552 A CN104629552 A CN 104629552A
- Authority
- CN
- China
- Prior art keywords
- parts
- environment
- friendly type
- type aqueous
- building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to an environment-friendly type aqueous fireproof paint used for building, which comprises the following raw materials by weight part: 10-20 parts of poly vinyl acetate emulsion, 10-20 parts of melamine, 10-15 parts of ammonium polyphosphate, 5-20 parts of pentaerythritol, 1-10 parts of triethanolamine, 1-5 parts of hydroxyethyl cellulose, 5-10 parts of mica powder and 20-40 parts of water. The environment-friendly type aqueous fireproof paint has good normal temperature usage performance and good high temperature foamability; expansion of a coating can generated under effect of flame, and a foam carbonaceous layer which is dozens of times of the original coating thickness is formed, external heat source effect on the base material can be effectively prevented, the combustion generation is prevented, and flame destroy effect on a base material is reduced.
Description
Technical field
The present invention relates to
oneplanting buildings coating, being specifically related to a kind of environment-friendly type aqueous frie retardant coating for building.
Background technology
The current frie retardant coating principal item of China has modification to gather amino fire-proof dilatation, expansive Fire Retardant Coating, steel structure fire-proof paint, outdoor steel structure frie retardant coating, expanded polystyrene veneer latex fire-proof paint, expanded polystyrene veneer inorganic fireproof coating, fire retarding wood protection coating, transparent fire-resisting paint, finishing fire retardant paint, Water-borne inflation type refractory coating etc.
Surging along with environmental protection cry, the solvent-borne type frie retardant coating that content of volatile organic compound is very high uses and is more and more strictly controlled, and aqueous fire-proof coating and high-solid level frie retardant coating obtain increasing concern and research.
Summary of the invention
In order to overcome above-mentioned existing problem, the object of the present invention is to provide a kind of environment-friendly type aqueous frie retardant coating for building, there is good normal temperature use properties, there is again good high temperature foaminess; Coating can expand under the effect of flame, forms the foam carbonaceous layer of larger than original coat-thickness tens times, effectively can stop the effect of external heat source to base material, thus can stop the generation of burning or reduce flame to the destruction of base material.
In order to achieve the above object, the technical scheme that the present invention takes is:
For the environment-friendly type aqueous frie retardant coating built, the ratio of its raw materials by weight portion is:
Polyvinyl acetate emulsion 10 parts-20 parts
Trimeric cyanamide 10 parts-20 parts
Ammonium polyphosphate 10 parts-15 parts
Tetramethylolmethane 5 parts-20 parts
Trolamine 1 part-10 parts
Natvosol 1 part-5 parts
Mica powder 5 parts-10 parts
20 parts-40 parts, water
The object of the present invention is to provide a kind of environment-friendly type aqueous frie retardant coating for building, there is good normal temperature use properties, there is again good high temperature foaminess; Coating can expand under the effect of flame, forms the foam carbonaceous layer of larger than original coat-thickness tens times, effectively can stop the effect of external heat source to base material, thus can stop the generation of burning or reduce flame to the destruction of base material.
embodiment:
Below in conjunction with specific embodiment, the present invention is described in detail.
Embodiment 1
For the environment-friendly type aqueous frie retardant coating built, the ratio of its raw materials by weight portion is:
Polyvinyl acetate emulsion 12 parts
Trimeric cyanamide 15 parts
Ammonium polyphosphate 10 parts
Tetramethylolmethane 10 parts
Trolamine 5 parts
Natvosol 2 parts
Mica powder 6 parts
40 parts, water
The object of the present invention is to provide a kind of environment-friendly type aqueous frie retardant coating for building, there is good normal temperature use properties, there is again good high temperature foaminess; Coating can expand under the effect of flame, forms the foam carbonaceous layer of larger than original coat-thickness tens times, effectively can stop the effect of external heat source to base material, thus can stop the generation of burning or reduce flame to the destruction of base material.
Claims (2)
1. the environment-friendly type aqueous frie retardant coating for building, is characterized in that: the ratio of its raw materials by weight portion is:
Polyvinyl acetate emulsion 10 parts-20 parts
Trimeric cyanamide 10 parts-20 parts
Ammonium polyphosphate 10 parts-15 parts
Tetramethylolmethane 5 parts-20 parts
Trolamine 1 part-10 parts
Natvosol 1 part-5 parts
Mica powder 5 parts-10 parts
20 parts-40 parts, water.
2. a kind of environment-friendly type aqueous frie retardant coating for building according to claim 1, the ratio of its raw materials by weight portion is:
Polyvinyl acetate emulsion 12 parts
Trimeric cyanamide 15 parts
Ammonium polyphosphate 10 parts
Tetramethylolmethane 10 parts
Trolamine 5 parts
Natvosol 2 parts
Mica powder 6 parts
40 parts, water.