CN104625672A - 锯片铣刀的制备方法 - Google Patents
锯片铣刀的制备方法 Download PDFInfo
- Publication number
- CN104625672A CN104625672A CN201410833664.6A CN201410833664A CN104625672A CN 104625672 A CN104625672 A CN 104625672A CN 201410833664 A CN201410833664 A CN 201410833664A CN 104625672 A CN104625672 A CN 104625672A
- Authority
- CN
- China
- Prior art keywords
- mass parts
- manufacturing
- grinding
- grinding cutting
- heat treatment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种锯片铣刀的制备方法,包括如下步骤:1)将粗料钢进行外圆磨、热处理、酸洗、轧制沟槽;2)在11.5质量份去离子水中投入0.6质量份单乙醇胺、1.3质量份十二烷基磺酸钠、0.9质量份环氧乙烷,搅拌混合充分,再依次加入1.3质量份硫代硫酸钠、2.5质量份二元酸酐,充分搅拌均匀,得研磨切削工作液;3)对铣刀坯料进行研磨切削,研磨切削过程中使用上述研磨切削工作液;4)热处理、表面处理。本发明锯片铣刀的制备方法,其制备的铣刀具有较高表面质量,铣刀锋利,能用于精加工,且铣刀尺寸精度高,稳定性好,产品合格率高。
Description
技术领域
本发明涉及锯片铣刀的制备方法。
背景技术
现有锯片铣刀的制备方法,其制备的铣刀,尺寸精度、稳定性、表面质量都有待提高,影响产品合格率。
发明内容
本发明的目的在于提供一种锯片铣刀的制备方法,其制备的铣刀具有较高表面质量,铣刀锋利,能用于精加工,且铣刀尺寸精度高,稳定性好,产品合格率高。
为实现上述目的,本发明的技术方案是设计一种锯片铣刀的制备方法,包括如下步骤:
1)将粗料钢进行外圆磨、热处理、酸洗、轧制沟槽;
2)在11.5质量份去离子水中投入0.6质量份单乙醇胺、1.3质量份十二烷基磺酸钠、0.9质量份环氧乙烷,搅拌混合充分,再依次加入1.3质量份硫代硫酸钠、2.5质量份二元酸酐,充分搅拌均匀,得研磨切削工作液;
3)对铣刀坯料进行研磨切削,研磨切削过程中使用上述研磨切削工作液;
4)热处理、表面处理。
本发明的优点和有益效果在于:提供一种锯片铣刀的制备方法,其制备的铣刀具有较高表面质量,铣刀锋利,能用于精加工,且铣刀尺寸精度高,稳定性好,产品合格率高。
具体实施方式
下面结合实施例,对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案,而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是:
一种锯片铣刀的制备方法,包括如下步骤:
1)将粗料钢进行外圆磨、热处理、酸洗、轧制沟槽;
2)在11.5质量份去离子水中投入0.6质量份单乙醇胺、1.3质量份十二烷基磺酸钠、0.9质量份环氧乙烷,搅拌混合充分,再依次加入1.3质量份硫代硫酸钠、2.5质量份二元酸酐,充分搅拌均匀,得研磨切削工作液;
3)对铣刀坯料进行研磨切削,研磨切削过程中使用上述研磨切削工作液;
4)热处理、表面处理。
以上所述仅是本发明的优选实施方式,应当指出,对于本技术领域的普通技术人员来说,在不脱离本发明技术原理的前提下,还可以做出若干改进和润饰,这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.锯片铣刀的制备方法,其特征在于,包括如下步骤:
1)将粗料钢进行外圆磨、热处理、酸洗、轧制沟槽;
2)在11.5质量份去离子水中投入0.6质量份单乙醇胺、1.3质量份十二烷基磺酸钠、0.9质量份环氧乙烷,搅拌混合充分,再依次加入1.3质量份硫代硫酸钠、2.5质量份二元酸酐,充分搅拌均匀,得研磨切削工作液;
3)对铣刀坯料进行研磨切削,研磨切削过程中使用上述研磨切削工作液;
4)热处理、表面处理。